CN103627185A - 一种利用废旧衣物对铺路沥青进行改性的新工艺 - Google Patents
一种利用废旧衣物对铺路沥青进行改性的新工艺 Download PDFInfo
- Publication number
- CN103627185A CN103627185A CN201310522788.8A CN201310522788A CN103627185A CN 103627185 A CN103627185 A CN 103627185A CN 201310522788 A CN201310522788 A CN 201310522788A CN 103627185 A CN103627185 A CN 103627185A
- Authority
- CN
- China
- Prior art keywords
- asphalt
- waste
- clothing
- novel process
- clothes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种利用废旧衣物对铺路沥青进行改性的新工艺,工艺步骤如下:1)将废旧衣物清洗晾晒,至水分含量低于15%;2)将晾晒后的废旧衣服粉碎至直径不大于5mm;3)脱水后的衣服碎料放入烘干机烘干,温度控制在40-50℃,至水分含量在低于5%;4)将烘干后的衣服碎料在沥青熔炼过程中加入,并与沥青混合均匀,1吨沥青中添加衣服碎料200-300公斤;5)混合完成后的沥青直接用于铺路。本发明利用废旧衣服作为填充料加入到沥青中,不仅改善了铺路沥青的粘接、弹性、耐磨性能,增加了沥青产量,同时解决了废旧衣服处理的问题,避免了燃烧污染,提高了资源的利用率。
Description
技术领域
本发明涉及资源再利用技术领域,具体涉及一种利用废旧衣物对铺路沥青进行改性的新工艺
背景技术
随着我国国民经济的高速发展,交通量和交通强度在日益增加,公路迅猛发展。沥青路面因其表面平整、无接缝、行车舒适、振动小、噪音低、耐磨、不扬尘易清洗而广受青睐,在公路建设中沥青需求量越来越大,而且性能需要进一步提高,但现有沥青资源严重不足,性能亟待提高。
同时随着生活水平的提高,人们的衣物更新在加快,淘汰出来的废旧衣物越来越多,弃之可惜,烧之污染,存之堆积成山,如何处置和利用成为现实难题。
发明内容
本发明所要解决的技术问题在于提供一种方法简单,实际应用效果好的利用废旧衣物对铺路沥青进行改性的新工艺。
本发明所要解决的技术问题采用以下技术方案来实现:
一种利用废旧衣物对铺路沥青进行改性的新工艺,其工艺步骤如下:
1)将废旧衣物清洗晾晒,至水分含量低于15%;
2)将晾晒后的废旧衣服粉碎至直径不大于5mm;
3)脱水后的衣服碎料放入烘干机烘干,温度控制在40-50℃,至水分含量低于5%;
4)将烘干后的衣服碎料在沥青熔炼过程中加入,并与沥青混合均匀,1吨沥青中添加衣服碎料200-300公斤;
5)混合完成后的沥青直接用于铺路。
本发明的有益效果是:本发明利用废旧衣服作为填充料加入到沥青中,不仅改善了铺路沥青的粘接、弹性、耐磨性能,增加了沥青产量,同时解决了废旧衣服处理的问题,避免了燃烧污染,提高了资源的利用率。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种利用废旧衣物对铺路沥青进行改性的新工艺,其工艺步骤如下:
1)将废旧衣物清洗晾晒,至水分含量低于15%;
2)将晾晒后的废旧衣服粉碎至直径不大于5mm;
3)脱水后的衣服碎料放入烘干机烘干,温度控制在40-50℃,至水分含量低于5%;
4)将烘干后的衣服碎料在沥青熔炼过程中加入,并与沥青混合均匀,1吨沥青中添加衣服碎料200-300公斤;
5)混合完成后的沥青直接用于铺路。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.一种利用废旧衣物对铺路沥青进行改性的新工艺,其特征在于:工艺步骤如下,
1)将废旧衣物清洗晾晒,至水分含量低于15%;
2)将晾晒后的废旧衣服粉碎至直径不大于5mm;
3)脱水后的衣服碎料放入烘干机烘干,温度控制在40-50℃,至水分含量低于5%;
4)将烘干后的衣服碎料在沥青熔炼过程中加入,并与沥青混合均匀,1吨沥青中添加衣服碎料200-300公斤;
5)混合完成后的沥青直接用于铺路。