CN103669782B - 一种防火型硅金复合装饰板 - Google Patents

一种防火型硅金复合装饰板 Download PDF

Info

Publication number
CN103669782B
CN103669782B CN201310723737.1A CN201310723737A CN103669782B CN 103669782 B CN103669782 B CN 103669782B CN 201310723737 A CN201310723737 A CN 201310723737A CN 103669782 B CN103669782 B CN 103669782B
Authority
CN
China
Prior art keywords
sandwich layer
decorative panel
aqueous adhesives
layer
silicon
Prior art date
Application number
CN201310723737.1A
Other languages
English (en)
Other versions
CN103669782A (zh
Inventor
卞修清
Original Assignee
卞修清
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 卞修清 filed Critical 卞修清
Priority to CN201310723737.1A priority Critical patent/CN103669782B/zh
Publication of CN103669782A publication Critical patent/CN103669782A/zh
Application granted granted Critical
Publication of CN103669782B publication Critical patent/CN103669782B/zh

Abstract

一种防火型硅金复合装饰板,其特征在于:由芯层(1)和芯层(1)的至少一个侧面上固定的金属层(2)所构成;所述的芯层(1)由粉状二氧化硅、氢氧化镁和/或氢氧化铝、轻质碳酸钙和水性胶黏剂混合均匀经模具成型或辊压成型后干燥得到的板材,以质量百分比计,SiO2为35-45%、Mg(OH)2和/或Al(OH)35-15%、CaCO3为45-55%,水性胶黏剂的添加量为无机粉料总质量的10-25%。本装饰板经检测防火性能符合GB8624-2006标准规定,达A级。其他19项指标完全符合GB/T22412-2008规定,其中弯曲强度97MPa、剥离强度5.9N/mm、热变形温度89℃等均高于标准规定。

Description

一种防火型硅金复合装饰板
一、技术领域
[0001] 本发明涉及一种建筑材料,特别涉及建筑内、外墙装饰材料,具体地说是一种防火型硅金复合装饰板。
二、背景技术
[0002] 我国正处在经济高速发展时期,各行业发展均为突出,但建筑内外墙装饰材料及部分工业材料发展却非常滞后。
[0003]目前内、外墙装饰材料大多使用涂料、木质板材料、纤维胶合板或铝塑板类,材料品种可选择性小,且不防火、不防水、不耐久、不防霉菌。这些材料在使用过程中又都存在各种不同的问题,例:涂料档次低、性能差,且有挥发物质。木质板材料、纤维胶合板、铝塑板芯材等材料易燃且产生有毒气体,耐久性差。而金属材料密度大、造价高。
[0004] 继央视大火、上海静安区大火、沈阳大火以来,公安部消防总局连续发文,要求建筑外墙用保温、装饰材料防火等级必须达到A级,禁止使用可燃性保温装饰材料。研发一种防火、耐水、无毒害环保装饰材料以替代传统可燃性装饰材料势在必行。
三、发明内容
[0005] 本发明针对传统装饰板材存在的缺陷,旨在提供一种防火型硅金复合装饰板(以下简称硅金板),所要解决的技术问题是硅金板的防火及其他性能满足GB8624-2006、GB/T22412-2008 的规定。
[0006] 本娃金板由芯层I和芯层I的至少一个侧面上固定的金属装饰层2所构成,如图1所示。
[0007] 所述的芯层I由粉状二氧化硅(Si02)、氢氧化镁(Mg(OH)2)和/或氢氧化铝(Al (0H)3)、轻质碳酸钙(CaCO3)和水性胶黏剂混合均匀经模具成型或辊压成型后干燥得到的板材。以质量百分比计,S1^ 35-45%、Mg(0H) 2和 / 或 Al (OH) 35_15%、CaC03S 45-55%,水性胶黏剂的添加量为无机粉料总质量的10-25%。当同时加Mg (OH)2, Al (OH) 3时,总量不变,相互比例任意。
[0008]优选:
[0009] Si0240%、Mg (OH) 2和/或Al (OH) 310%、CaC0350%,水性胶黏剂的添加量为无机粉料总质量的15-20%。
[0010] 所述的粉状S12选自各种微孔或闭孔微硅粉或白炭黑。
[0011] 所述的水性胶黏剂选自硅溶胶、聚氨酯、丙烯酸酯、环氧树脂等一种或两种以上复合胶黏剂。
[0012] 所述的金属装饰层2选自金属片材或者带有各种色彩、图案、纹路或表面呈凹凸状的金属片材。金属片材如钢板、不锈钢、铝板、铜板或各种合金板等。优选铝板或者带有各种色彩、图案、纹路或或表面呈凹凸状的铝板。
[0013] 上述硅金板适合内墙和外墙装饰,同时起到防火作用,防火等级达到A级。将墙面找平后使用胶黏剂配合锚固件将硅金板固定在墙面上或龙骨上。
[0014] 为适应保温的需要,在芯层I的另一侧面上固定保温层3,若该侧面上也复合了金属层2时(如图2所示),则在该金属层2上固定保温层3构成保温装饰一体化的硅金板,如图3所示。
[0015] 所述的保温层3优选轻质防火的保温材料,如岩棉、玻纤等。
[0016] 将外墙或内墙墙面找平后使用胶黏剂配合锚固件将一体化硅金板固定到墙面上,起装饰、保温和防火作用。
[0017] 为方便与墙体的安装,在硅金板或一体化硅金板上设置连接件4,如图3所示。也可以在硅金板或一体化硅金板的左右两边或上下两边分别设置供卯榫连接用的卯眼和榫头。
[0018] 本发明原料易得,加工方便,既装饰保温,又防火,硅金板防火等级达到A级。
[0019] 根据不同要求,硅金板两面可以选用不同的金属材料复合,能够替代一定厚度的不锈钢、铜、招等贵重金属材料。
[0020] 本装饰板经《国家固定灭火系统和耐火构件质量监督检验中心》检测,防火性能符合GB8624-2006标准规定,达A级(报告编号:Gn201200715)。经《国家建筑材料测试中心》检测,19项指标完全符合GB/T22412-2008规定,其中弯曲强度97MPa、剥离强度5.9N/mm、热变形温度89°C等均高于标准规定(报告编号:20121 I 00231)。
四、附图说明
[0021 ] 图1是单面防火型硅金复合装饰板结构示意图。
[0022] 图2是双面防火型硅金复合装饰板结构示意图。
[0023]图3是具有保温性能的硅金复合保温装饰一体化板结构示意图及连接件4结构示意图。
五、具体实施方式
[0024](一)芯板的制备
[0025] 1、模具法
[0026] 先将40% 二氧化硅粉料与50%碳酸钙粉、10%氢氧化镁或者氢氧化铝粉混合,按照固体粉料重量的15%以上添加水性胶黏剂,充分搅拌均匀(机械或手工均可),倒入表面涂覆脱模剂的模具内摊压平整,固化成型后脱模,自然干燥得到1500X1000X4mm的芯板。
[0027] 2、辊压法
[0028] I)将40% 二氧化硅粉料与50%碳酸钙粉、8%氢氧化镁和2%氢氧化铝粉混合,按照固体粉料重量的20%以上添加水性胶黏剂,开动搅拌机2分钟以上使其搅拌成膏状。
[0029] 2)以挤出机或分料机将膏状无机芯材运至履带式送料机上,运料机表面以无机卷材(例如:无纺布)衬托,通过履带将膏状无机芯材向挤压钢辊方向输送。
[0030] 3)挤压钢辊有若干个独立辊组合成挤压线,前端挤压辊开口较高,便于进料,中后端逐渐变小,将膏状无机芯料挤压达到设计的厚度10mm,逐步将已挤压成型的板材上无纺布撤除,通过皮带式输送带送进烘箱内,干燥多余的水分。烘箱内增加循环风,温度大于80。。。
[0031] 4)将干燥的板材去除毛边后裁切成1500X 1000X4mm的芯板。
[0032] (二)防火型硅金复合装饰板的制备
[0033] 1、将无机芯板一面压光或砂光,涂上胶黏剂或覆高分子膜,再将金属铝板(0.48mm)与之复合压制;或先将金属铝板背面涂上胶黏剂或覆高分子膜,再与无机芯材复合,得到如图1所示的防火型硅金复合装饰板。
[0034] 2、将无机芯板的两面压光或砂光,涂上胶黏剂或覆高分子膜,两面分别与金属铝板压合构成硅金装饰板,如图2所示,其中一面再与保温材料玻璃棉板复合构成保温层3,如图3所示。
[0035] 3、在装饰板上设置连接件4,如图3所示。

Claims (4)

1.一种防火型硅金复合装饰板,其特征在于:由芯层(I)和芯层(I)的至少一个侧面上固定的金属装饰层(2)所构成;所述的芯层(I)由粉状二氧化硅、氢氧化镁和/或氢氧化铝、轻质碳酸钙和水性胶黏剂混合均匀经模具成型或辊压成型后干燥得到的板材,以质量百分比计,S12^ 35-45%, Mg(OH) 2和 / 或 Al (OH) 35_15%、CaCO3为 45-55%,水性胶黏剂的添加量为无机粉料总质量的15〜20% ; 所述的金属装饰层(2)为铝板或者带有各种色彩、图案、纹路或表面呈凹凸状的装饰铝板; 所述的粉状二氧化硅选自微孔或闭孔微硅粉或白炭黑; 所述的水性胶黏剂选自硅溶胶、聚氨酯、丙烯酸酯、环氧树脂中一种或两种以上复合胶黏剂。
2.根据权利要求1所述的装饰板,其特征在于:Si0240%、Mg(0H)jP /或Al (OH) 310%、CaC0350%。
3.根据权利要求1或2所述的装饰板,其特征在于:在芯层(I)的另一侧面上固定有保温层⑶。
4.根据权利要求1或2所述的装饰板,其特征在于:装饰板上设置有连接件(4)或者在装饰板的两边分别设置卯眼和榫头。
CN201310723737.1A 2013-12-25 2013-12-25 一种防火型硅金复合装饰板 CN103669782B (zh)