CN103627331A - 一种耐水的水性胶黏剂及其制备方法 - Google Patents

一种耐水的水性胶黏剂及其制备方法 Download PDF

Info

Publication number
CN103627331A
CN103627331A CN201310497288.3A CN201310497288A CN103627331A CN 103627331 A CN103627331 A CN 103627331A CN 201310497288 A CN201310497288 A CN 201310497288A CN 103627331 A CN103627331 A CN 103627331A
Authority
CN
China
Prior art keywords
parts
water
preparation
aqueous adhesives
trimethylolethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310497288.3A
Other languages
English (en)
Other versions
CN103627331B (zh
Inventor
石小强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Shi Fan Le Jianxin Materials Co ltd
Original Assignee
JIANGSU BOSIYUAN FIREPROOF MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU BOSIYUAN FIREPROOF MATERIAL TECHNOLOGY Co Ltd filed Critical JIANGSU BOSIYUAN FIREPROOF MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310497288.3A priority Critical patent/CN103627331B/zh
Publication of CN103627331A publication Critical patent/CN103627331A/zh
Application granted granted Critical
Publication of CN103627331B publication Critical patent/CN103627331B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐水的水性胶黏剂及其制备方法，水性胶黏剂由以下成分按照重量比组成：2-甲基丙烯酸乙酯为13～17份、木糖醇为5～7份、三羟甲基乙烷为4～6份、丙二醇为5～7份、乙酸乙烯酯为15～18份、双酚F型环氧树脂为16～17份、水为13～16份。通过搅拌和高速剪切等方式制备得到水性胶黏剂。制备得到的水性胶黏剂具有良好的耐水性能和较高的剥离强度，可以广泛应用于粘结使用当中。

Description

一种耐水的水性胶黏剂及其制备方法
技术领域
本发明涉及一种胶黏剂及其制备方法，特别是涉及一种耐水的水性胶黏剂及其制备方法。
背景技术
胶黏剂可以使用的范围很广，可以应用在许多途径中。例如保温板的粘结、木材的粘结等。其中水性胶黏剂是其中一个很重要的分类，水性胶黏剂的耐水性通常很差，由于其不具有良好的耐水性，因此限制了其在潮湿环境下的应用，进而影响了产品的整体性能，胶黏剂的剥离强度同样也很重要，若剥离强度太低，对胶黏剂的产品性能有很大的影响，影响了产品的整个粘合强度。
发明内容
要解决的技术问题：普通的水性胶黏剂耐水效果差、剥离强度低的问题。
技术方案：本发明公开了一种耐水的水性胶黏剂，水性胶黏剂由以下成分按照重量比组成：2-甲基丙烯酸乙酯为13～17份、木糖醇为5～7份、三羟甲基乙烷为4～6份、丙二醇为5～7份、乙酸乙烯酯为15～18份、双酚F型环氧树脂为16～17份、水为13～16份。
一种耐水的水性胶黏剂的制备方法，制备方法包括以下步骤：（1）将搅拌釜温度调节为75℃，首先取2-甲基丙烯酸乙酯为13～17份、木糖醇为5～7份、三羟甲基乙烷为4～6份、丙二醇为5～7份、乙酸乙烯酯为15～18份、双酚F型环氧树脂为16～17份、水为13～16份，加入搅拌釜中，搅拌转速为140～150rpm，时间为15～20min；（2）再将搅拌后浆料进行剪切处理，剪切转速为3000rpm，时间为5～10min；（3）将处理后的浆料装入密封罐中，制备得耐水水性胶黏剂。2-甲基丙烯酸乙酯优选为17份。三羟甲基乙烷优选为4份。双酚F型环氧树脂优选为16份。
有益效果：通过本发明制备得到的水性胶黏剂具有良好的耐水效果和较高的剥离强度，制备得到的胶黏剂放入水中浸泡50h后，重量增加量只有4.3wt%～7.5wt%，胶黏剂的剥离强度为12.6～16.4N/mm。
具体实施方式
实施例1
（1）将搅拌釜温度调节为75℃，首先取2-甲基丙烯酸乙酯为13kg、木糖醇为7kg、三羟甲基乙烷为4kg、丙二醇为7kg、乙酸乙烯酯为18kg、双酚F型环氧树脂为16kg、水为16kg，加入搅拌釜中，搅拌转速为150rpm，时间为15min；（2）再将搅拌后浆料进行剪切处理，剪切转速为3000rpm，时间为5min；（3）将处理后的浆料装入密封罐中，制备得耐水水性胶黏剂。
实施例2
（1）将搅拌釜温度调节为75℃，首先取2-甲基丙烯酸乙酯为15kg、木糖醇为5kg、三羟甲基乙烷为5kg、丙二醇为6kg、乙酸乙烯酯为17kg、双酚F型环氧树脂为17kg、水为13kg，加入搅拌釜中，搅拌转速为140rpm，时间为20min；（2）再将搅拌后浆料进行剪切处理，剪切转速为3000rpm，时间为10min；（3）将处理后的浆料装入密封罐中，制备得耐水水性胶黏剂。
实施例3
（1）将搅拌釜温度调节为75℃，首先取2-甲基丙烯酸乙酯为17kg、木糖醇为6kg、三羟甲基乙烷为6kg、丙二醇为5kg、乙酸乙烯酯为15kg、双酚F型环氧树脂为16kg、水为14kg，加入搅拌釜中，搅拌转速为150rpm，时间为15min；（2）再将搅拌后浆料进行剪切处理，剪切转速为3000rpm，时间为10min；（3）将处理后的浆料装入密封罐中，制备得耐水水性胶黏剂。
测定了制备得到水性胶黏剂的耐水性能和剥离强度，将实施例1、实施例2、实施例3的产品各取100g，完全浸入水中放置50h后测定其吸水后重量的增加百分比。剥离强度的测定标准为GB/T2791-1995。实验结果如下。
  实施例1 实施例2 实施例3
重量增加量 5.4wt% 4.3wt% 7.5wt%
剥离强度（N/mm） 16.4 12.6 14.7
制备得到的胶黏剂具有良好的耐水特性和较高的剥离强度，可以广泛应用于水性环境当中。

Claims (5)

1.一种耐水的水性胶黏剂，其特征在于水性胶黏剂由以下成分按照重量比组成：2-甲基丙烯酸乙酯为13～17份、木糖醇为5～7份、三羟甲基乙烷为4～6份、丙二醇为5～7份、乙酸乙烯酯为15～18份、双酚F型环氧树脂为16～17份、水为13～16份。
2.一种耐水的水性胶黏剂的制备方法，其特征在于制备方法包括以下步骤：（1）将搅拌釜温度调节为75℃，首先取2-甲基丙烯酸乙酯为13～17份、木糖醇为5～7份、三羟甲基乙烷为4～6份、丙二醇为5～7份、乙酸乙烯酯为15～18份、双酚F型环氧树脂为16～17份、水为13～16份，加入搅拌釜中，搅拌转速为140～150rpm，时间为15～20min；（2）再将搅拌后浆料进行剪切处理，剪切转速为3000rpm，时间为5～10min；（3）将处理后的浆料装入密封罐中，制备得耐水水性胶黏剂。
3.根据权利要求2所述的一种耐水的水性胶黏剂的制备方法，其特征在于2-甲基丙烯酸乙酯为17份。
4.根据权利要求2所述的一种耐水的水性胶黏剂的制备方法，其特征在于三羟甲基乙烷为4份。
5.根据权利要求2所述的一种耐水的水性胶黏剂的制备方法，其特征在于双酚F型环氧树脂为16份。
CN201310497288.3A 2013-10-22 2013-10-22 一种耐水的水性胶黏剂及其制备方法 Expired - Fee Related CN103627331B (zh)