CN103642369A - Dry and mixed matte powder paint - Google Patents
Dry and mixed matte powder paint Download PDFInfo
- Publication number
- CN103642369A CN103642369A CN201310394765.3A CN201310394765A CN103642369A CN 103642369 A CN103642369 A CN 103642369A CN 201310394765 A CN201310394765 A CN 201310394765A CN 103642369 A CN103642369 A CN 103642369A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mixed
- dry
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a dry and mixed matte powder paint. The paint is composed of the following raw materials, by weight, 6-10 parts of calcium carbonate, 2-3 parts of titanium dioxide, 2-3 parts of moire agent SPA-100, 1-2 parts of sodium antimonite, 60-70 parts of polyester resin TB-670, 10-20 parts of triglycidyl isocyanurate, 3-5 parts of polyisobutene, 6-10 parts of magnesium carbonate, 1-2 parts of dibutyltin dilaurate, 0.1-0.2 part of pyromellitic dianhydride and 10-20 parts of composite filling materials. The paint has fewer impurities, has good cut and scratch resistance, good impact resistance and good and comfortable gloss, is a solvent-free, thermoset, high-intensitive decorative wear-resistant material, and can achieve light extinction effects during solidification of the powder.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of dry mix sub-light powder paint.
Background technology
Powder coating is a kind of novel not containing solvent 100% solid powdery coating.There is solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, the physical strength high that reduces labor intensity and film, and be to improve at present reasonable mode of performance powder coating by the performance that adds different auxiliary agents to improve powder coating.
Summary of the invention
The object of the invention is exactly for a kind of dry mix sub-light powder paint is provided.
The present invention is achieved by the following technical solutions:
A dry mix sub-light powder paint, is characterized in that what it was comprised of the raw material of following weight parts:
Calcium carbonate 6-10, titanium dioxide 2-3, moire agent SPA-1002-3, sodium antimonate 1-2, vibrin TB-67060-70, isocyanuric acid three-glycidyl ester 10-20, polyisobutene 3-5, magnesiumcarbonate 6-10, dibutyl tin laurate 1-2, pyromellitic acid dianhydride 0.1-0.2, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Clay 40-50, iron ore ground-slag 40-50, Calucium Silicate powder 10-20, cuprichexafluorosilicate 2-3, aluminum nitride powder 1-2, nanometer jade powder 5-7, Imarcaptoacetate dioctyltin 0.2-0.3, Flos Rosae Rugosae quintessence oil 0.6-1, water are appropriate;
Above-mentioned Calucium Silicate powder is mixed with cuprichexafluorosilicate, aluminum nitride powder is joined in 3-5 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate after stirring, add nanometer jade powder after stirring, stirring heating 30-40 minute at 80-100 ℃, must expect a; Clay is mixed with iron ore ground-slag, and 600-700 ℃ of calcining 2-3 hour, mixes with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grinds, and adds each raw material of residue, fully stirs, and dries, and obtains described compounded mix.
A preparation method for dry mix sub-light powder paint, comprises the following steps:
Above-mentioned vibrin TB-670, isocyanuric acid three-glycidyl ester, polyisobutene, compounded mix, magnesiumcarbonate, calcium carbonate are mixed, melt extrude, cooling, add each raw material of residue, be dry mixed, Crushing of Ultrafine, crosses screen sizing, obtains described dry mix sub-light powder paint.
Advantage of the present invention is:
Coating impurity of the present invention is few, has good anti-delineation, impact resistance and good comfortable gloss, is a kind of solvent-free, and thermoset, high strength are decorated high-abrasive material, can meet powder and when curing, reach extinction effect.
Embodiment
Embodiment 1,
A dry mix sub-light powder paint, it by following weight parts (kilogram) raw material form:
Calcium carbonate 10, titanium dioxide 2, moire agent SPA-1003, sodium antimonate 1, vibrin TB-67070, isocyanuric acid three-glycidyl ester 20, polyisobutene 5, magnesiumcarbonate 10, dibutyl tin laurate 1, pyromellitic acid dianhydride 0.2, compounded mix 20;
Described compounded mix is comprised of the raw material of following weight parts:
Clay 50, iron ore ground-slag 50, Calucium Silicate powder 20, cuprichexafluorosilicate 2, aluminum nitride powder 1, nanometer jade powder 5, Imarcaptoacetate dioctyltin 0.3, Flos Rosae Rugosae quintessence oil 0.6, water are appropriate;
Above-mentioned Calucium Silicate powder is mixed with cuprichexafluorosilicate, aluminum nitride powder is joined in 3 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate after stirring, add nanometer jade powder after stirring, stirring heating is 40 minutes at 100 ℃, must expect a; Clay is mixed with iron ore ground-slag, calcine 2 hours for 700 ℃, mix with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grind, add each raw material of residue, fully stir, dry, obtain described compounded mix.
A preparation method for dry mix sub-light powder paint, comprises the following steps:
Above-mentioned vibrin TB-670, isocyanuric acid three-glycidyl ester, polyisobutene, compounded mix, magnesiumcarbonate, calcium carbonate are mixed, melt extrude, cooling, add each raw material of residue, be dry mixed, Crushing of Ultrafine, crosses screen sizing, obtains described dry mix sub-light powder paint.
Performance test:
Artificial accelerated aging time >=500h;
Exposure to weather(ing) 12 months is non-foaming, non-corrosive, do not ftracture, do not peel off;
Washability number of times >=10000 time.
Claims (2)
1. a dry mix sub-light powder paint, is characterized in that what it was comprised of the raw material of following weight parts:
Calcium carbonate 6-10, titanium dioxide 2-3, moire agent SPA-1002-3, sodium antimonate 1-2, vibrin TB-67060-70, isocyanuric acid three-glycidyl ester 10-20, polyisobutene 3-5, magnesiumcarbonate 6-10, dibutyl tin laurate 1-2, pyromellitic acid dianhydride 0.1-0.2, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Clay 40-50, iron ore ground-slag 40-50, Calucium Silicate powder 10-20, cuprichexafluorosilicate 2-3, aluminum nitride powder 1-2, nanometer jade powder 5-7, Imarcaptoacetate dioctyltin 0.2-0.3, Flos Rosae Rugosae quintessence oil 0.6-1, water are appropriate;
Above-mentioned Calucium Silicate powder is mixed with cuprichexafluorosilicate, aluminum nitride powder is joined in 3-5 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate after stirring, add nanometer jade powder after stirring, stirring heating 30-40 minute at 80-100 ℃, must expect a; Clay is mixed with iron ore ground-slag, and 600-700 ℃ of calcining 2-3 hour, mixes with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grinds, and adds each raw material of residue, fully stirs, and dries, and obtains described compounded mix.
2. a preparation method for dry mix sub-light powder paint as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned vibrin TB-670, isocyanuric acid three-glycidyl ester, polyisobutene, compounded mix, magnesiumcarbonate, calcium carbonate are mixed, melt extrude, cooling, add each raw material of residue, be dry mixed, Crushing of Ultrafine, crosses screen sizing, obtains described dry mix sub-light powder paint.