CN103643237A - 盐酸复合缓蚀剂 - Google Patents

盐酸复合缓蚀剂 Download PDF

Info

Publication number
CN103643237A
CN103643237A CN201310556200.0A CN201310556200A CN103643237A CN 103643237 A CN103643237 A CN 103643237A CN 201310556200 A CN201310556200 A CN 201310556200A CN 103643237 A CN103643237 A CN 103643237A
Authority
CN
China
Prior art keywords
corrosion inhibitor
composite corrosion
hydrochloric acid
polyoxyethylene ether
corrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310556200.0A
Other languages
English (en)
Other versions
CN103643237B (zh
Inventor
张明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU SUOLONG FIRE SCIENCE AND TECHNOLOGY Co.,Ltd.
Original Assignee
Qingdao Baizhong Chemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Baizhong Chemical Technology Co Ltd filed Critical Qingdao Baizhong Chemical Technology Co Ltd
Priority to CN201310556200.0A priority Critical patent/CN103643237B/zh
Publication of CN103643237A publication Critical patent/CN103643237A/zh
Application granted granted Critical
Publication of CN103643237B publication Critical patent/CN103643237B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种盐酸复合缓蚀剂，其特征在于，所述复合缓蚀剂由以下组分按质量百分比组成：盐酸3-7%；2-苯基咪唑啉季铵盐0.05-0.35%；碘化钾0.05-0.17%；三乙醇胺0.08-0.15%；脂肪醇聚氧乙烯醚0.02-0.05%；烷基酚聚氧乙烯醚0.016-0.027%;余量为水。本发明所用的2-苯基咪唑啉季铵盐，属于环境友好产品，化学性质稳定、毒性低。加之利用缓蚀剂之间的协同效应缓蚀效果及适用性好，加入少量即可起缓蚀作用，废液无恶臭，毒性低，符合排放标准。

Description

盐酸复合缓蚀剂
技术领域
本发明涉及一种复合缓蚀剂，尤其涉及一种盐酸复合缓蚀剂。
背景技术
近年来，锅炉酸洗用缓蚀剂为目前锅炉化学清洗中急需的一种专用缓蚀剂。然而 现有的锅炉酸洗用缓蚀剂性能不够稳定，保质期短，且有较强刺激性气味。由于采用单一性组份作为缓蚀剂，往往达不到酸洗的要求。随着人类环保意识的增强，在应用开发缓蚀剂过程中，着重开发低毒的缓蚀剂。
发明内容
本发明公开了一种盐酸复合缓蚀剂，其特征在于，所述复合缓蚀剂由以下组分按质量百分比组成：
盐酸                        3-7%；               
2-苯基咪唑啉季铵盐          0.05-0.35% ；
碘化钾                      0.05-0.17%；
三乙醇胺                    0.08-0.15%；
脂肪醇聚氧乙烯醚            0.02-0.05%；
烷基酚聚氧乙烯醚            0.016-0.027%；
余量为水。
优选的，盐酸复合缓蚀剂由以下组分按质量百分比组成：
盐酸                        3-6%；               
2-苯基咪唑啉季铵盐          0.05-0.15% ；
碘化钾                      0.05-0.11%；
三乙醇胺                    0.09-0.12%；
脂肪醇聚氧乙烯醚            0.02-0.04%；
烷基酚聚氧乙烯醚            0.016-0.024%；
余量为水。
优选的，所述复合剂酸洗温度为50°C -60°C。
优选的，所述复合剂酸洗时间为4-6h。
优选的，所述复合剂酸洗液使用时需用碱液调节PH3.5-4.0。 
优选的，所用碱液为氨水。
本发明的有益效果具体体现为：
本发明所用的2-苯基咪唑啉季铵盐，属于环境友好产品，化学性质稳定、毒性低。
加之利用缓蚀剂之间的协同效应缓蚀效果及适用性好，加入少量即可起缓蚀作用，静态腐蚀速度低于0.4g/ m2·h，并不会产生针状点蚀或扩大加深原始的腐蚀斑痕；清洗后试片光亮，不残留有害 薄膜，无明显镀铜现象；溶垢能力强，不会在52°C内快速分解、变质，耐长期存放；废液无恶臭，毒性低，符合排放标准。
具体实施方式
实施例1
原料制备：
盐酸                        3公斤；               
2-苯基咪唑啉季铵盐          0.05公斤 ；
碘化钾                      0.05公斤；
三乙醇胺                    0.08公斤；
脂肪醇聚氧乙烯醚            0.02公斤；
烷基酚聚氧乙烯醚            0.016公斤；
水                          96.784公斤。
连接锅炉清洗系统，调试锅炉水压至符合要求锅炉上水至汽包低水位，隔离与清洗无关系统，升温至52°C左右，加入本发明的盐酸复合缓蚀剂，保持该温度下循环，时间 控制在4-6 小时，用氨水调节酸洗液PH在4.0。
经测试，锅炉钢中静态腐蚀速度0.4g/ m2·h，并不会产生针状点蚀或扩大加深原始的腐蚀斑痕；清洗后试片光亮，不残留有害薄膜，无明显镀铜现象；溶垢能力强， 不会在52°C内快速分解、变质，耐长期存放；废液无恶臭，毒性低，符合排放标准。
按照中华人民共和国国家标准GB/T16632-200“水处理阻垢性能的测定碳酸钙沉积法”进行了静态阻垢试验。
         测试结果         静态阻垢试验阻碳酸钙率95.17%。
 
实施例2
原料制备：
盐酸                       6公斤；               
2-苯基咪唑啉季铵盐          0.15公斤 ；
碘化钾                      0.11公斤；
三乙醇胺                    0.12公斤；
脂肪醇聚氧乙烯醚            0.04公斤；
烷基酚聚氧乙烯醚            0.024公斤；
水                          93.556公斤。
连接锅炉清洗系统，调试锅炉水压至符合要求锅炉上水至汽包低水位，隔离与清洗无关系统，升温至52°C左右，加入本发明的盐酸复合缓蚀剂，保持该温度下循环，时间 控制在 4-6 小时，用氨水调节酸洗液PH在4.0。
经测试，锅炉钢中静态腐蚀速度0.18g/ m2·h，并不会产生针状点蚀或扩大加深原始的腐蚀斑痕；清洗后试片光亮，不残留有害薄膜，无明显镀铜现象；溶垢能力强，不会在52°C内快速分解、变质，耐长期存放；废液无恶臭，毒性低，符合排放标准。
按照中华人民共和国国家标准GB/T16632-200“水处理阻垢性能的测定碳酸钙沉积法”进行了静态阻垢试验。
         测试结果         静态阻垢试验阻碳酸钙率95.48%
实施例3
原料制备：
盐酸                       7公斤；               
2-苯基咪唑啉季铵盐          0.35公斤 ；
碘化钾                      0.17公斤；
三乙醇胺                    0.15公斤；
脂肪醇聚氧乙烯醚            0.05公斤；
烷基酚聚氧乙烯醚            0.027公斤；
水                          92.253公斤。
连接锅炉清洗系统，调试锅炉水压至符合要求锅炉上水至汽包低水位，隔离与清洗无关系统，升温至52°C左右，加入本发明的盐酸复合缓蚀剂，保持该温度下循环，时间 控制在 4-6小时，用氨水调节酸洗液PH在4.0。
经测试，锅炉钢中静态腐蚀速度0.18g/ m2·h，并不会产生针状点蚀或扩大加深原始的腐蚀斑痕；清洗后试片光亮，不残留有害薄膜，无明显镀铜现象；溶垢能力强， 不会在52°C内快速分解、变质，耐长期存放；废液无恶臭，毒性低，符合排放标准。
按照中华人民共和国国家标准GB/T16632-200“水处理阻垢性能的测定碳酸钙沉积法”进行了静态阻垢试验。
         测试结果         静态阻垢试验阻碳酸钙率95.46%。

Claims (6)

1.一种盐酸复合缓蚀剂，其特征在于，所述复合缓蚀剂由以下组分按质量百分比组成：
盐酸                        3-7%；               
2-苯基咪唑啉季铵盐          0.05-0.35% ；
碘化钾                      0.05-0.17%；
三乙醇胺                    0.08-0.15%；
脂肪醇聚氧乙烯醚            0.02-0.05%；
烷基酚聚氧乙烯醚            0.016-0.027%;
余量为水。
2.根据权利要求1所述复合缓蚀剂，其特征在于，所述复合缓蚀剂由以下组分按质量百分比组成：
盐酸                        3-6%；               
2-苯基咪唑啉季铵盐          0.05-0.15% ；
碘化钾                      0.05-0.11%；
三乙醇胺                    0.09-0.12%；
脂肪醇聚氧乙烯醚            0.02-0.04%；
烷基酚聚氧乙烯醚            0.016-0.024%；
余量为水。
3.根据权利要求书1或2所述复合缓蚀剂，其特征在于，所述复合剂酸洗温度为50°C -60°C。
4.根据权利要求书3所述复合缓蚀剂，其特征在于，所述复合剂酸洗时间为4-6h。
5. 根据权利要求书3所述复合缓蚀剂，其特征在于，所述复合剂酸洗液使用时需用碱液调节PH3.5-4.0。
6. 根据权利要求书4所述股配缓蚀剂，其特征在于，所用碱液为氨水。
CN201310556200.0A 2013-11-11 2013-11-11 盐酸复合缓蚀剂 Active CN103643237B (zh)