CN103681947A - Preparation method for organic resin reflective suede-face glass and suede-face glass - Google Patents
Preparation method for organic resin reflective suede-face glass and suede-face glass Download PDFInfo
- Publication number
- CN103681947A CN103681947A CN201210356116.XA CN201210356116A CN103681947A CN 103681947 A CN103681947 A CN 103681947A CN 201210356116 A CN201210356116 A CN 201210356116A CN 103681947 A CN103681947 A CN 103681947A
- Authority
- CN
- China
- Prior art keywords
- organic resin
- glass
- convex
- concave
- reflective matte
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed is a preparation method for organic resin reflective suede-face glass: step1: coating or printing a UV light-cured organic resin film on the surface of the glass; step2: mold pressing a 3D convex and concave reflective suede-face template with prefabricated patterns on the organic resin film or rolling a 3D convex and concave reflective suede-face press roll with fabricated patterns on the UV light-cured organic resin film and convex so as to form concave reflective suede-face pressing marks on the upper surface of the UV light-cured organic resin film; step3: curing the UV light-cured organic resin film on the surface of the glass through ultraviolet radiation.
Description
Technical field:
The present invention relates to preparation method and the matte glass of the reflective matte glass of organic resin.
Background technology:
Existing plate glass, incident light can reflect at glass planar, reduces the light that penetrates glass, the glass that especially solar module is used, glass light reflection can reduce the photoelectric conversion efficiency of solar module.
Summary of the invention:
The object of the invention is: 1, by glass surface mold pressing or the reflective matte of roll-in organic resin 3D convex-concave, reduce the light reflection of glass, increase the light that penetrates glass, improve the photoelectric conversion efficiency of solar module.2, below the reflective matte of glass surface organic resin 3D convex-concave, quantum dot adhesive film is set, by quantum dot adhesive film, absorb the acting in conjunction that wide excitation spectrum and narrow emission spectra and the reflective matte increase of organic resin 3D convex-concave penetrate the amount of light of glass, improve photovoltaic solar cell plate photoelectric conversion efficiency.
The preparation method of the reflective matte glass of a kind of organic resin that the present invention proposes: step 1: glass surface is coated with or printing UV photocuring organic resin film; Step 2: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed in to organic resin film or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on UV photocuring organic resin film, UV photocuring organic resin film upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated UV photocuring organic resin film and is solidificated in glass surface.
The preparation method of the reflective matte glass of another kind of organic resin that the present invention proposes: step 1: lower glass surface is manufactured quantum dot material layer, quanta point material layer surface is coated with overcoat; Step 2: surface on glass is coated with or printing UV photocuring organic resin glued membrane, step 3: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed on organic resin glued membrane or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on organic resin glued membrane, and organic resin glued membrane upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated or heating, and the reflective matte organic resin of convex-concave glued membrane is solidificated in surface on glass.
The preparation method of the reflective matte glass of another kind of organic resin that the present invention proposes: step 1: quantum dot material layer is manufactured on surface on glass, quanta point material layer surface is coated with or printing UV photocuring organic resin glued membrane, step 3: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed on organic resin glued membrane or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on organic resin glued membrane, and organic resin glued membrane upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated or heating, and the reflective matte organic resin of convex-concave glued membrane is solidificated in surface on glass; Step 4: glass back is manufactured quantum dot material layer, quanta point material layer surface is coated with or printing UV photocuring organic resin glued membrane, and ultraviolet ray is irradiated or heating, and organic resin glued membrane is solidificated in quanta point material layer surface.
In the preparation method of the reflective matte glass of above-mentioned organic resin, quanta point material is manufactured on glass surface with meteorological transmission sedimentation or space sublimed method or sputtering method or ion electroplating method, but is not limited to said method.
In the preparation method of the reflective matte glass of above-mentioned organic resin, quanta point material comprises: copper indium diselenide material or Copper Indium Gallium Selenide material or cadmium telluride material, but be not limited to above-mentioned material.
The reflective matte glass of a kind of organic resin that the present invention proposes, comprising: glass, the reflective matte organic resin film of 3D convex-concave, the reflective matte organic resin film of surface binded 3D convex-concave on glass.
The reflective matte glass of another kind of organic resin that the present invention proposes, comprising: glass, and quanta point material, the reflective matte organic resin film of 3D convex-concave, quanta point material, the reflective matte organic resin of quanta point material surface binded 3D convex-concave diaphragm are manufactured in surface on glass.
The reflective matte glass of another kind of organic resin that the present invention proposes; comprise: glass; quanta point material; the reflective matte organic resin film of 3D convex-concave; quantum dot tree material is manufactured on surface on glass; the reflective matte organic resin of quanta point material surface binded 3D convex-concave diaphragm, glass back is manufactured quanta point material, quanta point material surface binded organic resin diaphragm.
The reflective matte organic resin film of 3D convex-concave is that the reflective matte template of 3D convex-concave or matte pressure roller are pressed in to the reflective matte impression of the convex-concave forming on organic resin glued membrane.
Accompanying drawing explanation:
Below in conjunction with drawings and Examples, the invention will be further described.
Fig. 1 has the reflective matte organic resin film of feature of the present invention surface binded 3D on glass convex-concave structure chart.
Fig. 2 has the reflective matte organic resin film of feature of the present invention surface binded 3D on glass convex-concave, the bonding quantum dot resin glue of lower glass surface membrane structure figure.
Fig. 3 has feature of the present invention lower surface bonds quantum dot on glass resin glued membrane, the reflective matte organic resin film of quantum dot resin glued membrane surface binded 3D convex-concave structure chart.
Embodiment:
Embodiment 1:
The reflective matte organic resin film of surface binded 3D convex-concave on glass structure chart as shown in Figure 1, wherein: the reflective matte organic resin film of the 1st, 3D convex-concave, the 2nd, glass.
Manufacturing process is as follows: step 1: glass surface is coated with or printing UV photocuring organic resin film; Step 2: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed in to organic resin film or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on UV photocuring organic resin film, UV photocuring organic resin film upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated UV photocuring organic resin film and is solidificated in glass surface.
Embodiment 2:
The reflective matte organic resin film of surface binded 3D convex-concave on glass, the bonding quantum dot resin glue of lower glass surface membrane structure figure as shown in Figure 2, wherein: the reflective matte organic resin film of the 3rd, 3D convex-concave, the 4th, glass, the 5th, quanta point material, the 6th, quanta point material overcoat.
Manufacturing process is as follows: step 1: surface on glass is coated with or printing UV photocuring organic resin glued membrane, step 2: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed on organic resin glued membrane or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on UV photocuring organic resin glued membrane, and UV photocuring organic resin glued membrane upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated, and the reflective matte organic resin of UV photocuring convex-concave glued membrane is solidificated in surface on glass; Step 4: quanta point material is manufactured on to lower glass surface with meteorological transmission sedimentation or space sublimed method or sputtering method or ion electroplating method; Step 5: quanta point material lower surface is coated with or printing quantum dot material protection film, and ultraviolet ray is irradiated, and quantum dot resin glue protecting film is solidificated in quanta point material lower surface.
Embodiment 3:
Lower surface bonds quanta point material resin glued membrane on glass, the reflective matte organic resin film of quanta point material surface binded 3D convex-concave structure chart as shown in Figure 3, wherein: the reflective matte organic resin film of the 7th, 3D convex-concave, the 8th, upper strata quanta point material, the 9th, glass, 10Shi lower floor quanta point material, the 11st, quanta point material overcoat.
Manufacturing process is as follows: step 1: with meteorological transmission sedimentation or space sublimed method or sputtering method or ion electroplating method, quanta point material is manufactured on to glass front; Step 2: quanta point material surface is coated with or printing UV photocuring organic resin protection film; Step 3: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed in to organic resin protection film or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on UV photocuring organic resin protection film, UV photocuring organic resin protection film upper surface forms the reflective matte impression of convex-concave; Step 4: ultraviolet ray is irradiated, and UV photocuring organic resin film is solidificated in quanta point material surface; Step 5: quanta point material is manufactured on to glass back with meteorological transmission sedimentation or space sublimed method or sputtering method or ion electroplating method; Step 6: quanta point material below is coated with or printing UV photocuring organic resin protection film, and ultraviolet ray is irradiated, UV photocuring organic resin protection film is solidificated in quanta point material below.
Claims (9)
1. the preparation method of the reflective matte glass of organic resin: step 1: glass surface is coated with or printing UV photocuring organic resin film; Step 2: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed in to organic resin film or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on UV photocuring organic resin film, UV photocuring organic resin film upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated UV photocuring organic resin film and is solidificated in glass surface.
2. the preparation method of the reflective matte glass of organic resin: step 1: lower glass surface is manufactured quantum dot material layer, quanta point material layer surface is coated with overcoat; Step 2: surface on glass is coated with or printing UV photocuring organic resin glued membrane, step 3: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed on organic resin glued membrane or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on organic resin glued membrane, and organic resin glued membrane upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated or heating, and the reflective matte organic resin of convex-concave glued membrane is solidificated in surface on glass.
3. the preparation method of the reflective matte glass of organic resin: step 1: quantum dot material layer is manufactured on surface on glass, quanta point material layer surface is coated with or printing UV photocuring organic resin glued membrane, step 3: the reflective matte template of the 3D convex-concave of pre-fabricated patterns is embossed on organic resin glued membrane or by the reflective matte pressure roller of the 3D convex-concave roll-in of pre-fabricated patterns on organic resin glued membrane, and organic resin glued membrane upper surface forms the reflective matte impression of convex-concave; Step 3: ultraviolet ray is irradiated or heating, and the reflective matte organic resin of convex-concave glued membrane is solidificated in surface on glass; Step 4: glass back is manufactured quantum dot material layer, quanta point material layer surface is coated with or printing UV photocuring organic resin glued membrane, and ultraviolet ray is irradiated or heating, and organic resin glued membrane is solidificated in quanta point material layer surface.
4. as claim 2 or 3, state the preparation method of the reflective matte glass of organic resin, it is characterized in that: quanta point material comprises: copper indium diselenide material or curing Copper Indium Gallium Selenide material or cadmium telluride material, but be not limited to above-mentioned material.
5. by claim 1 or 2 or 3, state the reflective matte glass of preparation method's manufacture of the reflective matte glass of organic resin, comprising: glass, the reflective matte organic resin film of 3D convex-concave, is characterized in that: the reflective matte organic resin film of surface binded 3D convex-concave on glass.
6. by claim 2, state the reflective matte glass of organic resin of preparation method's manufacture of the reflective matte glass of organic resin; comprise: glass; quanta point material; the reflective matte organic resin film of 3D convex-concave; it is characterized in that: quanta point material, the reflective matte organic resin of quanta point material surface binded 3D convex-concave diaphragm are manufactured in surface on glass.
7. by claim 3, state the reflective matte glass of organic resin of preparation method's manufacture of the reflective matte glass of organic resin; comprise: glass; quanta point material; the reflective matte organic resin film of 3D convex-concave; it is characterized in that: quantum dot tree material is manufactured on surface on glass; the reflective matte organic resin of quanta point material surface binded 3D convex-concave diaphragm, glass back is manufactured quanta point material, quanta point material surface binded organic resin diaphragm.
8. matte glass as reflective in organic resin as described in claim 4 or 5 or 6, is characterized in that: quanta point material comprises: copper indium diselenide material or Copper Indium Gallium Selenide material or cadmium telluride material, but be not limited to above-mentioned material.
9. matte glass as reflective in organic resin as described in claim 4 or 5 or 6, is characterized in that: quanta point material is manufactured on glass surface with meteorological transmission deposition or space distillation or sputter or plating.