CN103642296A - Novel radiation-proof putty powder - Google Patents
Novel radiation-proof putty powder Download PDFInfo
- Publication number
- CN103642296A CN103642296A CN201310710505.2A CN201310710505A CN103642296A CN 103642296 A CN103642296 A CN 103642296A CN 201310710505 A CN201310710505 A CN 201310710505A CN 103642296 A CN103642296 A CN 103642296A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty powder
- novel radiation
- weight
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to novel radiation-proof putty powder which consists of 3-15 parts by weight of polyvinyl alcohol, white latex and polyurethane or allylthiourea-modified carboxymethylcellulose which are used as adhesives, 100 parts by weight of white cement, barium sulfate and ash-calcium-powder which are used as aggregate, and 1-2 parts by weight of a mixture of palm oil and acrylamide-modified carboxymethylcellulose which is used as an anti-cracking additive. The paint, namely the novel radiation-proof putty powder can effectively shield radioactive substances; after the putty powder disclosed by the invention is coated to be 0.4-0.5mm, the index of the radioactive substances is reduced to 0.2-0.4baker/Kg; moreover, the novel radiation-proof putty powder has the characteristics of high hardness, cracking prevention and washing durability and never fades away.
Description
Technical field
The present invention relates to a kind of formula of Novel radiation-protection putty powder, this formula has been strengthened the anti-aging of putty powder, high rigidity and water tolerance.
Background technology
The high hard water-fastness putty rubber powder of NSJF-2A type is white meal, to adopt Germany technology to process through science, nontoxic, tasteless, "dead", can be dissolved in rapidly cold water, have dissolve fast, consumption is little, viscosity is high, film forming is fast, suspension, moisturizing, antienzyme, ageing-resistant, the shelf time long, easy to use, steady performance.With the putty powder of its preparation, easy construction, do not roll up skin while using, film forming is fast, hardness is high, water-tolerant, anti crack performance are good, is a kind of new green environment protection type putty powder that can water modulation.The height that is made into this rubber powder is hard, water-proof putty powder can increase putty with the bonding force of exterior wall, reduces usage quantity 20% left and right of exterior coating, and water resistance is good, can be more and more harder in water, and also the cost of preparation putty powder will reduce by 30% left and right than other rubber powder.Product application scope: 1. mainly make putty rubber powder in building putty powder, hard, the water-fastness putty powder for exterior wall of processing height, the colored spackling of outdoor tile, the aspects such as outdoor tile tamanori are used, quality is high, effective, in national building putty powder industry, has obtained promoting the use of rapidly.In building trade for the manufacture of building mortar.This product adds in the slurry of cement, sand or lime, has good agglutinating value(of coal), and is easy to mix and condense, the hard and excess shrinkage not of made goods.In the time of coagulation of controlling cement slurry, raising flexural strength and compressive strength, reduce the aspects such as shrinking percentage and there is unusual effect.As hard in height, laundry-resistant mosaic (ceramic tile) exterior wall NSJF-2A rubber powder 1.5～1.9%, white cement (black cement) 40%, dry powder 20 ~ 40%, ash calcium powder 20 ~ 30%, the anticracking of resistance to think of additive 1～3%, silica powder (180# sand) 20%, production method: add dry powder in putty powder stirrer, then add the high hard water-fastness putty rubber powder of major ingredient NSJF-2A type and Nai Si anticracking additive to mix 2～3 minutes, finally add cement, grey calcium powder, (silica powder), forward stirs 10 minutes, and reverse agitating function 10 minutes, can pack as finished product.This putty powder has following effect: 1. easy to use, add the i.e. use of water, according to the ratio of powder: water=1:0.4, add water and stir and can construct (1 kilogram of putty powder adds 0.4 kilogram of left and right of water).Also can be according to individual service requirements, add water and be modulated to suitable denseness and can construct, batching can be rare can be thick.The available hand blender of extensive construction stirs, better effects if.2. putty is criticized and is scraped rear its 48 hours primary solidification in surface twice, and hardness improves, and water tolerance improves.
But research and development Novel radiation-protection, anti-aging, laundry-resistant putty powder are in bottleneck always.
Summary of the invention
The object of the present invention is to provide a kind of novel radiation-resistant putty powder, through scientific formula and proportioning, make there is high radioprotective, the putty powder of anti-aging, water-fastness effect.
The present invention realizes above-mentioned purpose like this:
A Novel radiation-protection putty powder, comprises caking agent, aggregate, and anticracking additive, counts by weight, and aggregate is 100 parts, caking agent 3-15 part, anticracking additive 1-2 part.More preferably aggregate is 100 parts, 12 parts of caking agents, 1.6 parts of anticracking additives.
Described caking agent is one or more in the carboxymethyl cellulose of polyvinyl alcohol, white glue with vinyl, urethane, the modification of propenyl thiocarbamide.
Described aggregate, for being milled to 300-400 object white cement, barium sulfate and grey calcium powder, is counted by weight, and white cement is 10-22 part, barium sulfate 40-80 part, grey calcium powder 5-15 part.Preferred white cement is 20 parts, 65 parts, barium sulfate, 15 parts of grey calcium powders.
Described anticracking additive is the mixture of plam oil and acrylic amide modified carboxymethyl cellulose, meter by weight, and plam oil is 0.1 ~ 0.8 part, acrylic amide modified carboxymethyl cellulose is 1.0 ~ 1.2 parts.Preferred plam oil is 0.6 part, and acrylic amide modified carboxymethyl cellulose is 1.0 parts.
A preparation method for Novel radiation-protection putty powder, after white cement, barium sulfate, grey calcium powder are fully mixed, adds caking agent, after stirring 2-7min, adds anticracking additive, and the 25-30min that reverses after forward 25-30min makes.
Adopt radioprotective putty powder of the present invention to be coated in after surface of wall, can shield effectively to greatest extent its radioactive substance, apply after the putty powder of the present invention of one deck 0.4mm-0.5mm, after testing near 0.2-0.4 Bake under its radioactive substance index/kilogram, (in country, penetrate the standard of index be < 1 Bake/kilogram), tradition radioprotective putty powder is just used blaue fixe as auxiliary material, and the present invention uses blaue fixe as aggregate, add appropriate high-quality white portland cement simultaneously, its effect is better than traditional radioprotective putty powder greatly, major advantage is: shielding is stronger, high hard, anticracking, water-fastness, will never fade, it is the optimal selection of finishing material in vast building property, the best of high-risk Working environment is first-selected especially, (as various big hospital, scientific research institution etc.).
Embodiment
embodiment 1
A Novel radiation-protection putty powder, comprises 3kg caking agent, 100kg aggregate, and 1kg anticracking additive, described caking agent is that the carboxymethyl cellulose of polyvinyl alcohol and the modification of propenyl thiocarbamide be take the mixture that mass ratio is 1:2; Described aggregate was for being milled to 300-400 object white cement 15kg, barium sulfate 80kg, grey calcium powder 5kg; Described anticracking additive is the mixture of the acrylic amide modified carboxymethyl cellulose of 0.2kg plam oil and 0.8kg.
embodiment 2
A Novel radiation-protection putty powder, comprises 10kg caking agent, 100kg aggregate, and 2kg anticracking additive, described caking agent is that the carboxymethyl cellulose of white glue with vinyl and the modification of propenyl thiocarbamide be take the mixture that mass ratio is 1:1.5; Described aggregate was for being milled to 300-400 object white cement 20kg, barium sulfate 65kg, grey calcium powder 15kg; Described anticracking additive is the mixture of the acrylic amide modified carboxymethyl cellulose of 0.8kg plam oil and 1.2kg.
embodiment 3
A Novel radiation-protection putty powder, comprises 8.5kg caking agent, 100kg aggregate, and 1.8kg anticracking additive, described caking agent is that the carboxymethyl cellulose of urethane and the modification of propenyl thiocarbamide be take the mixture that mass ratio is 1:1; Described aggregate was for being milled to 300-400 object white cement 22kg, barium sulfate 73kg, grey calcium powder 5kg; Described anticracking additive is the mixture of the acrylic amide modified carboxymethyl cellulose of 0.6kg plam oil and 1.2kg.
embodiment 4
A Novel radiation-protection putty powder, comprises 12kg caking agent, 100kg aggregate, and 1.6kg anticracking additive, described caking agent is that polyvinyl alcohol, white glue with vinyl, urethane be take the mixture that mass ratio is 1:1:0.5; Described aggregate was for being milled to 300-400 object white cement 20kg, barium sulfate 65kg, grey calcium powder 15kg; Described anticracking additive is the mixture of the acrylic amide modified carboxymethyl cellulose of 0.6kg plam oil and 1.0kg.
Claims (7)
1. a Novel radiation-protection putty powder, comprises caking agent, aggregate, and anticracking additive, is characterized in that, counts by weight, aggregate is 100 parts, caking agent 3-15 part, anticracking additive 1-2 part.
2. Novel radiation-protection putty powder according to claim 1, is characterized in that, percentage ratio meter by weight, and aggregate is 100 parts, 12 parts of caking agents, 1.6 parts of anticracking additives.
3. Novel radiation-protection putty powder according to claim 1 and 2, is characterized in that, described caking agent is one or more in the carboxymethyl cellulose of polyvinyl alcohol, white glue with vinyl, urethane, the modification of propenyl thiocarbamide.
4. Novel radiation-protection putty powder according to claim 1 and 2, is characterized in that, described aggregate was for being milled to 300-400 object white cement, barium sulfate and grey calcium powder, count by weight, white cement is 10-22 part, barium sulfate 40-80 part, grey calcium powder 5-15 part.
5. Novel radiation-protection putty powder according to claim 4, is characterized in that, percentage ratio meter by weight, and white cement is 20 parts, 65 parts, barium sulfate, 15 parts of grey calcium powders.
6. Novel radiation-protection putty powder according to claim 1, it is characterized in that, described anticracking additive is the mixture of plam oil and acrylic amide modified carboxymethyl cellulose, count by weight, plam oil is 0.1 ~ 0.8 part, and acrylic amide modified carboxymethyl cellulose is 1.0 ~ 1.2 parts.
7. Novel radiation-protection putty powder according to claim 6, is characterized in that, counts by weight, and plam oil is 0.6 part, and acrylic amide modified carboxymethyl cellulose is 1.0 parts.