CN103613364B - 一种简易砖瓦烧制方法 - Google Patents
一种简易砖瓦烧制方法 Download PDFInfo
- Publication number
- CN103613364B CN103613364B CN201310617272.1A CN201310617272A CN103613364B CN 103613364 B CN103613364 B CN 103613364B CN 201310617272 A CN201310617272 A CN 201310617272A CN 103613364 B CN103613364 B CN 103613364B
- Authority
- CN
- China
- Prior art keywords
- mud
- kiln
- brick
- tile
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供的一种简易砖瓦烧制方法，属于砖瓦烧制技术领域，主要解决现有技术所烧制的砖瓦容易出现烧结现象，产品质地不匀，且烧制工艺复杂，制造成本较高的问题，其特点是：包括制砖工序和制瓦工序；所述制砖工序包括用水将原料土浸泡16小时；砖坯水分控制在14％至14.8％；烧制时保持窑温在850至890℃，持续132小时；所述制瓦工序包括黄土用140目的筛子筛过；用水将所述粘质土浸泡16小时；制作瓦筒时用打泥板击打转动的泥片，打击25至30次；瓦坯水分控制在16％至18％；烧制时窑内温度保持在820-980℃，持续132小时，即可出窑。
Description
技术领域
本发明属于砖瓦烧制技术领域，具体涉及一种简易砖瓦烧制方法。
背景技术
现有技术所烧制的砖瓦容易出现烧结现象，产品质地不匀，在砌筑墙体时，无法进行正常切割，且烧制工艺复杂，制造成本较高。
发明内容
本发明主要是解决现有技术存在的问题，提供一种简易砖瓦烧制方法。
本发明为解决上述技术问题而采取的技术方案是：
一种简易砖瓦烧制方法，其特点是：其步骤包括：制砖工序和制瓦工序；
所述制砖工序包括下列具体步骤：
第一步备料，取一定量细粒土；原料为黄土；所述细粒土为用200目的筛子筛过的黄土；
第二步和泥，用水将原料土浸泡16小时；用铁锹和泥，翻倒五次；
第三步打土坯，人工取泥填入坯模，压实，用刮板将多余泥料刮掉；
第四步脱模晾晒；砖坯水分质量百分比控制在14％至14.8％；
第五步砖坯装窑；
第六步泥封窑门；窑装满以后，进料的窑门用土坯筑墙，再用泥抹严实；
第七步烧制，保持窑温在850至890℃，持续132小时，即可出窑。
所述制瓦工序包括下列具体步骤：
第一步备料；取一定量粘质土；所用黄土用140目的筛子筛过；
第二步踩泥，用水将所述粘质土浸泡16小时；人工踩泥；踩成片后，堆起，再踩，如此循环若干次；
第三步垛泥墙，将踩好的泥垛成泥墙；
第四步割泥片，把垛好的泥墙再从左到右一层一层地割成泥片；
第五步瓦楦裹布套；
第六步把泥片裹在第五步裹布套后的瓦楦上；
第七步制作瓦筒，转动瓦楦，用打泥板击打转动的泥片，打击25至30次，停止打击；
第八步切割瓦筒，取下瓦筒，将其内部的布套取出，用刀片正交由上至下，切割瓦筒两刀；把瓦筒分割成4块瓦坯；
第九步晾晒，瓦坯水分质量百分比控制在16％至18％；
第十步装窑；
第十一步泥封窑门；窑装满以后，进料的窑门用土坏筑墙，再用泥抹严实；
第十二步点火烧制，先用干柴点着，然后加煤面，炉火点着以后，窑内温度保持在820-980℃，持续132小时，即可出窑。
所述砖坯及瓦坯混装于一窑中进行烧制。
本发明与现有技术相比，具有以下有益效果：
本发明采用人工制作，可以少量制作仿古制砖瓦，投资成本低。
具体实施方式
一种简易砖瓦烧制方法，其特点是：其步骤包括：制砖工序和制瓦工序；
所述制砖工序包括下列具体步骤：
第一步备料，制备细粒土；原料为黄土；经200目的筛子筛过得到所述细粒土；
第二步和泥，用水将原料土浸泡16小时；用铁锹和泥，翻倒五次；翻泥次数可以尽量多，最少五次；烧成的砖内部质地均匀细密，结实坚硬；
第三步打土坯，人工取泥填入坯模，压实，用刮板将多余泥料刮掉；取泥时，泥团一次取的量略大于坯模容积；以便填满压实；
第四步脱模晾晒；砖坯水分质量百分比控制在14％至14.8％；
第五步砖坯装窑；
第六步泥封窑门；窑装满以后，进料的窑门用土坏筑墙，再用泥抹严实，确保不跑火。
第七步烧制，保持窑温在850至890摄氏度，持续132小时，即可出窑。通过窑顶上的若干烟筒的开闭，调节窑内温度。
所述制瓦工序包括下列具体步骤：
第一步备料；取一定量粘质土；所用黄土必须用140目的筛子筛过；
第二步踩泥，用水将原料土浸泡十六小时；人工踩泥；踩成片后，堆起，再踩，如此循环若干次；
第三步垛泥墙，将踩好的泥垛成泥墙；
第四步割泥片，把垛好的泥墙再从左到右一层一层地割成泥片；
第五步瓦楦裹布套；
第六步把泥片裹在第五步裹布套后的瓦楦上；
第七步制作瓦筒，转动瓦楦，用打泥板击打转动的泥片，打击25至30次，停止打击；
第八步切割瓦筒，取下瓦筒，将其内部的布套取出，用刀片正交由上至下，切割瓦筒两刀；把瓦筒分割成4块瓦坯；
第九步晾晒，瓦坯水分控制在16％至18％；
第十步装窑；
第十一步点火烧制，先用干柴点着，然后加煤面，炉火点着以后，窑内温度保持在820-980℃，持续132小时，即可出窑。
所述砖坯及瓦坯混装于一窑中进行烧制。
Claims (2)
1.一种简易砖瓦烧制方法，其特征是：其步骤包括：制砖工序和制瓦工序；
所述制砖工序包括下列具体步骤：
第一步备料，取一定量细粒土；原料为黄土；所述细粒土为用200目的筛子筛过的黄土；
第二步和泥，用水将原料土浸泡16小时；用铁锹和泥，翻倒五次；
第三步打土坯，人工取泥填入坯模，压实，用刮板将多余泥料刮掉；
第四步脱模晾晒；砖坯水分质量百分比控制在14％至14.8％；
第五步砖坯装窑；
第六步泥封窑门；窑装满以后，进料的窑门用土坯筑墙，再用泥抹严实；
第七步烧制，保持窑温在850至890℃，持续132小时，即可出窑；
所述制瓦工序包括下列具体步骤：
第一步备料；取一定量粘质土；所用黄土用140目的筛子筛过；
第二步踩泥，用水将所述粘质土浸泡16小时；人工踩泥；踩成片后，堆起，再踩，如此循环若干次；
第三步垛泥墙，将踩好的泥垛成泥墙；
第四步割泥片，把垛好的泥墙再从左到右一层一层地割成泥片；
第五步瓦楦裹布套；
第六步把泥片裹在第五步裹布套后的瓦楦上；
第七步制作瓦筒，转动瓦楦，用打泥板击打转动的泥片，打击25至30次，停止打击；
第八步切割瓦筒，取下瓦筒，将其内部的布套取出，用刀片正交由上至下，切割瓦筒两刀；把瓦筒分割成4块瓦坯；
第九步晾晒，瓦坯水分质量百分比控制在16％至18％；
第十步装窑；
第十一步泥封窑门；窑装满以后，进料的窑门用土坯筑墙，再用泥抹严实；
第十二步点火烧制，先用干柴点着，然后加煤面，炉火点着以后，窑内温度保持在820-980℃，持续132小时，即可出窑。
2.根据权利要求1所述的简易砖瓦烧制方法，其特征是：所述砖坯及瓦坯混装于一窑中进行烧制。