CN103643401A - Production process of real silk knitted fabric - Google Patents
Production process of real silk knitted fabric Download PDFInfo
- Publication number
- CN103643401A CN103643401A CN201310622719.4A CN201310622719A CN103643401A CN 103643401 A CN103643401 A CN 103643401A CN 201310622719 A CN201310622719 A CN 201310622719A CN 103643401 A CN103643401 A CN 103643401A
- Authority
- CN
- China
- Prior art keywords
- silk
- minutes
- knitting
- knitted fabric
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a real silk knitted fabric. The production process includes the steps: 1) uniformly attaching 35-45 parts by weight of natural silk on the surface of 55-65 parts by weight of spandex silk in a silk reeling mode to manufacture core spun silk; 2) twisting and winding the core spun silk into a core spun silk cylinder; 3) knitting; 4) scutching and expanding a ropy silk fabric into an open-width state; 5) setting the fabric for 15 minutes at the high temperature ranging from 190 DEG C to 195 DEG C; 6) refining and dressing; 7) secondarily setting the fabric for 10 minutes at the high temperature ranging from 198 DEG C to 200 DEG C; 8) dyeing; 9) flatting the fabric by the aid of steam for 35 minutes in an environment with 7Pa high-pressure steam to obtain the real silk knitted fabric. The mass percentage concentration of alkali is 5-6%, and the temperature ranges from 65 DEG C to 70 DEG C and is kept for 70 minutes. The production process of the real silk knitted fabric is easy to implement and low in production cost, and the produced fully-elastic real silk knitted fabric is fine in quality and wide in application range.
Description
Technical field
The present invention relates to real silk knitted fabrics production technology.
Background technology
Reel silk from cocoons makes cored silk and applies to actual production and also have significant limitation.Cannot, for reticulate pattern tissue and Yarn-dyed fabric, lack the popularity of use.Its reason is that silk in process of production must be whole by the technique such as add water, the heat refining of coming unstuck, and just can reach soft, inhale look and the sliding effect of silk.And spandex thread is met water and significantly shunk, make the series of processes making such as cored silk cannot carry out network, spelling, beats, sth. made by twisting.The characteristic of two kinds of raw materials is conflicted completely, can not general character, and the cored silk therefore mixing is very narrow on applicable surface.
Summary of the invention
The object of the present invention is to provide a kind of real silk knitted fabrics production technology, it is easy to implement, and production cost is low, and the full elastic real silk knitted fabrics quality better of production, has wide range of applications.
For achieving the above object, technical scheme of the present invention is a kind of real silk knitted fabrics production technology of design, comprises the steps:
1) by filature mode, allow 35-45 parts by mass silk be attached to equably 55-65 parts by mass spandex thread surface, make cored silk;
2) doff: cored silk twisting winding is become to cored silk cylinder;
3) knitting and weaving: comprise through compiling and weft knitting, through compiling, for yarn is arranged in parallel, be wound into warp beam, weft knitting is for to be placed on every one thread of cored silk cylinder on each knitting needle of weft-knitting machine, to form weft-knitted fabric along broadwise order ground cushion, then the machine of going up is produced, and obtains rope form silk fabrics;
4) rope form silk fabrics open-width is extended to open width state;
5) 190-195 ℃ of high-temperature shaping 15 minutes;
6) refine whole: alkali mass percentage concentration is 5-6%, and temperature is 65-70 ℃, is incubated 70 minutes;
7) 198-200 ℃ of secondary high-temperature sizing 10 minutes;
8) dyeing;
9) under the environment of steam high pressure 7Pa, steam mud is put down 35 minutes, obtains real silk knitted fabrics.
Advantage of the present invention and beneficial effect are: a kind of real silk knitted fabrics production technology is provided, and it is easy to implement, and production cost is low, and the full elastic real silk knitted fabrics quality better of production, has wide range of applications.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A real silk knitted fabrics production technology, comprises the steps:
1) by filature mode, allow 45 parts by mass silks be attached to equably 65 parts by mass spandex thread surfaces, make cored silk;
2) doff: cored silk twisting winding is become to cored silk cylinder;
3) knitting and weaving: comprise through compiling and weft knitting, through compiling, for yarn is arranged in parallel, be wound into warp beam, weft knitting is for to be placed on every one thread of cored silk cylinder on each knitting needle of weft-knitting machine, to form weft-knitted fabric along broadwise order ground cushion, then the machine of going up is produced, and obtains rope form silk fabrics;
4) rope form silk fabrics open-width is extended to open width state;
5) 195 ℃ of high-temperature shapings 15 minutes;
6) refine whole: alkali mass percentage concentration is 6%, and temperature is 70 ℃, is incubated 70 minutes;
7) 200 ℃ of secondary high-temperature sizings 10 minutes;
8) dyeing;
9) under the environment of steam high pressure 7Pa, steam mud is put down 35 minutes, obtains real silk knitted fabrics.
Embodiment 2
A real silk knitted fabrics production technology, comprises the steps:
1) by filature mode, allow 35 parts by mass silks be attached to equably 55 parts by mass spandex thread surfaces, make cored silk;
2) doff: cored silk twisting winding is become to cored silk cylinder;
3) knitting and weaving: comprise through compiling and weft knitting, through compiling, for yarn is arranged in parallel, be wound into warp beam, weft knitting is for to be placed on every one thread of cored silk cylinder on each knitting needle of weft-knitting machine, to form weft-knitted fabric along broadwise order ground cushion, then the machine of going up is produced, and obtains rope form silk fabrics;
4) rope form silk fabrics open-width is extended to open width state;
5) 190 ℃ of high-temperature shapings 15 minutes;
6) refine whole: alkali mass percentage concentration is 5%, and temperature is 65 ℃, is incubated 70 minutes;
7) 198 ℃ of secondary high-temperature sizings 10 minutes;
8) dyeing;
9) under the environment of steam high pressure 7Pa, steam mud is put down 35 minutes, obtains real silk knitted fabrics.
Embodiment 3
A real silk knitted fabrics production technology, comprises the steps:
1) by filature mode, allow 40 parts by mass silks be attached to equably 60 parts by mass spandex thread surfaces, make cored silk;
2) doff: cored silk twisting winding is become to cored silk cylinder;
3) knitting and weaving: comprise through compiling and weft knitting, through compiling, for yarn is arranged in parallel, be wound into warp beam, weft knitting is for to be placed on every one thread of cored silk cylinder on each knitting needle of weft-knitting machine, to form weft-knitted fabric along broadwise order ground cushion, then the machine of going up is produced, and obtains rope form silk fabrics;
4) rope form silk fabrics open-width is extended to open width state;
5) 193 ℃ of high-temperature shapings 15 minutes;
6) refine whole: alkali mass percentage concentration is 5.6%, and temperature is 67 ℃, is incubated 70 minutes;
7) 199 ℃ of secondary high-temperature sizings 10 minutes;
8) dyeing;
9) under the environment of steam high pressure 7Pa, steam mud is put down 35 minutes, obtains real silk knitted fabrics.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. real silk knitted fabrics production technology, is characterized in that, comprises the steps:
1) by filature mode, allow 35-45 parts by mass silk be attached to equably 55-65 parts by mass spandex thread surface, make cored silk;
2) doff: cored silk twisting winding is become to cored silk cylinder;
3) knitting and weaving: comprise through compiling and weft knitting, through compiling, for yarn is arranged in parallel, be wound into warp beam, weft knitting is for to be placed on every one thread of cored silk cylinder on each knitting needle of weft-knitting machine, to form weft-knitted fabric along broadwise order ground cushion, then the machine of going up is produced, and obtains rope form silk fabrics;
4) rope form silk fabrics open-width is extended to open width state;
5) 190-195 ℃ of high-temperature shaping 15 minutes;
6) refine whole: alkali mass percentage concentration is 5-6%, and temperature is 65-70 ℃, is incubated 70 minutes;
7) 198-200 ℃ of secondary high-temperature sizing 10 minutes;
8) dyeing;
9) under the environment of steam high pressure 7Pa, steam mud is put down 35 minutes, obtains real silk knitted fabrics.