CN103665675A - 一种密封性好强度高的密封垫材料及其制备方法 - Google Patents

一种密封性好强度高的密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103665675A
CN103665675A CN201310571913.4A CN201310571913A CN103665675A CN 103665675 A CN103665675 A CN 103665675A CN 201310571913 A CN201310571913 A CN 201310571913A CN 103665675 A CN103665675 A CN 103665675A
Authority
CN
China
Prior art keywords
parts
gasket material
mixing
carbon black
attapulgite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310571913.4A
Other languages
English (en)
Other versions
CN103665675B (zh
Inventor
王慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Original Assignee
ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd filed Critical ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Priority to CN201310571913.4A priority Critical patent/CN103665675B/zh
Publication of CN103665675A publication Critical patent/CN103665675A/zh
Application granted granted Critical
Publication of CN103665675B publication Critical patent/CN103665675B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种密封性好强度高的密封垫材料，其特征在于，由下列重量份的原料制成：氟橡胶70-75、聚四氟乙烯20-30、活性氧化镁3-4、超细氢氧化钙2-3、氢化聚丁二烯2-3、十溴联苯醚3-4、古马隆树脂8-10、防老剂RD1-2、促进剂DM1-2、促进剂M1-2、甘油三醋酸酯10-12、3-氨丙基三甲氧基硅烷3-4、炭黑N22020-25、N351炭黑30-34、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有较低的压缩性变，保证长时间的密封性，强度高，耐磨性能好。

Description

一种密封性好强度高的密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种密封性好强度高的密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。
发明内容
本发明的目的是提供一种密封性好强度高的密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种密封性好强度高的密封垫材料，由下列重量份的原料制成：氟橡胶70-75、聚四氟乙烯20-30、活性氧化镁3-4、超细氢氧化钙2-3、氢化聚丁二烯2-3、十溴联苯醚3-4、古马隆树脂8-10、防老剂RD1-2、促进剂DM1-2、促进剂M1-2、甘油三醋酸酯10-12、3-氨丙基三甲氧基硅烷3-4、炭黑N22020-25、N351炭黑30-34、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述密封性好强度高的密封垫材料，由以下具体步骤制成：将氟橡胶、聚四氟乙烯、活性氧化镁、超细氢氧化钙加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入氢化聚丁二烯、十溴联苯醚、古马隆树脂、防老剂RD、促进剂DM，混炼6-8min，再加入促进剂M、甘油三醋酸酯、3-氨丙基三甲氧基硅烷、炭黑N220继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有较低的压缩性变，保证长时间的密封性，强度高，耐磨性能好。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种密封性好强度高的密封垫材料，由下列重量份（公斤）的原料制成：氟橡胶70、聚四氟乙烯20、活性氧化镁3、超细氢氧化钙2、氢化聚丁二烯2、十溴联苯醚3、古马隆树脂8、防老剂RD1、促进剂DM1、促进剂M1、甘油三醋酸酯10、3-氨丙基三甲氧基硅烷3、炭黑N22020、N351炭黑30、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土12、1,6-己二异氰酸酯3、二缩三丙二醇二丙烯酸酯2、纳米二氧化钛3、纳米二氧化硅1、氧化锌1、促进剂TMTD1、阳起石粉8、花椒籽油1；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述密封性好强度高的密封垫材料，由以下具体步骤制成：将氟橡胶、聚四氟乙烯、活性氧化镁、超细氢氧化钙加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入氢化聚丁二烯、十溴联苯醚、古马隆树脂、防老剂RD、促进剂DM，混炼6-8min，再加入促进剂M、甘油三醋酸酯、3-氨丙基三甲氧基硅烷、炭黑N220继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。
Figure BDA0000415324770000021
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。

Claims (2)

1.一种密封性好强度高的密封垫材料，其特征在于，由下列重量份的原料制成：氟橡胶70-75、聚四氟乙烯20-30、活性氧化镁3-4、超细氢氧化钙2-3、氢化聚丁二烯2-3、十溴联苯醚3-4、古马隆树脂8-10、防老剂RD1-2、促进剂DM 1-2、促进剂M1-2、甘油三醋酸酯10-12、3-氨丙基三甲氧基硅烷3-4、炭黑N220 20-25、N351炭黑30-34、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD 1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述密封性好强度高的密封垫材料，其特征在于，由以下具体步骤制成：将氟橡胶、聚四氟乙烯、活性氧化镁、超细氢氧化钙加入密炼机中，加热至30-40℃，混炼3-5min；然后升温至50-60℃，再加入氢化聚丁二烯、十溴联苯醚、古马隆树脂、防老剂RD、促进剂DM，混炼6-8min，再加入促进剂M、甘油三醋酸酯、3-氨丙基三甲氧基硅烷、炭黑N220继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
CN201310571913.4A 2013-11-15 2013-11-15 一种密封性好强度高的密封垫材料及其制备方法 Expired - Fee Related CN103665675B (zh)