CN103603457A - Foamed clay sintered brick and preparation technique thereof - Google Patents
Foamed clay sintered brick and preparation technique thereof Download PDFInfo
- Publication number
- CN103603457A CN103603457A CN201310560678.0A CN201310560678A CN103603457A CN 103603457 A CN103603457 A CN 103603457A CN 201310560678 A CN201310560678 A CN 201310560678A CN 103603457 A CN103603457 A CN 103603457A
- Authority
- CN
- China
- Prior art keywords
- brick
- foamed
- clay
- sintered brick
- foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a foamed clay sintered brick, relating to the technical field of. The foamed clay sintered brick is composed of the following components in percentage by mass: 70% of clay, 4% of foaming agent, 4% of activator, 20% of mineral and 2% of combustion improver. The preparation technique comprises the following steps: scientifically proportioning, foaming to form, airing, and sintering in a kiln to obtain the foamed clay sintered brick. The foamed clay sintered brick not only has the advantages of low heat conductivity, heat transfer coefficient, light weight, high strength, fire resistance, acid resistance, alkali resistance, sound insulation, environment friendliness, convenience for construction and the like in the foamed concrete brick, but also has the advantage of load bearing in the traditional internal combustion clay brick.
Description
Technical field
The present invention relates to building material technical field, be specifically related to a kind of foaming clay brick and preparation technology thereof.
Background technology
At present, building brick kind is more, is substantially divided into two classes, a class bearing bricks, and a class furring tile wherein bearing bricks mostly is solid brick, have vitrified bond, has concrete formation, is used for brick-and-concrete buildings, and construction cost is relatively low; Furring tile mostly is light body and turns, and has foamed bricks, hollow brick, and lightweight brick heat-insulating property is higher, can reduce basic engineering, reduces foundation construction cost and drops into, but need reinforced frame structure design, and often cost is higher.
Still there is no at present a kind of light body bearing bricks, light body bearing bricks has three aspects: advantage: good heat insulating, load-bearing property can reduce basic engineering, reduces Frame Design standard, totally reduces building costs and drops into.
Summary of the invention
It is a kind of from heavy and light, low, energy-conservation foaming clay brick and the preparation technology thereof of cost that technical problem to be solved by this invention is to provide.
Technical problem to be solved by this invention realizes by the following technical solutions:
A foaming clay brick, is comprised of the component of following mass percent,
Described mineral matter is inorganic mineral or inorganic compounding mineral matter.
Another object of the present invention is to provide a kind of technique of preparing the clay brick that foams, comprises following processing step,
1) take in mass ratio clay, activator, blowing agent, mineral matter, combustion adjuvant, mix, obtain material a stand-by;
2) material a is put into mixing plant and stir 3-6 hour, obtain material b;
4) material b is foamed, then put into former and carry out extrusion modling, according to specification, be made into adobe, obtain material c stand-by;
5) after being dried naturally, material c enters klining knot.
The invention has the beneficial effects as follows: the present invention passes through scientific formula, carry out foaming, after drying, entering klining knot forms, Novel foaming clinker brick, except thering is the peculiar low heat conduction of foam concrete block, thermal transmittance, outside the advantages such as light body, high strength, fire prevention, acid and alkali resistance, sound insulation, environmental protection, easy construction, also have the pressure-bearing advantage of traditional internal combustion loam brick concurrently.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach object and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
A foaming clay brick, is comprised of the component of following mass percent,
Described mineral matter is inorganic mineral or inorganic compounding mineral matter.
Another object of the present invention is to provide a kind of technique of preparing the clay brick that foams, comprises following processing step,
1) take in mass ratio clay, activator, blowing agent, mineral matter, combustion adjuvant, mix, obtain material a stand-by;
2) material a is put into mixing plant and stir 3-6 hour, obtain material b;
4) material b is foamed, then put into former and carry out extrusion modling, according to specification, be made into adobe, obtain material c stand-by;
5) after being dried naturally, material c enters klining knot.
More than show and described basic principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and manual, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. a foaming clay brick, is characterized in that: the component by following mass percent forms,
2. a kind of foaming clay brick according to claim 1, is characterized in that: described mineral matter is inorganic mineral or inorganic compounding mineral matter.
3. a technique of preparing the clay brick that foams described in claim 1, is characterized in that: comprise following processing step,
1) take in mass ratio clay, activator, blowing agent, mineral matter, combustion adjuvant, mix, obtain material a stand-by;
2) material a is put into mixing plant and stir 3-6 hour, obtain material b;
4) material b is foamed, then put into former and carry out extrusion modling, according to specification, be made into adobe, obtain material c stand-by;
5) after being dried naturally, material c enters klining knot.