CN103555441B

CN103555441B - Tile seam cleaner

Info

Publication number: CN103555441B
Application number: CN201310508632.4A
Authority: CN
Inventors: 李秋雁; 王金平; 童星; 杜永卫
Original assignee: JIANGSU XUEBAO DAILY CHEMICAL CO Ltd
Current assignee: JIANGSU XUEBAO DAILY CHEMICAL CO Ltd
Priority date: 2013-10-25
Filing date: 2013-10-25
Publication date: 2015-07-01
Anticipated expiration: 2033-10-25
Also published as: CN103555441A

Abstract

The invention discloses a tile seam cleaner comprising the following components in percentage by weight: 1.5-10% of nonionic surfactant, 1-8% of sodium polyoxyethylene fatty alcohol sulfate, 3-20% of aminosulfonic acid, 0.3-4% of citric acid, 0.5-10% of propanediol butyl ether, 0.2-0.8% of silicon-fluorine resin, 3.0-10.0% of modified acrylic resin, 0.2-0.9% of sodium citrate, 0.1-6% of mildew preventive and 0.1-0.5% of bactericide. The tile seam cleaner is prepared according to a natural environment-friendly formula, is neutral and belongs to a green product; after the tile seam cleaner is used at a tile seam, oxides such as dust and the like can be removed, the tile seam has no water marks and is bright after the cleaner is volatilized, seam materials such as cement and the like at the seam are not corroded, and meanwhile, the surface of a seam material can form a layer of protective film which has pollution resistance; the tile seam cleaner is low in cost, convenient to use, good in cleaning effect, capable of meeting the requirements of people and relatively wide in market prospect.

Description

A kind of Tile seam cleaner

Technical field

The present invention relates to a kind of household chemicals field, especially a kind of powerful Tile seam cleaner.

Background technology

Along with the progress of society, due to ceramic tile natural, attractive in appearance, magnificent, waterproof and easily install, domestic and international various construction wall, flooring, kitichen and toilet is more and more extensive to the application of ceramic tile, but along with the growth of duration of service, if do not cleaned ceramic tile over a long time, ceramic tile surface will burnt hair dimmed, go mouldy, and easily grow bacterium, affect attractive in appearance.Dirt on high buildings and large mansions buildings ceramic tile is mainly: the weathering oxidation of dust, cement, mortar exudate and ceramic tile surface. so good luminance brightness will be kept, need clean ceramic tile at set intervals.Traditional ceramic tile cleaner only has cleaning action; washmarking can be left after cleaning; affect cleaning effect; and provide protection is not had to ceramic tile, need to clean frequently, current most clean-out system is alkalescence in addition; the joint fillers such as the cement at butt seam place form corrosion; life-time service, affects wall quality, and has certain pollution to environment.

Summary of the invention

The object of the invention is to overcome the defect existed in prior art, develop a kind of thorough de-sludging, anti-soil, mildew-resistant and to Tile seam material not become corrosion environment protection tile seam cleaner.

For achieving the above object, technical scheme of the present invention there is provided a kind of Tile seam cleaner, and described Tile seam cleaner is made up of following component, and the weight percent of described component is:

Nonionogenic tenside 1.5%-10%;

Polyoxyethylenated alcohol sodium sulfate 1%-8%;

Thionamic acid 3%-20%;

Citric acid 0.3%-4%;

Propandiol butyl ether 0.5%-10%;

Fluosilicic resin 0.2%-0.8%;

Acrylic acid modified resin 3.0%-10.0%;

Trisodium Citrate 0.2%-0.9%;

Mould inhibitor 0.1%-6%;

Sterilant 0.1%-0.5%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, preferred technical scheme is, described Tile seam cleaner also comprises the essence that weight percent is less than 0.5%.

Wherein, preferred technical scheme is, described nonionogenic tenside comprises alkyl glycoside or fatty alcohol-polyoxyethylene ether (JFC permeate agent).

Wherein, preferred technical scheme is, the per-cent that described alkyl glycoside weight accounts for each composition weight is 1 ~ 5%, and the per-cent that the weight of fatty alcohol-polyoxyethylene ether accounts for each composition weight is 0.5 ~ 5%.

Wherein, preferred technical scheme is, described mould inhibitor is Sorbic Acid, propylben, at least one in ethyl p-hydroxybenzoate.

Wherein, preferred technical scheme is, sterilant is CDMP (PCMX) or triclosan.

Wherein, preferred technical scheme is, the composition of described Tile seam cleaner and the weight percent of component are:

Alkyl glycoside 1% ~ 5%;

Fatty alcohol-polyoxyethylene ether 0.5% ~ 5%;

Polyoxyethylenated alcohol sodium sulfate 1% ~ 8%;

Thionamic acid 3%-20%;

Citric acid 0.3% ~ 4%;

Propandiol butyl ether 0.5%-10%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 3.0% ~ 10.0%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Alkyl glycoside 3%;

Fatty alcohol-polyoxyethylene ether 2%;

Polyoxyethylenated alcohol sodium sulfate 4%;

Thionamic acid 12%;

Citric acid 2%;

Propandiol butyl ether 5.5%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 6%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Preparation method of the present invention is: joined by deionized water in agitator kettle, start stirring, adds above raw material successively in agitator kettle, stirs after 30 minutes, dissolves completely, leaves standstill.Sample examination, qualified rear filling.

Advantage of the present invention and beneficial effect are: the present invention adopts high-tech environmental-friendly natural formula, and clean-out system, in neutral, belongs to green product; With the addition of fluosilicic resin and acrylic acid modified resin, effectively can improve anti-fouling effect; Add mould inhibitor, improve anti-mold effect; The present invention, after Tile seam place uses, can dispel the oxide compounds such as dust, not stay washmarking after volatilization, light, and the joint fillers such as the cement at butt seam place do not form corrosion, can also form layer protecting film simultaneously, have pollution resistance on its surface; Cost of the present invention is low, easy to use, and clean effect is good, can meet the demand of people, has larger market outlook.

Preparation technology of the present invention is simple, easy to operate, is applicable to the scale production of this formula.

Embodiment

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

embodiment 1

A kind of Tile seam cleaner, described Tile seam cleaner is made up of following component, and the weight percent of described component is:

Nonionogenic tenside 10%;

Polyoxyethylenated alcohol sodium sulfate 8%;

Thionamic acid 3%;

Citric acid 0.3%;

Propandiol butyl ether 0.5%;

Fluosilicic resin 0.2%;

Acrylic acid modified resin 3.0%;

Trisodium Citrate 0.2%;

Mould inhibitor 0.1%;

Sterilant 0.1%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, nonionogenic tenside is fatty alcohol-polyoxyethylene ether, and described mould inhibitor is Sorbic Acid; Sterilant is triclosan.

embodiment 2

Nonionogenic tenside 1.5%;

Polyoxyethylenated alcohol sodium sulfate 1%;

Thionamic acid 20%;

Citric acid 4%;

Propandiol butyl ether 10%;

Fluosilicic resin 0.8%;

Acrylic acid modified resin 10.0%;

Trisodium Citrate 0.9%;

Mould inhibitor 6%;

Sterilant 0.5%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, nonionogenic tenside is alkyl glycoside; Described mould inhibitor is propylben; Sterilant is CDMP (PCMX).

embodiment 3

Alkyl glycoside 1%;

Fatty alcohol-polyoxyethylene ether 5%;

Polyoxyethylenated alcohol sodium sulfate 3%;

Thionamic acid 10%;

Citric acid 2%;

Propandiol butyl ether 4%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 7%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, described mould inhibitor is Sorbic Acid; Sterilant is CDMP (PCMX).

embodiment 4

The composition of described Tile seam cleaner and the weight percent of component are:

Alkyl glycoside 5%;

Fatty alcohol-polyoxyethylene ether 0.5%;

Polyoxyethylenated alcohol sodium sulfate 5%;

Thionamic acid 17%;

Citric acid 0.5%;

Propandiol butyl ether 8%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 4%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, described mould inhibitor is propylben; Sterilant is triclosan.

embodiment 5

Alkyl glycoside 3%;

Fatty alcohol-polyoxyethylene ether 2%;

Polyoxyethylenated alcohol sodium sulfate 4%;

Thionamic acid 12%;

Citric acid 2%;

Propandiol butyl ether 5.5%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 6%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

Wherein, described mould inhibitor is in ethyl p-hydroxybenzoate; Sterilant is CDMP (PCMX) and triclosan, and the proportioning of the two is 1:1.

The present invention can dilute 50 times of uses, and cost is low, easy to use, and technique is simple, and clean effect is good, can meet the demand of people, and environmental protection, there are larger market outlook.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims

1. a Tile seam cleaner, is characterized in that, described Tile seam cleaner is made up of following component, and the weight percent of described component is:

Nonionogenic tenside 1.5%-10%;

Polyoxyethylenated alcohol sodium sulfate 1%-8%;

Thionamic acid 3%-20%;

Citric acid 0.3%-4%;

Propandiol butyl ether 0.5%-10%;

Fluosilicic resin 0.2%-0.8%;

Acrylic acid modified resin 3.0%-10.0%;

Trisodium Citrate 0.2%-0.9%;

Mould inhibitor 0.1%-6%;

Sterilant 0.1%-0.5%;

Deionized water surplus;

The weight percent sum of each component is 100%.

2, a Tile seam cleaner, is characterized in that, described Tile seam cleaner is made up of following component, and the weight percent of described component is:

Nonionogenic tenside 1.5%-10%;

Polyoxyethylenated alcohol sodium sulfate 1%-8%;

Thionamic acid 3%-20%;

Citric acid 0.3%-4%;

Propandiol butyl ether 0.5%-10%;

Fluosilicic resin 0.2%-0.8%;

Acrylic acid modified resin 3.0%-10.0%;

Trisodium Citrate 0.2%-0.9%;

Mould inhibitor 0.1%-6%;

Sterilant 0.1%-0.5%;

Deionized water surplus;

Described Tile seam cleaner also comprises the essence that weight percent is less than 0.5%, and the weight percent sum of each component is 100%.

3, according to the Tile seam cleaner described in claim 2, it is characterized in that, described nonionogenic tenside comprises alkyl glycoside or fatty alcohol-polyoxyethylene ether.

4, according to the Tile seam cleaner described in claim 3, it is characterized in that, the per-cent that described alkyl glycoside weight accounts for each composition weight is 1% ~ 5%, and the per-cent that the weight of fatty alcohol-polyoxyethylene ether accounts for each composition weight is 0.5%-5%.

5, according to the Tile seam cleaner described in claim 4, it is characterized in that, described mould inhibitor is Sorbic Acid, propylben, at least one in ethyl p-hydroxybenzoate.

6, according to the Tile seam cleaner described in claim 5, it is characterized in that, described sterilant is CDMP or triclosan.

7, Tile seam cleaner according to claim 2, is characterized in that, the composition of described Tile seam cleaner and the weight percent of component are:

Alkyl glycoside 1% ~ 5%;

Fatty alcohol-polyoxyethylene ether 0.5% ~ 5%;

Polyoxyethylenated alcohol sodium sulfate 1% ~ 8%;

Thionamic acid 3%-20%;

Citric acid 0.3 ~ 4%;

Propandiol butyl ether 0.5%-10%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 3.0% ~ 10.0%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.

8, Tile seam cleaner according to claim 7, is characterized in that, the composition of described Tile seam cleaner and the weight percent of component are:

Alkyl glycoside 3%;

Fatty alcohol-polyoxyethylene ether 2%;

Polyoxyethylenated alcohol sodium sulfate 4%;

Thionamic acid 12%;

Citric acid 2%;

Propandiol butyl ether 5.5%;

Fluosilicic resin 0.5%;

Acrylic acid modified resin 6%;

Trisodium Citrate 0.6%;

Mould inhibitor 0.3%;

Sterilant 0.2%;

Essence 0.3%;

Deionized water surplus;

The weight percent sum of each component is 100%.