CN103556727B - Rectorite environment friendly acoustical absorption plate - Google Patents
Rectorite environment friendly acoustical absorption plate Download PDFInfo
- Publication number
- CN103556727B CN103556727B CN201310475255.9A CN201310475255A CN103556727B CN 103556727 B CN103556727 B CN 103556727B CN 201310475255 A CN201310475255 A CN 201310475255A CN 103556727 B CN103556727 B CN 103556727B
- Authority
- CN
- China
- Prior art keywords
- rectorite
- foaming agent
- compound foaming
- built
- frame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of rectorite environment friendly acoustical absorption plate, the main points of its technical scheme are, built-in frame is lain on mould, after short steel pipes in built-in frame inserts column, rectorite compound foaming agent is adopted to be cast in built-in frame periphery, built-in frame is embedded in the inside of compound foaming agent completely, after standing solidification process, roasting and cooling, is packaged as rectorite environment friendly acoustical absorption board finished product.Rectorite compound foaming agent is made up of raw materials such as rectorite powder, concave convex rod potter's clay powder and hydrogen peroxide; The solidification of rectorite compound foaming agent forms an integrated entirety afterwards with built-in frame, add the bulk strength of rectorite environment friendly acoustical absorption plate, bending resistance and practical effect, not only there is the effect strengthening sound-absorbing and control noises pollution, the function that also there is insulation, adsorb and purify air.Rectorite environment friendly acoustical absorption plate is applicable to be arranged in the facilities such as speedway, viaduct, urban light rail, subway, factory, warehouse, public place.
Description
Technical field
The present invention relates to abatvoix, be specifically related to a kind of rectorite environment friendly acoustical absorption plate.
Background technology
City noise drastically influence normal life and the health of human body of townsfolk, city noise mainly refers to traffic noise, factory noise, construction noise pollution and noise of social activities, the influence basin of its noise and influence degree are day by day serious, on the impact of civic living environment greatly, one of noticeable city environmental pollution problem is become.
Usual employing damping material is produced the products such as some abatvoixs, noise barrier, sound-absorbing net and noise damper and is carried out control noises pollution, also has some damping materials to be by producing the products such as abatvoix, to improve the performance of product after foaming process.
The abatvoix quality of selling in the market after foaming is more crisp, and the bulk strength of abatvoix, bending resistance and result of use are undesirable; Be installed in the process on building wall at abatvoix, abatvoix needs the on-the-spot bolt hole boring more than 4, not only time-consuming, increase difficulty of construction, and be easy to when holing abatvoix to be broken or shatter, when abatvoix is arranged on after on building wall, due to the effect of gravity, the abatvoix after boring can be caused to come off from fragmentation building wall.
Summary of the invention
The object of the invention is to overcome weak point in prior art, a kind of rectorite environment friendly acoustical absorption plate is provided.
Rectorite environment friendly acoustical absorption plate is made up of rectorite compound foaming agent and built-in frame, built-in frame is lain on mould, after short steel pipes in built-in frame inserts column, rectorite compound foaming agent is adopted to be cast in built-in frame periphery, built-in frame is embedded in the inside of compound foaming agent completely, after standing solidification process, roasting and cooling, be packaged as rectorite environment friendly acoustical absorption board finished product.
Rectorite is the special aluminium silicate mineral of crystal structure, and meet water electrode and easily disperse, film forming is smooth, is one of natural minerals of easily separated one-tenth nanoscale microplate few in number; After rectorite adds a small amount of alkali treatment, dispersion effect is better, and can keep for a long time suspending, and easily bond shaping, dries or sinter not crack; Rectorite can adsorb various inorganic ions, organic molecule and gas molecule, and this absorption and exchange are reversible, rectorite is natural possesses good UV blocking capability, remarkable to the absorption barriering effect of short wavelength light or ray, degree of fire resistance up to 1650 DEG C, and can be stablized by holding structure under 500 DEG C of states.
The concave convex rod potter's clay powder with air purification function glues Concave-convex clay rod by height, attapulite constant humidity amendment, natural-minerals adsorptive filter medium, cacumen biotae, aluminium silicate fiber peacekeeping polyacrylamide form; there is good caking property, plasticity, thixotropy, refractoriness and heat stability; can the hazardous substances such as formaldehyde, ammonia and benzene in effective absorbed air, protection of the environment and promote the healthy of people.
High sticky Concave-convex clay rod is the Concave-convex clay rod adopting the processing technology improving viscosity of attapulgite clay to produce, Concave-convex clay rod soil property is fine and smooth, there is oily soapy, light weight, property are crisp, fracture is conchoidal or irregular shape, and water imbibition is strong, tool viscosity and plasticity time wet, its viscosity can reach more than 3000mPas, is conducive to the bonding between raw material.
High sticky Concave-convex clay rod powder refers to gets 28.0g Concave-convex clay rod powder sample, add in the suspension cup of homogenizer, add 372g water again, suspension cup is placed on homogenizer, stir 20 minutes under the rotating speed of 11000 revs/min, to pour in the beaker of 250mL through high-speed stirred sample suspension again, use the viscosity of NDJ-1 type rotation viscometer test suspension liquid, tested viscosity value>=2200
mPasconcave-convex clay rod powder.
Hydrogen peroxide is commonly called as hydrogen peroxide, outward appearance is colourless transparent liquid, be a kind of strong oxidizer, the present invention selects mass fraction >=35% of industrial hydrogen peroxide, with rectorite powder and the concave convex rod potter's clay powder etc. with air purification function prepare burden mix after can generate a large amount of bubbles.
DDAO is a kind of amphoteric surfactant, colourless transparent liquid, for weak cation surfactant, in cationic in acid medium, in nonionic in alkaline medium, there is good thickening, antistatic, soft, foam enhancing and detergency ability, foaming abundancy and stablizing, the gentle excitant of character is low, has excellent antistatic behaviour and flexibility.
Cocounut oil acyl diethanol amine is water-soluble, has excellent decontamination, emulsification, foaming, steady bubble, dispersion, solubilising power.
Silicones polyethers emulsion is a kind of novel high polymer foam stabilizer, put in order by changing intramolecule, surfactant is steeped arrange closely neatly between bubble, thus form fine and close inner layer film, make anti-pressure ability strong especially, the structural stability of air bubble liquid-membrane can be controlled, make surfactant molecule in the Methodistic distribution of the liquid film of bubble, give elasticity and the self-reparing capability of have good lather, thus reach steady bubble effect desirable especially.
Polyether modified silicon oil is the organosilicon non-ionic surface active agent of a kind of unique properties adopting polyethers and dimethyl siloxane graft copolymerization, can reduce internal friction, the stress of its molecule, thus play levelling, froth breaking for the present invention.
The present invention is achieved by following technical proposals:
Rectorite environment friendly acoustical absorption plate is a kind of rectangular plate-shaped body, is made up of built-in frame and rectorite compound foaming agent, is designed with 4 ~ 32 short steel pipes in built-in frame, and the endoporus of short steel pipes is the installing hole of rectorite environment friendly acoustical absorption plate; Built-in frame is lain on mould, after short steel pipes in built-in frame inserts column, adopt rectorite compound foaming agent to be cast in built-in frame periphery, built-in frame is rectorite environment friendly acoustical absorption boards half-finished product after being embedded in the inside of rectorite compound foaming agent completely; After the standing solidification process of 1 ~ 7 day, taken out from mould by rectorite environment friendly acoustical absorption boards half-finished product, be transported to roasting in tunnel cave, sintering temperature controls at 450 ~ 750 DEG C, roasting time controls at 3 ~ 8 hours, is packaged as rectorite environment friendly acoustical absorption board finished product after cooling.
Rectorite compound foaming agent batching is made up of following component by weight percentage: rectorite compound foaming agent paste 25 ~ 80%, hydrogen peroxide 2 ~ 35%, polyether modified silicon oil 0.001 ~ 5% and water 1 ~ 45%; The production method of rectorite compound foaming agent: stir in rectorite compound foaming agent batching input homogenizer, the speeds control of mixer is at 1400 ~ 1800 revs/min, mixing time controls at 2 ~ 30 minutes, be rectorite compound foaming agent after stirring, containing intensive bubble stable in a large number in rectorite compound foaming agent.
Rectorite compound foaming agent paste batching is made up of following component by weight percentage: rectorite powder 15 ~ 55%, the concave convex rod potter's clay powder 5 ~ 35% with air purification function, DDAO 0.01 ~ 25%, cocounut oil acyl diethanol amine 0.01 ~ 20%, silicones polyethers emulsion 0.01 ~ 5% and water 5 ~ 55%; The production method of rectorite compound foaming agent paste: stir in rectorite compound foaming agent paste batching input low-speed mixer, the speeds control of mixer is at 600 ~ 800 revs/min, mixing time controls at 2 ~ 20 minutes, for rectorite compound foaming agent paste after stirring, generating portion bubble in rectorite compound foaming agent paste.
Rectorite compound foaming agent has applied for patent of invention, China Patent Publication No.: CN103274738A, publication date: on 09 04th, 2013.
Built-in frame is a kind of rectangular steel structure frame, is made up of in built-in frame 4 ~ 32 short steel pipes, 4 ~ 52 pieces of punching expanded metal laths and 2 ~ 42 reinforcing ribs; The upper plane of short steel pipes is processed as a kind of counter sink, a rectangular frame is welded as with punching expanded metal lath between short steel pipes and short steel pipes, punching expanded metal lath hole is circular opening, the horizontal center line at short steel pipes height 1/2 place and the horizontal center line at punching expanded metal lath width 1/2 place overlap, in rectangular frame with the diagonal at height 1/2 place between short steel pipes and short steel pipes for interface, reinforcing rib is welded as, a common composition built-in frame with screw-thread steel; In built-in frame, the plane of short steel pipes top counter sink consists of plane on built-in frame jointly, and short steel pipes lower flat consists of built-in frame lower plane jointly;
For the production of the built-in frame separate case application utility model patent of abatvoix, number of patent application is: 201320579228.1, the applying date: on September 18th, 2013.
Mould is a kind of rectangular mould, is made up of a block length square floor, rectangle locating slot, rectangle frame, 2 rectangle handles and 4 ~ 32 cylindrical columns; Locating slot is welded on the upper plane of die bottom plate according to the position dimension of design, column is arranged on the upper plane of die bottom plate according to the relative position size of design, frame is placed in locating slot, 2 handles are arranged on middle outside frame the right and left respectively, and the lower plane of die bottom plate is placed on vibrations workbench;
For the production of the mould separate case application utility model patent of abatvoix, number of patent application is: 201320575991.7, the applying date: on September 17th, 2013.
Built-in frame has been inlayed in rectorite environment friendly acoustical absorption plate, the solidification of rectorite compound foaming agent forms an integrated entirety afterwards with built-in frame, rectorite environment friendly acoustical absorption boards half-finished product, after roasting, considerably increases the bulk strength of rectorite environment friendly acoustical absorption plate, bending resistance and practical effect.
At construction site, do not need boring, directly with cross recessed countersunk head tapping screw, rectorite environment friendly acoustical absorption plate is arranged on the metope of building, saving of work and time, rectorite environment friendly acoustical absorption plate also can not be caused to come off from fragmentation building wall.
It is evenly fine and smooth that rectorite compound foaming agent in rectorite environment friendly acoustical absorption plate has the abscess that foaming capacity is strong, coefficient of foaming is high, unit volume bubble production volume large, produce, foam adventitia good toughness is not easily broken, foam stability is good, can not froth breaking for a long time, invalid bubble is produced to reduce product surface, improve the make rate of abscess, the effect of the mould that prevents from collapsing.
Rectorite environment friendly acoustical absorption plate there will not be layering in casting process, and product stripping speed is fast, and finish is good, further increases the later strength of product.
Rectorite compound foaming agent adopts the rectorite potter's clay powder with air purification function for mainly raw material; there is good caking property, plasticity, thixotropy, refractoriness and heat stability; can the hazardous substances such as formaldehyde, ammonia and benzene in effective absorbed air, protection of the environment and promote the healthy of people.
Rectorite environment friendly acoustical absorption plate not only has the effect strengthening sound-absorbing and control noises pollution, the function also having insulation, adsorb and purify air.
Rectorite environment friendly acoustical absorption plate is applicable to be arranged in the facilities such as speedway, viaduct, urban light rail, subway, factory, warehouse, public place.
Accompanying drawing explanation
Fig. 1 is rectorite environment friendly acoustical absorption plate schematic diagram, and Fig. 2 is the A-A direction view of Fig. 1, and Fig. 3 is the schematic diagram that built-in frame lies in when pouring into a mould in mould, and Fig. 4 is the schematic diagram be arranged on by rectorite environment friendly acoustical absorption plate on building wall.
As shown in the figure: 1 is rectorite environment friendly acoustical absorption plate, and 2 is built-in frames, and 3 is rectorite compound foaming agents, and 4 is moulds, and 5 is short steel pipes, and 6 is columns, and 7 is cross recessed countersunk head tapping screws, 8 is metopes of building.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Rectorite environment friendly acoustical absorption plate is a kind of rectangular plate-shaped body 1, is made up of built-in frame 2 and rectorite compound foaming agent 3, is designed with 6 short steel pipes 5 in built-in frame 2; Built-in frame 2 is lain on mould 4, after short steel pipes 5 in built-in frame 2 inserts column 6, adopt rectorite compound foaming agent 3 to be cast in built-in frame 2 peripheral, built-in frame 2 is rectorite environment friendly acoustical absorption boards half-finished product after being embedded in the inside of rectorite compound foaming agent 3 completely; After the standing solidification process of 7 days, taken out from mould by rectorite environment friendly acoustical absorption boards half-finished product, be transported to roasting in tunnel cave, sintering temperature controls at 600 ~ 700 DEG C, and roasting time controls at 6 hours, is packaged as rectorite environment friendly acoustical absorption board finished product after cooling.
Rectorite compound foaming agent batching is made up of following component by weight percentage: rectorite compound foaming agent paste 64%, hydrogen peroxide 25.95%, polyether modified silicon oil 0.05% and water 10%; The production method of rectorite compound foaming agent: stir in rectorite compound foaming agent batching input homogenizer, the speeds control of mixer is at 1500 ~ 1600 revs/min, mixing time controls at 12 minutes, is rectorite compound foaming agent after stirring.
Rectorite compound foaming agent paste batching is made up of following component by weight percentage: rectorite powder 44%, the concave convex rod potter's clay powder 14% with air purification function, DDAO 3%, cocounut oil acyl diethanol amine 2%, silicones polyethers emulsion 1% and water 36%; The production method of rectorite compound foaming agent paste: stir in rectorite compound foaming agent paste batching input low-speed mixer, the speeds control of mixer is at 650 ~ 750 revs/min, mixing time controls at 6 minutes, is rectorite compound foaming agent paste after stirring.
At construction site, directly with cross recessed countersunk head tapping screw 7, rectorite environment friendly acoustical absorption plate 1 is arranged on the metope 8 of building.
Claims (1)
1. a rectorite environment friendly acoustical absorption plate, is characterized in that, rectorite environment friendly acoustical absorption plate is a kind of rectangular plate-shaped body, is made up of built-in frame and rectorite compound foaming agent, is designed with 4 ~ 32 short steel pipes in built-in frame; Built-in frame is lain on mould, after short steel pipes in built-in frame inserts column, adopt rectorite compound foaming agent to be cast in built-in frame periphery, built-in frame is rectorite environment friendly acoustical absorption boards half-finished product after being embedded in the inside of rectorite compound foaming agent completely; After the standing solidification process of 1 ~ 7 day, taken out from mould by rectorite environment friendly acoustical absorption boards half-finished product, be transported to roasting in tunnel cave, sintering temperature controls at 450 ~ 750 DEG C, roasting time controls at 3 ~ 8 hours, is packaged as rectorite environment friendly acoustical absorption board finished product after cooling;
Described rectorite compound foaming agent batching is made up of following component by weight percentage: rectorite compound foaming agent paste 25 ~ 80%, hydrogen peroxide 2 ~ 35%, polyether modified silicon oil 0.001 ~ 5% and water 1 ~ 45%; The production method of rectorite compound foaming agent: stir in rectorite compound foaming agent batching input homogenizer, the speeds control of mixer is at 1400 ~ 1800 revs/min, mixing time controls at 2 ~ 30 minutes, is rectorite compound foaming agent after stirring;
Described rectorite compound foaming agent paste batching is made up of following component by weight percentage: rectorite powder 15 ~ 55%, the concave convex rod potter's clay powder 5 ~ 35% with air purification function, DDAO 0.01 ~ 25%, cocounut oil acyl diethanol amine 0.01 ~ 20%, silicones polyethers emulsion 0.01 ~ 5% and water 5 ~ 55%; The production method of rectorite compound foaming agent paste: stir in rectorite compound foaming agent paste batching input low-speed mixer, the speeds control of mixer is at 600 ~ 800 revs/min, mixing time controls at 2 ~ 20 minutes, is rectorite compound foaming agent paste after stirring.