CN103666144A - 一种丙烯酸树脂车用防锈漆及其制备方法 - Google Patents

一种丙烯酸树脂车用防锈漆及其制备方法 Download PDF

Info

Publication number
CN103666144A
CN103666144A CN201310410045.1A CN201310410045A CN103666144A CN 103666144 A CN103666144 A CN 103666144A CN 201310410045 A CN201310410045 A CN 201310410045A CN 103666144 A CN103666144 A CN 103666144A
Authority
CN
China
Prior art keywords
parts
acrylic resin
minute
preparation
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310410045.1A
Other languages
English (en)
Inventor
孔华英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING SIDE TECHNOLOGY Co Ltd
Original Assignee
TONGLING SIDE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING SIDE TECHNOLOGY Co Ltd filed Critical TONGLING SIDE TECHNOLOGY Co Ltd
Priority to CN201310410045.1A priority Critical patent/CN103666144A/zh
Publication of CN103666144A publication Critical patent/CN103666144A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种丙烯酸树脂车用防锈漆，其由下列重量份的原料组分制备而成：丙烯酸树脂45-50、胺类固化剂6-9、碳纤维2-3、羟基乙叉二磷酸2-3、磷酸三丁酯1-2、三异丙醇胺1-2、氯化钙2-3、三丁甲基乙醚12-14、乙酸异丙酯9-12、成膜助剂6-7。本发明原料无毒，且环境友好，因此生产和使用过程对人体毒害小，且对环境污染低；配方中添加成膜助剂，提高了各成分的相容性，大大提高了成膜效果。所得的漆膜耐水、防腐性能优异，且粘接强度牢固，耐碱、耐水性均优良。

Description

一种丙烯酸树脂车用防锈漆及其制备方法
技术领域
本发明涉及金属防锈技术领域，具体涉及一种丙烯酸树脂车用防锈漆及其制备方法。
背景技术
金属腐蚀是人们面临的一个十分严重的问题。全世界每年因金属腐蚀而报废的金属达几亿吨以上，经济损失占国民经济总产值的1.5%～2.5%。金属生锈是最普遍、损失最大的一种腐蚀。防锈工作历来是国内外的重大科研课题之一，人们研究出多种措施防止和抑制金属的锈蚀，以涂料防锈便是一种有效的方法。
发明内容
本发明的目的是提供一种丙烯酸树脂车用防锈漆及其制备方法，对多种金属具有防锈功能。
本发明的技术方案如下：
一种丙烯酸树脂车用防锈漆，其特征在于，其由下列重量份的原料组分制备而成：
丙烯酸树脂45-50、胺类固化剂6-9、碳纤维2-3、羟基乙叉二磷酸2-3、磷酸三丁酯1-2、三异丙醇胺1-2、氯化钙2-3、三丁甲基乙醚12-14、乙酸异丙酯9-12、成膜助剂6-7。
所述的丙烯酸树脂车用防锈漆，其特征在于：所述的成膜助剂由下列重量份的原料制备而成：
醇酯十二15-18、过氧化甲乙酮1-2、硅烷偶联剂KH-5501-1.3、丙烯酸-2-羟基丙酯2-3、刚玉粉1-1.4、茶多酚1-2、聚异丁烯1-1.4、乙酸乙酯12-14、冬青油1-2；
制备方法是将丙烯酸-2-羟基丙酯、刚玉粉、茶多酚、聚异丁烯、乙酸乙酯混合，加入过氧化甲乙酮，搅拌反应45-60分钟，然后，升温至70-80℃，加入硅烷偶联剂KH550、醇酯十二，继续搅拌反应60-90分钟，然后，加入其它剩余成分，搅拌30-40分钟，用500目滤布过滤即得。
所述的丙烯酸树脂车用防锈漆的制备方法，其特征在于，包括以下步骤：
（1）先将过氧化甲乙酮、和部分二甲苯加入到反应釜混合均匀；
（2）然后再依次加入不饱和聚酯树脂、二乙烯三胺，碳化硼、氯化聚乙烯、石英砂，控制温度为45-50℃，先以300-500r/min的速度搅拌8-10分钟，然后再以600-800r/min的速度搅拌20-25分钟，再将配方中的其余物料全部加入到釜里，以1200-1500r/min的速度高速分散20-25分钟，然后将分散好的混合物料投入砂磨机里研磨，再用400目过滤布过滤，即可。
本发明的有益效果：
本发明原料无毒，且环境友好，因此生产和使用过程对人体毒害小，且对环境污染低，配方中添加成膜助剂，提高了各成分的相容性，大大提高了成膜效果。所得的漆膜耐水、防腐性能优异，且粘接强度牢固，耐碱、耐水性均优良。
具体实施方式：
实施例
一种丙烯酸树脂车用防锈漆，其由下列重量（kg）的原料组分制备而成：
丙烯酸树脂50、胺类固化剂8、碳纤维2、羟基乙叉二磷酸3、磷酸三丁酯1、三异丙醇胺1、氯化钙3、三丁甲基乙醚13、乙酸异丙酯10、成膜助剂6；
具体制备方法，包括以下步骤：
1、成膜助剂的制备：
按重量（kg）称取醇酯十二17、过氧化甲乙酮1、硅烷偶联剂KH-5501.2、丙烯酸-2-羟基丙酯2、刚玉粉1.2、茶多酚2、聚异丁烯1.2、乙酸乙酯13、冬青油2；
制备方法是将丙烯酸-2-羟基丙酯、刚玉粉、茶多酚、聚异丁烯、乙酸乙酯混合，加入过氧化甲乙酮，搅拌反应50分钟，然后，升温至70℃，加入硅烷偶联剂KH550、醇酯十二，继续搅拌反应65分钟，然后，加入其它剩余成分，搅拌35分钟，用500目滤布过滤即得。
2、丙烯酸树脂车用防锈漆的制备，按以下步骤制成：
（1）先将过氧化甲乙酮、和部分二甲苯加入到反应釜混合均匀；
（2）然后再依次加入不饱和聚酯树脂、二乙烯三胺，碳化硼、氯化聚乙烯、石英砂，控制温度为45-50℃，先以300-500r/min的速度搅拌8-10分钟，然后再以600-800r/min的速度搅拌20-25分钟，再将配方中的其余物料全部加入到釜里，以1200-1500r/min的速度高速分散20-25分钟，然后将分散好的混合物料投入砂磨机里研磨，再用400目过滤布过滤，即可。
试验数据
对上述实施例制备的防锈漆按照标准：HG/T2244-1991《机床底漆》进行测试，结果如下表1。
表1防锈漆的检测结果
Figure BDA0000380151810000031

Claims (3)

1.一种丙烯酸树脂车用防锈漆，其特征在于，其由下列重量份的原料组分制备而成：
丙烯酸树脂45-50、胺类固化剂6-9、碳纤维2-3、羟基乙叉二磷酸2-3、磷酸三丁酯1-2、三异丙醇胺1-2、氯化钙2-3、三丁甲基乙醚12-14、乙酸异丙酯9-12、成膜助剂6-7。
2.根据权利要求1所述的丙烯酸树脂车用防锈漆，其特征在于：所述的成膜助剂由下列重量份的原料制备而成：
醇酯十二15-18、过氧化甲乙酮1-2、硅烷偶联剂KH-550 1-1.3、丙烯酸-2- 羟基丙酯2-3、刚玉粉1-1.4、茶多酚1-2、聚异丁烯1-1.4、乙酸乙酯12-14、冬青油1-2；
制备方法是将丙烯酸-2- 羟基丙酯、刚玉粉、茶多酚、聚异丁烯、乙酸乙酯混合，加入过氧化甲乙酮，搅拌反应45-60分钟，然后，升温至70-80℃，加入硅烷偶联剂KH550、醇酯十二，继续搅拌反应60-90分钟，然后，加入其它剩余成分，搅拌30-40分钟，用500目滤布过滤即得。
3.根据权利要求1所述的丙烯酸树脂车用防锈漆的制备方法，其特征在于，包括以下步骤：
（1）先将过氧化甲乙酮、和部分二甲苯加入到反应釜混合均匀；
（2）然后再依次加入不饱和聚酯树脂、二乙烯三胺，碳化硼、氯化聚乙烯、石英砂，控制温度为45-50℃，先以300-500r/min的速度搅拌8-10分钟，然后再以600-800r/min的速度搅拌20-25分钟，再将配方中的其余物料全部加入到釜里，以1200-1500r/min的速度高速分散20-25分钟，然后将分散好的混合物料投入砂磨机里研磨，再用400目过滤布过滤，即可。
CN201310410045.1A 2013-09-10 2013-09-10 一种丙烯酸树脂车用防锈漆及其制备方法 Pending CN103666144A (zh)