CN103642189A - 一种改性三元乙丙橡胶复合密封垫材料及其制备方法 - Google Patents

一种改性三元乙丙橡胶复合密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103642189A
CN103642189A CN201310577511.5A CN201310577511A CN103642189A CN 103642189 A CN103642189 A CN 103642189A CN 201310577511 A CN201310577511 A CN 201310577511A CN 103642189 A CN103642189 A CN 103642189A
Authority
CN
China
Prior art keywords
parts
ethylene propylene
diene monomer
propylene diene
gasket material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310577511.5A
Other languages
English (en)
Other versions
CN103642189B (zh
Inventor
胡建强
胡巍
李丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Saiying Electronics Technology Development Inc
Original Assignee
Bengbu Saiying Electronics Technology Development Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Saiying Electronics Technology Development Inc filed Critical Bengbu Saiying Electronics Technology Development Inc
Priority to CN201310577511.5A priority Critical patent/CN103642189B/zh
Publication of CN103642189A publication Critical patent/CN103642189A/zh
Application granted granted Critical
Publication of CN103642189B publication Critical patent/CN103642189B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改性三元乙丙橡胶复合密封垫材料，其特征在于，由下列重量份的原料制成：三元乙丙橡胶30-35、一元均聚氯醇橡胶52-57、共聚氯醇橡胶12-18、硬脂酸锌4-5、防老剂RD1-3、电炉除尘灰10-15、硅粉2-3、硫磺1.5-3、促进剂DM2-4、N351炭黑35-40、N660炭黑14-18、马来酸二辛酯10-12、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有很好的力学性质，弹性好，压缩形变低，耐磨损性好，密封性高，配方合理，工艺简单，成本低，适合工业化生产。

Description

一种改性三元乙丙橡胶复合密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种改性三元乙丙橡胶复合密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。
发明内容
本发明的目的是提供一种改性三元乙丙橡胶复合密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种改性三元乙丙橡胶复合密封垫材料，由下列重量份的原料制成：三元乙丙橡胶30-35、一元均聚氯醇橡胶52-57、共聚氯醇橡胶12-18、硬脂酸锌4-5、防老剂RD1-3、电炉除尘灰10-15、硅粉2-3、硫磺1.5-3、促进剂DM2-4、N351炭黑35-40、N660炭黑14-18、马来酸二辛酯10-12、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土13-16、1,6-己二异氰酸酯4-5、二缩三丙二醇二丙烯酸酯2-3、轻质碳酸钙2-3、氧化锌1-2、硅灰石粉3-4、氢氧化镁10-12、氯化石蜡1-2、硅藻土4-5、柠檬酸三丁酯2-3、玉石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土、硅藻土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述改性三元乙丙橡胶复合密封垫材料，由以下具体步骤制成：将三元乙丙橡胶、硬脂酸、防老剂RD加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至140-160℃，再加入电炉除尘灰、硅粉、硫磺、促进剂DM、N351炭黑，混炼6-8min，再加入N660炭黑、马来酸二辛酯继续混炼4-6min；然后降温至80-90℃，加入其余剩余成分混炼6-8min，即得。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有很好的力学性质，弹性好，压缩形变低，耐磨损性好，密封性高，配方合理，工艺简单，成本低，适合工业化生产。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种改性三元乙丙橡胶复合密封垫材料，由下列重量份（公斤）的原料制成：三元乙丙橡胶30、一元均聚氯醇橡胶52、共聚氯醇橡胶12、硬脂酸锌4、防老剂RD1、电炉除尘灰10、硅粉2、硫磺1.5、促进剂DM2、N351炭黑35、N660炭黑14、马来酸二辛酯10、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土13、1,6-己二异氰酸酯4、二缩三丙二醇二丙烯酸酯2、轻质碳酸钙2、氧化锌1、硅灰石粉3、氢氧化镁10、氯化石蜡1、硅藻土4、柠檬酸三丁酯2、玉石粉8、花椒籽油1；制备方法是将凹凸棒土、粘土、硅藻土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述改性三元乙丙橡胶复合密封垫材料，由以下具体步骤制成：将三元乙丙橡胶、硬脂酸、防老剂RD加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至140-160℃，再加入电炉除尘灰、硅粉、硫磺、促进剂DM、N351炭黑，混炼6-8min，再加入N660炭黑、马来酸二辛酯继续混炼4-6min；然后降温至80-90℃，加入其余剩余成分混炼6-8min，即得。
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。
Figure BDA0000414996180000021
Figure BDA0000414996180000031
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。

Claims (2)

1.一种改性三元乙丙橡胶复合密封垫材料，其特征在于，由下列重量份的原料制成：三元乙丙橡胶30-35、一元均聚氯醇橡胶52-57、共聚氯醇橡胶12-18、硬脂酸锌4-5、防老剂RD1-3、电炉除尘灰10-15、硅粉2-3、硫磺 1.5-3、促进剂DM2-4、N351炭黑35-40、N660炭黑14-18、马来酸二辛酯10-12、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土13-16、1,6-己二异氰酸酯4-5、二缩三丙二醇二丙烯酸酯2-3、轻质碳酸钙2-3、氧化锌1-2、硅灰石粉3-4、氢氧化镁10-12、氯化石蜡1-2、硅藻土4-5、柠檬酸三丁酯2-3、玉石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土、硅藻土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述改性三元乙丙橡胶复合密封垫材料，其特征在于，由以下具体步骤制成：将三元乙丙橡胶、硬脂酸、防老剂RD加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至140-160℃，再加入电炉除尘灰、硅粉、硫磺、促进剂DM、N351炭黑，混炼6-8min，再加入N660炭黑、马来酸二辛酯继续混炼4-6min；然后降温至80-90℃，加入其余剩余成分混炼6-8min，即得。
CN201310577511.5A 2013-11-15 2013-11-15 一种改性三元乙丙橡胶复合密封垫材料及其制备方法 Expired - Fee Related CN103642189B (zh)