CN103586641B - 过硫酸铵用钛钽铂复合板材的制备方法 - Google Patents

过硫酸铵用钛钽铂复合板材的制备方法 Download PDF

Info

Publication number
CN103586641B
CN103586641B CN201310579290.5A CN201310579290A CN103586641B CN 103586641 B CN103586641 B CN 103586641B CN 201310579290 A CN201310579290 A CN 201310579290A CN 103586641 B CN103586641 B CN 103586641B
Authority
CN
China
Prior art keywords
tantalum
plate
titanium
composite
composite plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310579290.5A
Other languages
English (en)
Other versions
CN103586641A (zh
Inventor
蒋忠于
杜向杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Shiji Chuangyou Metal Materials Co ltd
Original Assignee
BAOJI ZHONGBANG RARE METAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAOJI ZHONGBANG RARE METAL MATERIALS Co Ltd filed Critical BAOJI ZHONGBANG RARE METAL MATERIALS Co Ltd
Priority to CN201310579290.5A priority Critical patent/CN103586641B/zh
Publication of CN103586641A publication Critical patent/CN103586641A/zh
Application granted granted Critical
Publication of CN103586641B publication Critical patent/CN103586641B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

提供一种过硫酸铵用钛钽铂复合板材的制备方法，首先将钛板和钽板表面进行抛光处理；然后在钽板表面均匀涂刷保护层；再将钽板置于钛板上端，然后在钽板表面均匀布置炸药进行爆炸复合得到钛钽复合板；将钛钽复合板经超声波探伤合格后放入热处理炉内加热到500℃～650℃，保温1h～5h进行退火处理；将退火处理后的钛钽复合板切边、校平、矫直后，再经过板材轧机进行压延轧制得薄钛钽复合板；最后利用滚焊机将铂箔条滚焊在薄钛钽复合板的钽板表面得成品钛钽铂复合板材。本发明主要解决了钽、铂箔复合后铂箔易脱落的问题，同时延长了复合板材在过硫酸铵使用中的寿命。

Description

过硫酸铵用钛钽铂复合板材的制备方法
技术领域
本发明属板材制备技术领域，具体涉及一种过硫酸铵用钛钽铂复合板材的制备方法。
背景技术
在过硫酸铵的生产行业，经常采用钽铜复合棒来作为腐蚀性溶液中导电的材料，钽有良好的抗腐蚀性能，保护了有良好导电性能的铜，是一种具有良好的综合性能的导电材料，被广泛应用于氯碱、电镀等化工行业，但是，但由于在棒状电极上焊接铂金时，铂金与棒状电极为线接触，在电解槽中也容易脱落，另外，棒状电极在使用时，通常是一长排悬挂在一起沉入电解槽中，当其中一个出现问题需要检修时，往往需要把很多电极棒取下才能达到目的，费工费时，因此有必要寻求一种更为方便合适的新型替代材料。
发明内容
本发明解决的技术问题：提供一种过硫酸铵用钛钽铂复合板材的制备方法，主要解决了钽、铂箔复合后铂箔易脱落的问题，同时延长了复合板材在过硫酸铵使用中的寿命。
本发明采用的技术方案：过硫酸铵用钛钽铂复合板材的制备方法，包含下述步骤：
1）将钛板和钽板表面进行抛光处理；
2）将钽板置于钛板上端，然后在钽板表面均匀布置炸药进行爆炸复合得到钛钽复合板；
3）钛钽复合板经超声波探伤合格后放入热处理炉内加热到500℃～650℃，保温1h～5h进行退火处理；
4）将退火处理后的钛钽复合板切边、校平、矫直后，再经过板材轧机进行压延轧制得薄钛钽复合板；
5）利用滚焊机将铂箔条滚焊在薄钛钽复合板的钽板表面得成品钛钽铂复合板材。
上述步骤1）中，钛板和钽板的表面粗糙度达到0.5μm～10μm。
上述步骤4）中，压延轧制时压下量控制在0.2㎜/道次，轧制速度控制在2m/min。
上述步骤5）中，滚焊电压24V，电流1500A，线速度2m/min。
本发明与现有技术相比在钛板上复合钽板，在钽板上焊接条状铂箔，不仅耐腐蚀而且使铂箔与钽板结合更加牢固，延长了复合板材的使用寿命，具有很高的实用价值。
具体实施方式
过硫酸铵用钛钽铂复合板材的制备方法，成品尺寸：钛板厚1.5㎜；钽板厚0.2㎜；铂箔条尺寸：δ0.02×3×L。
1）δ3×800×1000㎜的纯钛板和δ0.8×800×1000㎜的钽板的表面进行抛光处理，表面粗糙度Ra均为0.5μm～10μm；
2）接着将钽板置于钛板上端，在钽板表面均匀布置炸药，对钽板、钛板进行爆炸复合得到钛钽复合板；
3）然后采用热处理炉对经超声波探伤检验合格的钽/钛复合板进行退火处理。退火处理的温度为500℃～650℃，退火时间1h～5h；
4）将退火处理后的钛钽复合板经过切边、校平、矫直后，再经过板材轧机进行压延轧制，压下量控制在0.2㎜/道次，轧制速度控制在2m/min，制成1.5㎜+0.2㎜的薄钛钽复合板。
5）利用滚焊机将δ0.02×3×L的铂箔条滚焊在薄钛钽复合板的钽板表面上得成品钛钽铂复合板，滚焊电压24V，电流1500A，线速度2m/min。
钽的密度为16.88g/cm3,钛的密度为4.5g/cm3,铂箔的密度为21.45g/cm3,钽的密度更接近铂金，这样条状铂箔焊接在钽材上比直接焊在钛材上更牢固，也就是铂箔不容易从钽材上脱落，同时，钽是一种强抗腐蚀性的物质，热的浓硫酸都不能对其造成腐蚀，从而延长复合板材的使用寿命。
上述实施例，只是本发明的较佳实施例，并非用来限制本发明实施范围，故凡以本发明权利要求所述内容所做的等效变化，均应包括在本发明权利要求范围之内。

Claims (1)

1.过硫酸铵用钛钽铂复合板材的制备方法，其特征在于包含下述步骤：
1)将钛板和钽板表面进行抛光处理；
2)将钽板置于钛板上端，然后在钽板表面均匀布置炸药进行爆炸复合得到钛钽复合板；
3)钛钽复合板经超声波探伤合格后放入热处理炉内加热到500℃～650℃，保温1h～5h进行退火处理；
4)将退火处理后的钛钽复合板切边、校平、矫直后，再经过板材轧机进行压延轧制得薄钛钽复合板；
5)利用滚焊机将铂箔条滚焊在薄钛钽复合板的钽板表面得成品钛钽铂复合板材；
上述步骤1)中，钛板和钽板的表面粗糙度达到0.5μm～10μm；
上述步骤4)中，压延轧制时压下量控制在0.2㎜/道次，轧制速度控制在2m/min；
上述步骤5)中，滚焊电压24V，电流1500A，线速度2m/min。
CN201310579290.5A 2013-11-15 2013-11-15 过硫酸铵用钛钽铂复合板材的制备方法 Active CN103586641B (zh)