CN103555079B - A kind of anti-mildew is except the brushing method of methanal paint - Google Patents
A kind of anti-mildew is except the brushing method of methanal paint Download PDFInfo
- Publication number
- CN103555079B CN103555079B CN201310557785.8A CN201310557785A CN103555079B CN 103555079 B CN103555079 B CN 103555079B CN 201310557785 A CN201310557785 A CN 201310557785A CN 103555079 B CN103555079 B CN 103555079B
- Authority
- CN
- China
- Prior art keywords
- coating
- nano
- tio
- zno
- mildew
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the brushing method of a kind of anti-mildew except methanal paint, this system component comprises: polystyrene-acrylic copolymer or acrylic copolymer or Vinyl Acetate Copolymer-acrylic copolymer, talcum powder, auxiliary agent, pigment, antimildew disinfectant, sorbent material, water, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=(1 ~ 2): 1:0.5.Bottom of the present invention and transition layer all adopt brushing method, and ensure being coated with property and the effect of coating, last investment precoat adopts spraying, ensure surface layer smooth and beautiful appearance, coating through this method of application brushing does not chap, non-scale, and method is simple and easy to implement, and it is both artistic and practical to be coated with brushing effects.
Description
Technical field
The present invention relates to chemical field, particularly a kind of anti-mildew is except the brushing method of methanal paint.
Background technology
At present, in house decoration, the house ornamentation that the objectionable impurities such as formaldehyde, benzene homologues, TVOC brought due to various finishing material causes pollutes and the exceeding standard of objectionable impurities in room air.Seriously disturb daily life.Human body absorbs this gas containing formaldehyde for a long time and can give rise to diseases, serious also can crisis to the life security of people.Therefore to carry out the improvement of room air pollution to the room after finishing and the new furniture bought, and eliminate the pollution of the obnoxious flavour that new furniture brings.To ensure that the content of indoor harmful gas is within the scope of national regulation, people are lived in a healthy environment.
In recent years, lot of domestic and international scientific research institution is all in a kind of safety of development, the method of efficient control formaldehyde pollution, as application number be 200910106091.6 application discloses a kind of air purification environment-friendly coating, this system component and weight percent are: water: 35%, talcum powder: 25%, kaolin: 20%, multifunctional assistant: 2.5%, thickening material: 1.5%, compound flow agent: 1.5%, defoamer: 1.5%, wetting agent: 1.5%, antiseptic-germicide: 5%, plant fragrance agent: 0.5%, film coalescence aid: 2.0%, sanitas: 1.5%, mould inhibitor: 1.5%, dispersion agent: 0.5%, whitening agent: 0.5%.
Although this kind of coating of the prior art has certain effect for removing formaldehyde, complicated due to its component, the ability that its anti-mildew becomes is poor, extremely affects the outward appearance of upholstery after going mouldy.Although wherein also with the addition of some mould inhibitors, its effect is still undesirable, and the time that opposing is gone mouldy is still shorter.
Summary of the invention
Ability, time length short problem is become for solving finishing coating anti-mildew in prior art, an object of the present invention is the brushing method providing a kind of anti-mildew except methanal paint, this coating effectively can be resisted and go mouldy, and effect is lasting, this coating is with the effect of removing formaldehyde simultaneously, and the coating through this brushing method brushing can ensure the realization of this coating beneficial effect further.
The present invention adopts following technical scheme to realize:
A kind of anti-mildew is except the brushing method of methanal paint, this system component proportioning (by weight) is as follows: polystyrene-acrylic copolymer or acrylic copolymer or Vinyl Acetate Copolymer-acrylic copolymer 100 parts, talcum powder 26-30 part, auxiliary agent 5-8 part, pigment 6-10 part, antimildew disinfectant 8-10 part, sorbent material 3-5 part, water 40-50 part, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=(1 ~ 2): 1:0.5, described brushing method comprises the steps:
1) pretreatment procedure, first polishes metope to be brushed with sand paper, then carries out surface dust process;
2) brush priming paint, first the metope conventional base coat after pre-treatment is brushed, polish again after dry 3 hours at 45 ± 2 DEG C;
3) again priming paint is brushed, step 2) metope after process brushes priming paint again, polishes again after dry 3 hours at 45 ± 2 DEG C;
4) above-mentioned coating of the present invention and water are blent according to the ratio of 4-6:1, and the coating diluent that stirs to obtain, then the metope after step 3) process is brushed this coating diluent, polishing after dry 5 hours at 30-35 DEG C;
5) repeating step 4) method brush 1 layer of above-mentioned coating diluent again;
6) brush above-mentioned anti-mildew after step 5) except methanal paint, under room temperature, dry 2-3 days;
7) the above-mentioned anti-mildew of last spraying is except methanal paint; And at room temperature dry 5-7 days.
Wherein said talcum powder granularity is less than 100 microns.
Wherein said auxiliary agent is one or more in dispersion agent, wetting agent, defoamer, thickening material.
Wherein said pigment is ultramarine, titanium dioxide etc.
Described sorbent material is one or more in bamboo charcoal, gac, diatomite, perlite.
The beneficial effect of the coating prepared by the inventive method is:
Nano-TiO
2make organic substance decomposing based on light-catalyzed reaction and there is antibacterial effect, the hole utilizing conductor photocatalysis to produce and be formed at the active oxygen on semiconductor grain surface and bacterial cell or intracellular composition and carry out biochemical reaction, makes Bacteria head unit inactivation and causes necrocytosis.Nano-ZnO is a kind of inorganic antiseptic inherently, when contacting with bacterium, zine ion slow releasing, because zine ion has oxidation-reduction quality, and can with the reactions such as organic carboxyl, hydroxyl, destroy its structure, destroy after entering cell electron transfer system enzyme and with-SH radical reaction, reach sterilization object.After kill bacteria, zine ion can dissociate out from cell, repeats said process.Nano-ZnO, except the anti-microbial effect with traditional Z nO, also has photocatalytic as nano-titanium oxide, under ultraviolet irradiation condition, also can discharge hole and electronics, its Antibacterial Mechanism and TiO
2identical.By by TiO
2be combined with ZnO and can play extraordinary antimycotic antiseptic effect.Applicant finds, the two combine play good antibiotic and sterilizing basis on, then coordinate appropriate ZrO
2use, will improve sterilization antibacterial ability further, experiment shows, by the collocation of three's suitable proportion, as the TiO that the application limits
2: ZnO:ZrO
2=(1 ~ 2): 1:0.5, will than being used alone TiO
2or ZnO sterilization effect promotes more than 50%, than conbined usage TiO
2more than 20% is promoted with the sterilization effect of ZnO.Thus, coating of the present invention can keep sterilization anti-mildew effect for a long time, extends the work-ing life of mildew-resistant anti-mildew paint.Meanwhile, the sorbent material added in coating can by possibility in air to mould various bacterial adsorptions to surface.Therefore the combination of antimildew disinfectant of the present invention and sorbent material effectively can be resisted and be gone mouldy, because the antimildew disinfectant adopted and sorbent material are all inorganic components, therefore anti-mildew effect is lasting.Simultaneously due to sorbent material and nano-TiO
2combination, making this coating with removing the effect of formaldehyde, through measuring and calculating, indoor formaldehyde can be made to reduce by more than 97%.By the coating of brushing the application, move into due to furniture etc. the problem causing indoor formaldehyde concentration to exceed standard in indoor after family or office space finishing can be made and solved.
Brushing method of the present invention adopts conventional priming paint bottoming, and polish under noting be used in absolutely dry condition after bottoming, determined by a large amount of experiments and apply the bottom of coating of the present invention and the drying temperature of surface layer, and adopt the diluent of coating of the present invention as the transition layer of prime coat and surface layer, by applying two transition layers, play good linking effect, bottom of the present invention and transition layer all adopt brushing method, ensure being coated with property and the effect of coating, and it is simple to operate, convenient, last investment precoat adopts spraying, ensure surface layer smooth and beautiful appearance, coating through this method of application brushing does not chap, non-scale, method is simple and easy to implement, and it is both artistic and practical to be coated with brushing effects, and the realization of coating beneficial effect of the present invention can be ensured.
Embodiment
Embodiment one
A kind of anti-mildew is except the brushing method of methanal paint, this system component proportioning (by weight) is as follows: polystyrene-acrylic copolymer 100 parts, be less than the talcum powder 26 parts of 100 microns, wetting agent 8 parts, titanium dioxide 6 parts, antimildew disinfectant 10 parts, bamboo charcoal 3 parts, 40 parts, water, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=1:1:0.5, described brushing method comprises the steps:
1) pretreatment procedure, first polishes metope to be brushed with sand paper, then carries out surface dust process;
2) brush priming paint, first the metope conventional base coat after pre-treatment is brushed, polish again after dry 3 hours at 43 DEG C;
3) again priming paint is brushed, step 2) metope after process brushes priming paint again, polishes again after dry 3 hours at 43 DEG C;
4) above-mentioned coating of the present invention and water are blent according to the ratio of 4:1, and the coating diluent that stirs to obtain, then the metope after step 3) process is brushed this coating diluent, polishing after dry 5 hours at 30 DEG C;
5) repeating step 4) method brush 1 layer of above-mentioned coating diluent again;
6) brush above-mentioned anti-mildew after step 5) except methanal paint, under room temperature, dry 2 days;
7) the above-mentioned anti-mildew of last spraying is except methanal paint; And at room temperature dry 5 days.
After testing: mildew resistance 0 grade, antibiotic rate 98%, formaldehyde removing rate 97%.
Embodiment two
A kind of anti-mildew is except the brushing method of methanal paint, this system component proportioning (by weight) is as follows: acrylic copolymer 100 parts, be less than the talcum powder 30 parts of 100 microns, dispersion agent 3 powder, wetting agent 4 parts, 10 parts, ultramarine, antimildew disinfectant 8 parts, 5 parts, diatomite, 50 parts, water, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=2:1:0.5, described brushing method comprises the steps:
1) pretreatment procedure, first polishes metope to be brushed with sand paper, then carries out surface dust process;
2) brush priming paint, first the metope conventional base coat after pre-treatment is brushed, polish again after dry 3 hours at 47 DEG C;
3) again priming paint is brushed, step 2) metope after process brushes priming paint again, polishes again after dry 3 hours at 47 DEG C;
4) above-mentioned coating of the present invention and water are blent according to the ratio of 6:1, and the coating diluent that stirs to obtain, then the metope after step 3) process is brushed this coating diluent, polishing after dry 5 hours at 35 DEG C;
5) repeating step 4) method brush 1 layer of above-mentioned coating diluent again;
6) brush above-mentioned anti-mildew after step 5) except methanal paint, under room temperature, dry 3 days;
7) the above-mentioned anti-mildew of last spraying is except methanal paint; And at room temperature dry 7 days.
After testing: mildew resistance 0 grade, antibiotic rate 98.5%, formaldehyde removing rate 97.5%.
Embodiment three
A kind of anti-mildew is except the brushing method of methanal paint, this system component proportioning (by weight) is as follows: Vinyl Acetate Copolymer-acrylic copolymer 100 parts, be less than the talcum powder 28 parts of 100 microns, dispersion agent 2 parts, wetting agent 2 parts, defoamer 2 parts, thickening material 2 parts, titanium dioxide 8 parts, antimildew disinfectant 9 parts, gac 2 parts, 1 part, diatomite, perlite 1 part, 45 parts, water, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=1.5:1:0.5, described brushing method comprises the steps:
1) pretreatment procedure, first polishes metope to be brushed with sand paper, then carries out surface dust process;
2) brush priming paint, first the metope conventional base coat after pre-treatment is brushed, polish again after dry 3 hours at 45 DEG C;
3) again priming paint is brushed, step 2) metope after process brushes priming paint again, polishes again after dry 3 hours at 45 DEG C;
4) above-mentioned coating of the present invention and water are blent according to the ratio of 5:1, and the coating diluent that stirs to obtain, then the metope after step 3) process is brushed this coating diluent, polishing after dry 5 hours at 33 DEG C;
5) repeating step 4) method brush 1 layer of above-mentioned coating diluent again;
6) brush above-mentioned anti-mildew after step 5) except methanal paint, under room temperature, dry 3 days;
7) the above-mentioned anti-mildew of last spraying is except methanal paint; And at room temperature dry 7 days.
After testing: mildew resistance 0 grade, antibiotic rate 98.6%, formaldehyde removing rate 97.3%.
Applicant states, the present invention illustrates detailed process equipment and process flow process of the present invention by above-described embodiment, but the present invention is not limited to above-mentioned detailed process equipment and process flow process, namely do not mean that the present invention must rely on above-mentioned detailed process equipment and process flow process and could implement.Person of ordinary skill in the field should understand, any improvement in the present invention, to equivalence replacement and the interpolation of ancillary component, the concrete way choice etc. of each raw material of product of the present invention, all drops within protection scope of the present invention and open scope.
Claims (4)
1. an anti-mildew is except the brushing method of methanal paint, it is characterized in that, this system component proportioning is as follows by weight: polystyrene-acrylic copolymer or Vinyl Acetate Copolymer-acrylic copolymer 100 parts, talcum powder 26-30 part, auxiliary agent 5-8 part, pigment 6-10 part, antimildew disinfectant 8-10 part, sorbent material 3-5 part, water 40-50 part, described antimildew disinfectant is nano-TiO
2, nano-ZnO and ZrO
2mixture, nano-TiO
2, nano-ZnO granularity be 30 ~ 50 nanometers, ZrO
2granularity be-400 orders, the ratio of three is TiO
2: ZnO:ZrO
2=(1 ~ 2): 1:0.5, described brushing method comprises the steps:
1) pretreatment procedure, first polishes metope to be brushed with sand paper, then carries out surface dust process;
2) brush priming paint, first the metope conventional base coat after pre-treatment is brushed, polish again after dry 3 hours at 45 ± 2 DEG C;
3) again priming paint is brushed, step 2) metope after process brushes priming paint again, polishes again after dry 3 hours at 45 ± 2 DEG C;
4) above-mentioned coating of the present invention and water to be blent according to the ratio of 4-6:1, and the coating diluent that stirs to obtain, then by step 3) metope after process brushes this coating diluent, polishing after dry 5 hours at 30-35 DEG C;
5) repeating step 4) method brush 1 layer of above-mentioned coating diluent again;
6) step 5) brush above-mentioned anti-mildew afterwards except methanal paint, dry 2-3 days under room temperature;
7) the above-mentioned anti-mildew of last spraying is except methanal paint; And at room temperature dry 5-7 days.
2. the brushing method of coating as claimed in claim 1, it is characterized in that, wherein said talcum powder granularity is less than 100 microns.
3. the brushing method of coating as claimed in claim 1 or 2, is characterized in that, wherein said auxiliary agent is one or more in dispersion agent, wetting agent, defoamer, thickening material.
4. the brushing method of coating as claimed in claim 1 or 2, is characterized in that, described sorbent material is one or more in bamboo charcoal, gac, diatomite, perlite.