CN103555226A - 一种快速调和腻子或水泥的胶粉和胶液 - Google Patents
一种快速调和腻子或水泥的胶粉和胶液 Download PDFInfo
- Publication number
- CN103555226A CN103555226A CN201310558950.1A CN201310558950A CN103555226A CN 103555226 A CN103555226 A CN 103555226A CN 201310558950 A CN201310558950 A CN 201310558950A CN 103555226 A CN103555226 A CN 103555226A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- putty
- glue
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于建筑胶粘剂技术领域,涉及一种快速调和腻子或水泥的胶粉和胶液。该胶粉主要包括以下重量份的成分:PVA:20份~65份,PAM:10份~42份,HPMC:4.0份~18份。该胶液在所述胶粉的基础上增加醇或去离子水即可。与现有的胶粉和胶液相比,本发明的产品具有调配工艺简便,1小时内即可完成配制,开放时间30秒,胶液透明,粘度可根据使用要求自由调整,成本低廉,贮存稳定等优点。用于调和水泥、建筑腻子等可加速其初凝,并提高对基材的粘结力,提高工效。
Description
技术领域
本发明属于化工合成胶粘剂技术领域,涉及一种快速调和腻子或水泥的胶粉和胶液,主要用于家具制作、装修装饰、水泥砂浆制作过程中替代或者部分替代自来水,可以使制得的砂浆对基体材料或墙体的粘结力得到提高、减少工时、节约成本。
背景技术
建筑行业每天都要消耗大量的水泥和嵌缝、补疵的批泥,家具和装饰行业则要使用无数的腻子。以往的腻子一般是由基料(水泥和有机聚合物)、填料(重钙、滑石粉、灰钙、石灰粉)、水和助剂等组成的,也有加入聚乙烯醇、瓜尔胶(一种生物质化工原料)、聚马来酸酐、PVA、淀粉改性物加热溶解配制成的胶液来提高强度的,不仅加热需要耗能,而且一时半会儿很难溶解均匀完全。
现在市售的腻子粉在调配胶液时,需要使用50~85℃的热水浸泡1~2小时才能溶解通透均匀,而且胶液在储存过程中容易发生表面“结皮”、稠度变稀,甚至分层的现象。使用效果比较单一,在粘结强度、柔韧性、抗裂性等方面很难协调。
发明内容
本发明要解决的技术问题是调整腻子及水泥等建筑辅料用的胶粉和胶液的配方,在调配砂浆过程中使用该胶粉和胶液替代或者部分替代自来水,可以增加建筑辅料对涂覆基体的胶粘强度,降低配方成本,提高建筑装饰工作的速率。应用本专利技术或产品,不需要加热溶解配料,可加速水泥和腻子的初凝速度、节省施工时间30分钟,大大提高工作效率,同时提高对所粘结的墙体、家具、饰品的粘结力20%以上。
为解决上述技术问题,本发明所采用的技术方案是:
一种快速调和腻子或水泥的胶粉,由以下重量份的成分组成:
聚乙烯醇 20份~65份;
聚丙烯酰胺 10份-42份;
羟丙基纤维素 4份-18份。
一种快速调和腻子或水泥的胶液,由以下重量份的成分组成:
聚乙烯醇 20份-65份;
聚丙烯酰胺 10份-42份;
羟丙基纤维素 4份-18份;
醇 0.1份-5.0份;
去离子水 1份-65份。
所述快速调和腻子或水泥的胶液,优选由以下重量份的成分组成:
聚乙烯醇 20份-30份;
聚丙烯酰胺 10份-20份;
羟丙基纤维素 4份-10份。
乙醇 2份-5份;
去离子水 45份-60份。
所述聚乙烯醇原料优选型号为1788、1799、2488或24P中的一种或几种。
所述聚丙烯酰胺的相对分子量优选为200万~1500万,选自阴离子型、阳离子型或非离子型中的任意一种。
所述羟丙基纤维素的粘度优选为10~20万厘泊。
所述快速调和腻子或水泥的胶粉的配制工艺是将三种粉料按照配方称量配料、混合均匀,用80目筛筛分即可。
所述快速调和腻子或水泥的胶液的配制工艺是将聚乙烯醇、聚丙烯酰胺和羟丙基纤维素三种粉料直接用乙醇和去离子水搅拌30分钟,溶解均匀,用80-100目筛过滤即得。
下面对本发明做进一步解释和说明:
快速调和的腻子胶或水泥胶的胶粉和胶液所用原料PVA(化学名称为聚乙烯醇)的型号包括1788、1799、2488、24P;PAM(化学名称为聚丙烯酰胺)的型号包括阴离子型、阳离子型以及非离子型,相对分子量(代号Mn)100000~4800000;HPMC(化学名称为羟丙基纤维素)的型号包括粘度(代号η)为10~20万厘泊(即mPa.s);乙醇和去离子水为常见化学原料;成品用于调和水泥、建筑腻子等,可缩短其初凝时间,并提高对基材的粘结力,大大提高配制腻子和水泥砂浆的工效。
本发明的胶粉配制原料选用分子量大小、醇解度和粒度合适的聚乙烯醇(化工行业统一代号为PVA)、不同聚合工艺合成的聚丙烯酰胺(PAM)、粘度指数相当的羟丙基纤维素(HPMC),以乙醇和去离子水作为溶剂。其中,醇解度和粒度合适的聚乙烯醇具有较好的冷水溶解性、成膜性和柔韧性,聚丙烯酰胺具有较好的粘结强度和成膜硬度,羟丙基纤维素则能赋予制品较好的平整性和抗裂性,添加乙醇能够提高上述粉料的常温溶解速度。各组分之间的比例以协调它们在胶粉中的功能平衡和控制产品成本为目标做调整,具体组分及质量份以下:PVA:20~65%,PAM: 10~42%,HPMC: 5.0~18%,乙醇: 0~5.0%,去离子水: 0~56%。该胶粉的制备工艺过程包括配料、混合、过筛等,若要配制成胶液,则只需溶解在溶剂及去离子水中即可。
目前市售的腻子胶粉一般是由基料、填料、水和助剂等组成。现在市售的腻子粉在调配胶液时,需要使用50~85℃的热水浸泡1~2小时才能溶解通透均匀,初凝时间约为1-2小时,而且胶液在储存过程中容易发生表面“结皮”、稠度变稀,甚至分层的现象。使用效果比较单一,对木材件的粘结力约为32-38 kPa, 制得的腻子或水泥件虽然硬度较好,但表面平整性和抗冲击性较差,在粘结强度、柔韧性、抗裂性等方面很难协调。与之相比,本专利产品具有配制工艺简便,1小时内即可完成,开放时间30秒,胶液透明,粘度可根据使用要求自由调整,成本低廉,贮存稳定等优点。用于调和水泥、建筑腻子等可加速其初凝,并提高对基材的粘结力,提高工效。
与现有技术相比较,本发明的优势在于:
1. 本发明胶粉不含易挥发的有害溶剂,无毒,无污染,绿色环保,符合我国的环保政策和产业发展方向。
2. 使用本发明的快速调和腻子及水泥的胶粉及胶液替代或者部分替代自来水调和建筑辅料,无需加热混料,和合快速;固化后,对涂覆基体的粘接强度高,抗剥离性好。例如,在其它用料配方不变的前提下,用本发明的腻子胶液代替通用的腻子粉液调配水泥,可以使325标号水泥制品的强度达到425标号水泥的强度。
3. 按2013年6月的化工市场原料价格初步核算,该胶粉的原料成本约为15000元,25℃下2600mPa.s粘度的胶液的原料成本为400元以下,成本低,能够为用户提供足够的利润空间。
具体实施方式
下面结合实施例对本发明作进一步说明,但本发明的保护范围并不限于此。
实施例1:
一种快速调和腻子或水泥胶液包括以下成分及用量: PVA1799:20%(重量百分数,以下同),阴离子型相对分子量为300万的PAM: 16%,粘度为12万厘泊的HPMC:5%,乙醇:3%,去离子水:56%。
该胶液的制备工艺过程包括按照上述重量百分配比称取原料配料、用锥形垂直螺旋混合机、V型混合机或和面机进行混合、搅拌0.5小时,经摇动筛或振动筛过筛分除大颗粒等,先制成粉剂,取样对照技术指标进行质量检测,即制得可以快速调和溶解的胶粉产品。然后将其投入和面机中,加乙醇和自来水,搅拌40分钟可配制得到固含量为40%的胶液,其粘度为4600 mPa·s。
与现有的调胶粉或胶液相比,本产品具有制作工艺简便,1小时内即可配制完成,初凝时间为38秒,胶液透明,粘度可根据使用要求自由调整,对木材件的粘结强度达到45 kPa,成本低廉,贮存稳定等优点。用于调和水泥、建筑腻子等可加速其初凝,并提高对基材的粘结力,大大提高配制腻子和水泥砂浆的工效。
实施例2~5:
实施例2~5的胶粉以及胶液的制作工艺过程与上述实施例1基本相同,各例的原料配方见表1所示:
表1 实施例2~5胶的原料配方表 单位:%
Claims (10)
1.一种快速调和腻子或水泥的胶粉,其特征是,由以下重量份的成分组成:
聚乙烯醇 20份~65份;
聚丙烯酰胺 10份-42份;
羟丙基纤维素 4份-18份。
2.根据权利要求1所述快速调和腻子或水泥的胶粉,其特征是,所述聚乙烯醇选自型号为1788、1799、2488或24P中的一种或几种。
3.根据权利要求1所述快速调和腻子或水泥的胶粉,其特征是,所述聚丙烯酰胺的相对分子量为200万~1500万,选自阴离子型、阳离子型或非离子型中的任意一种。
4.根据权利要求1所述快速调和腻子或水泥的胶粉,其特征是,所述羟丙基纤维素的粘度为10万厘泊~20万厘泊。
5.一种快速调和腻子或水泥的胶液,其特征是,由以下重量份的成分组成:
聚乙烯醇 20份-65份;
聚丙烯酰胺 10份-42份;
羟丙基纤维素 4份-18份;
醇 0.1份-5.0份;
去离子水 1份-65份。
6.根据权利要求5所述快速调和腻子或水泥的胶液,其特征是,由以下重量份的成分组成:
聚乙烯醇 20份-30份;
聚丙烯酰胺 10份-20份;
羟丙基纤维素 4份-10份;
乙醇 2份-5份;
去离子水 45份-60份。
7.根据权利要求5或6所述快速调和腻子或水泥的胶液,其特征是,所述聚乙烯醇选自型号为1788、1799、2488或24P中的一种或几种。
8.根据权利要求5或6所述快速调和腻子或水泥的胶液,其特征是,所述聚丙烯酰胺的相对分子量200万~1500万,选自阴离子型、阳离子型或非离子型中的任意一种。
9.根据权利要求5或6所述快速调和腻子或水泥的胶液,其特征是,所述羟丙基纤维素的粘度为10万厘泊~20万厘泊。
10.根据权利要求5或6所述快速调和腻子或水泥的胶液,其特征是,配制方法是将聚乙烯醇、聚丙烯酰胺和羟丙基纤维素三种粉料直接用乙醇和去离子水搅拌30分钟,溶解均匀,用80-100目筛过滤即得。