CN103645084A - 一种金相制样法获取皮革截面图片用抛光液 - Google Patents
一种金相制样法获取皮革截面图片用抛光液 Download PDFInfo
- Publication number
- CN103645084A CN103645084A CN201310669511.8A CN201310669511A CN103645084A CN 103645084 A CN103645084 A CN 103645084A CN 201310669511 A CN201310669511 A CN 201310669511A CN 103645084 A CN103645084 A CN 103645084A
- Authority
- CN
- China
- Prior art keywords
- polishing
- leather
- sample preparation
- metallographic sample
- sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种使皮革截面清晰、边界明显，方便易得的金相制样法获取皮革截面图片用抛光液。其特征是由水、丙二醇、乙醇组成，各组分的质量份数为：水100份，丙二醇1-3份、乙醇3-20份。
Description
技术领域
本发明属抛光液技术领域，具体涉及一种金相制样法获取皮革截面图片用抛光液。
背景技术
皮革是多孔材料，环氧树脂、不饱和聚酯树脂等对皮革纤维是浸润的，所以当皮革接触粘度低、渗透性强的树脂时，能够将树脂“吸到”其它部位，浸润皮革，充分填充皮革纤维间的空隙。随着浸润到皮革中的树脂固化，皮革纤维被固定，得到具有一定硬度的皮革-树脂复合材料，完全可以对其进行镶嵌、打磨、抛光等金相制样操作。该方法目前还处在研究开发阶段，很少见报道。专利ZL201110179680.4《一种适用于金相显微镜观察的皮革样品制备方法》描述了针对皮革的金相制样方法，但在抛光步骤没有使用专用的抛光液进行抛光，所以图片不是很清晰，边界不明显，划痕较多，总体效果不理想。
金相制样的目的是显示样品的真实组织，使不同的组织相有不同的反光能力，并且有明显的相边界。金相制样中很关键的一步是抛光。现有抛光可分为金刚石抛光和氧化物抛光，分别使用各自的抛光膏或抛光液。将金刚石作为研磨料进行抛光时，能以最快速度获得最好的研磨平面，这是因为金刚石很硬，它几乎可以切任何材料和相。对于材质较软的样品，可采用氧化物抛光法，抛光在抛光布上完成。但现有抛光液都是针对传统的金相样品调制的，对于皮革这类柔软纤维样品就不适用了，其快速高效的抛光效果会使皮革纤维和包埋树脂基体达到相当的反光性，形成一相，分不清纤维边界，也就看不出纤维截面来了。所以急需开发一种适于金相制样法获取皮革截面图片专用抛光液。
发明内容
本发明的目的在于克服上述现有技术不足，提供一种使皮革截面清晰、边界明显，方便易得的金相制样法获取皮革截面图片用抛光液。
本发明是通过以下方式实现的：
一种金相制样法获取皮革样品截面图片用抛光液，其特征是由水、丙二醇、乙醇组成，各组分的质量份数为：水100份，丙二醇1-3份、乙醇3-20份。
一种适用于金相制样法获取皮革样品截面图片用抛光液，其制备方法为，将水、丙二醇、乙醇按比例混合均匀即可。
一种适用于金相制样法获取皮革样品截面图片用抛光液，其使用方法为：用常用喷雾器向绒布抛光盘均匀喷洒5-15ml抛光液，将打磨好的皮革样块放到抛光盘上，以100-200转/分钟的速度抛光1-3分钟，在样品上施加约10-30N的压力。
有益效果
本发明所述的抛光液，其成分为水、丙二醇、乙醇，不含金刚石及氧化物研磨料，所以在绒布上抛光时起研磨作用的是绒布，绒布对皮革纤维截面及树脂基体有很好的抛光作用，但由于皮革纤维和树脂的硬度是有差别的，所以绒布对二者的抛光作用又不完全相同，使得二者抛光后的反光效果不同，所以皮革纤维截面和树脂截面的显示是有明显区别的。乙醇能够溶解少量树脂，特别是纤维束相界面及纤维束内细纤维间的树脂，由于受到纤维束抛光时弹性晃动的作用，其损失更多一点，所以这些相界面就会有少许凹陷，在图片中就会颜色较深，从而使得边界明显。丙二醇具有一定润滑保湿作用，使得由于对水分吸收不同而产生的显示区别能够保持较长时间。所以经过抛光的样品可以省去显色过程直接到显微镜上观察。另外，水和乙醇在抛光过程中能起到很好的降温作用，防止由于抛光产生温度升高使皮革纤维变形。
附图说明
图1，专利ZL201110179680.4 中的皮革截面图；
图2，用金刚石抛光膏抛光后的牛皮蓝革截面图；
图3，用本发明实施例1抛光液抛光后的牛皮蓝革截面图；
图4，用本发明实施例2抛光液抛光后的牛皮蓝革截面图。
具体实施方式
实施例1
将1g丙二醇、3g乙醇加入100g水中，混合均匀，得到金相制样法获取皮革样品截面图片用抛光液。
用喷雾器向绒布抛光盘上均匀喷洒约5ml抛光液，将包埋打磨好的牛皮蓝革样块放到抛光盘上，以100转/分钟的速度抛光1分钟，在样品上施加约10N的压力，然后到显微镜下观察获取截面图片如图3。
实施例2
将3g丙二醇、20g乙醇加入100g水中，混合均匀，得到金相制样法获取皮革样品截面图片用抛光液。
用喷雾器向绒布抛光盘上均匀喷洒约15ml抛光液，将包埋打磨好的牛皮蓝革样块放到抛光盘上，以200转/分钟的速度抛光3分钟，在样品上施加约30N的压力，然后到显微镜下观察获取截面图片如图4。
从图3和图4可见，该发明抛光液抛光的皮革截面图片与专利ZL201110179680中的皮革截面图片（图1）和金刚石抛光膏抛光的皮革截面图片（图2）相比，图像更清晰，组织结构更精细，轮廓更明显。
以上实例仅用于说明本发明之用，而非对本发明的限制，有关技术领域的技术人员，在不脱离本发明的精神和范围的情况下，还可以作出各种变换或变型，因此所有等同的技术方案也应该属于本发明的范畴，应由各权利要求所限定。
Claims (3)
1.一种金相制样法获取皮革样品截面图片用抛光液，其特征是由水、丙二醇、乙醇组成，各组分的质量份数为：水100份，丙二醇1-3份、乙醇3-20份。
2.如权利要求1所述的适用于金相制样法获取皮革样品截面图片用抛光液，其制备方法为，将水、丙二醇、乙醇按比例混合均匀即可。
3.如权利要求1所述的适用于金相制样法获取皮革样品截面图片用抛光液，其使用方法为：用常用喷雾器向绒布抛光盘均匀喷洒5-15ml抛光液，将打磨好的皮革样块放到抛光盘上，以100-200转/分钟的速度抛光1-3分钟，在样品上施加约10-30N的压力。