CN103695828A - 一种电解用阳极板快速时效硬化装置及方法 - Google Patents

一种电解用阳极板快速时效硬化装置及方法 Download PDF

Info

Publication number
CN103695828A
CN103695828A CN201310717785.XA CN201310717785A CN103695828A CN 103695828 A CN103695828 A CN 103695828A CN 201310717785 A CN201310717785 A CN 201310717785A CN 103695828 A CN103695828 A CN 103695828A
Authority
CN
China
Prior art keywords
temperature
electrolysis
positive plate
age hardening
constant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310717785.XA
Other languages
English (en)
Inventor
张治生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI NANNING LANTIAN ELECTRODE MATERIAL Co Ltd
Original Assignee
GUANGXI NANNING LANTIAN ELECTRODE MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI NANNING LANTIAN ELECTRODE MATERIAL Co Ltd filed Critical GUANGXI NANNING LANTIAN ELECTRODE MATERIAL Co Ltd
Priority to CN201310717785.XA priority Critical patent/CN103695828A/zh
Publication of CN103695828A publication Critical patent/CN103695828A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电解用阳极板快速时效硬化装置及方法，快速时效硬化装置包括恒温室、加热源、温度控制器和温测仪，恒温室内侧壁其中三面的下半部安装有加热源，恒温室外侧安装温度控制器，温度控制器与加热源连接，温测仪安装于恒温室内，温测仪与温度控制器连接。快速时效硬化方法将浇注后的阳极板毛坯放在100—120℃的环境中静置20—40分钟。本发明温度恒定有效保证电解用铅合金阳极板的快速时效硬化，提高产品质量，而且时间由此前的7—10天缩短至30分钟，极大地缩短了生产周期，提高生产效率。

Description

一种电解用阳极板快速时效硬化装置及方法
技术领域
本发明属于湿法冶金领域，具体涉及一种电解用阳极板快速时效硬化装置及方法。
背景技术
在合金元素经固溶处理后，获得过饱和固溶体，在随后的室温放置或低温加热保温时，第二相从过饱和固溶体中析出，引起强度、硬度以及物理和化学性能的显著变化，这一过程被称为时效。经研究证实，时效强化的实质是从过饱和固溶体中析出许多非常细小的沉淀物颗粒(一般是金属化合物，也可能是过饱和固溶体中的溶质原子在许多微小地区聚集)，形成一些体积很小的溶质原子富集区。在时效处理前进行固溶处理时，加热温度必须严格控制,以便使溶质原子能最大限度地固溶到固溶体中,同时又不致使合金发生熔化。许多合金固溶处理加热温度容许的偏差只有5℃左右。进行人工时效处理,必须严格控制加热温度和保温时间，才能得到比较理想的强化效果。使强度提高，塑性降低，这种现象称为机械时效。随时间的进展使屈服强度和抗拉强度提高，伸长率和冲击韧性降低的现象，称为时效硬化。
电解用阳极板一般为铅合金板，目前已知的电解用阳极板铅合金浇注毛坯后，不采用任何装置进行时效处理，而是在自然条件下放置7到10天，让阳极板自行硬化，再进行下一工序的加工。该方法存在两个问题，一是造成合金板的性能整体不一致；二是合金强度难以达到工艺要求，最终造成产品的硬度低、易断裂和使用寿命短等问题，而且放置时间过长，延长了生产周期。
发明内容
本发明目的在于提供一种电解用阳极板快速时效硬化装置及方法，以实现铅合金阳极板的快速时效硬化，增强阳极板强度，缩短生产周期，提高生产效率。
为实现上述目的，本发明电解用阳极板快速时效硬化装置，其特征在于：包括恒温室、加热源、温度控制器和温测仪，所述恒温室内侧壁其中三面的下半部安装有加热源，另一面安装有开启门，恒温室外侧安装温度控制器，温度控制器与加热源连接，所述温测仪安装于恒温室内，温测仪与温度控制器连接。
本发明电解用阳极板快速时效硬化方法，其特征在于：将浇注后的阳极板毛坯放在100—120℃的环境中静置20—40分钟。
所述的快速时效硬化方法为将浇注后的阳极板毛坯放在120℃的环境中静置30分钟。
本发明的实质性特点和进步是：
本发明利用恒温装置对电解用阳极板就行快速时效硬化，温度恒定有效保证硬化效果，实现电解用铅合金阳极板的快速时效硬化，提高产品质量，而且时间由此前的7—10天缩短至30分钟，极大地缩短了生产周期，提高生产效率。
附图说明
图1是本发明电解用阳极板快速时效硬化装置示意图。
图中零部件序号及名称：
恒温室1，加热源2，温测仪3，温度控制器4，阳极板毛坯5。
具体实施方式
以下结合附图描述本发明装置的实施结构。
本电解用阳极板快速时效硬化装置，恒温室1内侧壁其中三面的下半部安装有加热源2，另一面安装有开启门，恒温室1外侧安装温度控制器4，温度控制器4与加热源2连接，温测仪3安装于恒温室1内，温测仪3与温度控制器4连接。
下面通过具体实施例进一步说明本发明的技术方案。
实施例1
将浇注完成的铅合金阳极板毛坯5，流转至恒温室1内，利用温度控制器4将恒温室1内的温度调节至120℃。温测仪3检测恒温室1内的温度，并反馈至温度控制器4，温度控制器4控制加热源2的开闭，以保证恒温室1内的温度恒定，使合金阳极板达到快速时效硬化。放置30分钟后，取出铅合金阳极板毛坯5，进行下一道工序的加工。
实施例2
将浇注完成的铅合金阳极板毛坯5，流转至恒温室1内，利用温度控制器4将恒温室1内的温度调节至100℃。温测仪3检测恒温室1内的温度，并反馈至温度控制器4，温度控制器4控制加热源2的开闭，以保证恒温室1内的温度恒定，使合金阳极板达到快速时效硬化。放置40分钟后，取出铅合金阳极板毛坯5，进行下一道工序的加工。

Claims (3)

1.一种电解用阳极板快速时效硬化装置，其特征在于：包括恒温室1、加热源2、温度控制器4和温测仪3，所述恒温室1内侧壁其中三面的下半部安装有加热源2，另一面安装有开启门，恒温室1外侧安装温度控制器4，温度控制器4与加热源2连接，所述温测仪3安装于恒温室1内，温测仪3与温度控制器4连接。
2.一种电解用阳极板快速时效硬化方法，其特征在于：将浇注后的阳极板毛坯5放在100—120℃的环境中静置20—40分钟。
3.根据权利要求2所述的电解用阳极板快速时效硬化方法，其特征在于：将浇注后的阳极板毛坯5放在120℃的环境中静置30分钟。
CN201310717785.XA 2013-12-24 2013-12-24 一种电解用阳极板快速时效硬化装置及方法 Pending CN103695828A (zh)