CN103589162A - Electroconductive silicone rubber for cable accessories - Google Patents
Electroconductive silicone rubber for cable accessories Download PDFInfo
- Publication number
- CN103589162A CN103589162A CN201310505145.2A CN201310505145A CN103589162A CN 103589162 A CN103589162 A CN 103589162A CN 201310505145 A CN201310505145 A CN 201310505145A CN 103589162 A CN103589162 A CN 103589162A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- electroconductive
- silicone rubber
- silicon rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electroconductive silicone rubber for cable accessories. The electroconductive silicone rubber comprises the following components in parts by weight: 50-120 parts of reinforced silicone rubber, 15-30 parts of granular electroconductive acetylene black, 5-15 parts of 2,4,4,6,6-hexamethylcyclotrisilazane, 2-6 parts of liquid silicone rubber, 0.5-1.5 parts of vulcanizing agent, and 0.1-0.5 part of scorch retarder. The electroconductive silicone rubber for cable accessories disclosed by the invention is simple in preparation method; a prepared electroconductive silicone rubber is a deep black rubber material, good in liquidity of rubber compounds, easily subjected to vulcanizing treatment, and high in qualified rate; the electroconductive silicone rubber for cable accessories is easily adhered to metals; and the tensile strength of the rubber is greater than or equal to 20 Mpa, and the rubber is good in ageing resistance, and suitable for producing electroconductive bushings and electroconductive rubber damping products.
Description
Technical field
The invention belongs to rubber technology field, be specifically related to a kind of cable accessory conductive silicon rubber.
Background technology
At present, conductive rubber products is very fast as the development of functional rubber goods, and range of application is increasingly extensive.
Conductive rubber belongs to conductive polymeric composite, and its electrical conduction mechanism mainly contains macroscopical seepage theory (conductive path mechanism), Bcs mechanics tunnel effect and Bcs mechanics field emission effect.Conductive path mechanism, tunnel effect and field emission effect exist in conductive rubber simultaneously, may be to take a certain or certain two kinds of mechanism as main under different condition.When conductive filler material is when critical is above, conductive path is main conduction pattern, take conductive path mechanism as main; When conductive filler material consumption is less or impressed voltage hour, the gap of isolated electron or its aggregate is compared with large and cannot participate in conduction, thermal vibration excited electron generation transition, forms larger tunnel current, now take tunnel effect as main; When amount of filler is less, between particle, internal electric field is very strong, matrix interlayer is equivalent to inner distributed capacity, and now field emission effect is more remarkable.
The conductive rubber that existing graphitized carbon black is filled, volume resistance can remain on several kilo-ohms conventionally, and because the carbon black using in existing formula is unreasonable, its tensile strength can only reach 12Mpa, can not meet actual needs far away.
Summary of the invention
The object of this invention is to provide the cable accessory conductive silicon rubber that a kind of manufacturing technique requirent is low, tensile strength meets service requirements.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is as follows:
A conductive silicon rubber, the component of described conductive silicon rubber is in weight part:
50~120 parts, reinforcement silicon rubber
15~30 parts of particulate state conductive acetylene carbon blacks
5~15 parts of pregnancy basic ring three silazane
2~6 parts of liquid silastics
0.5~1.5 part of vulcanizing agent
0.1~0.5 part of scorch retarder.
As improvement of the present invention, the component of above-mentioned conductive silicon rubber is in weight part:
100 parts, reinforcement silicon rubber
20 parts of particulate state conductive acetylene carbon blacks
10 parts of pregnancy basic ring three silazane
5 parts of liquid silastics
1 part of vulcanizing agent
0.2 part of scorch retarder.
The particle diameter of above-mentioned particulate state conductive acetylene carbon black is 15~20nm.
Above-mentioned vulcanizing agent is DCP.
Compared with prior art, beneficial effect of the present invention is as follows:
Preparation method of the present invention is simple, and the conductive silicon rubber of preparation is aterrimus sizing material, and rubber unvulcanizate good fluidity is easy to sulfuration processing, and qualification rate is high; And be easy to and metal bonding; Rubber tensile strength >=20Mpa, ageing-resistant performance is good, is applicable to producing conduction lining and conductive rubber cushioning product.
Embodiment
For ease of understanding the present invention, it is as follows that the present invention enumerates embodiment.Those skilled in the art should understand, described embodiment only, for helping to understand the present invention, should not be considered as concrete restriction of the present invention.
Embodiment 1
A kind of cable accessory by the component of conductive silicon rubber in weight part:
100 parts, reinforcement silicon rubber
Particle diameter is 20 parts of the particulate state conductive acetylene carbon blacks of 15~20nm
10 parts of pregnancy basic ring three silazane
5 parts of liquid silastics
Vulcanizing agent DCP1 part
0.2 part of scorch retarder.
Preparation method is prepared according to this area ordinary method.
The bonding force of the conductive silicon rubber of preparation detects according to GB GB/T11211-1989 standard, and result is 3.1MPa; The tensile strength of conductive silicon rubber detects according to GB GB/T528-1998 standard, and result is 20MPa; The conductivity of conductive silicon rubber detects according to GB GB/T2439-2001 standard, and result is 450k Ω.
Embodiment 2
A kind of cable accessory by the component of conductive silicon rubber in weight part:
50 parts, reinforcement silicon rubber
Particle diameter is 15 parts of the particulate state conductive acetylene carbon blacks of 15~20nm
5 parts of pregnancy basic ring three silazane
2 parts of liquid silastics
Vulcanizing agent DCP0.5 part
0.1 part of scorch retarder.
Preparation method is prepared according to this area ordinary method.
Embodiment 3
A kind of cable accessory by the component of conductive silicon rubber in weight part:
120 parts, reinforcement silicon rubber
Particle diameter is 30 parts of the particulate state conductive acetylene carbon blacks of 15~20nm
15 parts of pregnancy basic ring three silazane
6 parts of liquid silastics
Vulcanizing agent DCP1.5 part
0.5 part of scorch retarder.
Preparation method is prepared according to this area ordinary method.
Applicant's statement, person of ordinary skill in the field is on the basis of above-described embodiment, by the concrete content point value of above-described embodiment component, combined with the technical scheme of summary of the invention part, thereby the new numerical range producing, also be one of record scope of the present invention, the application, for making specification sheets simple and clear, is no longer enumerated these numerical ranges.
Claims (4)
1. a cable accessory conductive silicon rubber, is characterized in that, the component of described conductive silicon rubber is in weight part:
50~120 parts, reinforcement silicon rubber
15~30 parts of particulate state conductive acetylene carbon blacks
5~15 parts of pregnancy basic ring three silazane
2~6 parts of liquid silastics
0.5~1.5 part of vulcanizing agent
0.1~0.5 part of scorch retarder.
2. a kind of cable accessory conductive silicon rubber as claimed in claim 1, is characterized in that, the component of described conductive silicon rubber is in weight part:
100 parts, reinforcement silicon rubber
20 parts of particulate state conductive acetylene carbon blacks
10 parts of pregnancy basic ring three silazane
5 parts of liquid silastics
1 part of vulcanizing agent
0.2 part of scorch retarder.
3. a kind of cable accessory conductive silicon rubber as claimed in claim 1, is characterized in that: the particle diameter of described particulate state conductive acetylene carbon black is 15~20nm.
4. a kind of cable accessory conductive silicon rubber as claimed in claim 1, is characterized in that: described vulcanizing agent is DCP.