CN103612453A - Thermosetting-resin-base reinforcing material preform for metal surface decoration - Google Patents
Thermosetting-resin-base reinforcing material preform for metal surface decoration Download PDFInfo
- Publication number
- CN103612453A CN103612453A CN201310668854.2A CN201310668854A CN103612453A CN 103612453 A CN103612453 A CN 103612453A CN 201310668854 A CN201310668854 A CN 201310668854A CN 103612453 A CN103612453 A CN 103612453A
- Authority
- CN
- China
- Prior art keywords
- thin plate
- flame retardant
- retardant type
- structural foam
- thermosetting resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a thermosetting-resin-base reinforcing material preform for metal surface decoration, which comprises a (1) thermosetting resin reinforcing material A, a (2) thermosetting resin diversion medium, a (3) thermosetting resin reinforcing material B, a (4) thermosetting resin reinforcing material C, a (5) thermosetting resin reinforcing material D, a (6) spacing wire, a (7) flexible mold layer, a (8) side edge barrier strip, a (9) front metal decoration sheet, a (10) back metal decoration sheet and a (11) end surface barrier strip. The preform can be subjected to both curve molding and plane molding; and after arranging a vacuum tube and introducing an unsaturated resin through a resin guide tube in vacuum after molding and fixation, various curved or planar boards or special-shape decorations can be prepared. The preform can be widely used for manufacturing metal surface decorating materials in various industries.
Description
Technical field
The present invention relates to a kind of thermosetting resin based reinforcement material precast body, relate in particular to a kind of thermosetting resin based reinforcement material precast body for decoration of metal covering.
Background technology
Existing thermosetting resin base composite preform mostly is pre-preg or preformed base substrate, during use, need to be subject to the restriction of mould, release materials, water conservancy diversion material etc., do not there is adaptability and the free degree widely, make the decorated articles difficulties such as sheet material of large-scale, various curved surfaces or plane.
< < building and ornament materials precast body > > of number of patent application 2013103508213 publication number 103397755A of the prior art, the soft mold layer case hardness of the PVC plastic sheeting of the soft mold of this invention is low not durable, and thin lepthymenia, surface easily scratches, often cause transportation or a variety of causes before not vacuumizing run-down, use this invention in the unwitting situation of affiliated technical field staff after, make precast body vacuum suction resin and directly cause product rejection or because there being the trace of benefit to cause product quality to decline to a great extent after scratch repairing effectively, and its guide layer only has middle one deck, the speed of water conservancy diversion impregnating resin and gas are discharged slow, efficiency is low, can cause dipping not exclusively, and then goods are scrapped or Quality Down, producers' complex operation difficulty of technical field under the setting at its mozzle and bound edge and envelope angle makes, and the bound edge of coated mozzle also cracky cause can not vacuum, although the film of B1 level fire protection flame retarding PVC has facing in addition, not durable, the easy scuffing of surfacing, not environmental protection, can not adapt to the ornamental high-quality requirement of society to ornament materials surface now.
Summary of the invention
For solving, known of the prior artly for making the thermosetting resin based reinforcement material precast body of various curved surface sheet material or flat sheet, mostly be pre-preg or preformed base substrate, during use, need to be subject to mould, release materials, the restriction of water conservancy diversion material etc., do not there is adaptability and the free degree widely, even soft mold and reinforcing material are integrated the precast body of sealing, its soft mold layer is crossed thin easy scuffing, of poor quality not durable, not environmental protection, and the slow efficiency of individual layer guide layer water conservancy diversion impregnating resin speed is low, cause flooding the problems such as incomplete, mozzle and bound edge arrange loaded down with trivial details difficulty, the present invention proposes a kind of thermosetting resin based reinforcement material precast body for decoration of metal covering, can solve the deficiency of the problem such as above-mentioned.
The present invention solves the problems of the technologies described above adopted technical scheme to be: of the present invention being characterized as: include thermosetting resin reinforcing material A, thermosetting resin permeable medium, thermosetting resin reinforcing material B, thermosetting resin reinforcing material C, thermosetting resin reinforcing material D, spacing line, soft mold layer, side blend stop, front metal fancy veneer, reverse side metal finishing thin plate, end face blend stop, thermosetting resin reinforcing material B and thermosetting resin reinforcing material C are clipped in the middle the thermosetting resin permeable medium that accompanies thermosetting resin reinforcing material A, thermosetting resin reinforcing material D is by the thermosetting resin reinforcing material B after interlayer successively, thermosetting resin reinforcing material C, thermosetting resin permeable medium, thermosetting resin reinforcing material A is clipped in the middle, spacing line is by the thermosetting resin reinforcing material A of interlayer successively, thermosetting resin permeable medium, thermosetting resin reinforcing material B, D is spacing for thermosetting resin reinforcing material C thermosetting resin reinforcing material, soft mold layer is by the spacing thermosetting resin reinforcing material D of interlayer successively, thermosetting resin based reinforcement material C, thermosetting resin based reinforcement material B, thermosetting resin permeable medium, in the middle of thermosetting resin based reinforcement material A is compounded in, then at two sides, a side blend stop is set space respectively, two end faces arrange respectively an end face blend stop, intersection's fusion of side blend stop and end face blend stop is connected, front metal fancy veneer and reverse side metal finishing thin plate are by each layer of the spacing rear compound soft mold layer of interlayer successively, side blend stop, end face blend stop is clipped in the middle compound, by integral sealing.
Described thermosetting resin permeable medium, is characterized by: be one or more layers of following material one of them: middle alkali or alkali-free glass fibre continuous felt, carbon fiber continuous felt, Weaving type plastics flow-guiding screen, extrusion type plastics flow-guiding screen, fire-retardant Weaving type plastics flow-guiding screen, fire-retardant extrusion type plastics flow-guiding screen.
Described thermosetting resin reinforcing material A, is characterized by: be one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
Described thermosetting resin reinforcing material B, is characterized by: be one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
Described thermosetting resin reinforcing material C, is characterized by: be one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
Described thermosetting resin reinforcing material D, it is characterized by: be one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth.
Described spacing line, is characterized by: the material of spacing line is one of them of sewing thread, carbon fiber line, glass wire, nylon monofilament line;
Spacing line spacing be exactly by each layered suture together and by two sides lock seamings of the reinforcing material after interlayer successively, play the effect that can arbitrarily not be shifted between each layer that limits;
Spacing shape is grid (Integral net shaped quilting two sides of lockstitching a border), grid (whole grid-like quilting two sides of lockstitching a border), straight line (whole several parallel horizontal straight lines or the quilting of vertical curve two sides of lockstitching a border), oblique line (quilting two sides of lockstitching a border of whole several parallel oblique lines), lattice (whole design or whole quilting two sides of lockstitching a border that have the design of spacing), point type (the whole point type quilting that has spacing, and two sides of lockstitching a border, comprise circular some square dot, flower form point) one of them or other spacing shapes that play position-limiting action.
Described soft mold layer, is characterized by: be with metal have under caking property, normal temperature, be insoluble to styrene and resistant to bending following material one of them:
1) flame retardant type graft modification plastic sheeting or sheet material;
2) flame retardant type graft modification thermoplastic elastomer thin film or sheet material.
Described side blend stop and end face blend stop, is characterized by: be with metal have under caking property, normal temperature, be insoluble to styrene and resistant to bending following material one of them:
1) plastic strip of the graft modification plastics of the soft or semi-rigid of flame retardant type;
2) the elastomer adhesive tape of the graft modification thermoplastic elastomer (TPE) of the soft or semi-rigid of flame retardant type;
What side blend stop and being compounded with had between the side of the reinforcing material of each spacing layer successively of soft mold layer that a space separates imports the space of resin flows as vacuum, end face blend stop is to be close to the setting of end face reinforcing material, after intersection's docking fusion of side blend stop and end face blend stop, front metal fancy veneer and reverse side metal finishing thin plate, by the blend stop after fusion and by the compound whole reinforcing material of the soft mold layer compound closure that is clipped in the middle, seal whole precast body; Described side blend stop and the cross sectional shape of end face blend stop include the blend stop of rectangle (being highly greater than width), square or flat rectangular (width is greater than height).
Described front metal fancy veneer, is characterized by: be one of them of resistant to bending following metal finishing thin plate: the sheet metal that one side coating decoration sheet metal, one side pad pasting decorative metal thin plate, the sheet metal of single-sided colored stamp, the sheet metal of one side heat-tinting, antistatic sheet metal, the sheet metal of one side wire drawing, one side are radium-shine, the sheet metal of one side etching face, the sheet metal of one side minute surface are, the sheet metal of the sheet metal of single-side embossing, punch metal thin plate, one side sandblast.
Described reverse side metal finishing thin plate, is characterized by: be one of them of resistant to bending following metal finishing thin plate: the sheet metal that one side coating decoration sheet metal, one side pad pasting decorative metal thin plate, the sheet metal of single-sided colored stamp, the sheet metal of one side heat-tinting, antistatic sheet metal, the sheet metal of one side wire drawing, one side are radium-shine, the sheet metal of one side etching face, the sheet metal of one side minute surface are, the sheet metal of the sheet metal of single-side embossing, punch metal thin plate, one side sandblast.
The metal species of described front metal fancy veneer and reverse side metal finishing thin plate comprises: the metals such as aluminium, aluminium alloy, copper, copper alloy, steel, stainless steel, and it is outside that there is the one side of facing decorative effect metal surface, there is no the one side and soft mold layer, side blend stop, end face blend stop compound closure of facing decorative effect.
Beneficial effect of the present invention: the present invention is mainly used in take the metal covering reinforcing material precast body that unsaturated-resin is matrix, make ornamental various curved surface sheet material or flat sheet is not subject to mould for this, the restriction of release materials, complete closed moulding, do not need the demoulding, after simple plasticity is fixing, just can vacuum import unsaturated-resin moulding, so due to soft mold layer of the present invention and the compound not cracky of metal finishing thin plate, and the structure of distinctive pair of guide layer is divided into three layers by the of the prior art two-layer reinforcing material of required dipping, make same thickness and more even soon than the thicker precast body of thickness resin flow velocity when the vacuum suction unsaturated-resin, can better flood fast whole precast body and Exhaust Gas, significantly reduce because flooding the incomplete product rejection causing or the problem of Quality Down, the present invention does not have side bound edge and mozzle, the space being separated out with the side blend stop that space arranges replaces mozzle, make surface and the cross section of precast body smooth, need after solidifying, also to not remove the operations such as mozzle, and make the program of producing precast body simply improve speed of production, and the soft mold layer that metal surface has solved precast body of the prior art is the problem of not environmental protection of PVC plastic sheeting (discharging noxious material under high temperature), the present invention can be widely used in building and ornament materials, furniture style, artistic sculpture, boats and ships, the different decoration demand of the industry-by-industries such as vehicle.
Accompanying drawing explanation
Fig. 1 is cutaway view of the present invention: (1) is thermosetting resin reinforcing material A, (2) be thermosetting resin resin permeable medium, (3) be thermosetting resin reinforcing material B, (4) are thermosetting resin reinforcing material C, and (5) are thermosetting resin reinforcing material D, (6) be spacing line, (7) be soft mold layer, (8) are side blend stops, and (9) are front metal fancy veneers, (10) be reverse side metal finishing thin plate, (11) are end face blend stops.
Fig. 2 is the sectional view of end face of the present invention: (1) is thermosetting resin reinforcing material A, (2) be thermosetting resin resin permeable medium, (3) be thermosetting resin reinforcing material B, (4) be thermosetting resin reinforcing material C, (5) are thermosetting resin reinforcing material D, and (6) are spacing lines, (7) be soft mold layer, (8) be side blend stop, (9) are front metal fancy veneers, and (10) are reverse side metal finishing thin plates.
Fig. 3 is the sectional view of side of the present invention: (1) is thermosetting resin reinforcing material A, (2) be thermosetting resin permeable medium, (3) be thermosetting resin reinforcing material B, (4) be thermosetting resin reinforcing material C, (5) are thermosetting resin reinforcing material D, and (6) are spacing lines, (7) be soft mold layer, (9) be front metal fancy veneer, (10) are reverse side metal finishing thin plates, and (11) are end face blend stops.
The specific embodiment
The present invention is further illustrated with reference to the accompanying drawings.
According to Fig. 1, Fig. 2, shown in Fig. 3, thermosetting resin reinforcing material B(3) and thermosetting resin reinforcing material C(4) will accompany thermosetting resin reinforcing material A(1) thermosetting resin permeable medium (2) be clipped in the middle, thermosetting resin reinforcing material D(5) by the thermosetting resin reinforcing material B(3 after interlayer successively), thermosetting resin reinforcing material C(4), thermosetting resin permeable medium (2), thermosetting resin reinforcing material A(1) be clipped in the middle, spacing line (6) is by the thermosetting resin reinforcing material A(1 of interlayer successively), thermosetting resin permeable medium (2), thermosetting resin reinforcing material B(3), thermosetting resin reinforcing material C(4) thermosetting resin reinforcing material D(5) spacing, soft mold layer (7) is by the spacing thermosetting resin reinforcing material D(5 of interlayer successively), thermosetting resin based reinforcement material C(4), thermosetting resin based reinforcement material B(3), thermosetting resin permeable medium (2), thermosetting resin based reinforcement material A(1) in the middle of being compounded in, then at two sides, a side blend stop (8) is set space respectively, two end faces arrange respectively an end face blend stop (11), intersection's fusion of side blend stop (8) and end face blend stop (11) is connected, front metal fancy veneer (9) and reverse side metal finishing thin plate (10) be each layer of compound soft mold layer (7) after interlayer successively, side blend stop (8), end face blend stop (11) is clipped in the middle compound, by integral sealing.
Embodiment mono-:
Material is the thermosetting resin reinforcing material B of one or more layers of glass fibre plain and thermosetting resin reinforcing material C that material is one or more layers of glass fibre plain is that the material of the thermosetting resin reinforcing material A of the strong core felt of one or more layers of glass fibre is that the thermosetting resin permeable medium of one or more layers of extrusion type PE flow-guiding screen is clipped in the middle by accompanying material, material is that the thermosetting resin reinforcing material D of one or more layers of fiberglass surfacing mat is by the thermosetting resin reinforcing material B after interlayer successively, thermosetting resin reinforcing material C, thermosetting resin permeable medium, thermosetting resin reinforcing material A is clipped in the middle, material is that the spacing line of sewing thread is by the thermosetting resin reinforcing material A of interlayer successively, thermosetting resin permeable medium, thermosetting resin reinforcing material B, thermosetting resin reinforcing material C, D is spacing with mesh shape for thermosetting resin reinforcing material, material is the PE film that is added with maleic anhydride graft PE of V0 halogen-free flameproof or the soft mold layer of sheet material by the spacing thermosetting resin reinforcing material D of interlayer successively, thermosetting resin based reinforcement material C, thermosetting resin based reinforcement material B, thermosetting resin permeable medium, in the middle of thermosetting resin based reinforcement material A is compounded in, then at two sides, the side blend stop of the PE plastic strip that is added with maleic anhydride graft PE that one strip material is the soft or semi-rigid of B1 grade non-halogen flame-retardant is set space respectively, two end faces arrange respectively the end face blend stop of the PE plastic strip that is added with maleic anhydride graft PE that a strip material is the soft or semi-rigid of B1 grade non-halogen flame-retardant, intersection's fusion of side blend stop and end face blend stop is connected, material is the front metal fancy veneer of aluminium alloy sheet of one side wire-drawing surface and the reverse side metal finishing thin plate of the aluminium alloy sheet that material is one side wire-drawing surface by each layer of compound soft mold layer after interlayer successively, side blend stop, end face blend stop is clipped in the middle compound, by integral sealing,
Permeable medium can be also: one of them of the Weaving type PP flow-guiding screen of one or more layers of carbon fiber continuous felt, Weaving type PP flow-guiding screen, V0 fire-retardant (or B1 level is fire-retardant);
Soft mold layer can be also: the PP film or the sheet material that are added with maleic anhydride graft PP of V0 halogen-free flameproof, the PE film or the sheet material that are added with maleic anhydride graft LLDPE of V0 halogen-free flameproof, maleic anhydride graft eva film or the sheet material of V0 fire-retardant (or V0 halogen-free flameproof), maleic anhydride graft POE film or the sheet material of V0 fire-retardant (or V0 halogen-free flameproof), film or the sheet material of the maleic anhydride graft PE of V0 halogen-free flameproof, film or the sheet material of the maleic anhydride graft PP of V0 halogen-free flameproof, the PA6 film or the sheet material that are added with maleic anhydride graft PE of V0 fire-retardant (or V0 halogen-free flameproof), the PA66 film that is added with maleic anhydride graft PE of V0 fire-retardant (or V0 halogen-free flameproof) or one of them of sheet material,
Side blend stop and end face blend stop can be also: the PE plastic strip that is added with maleic anhydride graft PE of the soft or semi-rigid of V0 halogen-free flameproof, the PP plastic strip that is added with maleic anhydride graft PP of the soft or semi-rigid of V0 halogen-free flameproof, the plastic strip of the PP that is added with maleic anhydride graft PP of the soft or semi-rigid of B1 level fire-retardant (or B1 grade non-halogen flame-retardant), the PE plastic strip that is added with maleic anhydride graft LLDPE of the semi-rigid of V0 halogen-free flameproof, soft or the semi-rigid adhesive tape of the maleic anhydride graft EVA of V0 fire-retardant (or V0 halogen-free flameproof), soft or the semi-rigid adhesive tape of the maleic anhydride graft POE of V0 fire-retardant (or halogen-free flameproof), soft or the semi-rigid plastic bar of the maleic anhydride graft PE of V0 halogen-free flameproof, the plastic strip of the soft or semi-rigid of the maleic anhydride graft PP of V0 halogen-free flameproof, one of them of the EVA adhesive tape that is added with maleic anhydride graft EVA of the soft or semi-rigid of B1 grade non-halogen flame-retardant,
The one side of the wire-drawing surface decorative effect of one side wire drawing aluminium alloy sheet is outside, there is no the one side and soft mold layer, side blend stop, end face blend stop compound closure of facing decorative effect.
Embodiment bis-:
Material is the thermosetting resin reinforcing material B of one or more layers carbon fiber plain and thermosetting resin reinforcing material C that material is one or more layers glass fibre twill is that the material of the thermosetting resin reinforcing material A of the sandwich V-shaped valley hyperbolic of one or more layers cork wood thin plate is that the thermosetting resin permeable medium of one or more layers Weaving type PP flow-guiding screen is clipped in the middle by accompanying material, material is that the thermosetting resin reinforcing material D of one or more layers of glass fibre plain is by the thermosetting resin reinforcing material B after interlayer successively, thermosetting resin reinforcing material C, thermosetting resin permeable medium, thermosetting resin reinforcing material A is clipped in the middle, material is that the spacing line of sewing thread or nylon monofilament line is by the thermosetting resin reinforcing material A of interlayer successively, thermosetting resin permeable medium, thermosetting resin reinforcing material B, thermosetting resin reinforcing material C, D is spacing with straight line for thermosetting resin reinforcing material, material is the eva film that is added with maleic anhydride graft EVA of V0 grade non-halogen flame-retardant or the soft mold layer of sheet material by the spacing thermosetting resin reinforcing material D of interlayer successively, thermosetting resin based reinforcement material C, thermosetting resin based reinforcement material B, thermosetting resin permeable medium, in the middle of thermosetting resin based reinforcement material A is compounded in, then at two sides, the side blend stop of the EVA adhesive tape that is added with maleic anhydride graft EVA that one strip material is the soft or semi-rigid of B1 grade non-halogen flame-retardant is set space respectively, two end faces arrange respectively the end face blend stop of the EVA adhesive tape that is added with maleic anhydride graft EVA that a strip material is the soft or semi-rigid of B1 grade non-halogen flame-retardant, intersection's fusion of side blend stop and end face blend stop is connected, material is the front metal fancy veneer of copper sheet of one side minute surface and the reverse side metal finishing thin plate of the stainless sheet steel that material is one side heat-tinting by each layer of compound soft mold layer after interlayer successively, side blend stop, end face blend stop is clipped in the middle compound, by integral sealing,
Permeable medium can be also: extrusion type PE or the PVC flow-guiding screen of one or more layers of carbon fiber continuous felt or glass fibre continuous felt or V0 fire-retardant (or B1 level is fire-retardant);
Soft mold layer can be also: the PE film or the sheet material that are added with maleic anhydride graft PE of V0 halogen-free flameproof, the PE film or the sheet material that are added with maleic anhydride graft LDPE of V0 halogen-free flameproof, maleic anhydride graft eva film or the sheet material of V0 fire-retardant (or halogen-free flameproof), maleic anhydride graft POE film or the sheet material of V0 fire-retardant (or halogen-free flameproof), film or the sheet material of the maleic anhydride graft PE of V0 halogen-free flameproof, the film of the maleic anhydride graft PP of V0 halogen-free flameproof or one of them of sheet material,
Side blend stop and end face blend stop can be also: the PVC adhesive tape that is added with maleic anhydride graft EVA of the soft or semi-rigid that B1 level is fire-retardant, the PE adhesive tape that is added with maleic anhydride graft PE of the soft or semi-rigid of V0 halogen-free flameproof, the PE adhesive tape that is added with maleic anhydride graft PE of the soft or semi-rigid of B1 level fire-retardant (or B1 grade non-halogen flame-retardant), soft or the semi-rigid adhesive tape of the maleic anhydride graft EVA of V0 fire-retardant (or halogen-free flameproof), soft or the semi-rigid adhesive tape of the maleic anhydride graft POE of V0 fire-retardant (or halogen-free flameproof), the plastic strip of the soft or semi-rigid of the maleic anhydride graft PE of V0 halogen-free flameproof, one of them of the plastic strip of the soft or semi-rigid of the maleic anhydride graft PP of V0 halogen-free flameproof,
The one side of the facing decorative effect of the minute surface of the stainless sheet steel of the copper sheet of one side minute surface and one side heat-tinting and heat-tinting is outside, there is no the one side and soft mold layer, side blend stop, end face blend stop compound closure of facing decorative effect.
When the present invention uses, fixing (can fix or hole at side blend stop of the present invention or end face blend stop above by fixture the present invention is moulding, fixing with screw or nail), use vacuum diversion method, by any place at the side blend stop on one side any or both sides and place, the space, space between reinforcing material or many places boring or fluting, around inserting and seal with flexible pipe, this flexible pipe connects unsaturated-resin, then at any place of front metal fancy veneer of the present invention or reverse side metal finishing thin plate or many places boring or fluting also can or slot in the side blend stop of a side and the boring on vacancy or end face blend stop of reinforcing material, arrange afterwards around one or more groups flexible pipe sealing, this flexible pipe is connected with vavuum pump, then vacuum suction resin, unsaturated-resin should be low viscosity, low heat release, the resin of normal temperature cure, can according to circumstances add polymerization inhibitor or modified resin or reduce the consumption of curing agent and promoter or extend hardening time, the low heat release of resin normal temperature is solidified, resin flows to and after sky, enters permeable medium, through permeable medium water conservancy diversion, flood each layer, after thorough impregnation (according to circumstances, vacuum tube has a small amount of resin vacuolar membrane to flow out) pressurize solidifies, after basic curing molding, remove hole for injecting glue or vacuum port sealing (closing by the sealing rubber seal of silicon copper seal gum and so on) that connecting hose and equipment sealing are beaten, wait for that final solidifying can obtain designed various curved surfaces, the ornamental non-bearing wall body that the dalle that has metal finishing face of plane forms, cut off or hollow non-bearing edge list or other three-dimensional ornaments being formed by flexible plane etc., the present invention can also be by specification or shape cutting, cutting, then disconnected cross section is used with soft mold and be the plastic glue strip sweat soldering of one species plastics or extrude welding or use the fluid sealants such as silicon copper seal gum after whole disconnected cross section sealing, to use, also can solidify rear design cutting profile, after indivedual special shapes need to according to circumstances arrange overflow pipe, coated bound edge is used.
Above content is the further description of the present invention being made in conjunction with the specific embodiment, can not assert that the specific embodiment of the present invention is only limited to these explanations.For general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deduction or replace.
Claims (10)
1. thermosetting resin based reinforcement material precast body for the decoration of a metal covering, it is characterized by: include (1) thermosetting resin reinforcing material A, (2) thermosetting resin permeable medium, (3) thermosetting resin reinforcing material B, (4) thermosetting resin reinforcing material C, (5) thermosetting resin reinforcing material D, (6) spacing line, (7) soft mold layer, (8) side blend stop, (9) front metal fancy veneer, (10) reverse side metal finishing thin plate, (11) end face blend stop, thermosetting resin reinforcing material B(3) and thermosetting resin reinforcing material C(4) will accompany thermosetting resin reinforcing material A(1) thermosetting resin permeable medium (2) be clipped in the middle, thermosetting resin reinforcing material D(5) by the thermosetting resin reinforcing material B(3 after interlayer successively), thermosetting resin reinforcing material C(4), thermosetting resin permeable medium (2), thermosetting resin reinforcing material A(1) be clipped in the middle, spacing line (6) is by the thermosetting resin reinforcing material A(1 of interlayer successively), thermosetting resin permeable medium (2), thermosetting resin reinforcing material B(3), thermosetting resin reinforcing material C(4) thermosetting resin reinforcing material D(5) spacing, soft mold layer (7) is by the spacing thermosetting resin reinforcing material D(5 of interlayer successively), thermosetting resin based reinforcement material C(4), thermosetting resin based reinforcement material B(3), thermosetting resin permeable medium (2), thermosetting resin based reinforcement material A(1) in the middle of being compounded in, then at two sides, a side blend stop (8) is set space respectively, two end faces arrange respectively an end face blend stop (11), intersection's fusion of side blend stop (8) and end face blend stop (11) is connected, front metal fancy veneer (9) and reverse side metal finishing thin plate (10) be each layer of the spacing rear compound soft mold layer of interlayer (7) successively, side blend stop (8), end face blend stop (11) is clipped in the middle compound, by integral sealing.
2. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: thermosetting resin permeable medium (2) be one or more layers of following material one of them: middle alkali or alkali-free glass fibre continuous felt, carbon fiber continuous felt, Weaving type plastics flow-guiding screen, extrusion type plastics flow-guiding screen, fire-retardant Weaving type plastics flow-guiding screen, fire-retardant extrusion type plastics flow-guiding screen.
3. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: be thermosetting resin reinforcing material A(1) one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
4. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: be thermosetting resin reinforcing material B(3) one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
5. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: be thermosetting resin reinforcing material C(4) one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth, flame retardant type PVC structural foam profile thin plate, flame retardant type PVC structural foam punching profile thin plate, flame retardant type PVC structural foam fluting thin plate, flame retardant type PVC structural foam fluting punching thin plate, flame retardant type PVC structural foam V-shaped valley hyperbolic thin plate, flame retardant type PET structural foam profile thin plate, flame retardant type PET structural foam punching profile thin plate, flame retardant type PET structural foam fluting thin plate, flame retardant type PET structural foam fluting punching thin plate, flame retardant type PET structural foam V-shaped valley hyperbolic thin plate, flame retardant type SAN structural foam profile thin plate, flame retardant type SAN structural foam punching profile thin plate, flame retardant type SAN structural foam fluting thin plate, flame retardant type SAN structural foam fluting punching thin plate, flame retardant type SAN structural foam V-shaped valley hyperbolic thin plate, flame retardant type PMI structural foam profile thin plate, flame retardant type PMI structural foam punching profile thin plate, flame retardant type PMI structural foam fluting thin plate, flame retardant type PMI structural foam fluting punching thin plate, flame retardant type PMI structural foam V-shaped valley hyperbolic thin plate, the sandwich profile thin plate of cork wood, the sandwich punching profile of cork wood thin plate, the sandwich fluting thin plate of cork wood, the sandwich fluting punching of cork wood thin plate, the sandwich V-shaped valley hyperbolic of cork wood thin plate.
6. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: be thermosetting resin reinforcing material D(5) one or more layers of following material one of them: middle alkali or alkali-free glass fibre woven fabric, mold closing felt, middle alkali or alkali-free glass fibre felt, strong core felt, superhigh molecular weight polyethylene fibers woven fabric, superhigh molecular weight polyethylene fibers UD cloth, carbon glass shuffling cloth, carbon fiber woven fabric, carbon fiber felt, aramid fiber woven fabric, aramid fiber felt, carbon virtue shuffling cloth, virtue glass shuffling cloth, modification tossa woven fabric, modification sisal fiber woven fabric, modification flax fiber woven fabric, modified bamboo fibre machine is weaved cotton cloth, innovation wood fibre machine is weaved cotton cloth.
7. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: soft mold layer (7) be with metal have under caking property, normal temperature, be insoluble to styrene and resistant to bending following material one of them:
1) flame retardant type graft modification plastic sheeting or sheet material;
2) flame retardant type graft modification thermoplastic elastomer thin film or sheet material.
8. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: side blend stop (8) and end face blend stop (11) be with metal have under caking property, normal temperature, be insoluble to styrene and resistant to bending following material one of them:
1) plastic strip of the graft modification plastics of the soft or semi-rigid of flame retardant type;
2) the elastomer adhesive tape of the graft modification thermoplastic elastomer (TPE) of the soft or semi-rigid of flame retardant type.
9. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, it is characterized by: front metal fancy veneer (9) is one of them of resistant to bending following metal finishing thin plate: one side coating decoration sheet metal, one side pad pasting decorative metal thin plate, the sheet metal of single-sided colored stamp, the sheet metal of one side heat-tinting, antistatic sheet metal, the sheet metal of one side wire drawing, the sheet metal that one side is radium-shine, the sheet metal of one side etching face, the sheet metal of one side minute surface, the sheet metal of single-side embossing, punch metal thin plate, the sheet metal of one side sandblast.
10. according to thermosetting resin based reinforcement material precast body for the decoration of a kind of metal covering described in claim 1, its feature is: reverse side metal finishing thin plate (10) is one of them of resistant to bending following metal finishing thin plate: one side coating decoration sheet metal, one side pad pasting decorative metal thin plate, the sheet metal of single-sided colored stamp, the sheet metal of one side heat-tinting, antistatic sheet metal, the sheet metal of one side wire drawing, the sheet metal that one side is radium-shine, the sheet metal of one side etching face, the sheet metal of one side minute surface, the sheet metal of single-side embossing, punch metal thin plate, the sheet metal of one side sandblast.