CN103693934A - 一种用于建筑领域内的保温砂浆 - Google Patents
一种用于建筑领域内的保温砂浆 Download PDFInfo
- Publication number
- CN103693934A CN103693934A CN201310676587.3A CN201310676587A CN103693934A CN 103693934 A CN103693934 A CN 103693934A CN 201310676587 A CN201310676587 A CN 201310676587A CN 103693934 A CN103693934 A CN 103693934A
- Authority
- CN
- China
- Prior art keywords
- parts
- building field
- thermal insulation
- insulation mortar
- adjusted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于建筑领域内的保温砂浆,其是由下述重量份的原料制得:硅酸盐水泥30-35、氯氧镁水泥8-12、沙子20-30、浓度为10-15%的双氧水0.5-1.5,粉状有机硅消泡剂1-2、PP纤维2-3、废铝粉0.1-0.2、氧化石蜡皂0.1-0.2、丁香油0.2-0.4,维生素C1-2、生石灰2-4、氢氧化钠2-4、膨胀珍珠岩10-15,改性硅藻土10-12。
Description
技术领域
本发明涉及保温砂浆领域,确切地说是一种用于建筑领域内的保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料,以水泥为胶凝料,掺和一些改性添加剂,经生产企业搅拌混合而制成的一种预拌干粉砂浆。用于构筑建筑表面保温层的一种建筑材料。
发明内容
本发明的目的在于提供一种用于建筑领域内的保温砂浆。
上述目的通过以下方案实现:
一种用于建筑领域内的保温砂浆,其特征在于:其是由下述重量份的原料制得:硅酸盐水泥30-35、氯氧镁水泥8-12、沙子20-30、浓度为10-15%的双氧水0.5-1.5,粉状有机硅消泡剂1-2、PP纤维2-3、废铝粉0.1-0.2、氧化石蜡皂0.1-0.2、丁香油0.2-0.4,维生素C1-2、生石灰2-4、氢氧化钠2-4、膨胀珍珠岩10-15,改性硅藻土10-12。
所述的一种用于建筑领域内的保温砂浆,其特征在于:
所述的改性硅藻土的制备方法为:
取硅藻土,于600-700℃下烧结2-4小时,与相当于其重量份1-2%的咪唑啉、1-2%的丙烯酸甲酯、1-2%的抗氧剂2246混匀,再加加适量水,搅拌均匀,成悬浮液,再加浓度为10-15%的盐酸溶液调PH为5-6,研磨浆料至600-800目后,再加氢氧化钠调为中性,喷雾干燥,得粉末。
本发明的有益效果为:本发明通过调成保温砂浆的原料组分以及配比,从而制得了施工简易、性能好,涂抹在墙体外不易开裂的保温砂浆。
具体实施方式
一种用于建筑领域内的保温砂浆,其是由下述重量kg的原料制得:硅酸盐水泥35、氯氧镁水泥12、沙子30、浓度为15%的双氧水1.5,粉状有机硅消泡剂2、PP纤维3、废铝粉0.2、氧化石蜡皂0.2、丁香油0.4,维生素C2、生石灰4、氢氧化钠4、膨胀珍珠岩15,改性硅藻土12。
所述的改性硅藻土的制备方法为:
取硅藻土,于700℃下烧结2小时,与相当于其重量2%的咪唑啉、2%的丙烯酸甲酯、1%的抗氧剂2246混匀,再加加适量水,搅拌均匀,成悬浮液,再加浓度为15%的盐酸溶液调PH为6,研磨浆料至800目后,再加氢氧化钠调为中性,喷雾干燥,得粉末。
用于建筑领域内的保温砂浆的制备方法为:将用于建筑领域内的保温砂浆所有原料混匀后,加入适量水混匀,即得。
所得产品测试结果如下:
Claims (2)
1.一种用于建筑领域内的保温砂浆,其特征在于:其是由下述重量份的原料制得:硅酸盐水泥30-35、氯氧镁水泥8-12、沙子20-30、浓度为10-15%的双氧水0.5-1.5,粉状有机硅消泡剂1-2、PP纤维2-3、废铝粉0.1-0.2、氧化石蜡皂0.1-0.2、丁香油0.2-0.4,维生素C1-2、生石灰2-4、氢氧化钠2-4、膨胀珍珠岩10-15,改性硅藻土10-12。
2.根据权利要求1所述的一种用于建筑领域内的保温砂浆,其特征在于:
所述的改性硅藻土的制备方法为:
取硅藻土,于600-700℃下烧结2-4小时,与相当于其重量份1-2%的咪唑啉、1-2%的丙烯酸甲酯、1-2%的抗氧剂2246混匀,再加加适量水,搅拌均匀,成悬浮液,再加浓度为10-15%的盐酸溶液调PH为5-6,研磨浆料至600-800目后,再加氢氧化钠调为中性,喷雾干燥,得粉末。