CN103709895A - 一种用于管材的防腐涂料 - Google Patents

一种用于管材的防腐涂料 Download PDF

Info

Publication number
CN103709895A
CN103709895A CN201310643560.4A CN201310643560A CN103709895A CN 103709895 A CN103709895 A CN 103709895A CN 201310643560 A CN201310643560 A CN 201310643560A CN 103709895 A CN103709895 A CN 103709895A
Authority
CN
China
Prior art keywords
parts
thin slice
pipes
tubing
resins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310643560.4A
Other languages
English (en)
Other versions
CN103709895B (zh
Inventor
朱华明
陈德明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Jinbo New Materials Technology Co Ltd
Original Assignee
Jiangsu Jinbo New Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Jinbo New Materials Technology Co Ltd filed Critical Jiangsu Jinbo New Materials Technology Co Ltd
Priority to CN201310643560.4A priority Critical patent/CN103709895B/zh
Publication of CN103709895A publication Critical patent/CN103709895A/zh
Application granted granted Critical
Publication of CN103709895B publication Critical patent/CN103709895B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于管材的防腐涂料，属于管材技术领域。本发明通过树脂与金属薄片的融合，使金属薄片处于被树脂包覆的状态，在涂层中均匀分布，其层叠效果可形成良好的“搭接互锁-迷宫效应”，从而延长腐蚀介质到达基体路径，显著降低涂层的渗透率，更好地屏蔽环境中的水、氧等腐蚀因素，从而，提高了树脂的耐磨性，且使管材具有较好的耐候性。

Description

一种用于管材的防腐涂料
技术领域
本发明涉及一种防腐涂料，特别涉及一种用于管材的防腐涂料，属于管材技术领域。
背景技术
目前国内众多输送机械行业所用的托辊有钢管、尼龙管、钢外覆橡胶管、钢外套PE管等种类，单纯使用钢管做托辊存在易生锈、摩擦阻力大和对输送带磨损严重等缺陷；而使用尼龙管做托辊，生产长度只能在500mm之内，一旦加长则不能承载较大的负荷；钢管外覆橡胶虽然弹性较好，但同样存在摩擦阻力大的缺陷；而使用钢管外套聚乙烯管材，尽管在装配时可采用过盈配合使钢管与外套的聚乙烯管之间减少间隙，但由于在运行过程中经过摩擦后会产生一定的热量，而聚乙烯套管在受热后外径膨胀，从而出现打滑现象，使用寿命受到一定的影响。
发明内容
本发明的目的在于克服现有技术中的缺陷，提供一种用于管材的防腐涂料，该防腐涂料防腐性能好。
本发明是通过以下技术方案予以实现的。
一种用于管材的防腐涂料，由下列成分组成，按重量份计：
环氧树脂                    30-40份
氨基树脂                      10-20份
铝镁合金薄片                 10-25份
改性双酚环氧树                20-25份
酚醛环氧树脂                  15-20份
聚乙二醇                      0.5份
二氧化硅薄片                  2-5份
氧化锌薄片                    4- 5份
氯乙烯                         30-40份
滑石粉                         20-30份
溶剂                            45-60份
上述的用于管材的防腐涂料，其中，溶剂由乙酸乙酯和正丁醇组成，乙酸乙酯：正丁醇为2：1，按重量比计。
本发明中的金属薄片处于被树脂包覆的状态，在涂层中均匀分布，其层叠效果可形成良好的“搭接互锁-迷宫效应”，从而延长腐蚀介质到达基体路径，显著降低涂层的渗透率，更好地屏蔽环境中的水、氧等腐蚀因素。此此，通过铝镁合金薄片、二氧化硅薄片及氧化锌薄片相互融合使该金属薄片  具有较好的机械阻隔作用，且通过其自身的化学活动，在一定程度上与可将某些腐蚀介质发生电化学反应面将其逐步消耗，使之不能接触到基体表面，从而，延长了管材的使用寿命；且由于树脂中包覆有金属薄片，提高了树脂的耐磨性。
另外，由于金属薄片具有良好的耐热性，导热系数高，因此，可使管材具有较好的耐候性。
具体实施方式
以下通过具体实施例对本发明作进一步详细的说明。
实施例1
一种用于管材的防腐涂料，将环氧树脂30份、氨基树脂10-份、铝镁合金薄片10份、改性双酚环氧树20份、酚醛环氧树脂15份、聚乙二醇0.5份、二氧化硅薄片2份、氧化锌薄片4份、氯乙烯30份、滑石粉20份、溶剂45份组成，按重量份计，溶剂由乙酸乙酯和正丁醇组成，乙酸乙酯：正丁醇为2：1，按重量比计；在常温状态下，以转速为430r/min的条件，搅拌15分钟，各组成搅拌均匀即可。
实施例2
一种用于管材的防腐涂料，将环氧树脂35份、氨基树脂15份、铝镁合金薄片20份、改性双酚环氧树22份、酚醛环氧树脂15份、聚乙二醇0.5份、二氧化硅薄片5份、氧化锌薄片4份、氯乙烯35份、滑石粉25份、溶剂50份组成，按重量份计，溶剂由乙酸乙酯和正丁醇组成，乙酸乙酯：正丁醇为2：1，按重量比计，在常温状态下，以转速为430r/min的条件，搅拌15分钟，各组成搅拌均匀即可。
实施例3
一种用于管材的防腐涂料，将环氧树脂40份、氨基树脂20份、铝镁合金薄片25份、改性双酚环氧树25份、酚醛环氧树脂20份、聚乙二醇0.5份、二氧化硅薄片5份、氧化锌薄片4份、氯乙烯40份、滑石粉30份、溶剂60份组成，按重量份计，溶剂由乙酸乙酯和正丁醇组成，乙酸乙酯：正丁醇为2：1，按重量比计，在常温状态下，以转速为430r/min的条件，搅拌15分钟，各组成搅拌均匀即可。
二氧化硅薄片、氧化锌薄片和铝镁合金薄片的长度为4um,宽度为2um，厚度为1um。
本发明所述方法制备的复合管材的性能指标如下：
16小时表面磨耗率           <0.17%
悬臂梁冲击强度              ≥20KJ/m2
且可适用于-120℃。
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。

Claims (2)

1.一种用于管材的防腐涂料，其特征在于，由下列成分组成，按重量份计：
环氧树脂                    30-40份
氨基树脂                      10-20份
铝镁合金薄片                 10-25份
改性双酚环氧树                20-25份
酚醛环氧树脂                  15-20份
聚乙二醇                      0.5份
二氧化硅薄片                  2-5份
氧化锌薄片                    4- 5份
氯乙烯                         30-40份
滑石粉                         20-30份
溶剂                            45-60份。
2.如权利要求1所述的用于管材的防腐涂料，其特征在于，溶剂由乙酸乙酯和正丁醇组成，乙酸乙酯：正丁醇为2：1，按重量比计。
CN201310643560.4A 2013-12-05 2013-12-05 一种用于管材的防腐涂料 Expired - Fee Related CN103709895B (zh)