CN103666228A - Anti-corrosion paint for copper - Google Patents
Anti-corrosion paint for copper Download PDFInfo
- Publication number
- CN103666228A CN103666228A CN201310618546.9A CN201310618546A CN103666228A CN 103666228 A CN103666228 A CN 103666228A CN 201310618546 A CN201310618546 A CN 201310618546A CN 103666228 A CN103666228 A CN 103666228A
- Authority
- CN
- China
- Prior art keywords
- parts
- copper
- dioxide
- carbon black
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Anti-corrosion paint for copper comprises components in parts by mass as follows: 100 parts of methacrylic resin, 30-50 parts of isocyanate, 15-20 parts of n-butyl acetate, 20-25 parts of silicon dioxide, 10-15 parts of xylene, 20-25 parts of strontium chromate, 8-10 parts of a curing agent, 15-20 parts of carbon black, 25-30 parts of titanium dioxide, 0.1-1 part of tetraisopropyl titanate, 10-20 parts of methyl isobutyl ketone, 5-10 parts of cadmium yellow and 10-15 parts of diacetone alcohol. A product has a good binding force with copper, the adhesion reaches level 1; the weather resistance is high, and light is maintained; and the product is good in corrosion resistance, is resistant to acid rain corrosion, and can be widely produced and replace the conventional materials continuously.
Description
Technical field
The application belongs to paint field, relates in particular to a kind of anticorrosion copper coating.
Background technology
Protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, and metal etc. is played to etch-proof effect, the life-span that protection non-ferrous metal is used; Heavy-duty coating refers to relatively conventional protective system, can in relatively harsh corrosive environment, apply, and have a class protective system that can reach than the conventional longer protection period of protective system.
Protective system has become the important fresh combatants of paint field, and protective system is being brought into play increasing effect, and development prospect is considerable.But it is perfect that traditional product is improved gradually, new product is is constantly researched and developed appearance, adapt to new standard and requirement in anticorrosion market and environmental regulation development, still needs proactive, continues innovation, and the scientific research of the expression protective system that carries weight is early to start.The mankind are always continuous to the research of Yu Haiyang, and resource in ocean, the exploration of ocean is also slowly being advanced by leaps and bounds, and in ocean, progress be unable to do without top coat.China has a long way to go to protective system, along with the development of social city, technicalization, hommization, designs a kind of good weatherability, protects light, and the anticorrosion copper of acid rain resistant corrosion, is very important to meet the need of market with coating.
Summary of the invention
the technical problem solving:
The technical problems such as the application is poor for existing protective system weathering resistance, and acid rain resistant corrosion and sticking power is not low, provide a kind of anticorrosion copper coating.
technical scheme:
An anticorrosion copper coating, is comprised of following raw materials according, take mass fraction representation as 100 parts of methacrylic resins; Isocyanic ester 30-50 part; N-butyl acetate 15-20 part; Silicon-dioxide 20-25 part; Dimethylbenzene 10-15 part; Strontium yellow 20-25 part; Solidifying agent 8-10 part; Carbon black is 15-20 part; Titanium dioxide is 25-30 part; Tetra isopropyl titanate 0.1-1 part; Methyl iso-butyl ketone (MIBK) 10-20 part; Cadmium yellow 5-10 part; Diacetone alcohol 10-15 part.
As a preferred technical solution of the present invention: described composition be take mass fraction representation as 100 parts of methacrylic resins; 40 parts of isocyanic ester; 17 parts of n-butyl acetates; 22.5 parts of silicon-dioxide; 12.5 parts of dimethylbenzene; 22.5 parts of strontium yellows; 9 parts, solidifying agent; Carbon black is 17.5 parts; Titanium dioxide is 27.5 parts; 0.5 part of tetra isopropyl titanate; 15 parts of methyl iso-butyl ketone (MIBK); 7.5 parts of cadmium yellows; 12.5 parts of diacetone alcohols.
As a preferred technical solution of the present invention: described solidifying agent is triethylene tetramine.
beneficial effect:
A kind of anticorrosion copper of the present invention adopts above technical scheme compared with prior art with coating, has following technique effect: 1, product becomes good with copper bonding force, and sticking power reaches 1 grade; 2, weathering resistance is high, protects light; 3, product corrosion stability is good, and acid rain resistant corrosion can the not division of history into periods of widespread production be replaced current material.
Embodiment
embodiment 1:
An anticorrosion copper coating, its composition be take mass fraction representation as 100 parts of methacrylic resins; 30 parts of isocyanic ester; 15 parts of n-butyl acetates; 20 parts of silicon-dioxide; 10 parts of dimethylbenzene; 20 parts of strontium yellows; 8 parts of triethylene tetramines; Carbon black is 15 parts; Titanium dioxide is 25 parts; 0.1 part of tetra isopropyl titanate; 10 parts of methyl iso-butyl ketone (MIBK); 5 parts of cadmium yellows; 10 parts of diacetone alcohols.
Product and copper bonding force are good, are coated with 100 microns of thickness, and sticking power reaches 1 grade.
embodiment 2:
An anticorrosion copper coating, its composition be take mass fraction representation as 100 parts of methacrylic resins; 50 parts of isocyanic ester; 20 parts of n-butyl acetates; 25 parts of silicon-dioxide; 15 parts of dimethylbenzene; 25 parts of strontium yellows; 10 parts of triethylene tetramines; Carbon black is 20 parts; Titanium dioxide is 30 parts; 1 part of tetra isopropyl titanate; 20 parts of methyl iso-butyl ketone (MIBK); 10 parts of cadmium yellows; 15 parts of diacetone alcohols.
Product and copper bonding force are good, are coated with 100 microns of thickness, and sticking power reaches 1 grade.
embodiment 3:
An anticorrosion copper coating, is characterized in that: its composition be take mass fraction representation as 100 parts of methacrylic resins; 40 parts of isocyanic ester; 17 parts of n-butyl acetates; 22.5 parts of silicon-dioxide; 12.5 parts of dimethylbenzene; 22.5 parts of strontium yellows; 9 parts of triethylene tetramines; Carbon black is 17.5 parts; Titanium dioxide is 27.5 parts; 0.5 part of tetra isopropyl titanate; 15 parts of methyl iso-butyl ketone (MIBK); 7.5 parts of cadmium yellows; 12.5 parts of diacetone alcohols.
Product and copper bonding force are good, are coated with 100 microns of thickness, and sticking power reaches 1 grade.
All components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.
Claims (3)
1. an anticorrosion copper coating, is characterized in that: its composition be take mass fraction representation as 100 parts of methacrylic resins; Isocyanic ester 30-50 part; N-butyl acetate 15-20 part; Silicon-dioxide 20-25 part; Dimethylbenzene 10-15 part; Strontium yellow 20-25 part; Solidifying agent 8-10 part; Carbon black is 15-20 part; Titanium dioxide is 25-30 part; Tetra isopropyl titanate 0.1-1 part; Methyl iso-butyl ketone (MIBK) 10-20 part; Cadmium yellow 5-10 part; Diacetone alcohol 10-15 part.
2. a kind of anticorrosion copper coating according to claim 1, is characterized in that: its composition be take mass fraction representation as 100 parts of methacrylic resins; 40 parts of isocyanic ester; 17 parts of n-butyl acetates; 22.5 parts of silicon-dioxide; 12.5 parts of dimethylbenzene; 22.5 parts of strontium yellows; 9 parts, solidifying agent; Carbon black is 17.5 parts; Titanium dioxide is 27.5 parts; 0.5 part of tetra isopropyl titanate; 15 parts of methyl iso-butyl ketone (MIBK); 7.5 parts of cadmium yellows; 12.5 parts of diacetone alcohols.
3. a kind of anticorrosion copper coating according to claim 1, is characterized in that: described solidifying agent is triethylene tetramine.