CN103666709A - 一种润滑剂及其制备方法 - Google Patents

一种润滑剂及其制备方法 Download PDF

Info

Publication number
CN103666709A
CN103666709A CN201310637171.0A CN201310637171A CN103666709A CN 103666709 A CN103666709 A CN 103666709A CN 201310637171 A CN201310637171 A CN 201310637171A CN 103666709 A CN103666709 A CN 103666709A
Authority
CN
China
Prior art keywords
lubricant
parts
sulfonate
white oil
fatty acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310637171.0A
Other languages
English (en)
Other versions
CN103666709B (zh
Inventor
袁宏亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chao Runda Science and Technology Ltd. of Shenzhen
Original Assignee
NEOVOLTAIC ENERGY NANTONG CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NEOVOLTAIC ENERGY NANTONG CO Ltd filed Critical NEOVOLTAIC ENERGY NANTONG CO Ltd
Priority to CN201310637171.0A priority Critical patent/CN103666709B/zh
Publication of CN103666709A publication Critical patent/CN103666709A/zh
Application granted granted Critical
Publication of CN103666709B publication Critical patent/CN103666709B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种润滑剂及其制备方法，其中润滑剂以重量组分计包括：十二烷基苯磺酸钠16-25份，油酸15-20份，白油60-70份，三乙醇胺8-15份，吐温205-10份，聚甘油脂肪酸酯2-6份，琥珀酸酯磺酸钠1-4份，水15-20份；制备方法为将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时；本法明提供的润滑剂经检测具有很好的运动粘度与摩擦系数，能够更好地起到润滑作用，同时不会损坏机体。

Description

一种润滑剂及其制备方法
技术领域
    本发明属于化工领域，特别涉及一种润滑剂及其制备方法。
背景技术
润滑剂用以降低摩擦副的摩擦阻力、减缓其磨损的润滑介质。润滑剂对摩擦副还能起冷却、清洗和防止污染等作用。为了改善润滑性能，在某些润滑剂中可加入合适的添加剂。选用润滑剂时，一般须考虑摩擦副的运动情况、材料、表面粗糙度、工作环境和工作条件，以及润滑剂的性能等多方面因素。在机械设备中，润滑剂大多通过润滑系统输配给各需要润滑的部位。然而现有的润滑剂粘度较大，摩擦系数较高，对机体的机械磨损较高，因此需要开发一种低粘度以及低摩擦系数的润滑剂，更好的起到润滑与保护作用。
 
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种润滑剂及其制备方法。
本发明是通过以下技术手段实现的：
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 16-25份，油酸15-20份，白油60-70份，三乙醇胺8-15份，吐温20 5-10份，聚甘油脂肪酸酯2-6份，琥珀酸酯磺酸钠1-4份，水15-20份。
所述的润滑剂，可以优选为以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
一种以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
本法明提供的润滑剂经检测25℃时粘度达到了48cps以下；摩擦系数达到了0.023以下；运动粘度40℃时达到了36mm2/s以下，100℃时达到了8 mm2/s以下。
具体实施方式：
实施例1
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 16-25份，油酸15-20份，白油60-70份，三乙醇胺8-15份，吐温20 5-10份，聚甘油脂肪酸酯2-6份，琥珀酸酯磺酸钠1-4份，水15-20份。
以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
实施例2
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
实施例3
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
实施例4
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
实施例5
一种润滑剂，以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
以上所述的润滑剂的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
对以上实施例制备得到的润滑剂进行性能测试，结果见下表：
项目 实施例1 实施例2 实施例3 实施例4 实施例5
粘度25℃（cps） 48 45 43 44 46
摩擦系数 0.021 0.02 0.015 0.018 0.023
运动粘度40℃（mm2/s） 36 35 33 34 35
运动粘度100℃（mm2/s） 8 8 7 8 8
    从以上试验数据可以看出，本法明提供的润滑剂25℃时粘度达到了48cps以下；摩擦系数达到了0.023以下；运动粘度40℃时达到了36mm2/s以下，100℃时达到了8 mm2/s以下。

Claims (3)

1. 一种润滑剂，其特征在于，以重量组分计包括：十二烷基苯磺酸钠 16-25份，油酸15-20份，白油60-70份，三乙醇胺8-15份，吐温20 5-10份，聚甘油脂肪酸酯2-6份，琥珀酸酯磺酸钠1-4份，水15-20份。
2. 根据权利要求1所述的润滑剂，其特征在于，以重量组分计包括：十二烷基苯磺酸钠 18-23份，油酸16-18份，白油64-67份，三乙醇胺10-12份，吐温20 6-8份，聚甘油脂肪酸酯3-5份，琥珀酸酯磺酸钠2-3份，水16-18份。
3. 一种权利要求1或2所述的润滑剂的制备方法，其特征在于，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将水加入到反应釜中，升温至55-65℃，在搅拌下加入十二烷基苯磺酸钠、油酸、三乙醇胺、吐温20、白油、聚甘油脂肪酸酯和琥珀酸酯磺酸钠，于35-45℃下搅拌1-2小时。
CN201310637171.0A 2013-12-03 2013-12-03 一种润滑剂及其制备方法 Active CN103666709B (zh)