CN103641988B - A kind of Anti-static sponge and preparation method thereof - Google Patents
A kind of Anti-static sponge and preparation method thereof Download PDFInfo
- Publication number
- CN103641988B CN103641988B CN201310566798.1A CN201310566798A CN103641988B CN 103641988 B CN103641988 B CN 103641988B CN 201310566798 A CN201310566798 A CN 201310566798A CN 103641988 B CN103641988 B CN 103641988B
- Authority
- CN
- China
- Prior art keywords
- weight part
- sponge
- weight
- preparation
- properties
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Anti-static sponge and preparation method thereof, its constitutive material is: polyoxypropyleneglycol 100-120, isophorone diisocyanate 40-45, nano-attapulgite 7.5-8.5, conductive carbon fibre 2.0-3.0, triethylene diamine 0.3-0.6, ammonium oxide 0.7-0.9, stannous octoate 0.5-0.7, properties-correcting agent 1-2 and water 4.5-6.5; The present invention has the feature of excellent flexibility, elasticity, anti-electrostatic, water tolerance, and nano-attapulgite has good wettability, acidproof, high temperature resistant and corrosion resistance, and conductive carbon fibre forms conductive layer in sponge, effectively prevents electrostatic from producing.
Description
Technical field
The present invention relates to the preparation method of a kind of sponge, be specifically related to a kind of Anti-static sponge and preparation method thereof.
Background technology
Sponge product is popularized gradually in people's life, the household objects such as the seat wherein having sponge to make, sofa, mattress.People, except the household objects made of sponge, also utilize sponge to be used as cleaning appliance, as cleaned household with sponge product, cleaning bowls and chopsticks with sponge product, having a bath with sponge product.
Existing sponge production method technique is single, and product performance index can not meet market demand completely, and an urgent demand is studied from different aspects.
Summary of the invention
The object of the present invention is to provide a kind of Anti-static sponge and preparation method thereof.
The present invention adopts following technical scheme to achieve these goals:
A kind of Anti-static sponge, is characterized in that the weight part of its constitutive material is: polyoxypropyleneglycol 100-120, isophorone diisocyanate 40-45, nano-attapulgite 7.5-8.5, conductive carbon fibre 2.0-3.0, triethylene diamine 0.3-0.6, ammonium oxide 0.7-0.9, stannous octoate 0.5-0.7, properties-correcting agent 1-2 and water 4.5-6.5.
The preparation method of described properties-correcting agent is: 25-30 weight parts water is added reaction vessel, is heated to 80-90 DEG C; Get carboxymethyl cellulose 2-3 weight part to be added to the water, stirring and dissolving, then add 0.1-0.15 weight part nano-carbon powder, 1.2-1.3 weight part morpholine, 1-1.2 parts by weight of polyoxyethylene ether, 1-2 parts by weight of acrylic acid, stir, be cooled to 20-30 DEG C, add the Sodium Persulfate of 0.2-0.3 weight part, stir, reaction 30-45 minute, then, add 1-2 weight part catechol, 0.1-0.2 weight part Kathon again, continue stirring reaction 45-60 minute, to obtain final product.
The preparation method of described Anti-static sponge, it is characterized in that first the polyoxypropyleneglycol of above-mentioned formula ratio, isophorone diisocyanate, properties-correcting agent being dropped in mixing tank and mixing, stir, and be heated to 30-45 DEG C, again other remaining component of above-mentioned formula ratio is dropped in mixing tank and mix, high-speed stirring 10-30 pours mould into and foams and after solidifying, obtain Anti-static sponge after second.
Properties-correcting agent of the present invention can increase corrosion-resistant, the raw bacterium performance of going mouldy of sponge and flexibility and rebound resilience.
Beneficial effect of the present invention:
The present invention has the feature of excellent flexibility, elasticity, anti-electrostatic, water tolerance, and nano-attapulgite has good wettability, acidproof, high temperature resistant and corrosion resistance, and conductive carbon fibre forms conductive layer in sponge, effectively prevents electrostatic from producing.
Embodiment
Embodiment 1: Anti-static sponge, the weight part (kg) of its constitutive material is: polyoxypropyleneglycol 100, isophorone diisocyanate 40, nano-attapulgite 7.5, conductive carbon fibre 2.0, triethylene diamine 0.3, ammonium oxide 0.7, stannous octoate 0.5, properties-correcting agent 1 and water 4.5.
The preparation method of described properties-correcting agent is: 25 weight parts waters are added reaction vessel, is heated to 80-90 DEG C; Get carboxymethyl cellulose 2 weight part to be added to the water, stirring and dissolving, then add 0.1 weight part nano-carbon powder, 1.2 weight part morpholines, 1 parts by weight of polyoxyethylene ether, 1 parts by weight of acrylic acid, stir, be cooled to 20-30 DEG C, add the Sodium Persulfate of 0.3 weight part, stir, reaction 30-45 minute, then, add 1 weight part catechol, 0.2 weight part Kathon again, continue stirring reaction 45-60 minute, to obtain final product.
The preparation method of Anti-static sponge, it is characterized in that first the polyoxypropyleneglycol of above-mentioned formula ratio, isophorone diisocyanate, properties-correcting agent being dropped in mixing tank and mixing, stir, and be heated to 30-45 DEG C, again other remaining component of above-mentioned formula ratio is dropped in mixing tank and mix, high-speed stirring 10-30 pours mould into and foams and after solidifying, obtain Anti-static sponge after second.
The sponge performance data obtained by above-described embodiment 1 is as follows: hardness 50Kpa, resilience 40%.
Claims (1)
1. an Anti-static sponge, is characterized in that the weight part of its constitutive material is: polyoxypropyleneglycol 100-120, isophorone diisocyanate 40-45, nano-attapulgite 7.5-8.5, conductive carbon fibre 2.0-3.0, triethylene diamine 0.3-0.6, ammonium oxide 0.7-0.9, stannous octoate 0.5-0.7, properties-correcting agent 1-2 and water 4.5-6.5;
The preparation method of described properties-correcting agent is: 25-30 weight parts water is added reaction vessel, is heated to 80-90 DEG C; Get carboxymethyl cellulose 2-3 weight part to be added to the water, stirring and dissolving, then add 0.1-0.15 weight part nano-carbon powder, 1.2-1.3 weight part morpholine, 1-1.2 parts by weight of polyoxyethylene ether, 1-2 parts by weight of acrylic acid, stir, be cooled to 20-30 DEG C, add the Sodium Persulfate of 0.2-0.3 weight part, stir, reaction 30-45 minute, then, add 1-2 weight part catechol, 0.1-0.2 weight part Kathon again, continue stirring reaction 45-60 minute, to obtain final product;
The preparation method of described Anti-static sponge is: first the polyoxypropyleneglycol of above-mentioned formula ratio, isophorone diisocyanate, properties-correcting agent are dropped in mixing tank and mixed, stir, and be heated to 30-45 DEG C, again other remaining component of above-mentioned formula ratio is dropped in mixing tank and mix, high-speed stirring 10-30 pours mould into and foams and after solidifying, obtain Anti-static sponge after second.