CN103570878B - A kind of High-strength ethylene propylene diene monomer and preparation method thereof - Google Patents
A kind of High-strength ethylene propylene diene monomer and preparation method thereof Download PDFInfo
- Publication number
- CN103570878B CN103570878B CN201310596018.8A CN201310596018A CN103570878B CN 103570878 B CN103570878 B CN 103570878B CN 201310596018 A CN201310596018 A CN 201310596018A CN 103570878 B CN103570878 B CN 103570878B
- Authority
- CN
- China
- Prior art keywords
- district
- rubber
- machine barrel
- terpolymer
- ethylene propylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of High-strength ethylene propylene diene monomer and preparation method thereof, it is characterized in that this terpolymer EP rubber is made up of the component of following weight part: terpolymer EP rubber 90 ~ 110 parts, 2 ~ 8 parts, vinylformic acid, initiator 0.4 ~ 1 part, sodium stearate 1 ~ 5 part.High-strength ethylene propylene diene monomer of the present invention has excellent mechanics mechanical property, can be used for preparation middle-high voltage power cable, motor lead and shipboard cable etc.
Description
Technical field
The invention belongs to chemical technology field, be specifically related to a kind of High-strength ethylene propylene diene monomer and preparation method thereof.
Background technology
Terpolymer EP rubber (EPDM) through the rubber of solution copolymerization, then introduces Third monomer (ENB) by ethene, propylene.Terpolymer EP rubber is a kind of saturated superpolymer substantially, is the synthetic rubber of high comprehensive performance, has fabulous electrical property, aging resistance.But owing to not containing xln, so intensity is very low, the scope of application is very restricted.
Summary of the invention
The object of the invention is to overcome above-mentioned weak point and a kind of High-strength ethylene propylene diene monomer is provided.
Another object of the present invention is to provide the preparation method of above-mentioned High-strength ethylene propylene diene monomer.
The object of the invention is to realize in the following manner:
A kind of High-strength ethylene propylene diene monomer is made up of the component of following weight part:
Terpolymer EP rubber 90 ~ 110 parts, 2 ~ 8 parts, vinylformic acid, initiator 0.4 ~ 1 part, sodium stearate 1 ~ 5 part.
Above-mentioned terpolymer EP rubber is preferably made up of the component of following weight part: terpolymer EP rubber 100 parts, 4 ~ 6 parts, vinylformic acid, initiator 0.4 ~ 0.6 part, sodium stearate 2 ~ 3 parts.
Described initiator is peroxide initiator.Described peroxide initiator is preferably dicumyl peroxide (DCP).
The preparation method of above-mentioned High-strength ethylene propylene diene monomer comprises the following steps: terpolymer EP rubber, vinylformic acid, initiator, sodium stearate are added extruding pelletization in twin screw extruder, and the screw speed adopted during extruding pelletization is 40-50 rev/min; Twin screw extruder temperature arranges as shown in the table:
Beneficial effect of the present invention compared with the prior art: the present invention is by being cross-linked into as from aggressiveness by using stearate to make it after terpolymer EP rubber carboxyl grafting monomer to form physics, improve the intensity of virgin rubber.Meanwhile, ensure that other over-all propertieies of material obtained are all stable, to meet the demand of market diversification by increasing suitable subsidiary material again.
Embodiment
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
Test recipe:
Formula materials | Dosage (weight part) |
Terpolymer EP rubber | 100 |
Vinylformic acid | 6 |
Initiator DCP | 0.6 |
Sodium stearate | 2 |
Implementing process: terpolymer EP rubber, vinylformic acid, initiator, sodium stearate are added extruding pelletization in twin screw extruder, and the screw speed adopted during extruding pelletization is 40-50 rev/min; Twin screw extruder temperature arranges as shown in the table:
The EPDM below prepared for the embodiment of the present invention 1 and common EPDM performance comparison table, from table, correlation data can find out that EPDM tensile strength of the present invention and elongation at break all have excellent performance.
Embodiment 2
Test recipe:
Formula materials | Dosage (weight part) |
Terpolymer EP rubber | 95 |
Vinylformic acid | 4 |
Initiator DCP | 0.4 |
Sodium stearate | 3 |
Implementing process: terpolymer EP rubber, vinylformic acid, initiator, sodium stearate are added extruding pelletization in twin screw extruder, the screw speed adopted during extruding pelletization is 40-50 Zhuan ∕ minute; Twin screw extruder temperature arranges as shown in the table:
The EPDM below prepared for the embodiment of the present invention 2 and common EPDM performance comparison table, from table, correlation data can find out that EPDM tensile strength of the present invention and elongation at break all have excellent performance.
Claims (5)
1. a High-strength ethylene propylene diene monomer, is characterized in that this terpolymer EP rubber is made up of the component of following weight part: terpolymer EP rubber 90 ~ 110 parts, 2 ~ 8 parts, vinylformic acid, initiator 0.4 ~ 1 part, sodium stearate 1 ~ 5 part; This terpolymer EP rubber prepares by the following method: terpolymer EP rubber, vinylformic acid, initiator, sodium stearate are added extruding pelletization in twin screw extruder, and the screw speed adopted during extruding pelletization is 40-50 Zhuan ∕ minute; Twin screw extruder temperature arranges as follows: machine barrel one district is 100 ~ 110 DEG C, and machine barrel two district is 115 ~ 125 DEG C, and machine barrel three district is 120 ~ 130 DEG C, machine barrel four district is 140 ~ 150 DEG C, machine barrel five district is 145 ~ 155 DEG C, and machine barrel six district is 140 ~ 150 DEG C, and head temperature is 145 DEG C.
2. High-strength ethylene propylene diene monomer according to claim 1, is characterized in that this terpolymer EP rubber is made up of the component of following weight part: terpolymer EP rubber 100 parts, 4 ~ 6 parts, vinylformic acid, initiator 0.4 ~ 0.6 part, sodium stearate 2 ~ 3 parts.
3. High-strength ethylene propylene diene monomer according to claim 1 and 2, is characterized in that described initiator is peroxide initiator.
4. High-strength ethylene propylene diene monomer according to claim 3, is characterized in that described peroxide initiator is dicumyl peroxide.
5. the preparation method of the High-strength ethylene propylene diene monomer described in a claim 1 or 2, it is characterized in that described method comprises the following steps: terpolymer EP rubber, vinylformic acid, initiator, sodium stearate are added extruding pelletization in twin screw extruder, the screw speed adopted during extruding pelletization is 40-50 Zhuan ∕ minute; Twin screw extruder temperature arranges as follows: machine barrel one district is 100 ~ 110 DEG C, and machine barrel two district is 115 ~ 125 DEG C, and machine barrel three district is 120 ~ 130 DEG C, machine barrel four district is 140 ~ 150 DEG C, machine barrel five district is 145 ~ 155 DEG C, and machine barrel six district is 140 ~ 150 DEG C, and head temperature is 145 DEG C.