CN103554886A - Modified polycarbonate cup shell material and preparation method thereof - Google Patents
Modified polycarbonate cup shell material and preparation method thereof Download PDFInfo
- Publication number
- CN103554886A CN103554886A CN201310510398.9A CN201310510398A CN103554886A CN 103554886 A CN103554886 A CN 103554886A CN 201310510398 A CN201310510398 A CN 201310510398A CN 103554886 A CN103554886 A CN 103554886A
- Authority
- CN
- China
- Prior art keywords
- parts
- polycarbonate
- zinc oxide
- modified polycarbonate
- screw extruder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified polycarbonate cup shell material which is characterized by being prepared from the following raw materials in parts by weight: 500-520 parts of bisphenol-A aromatic polycarbonate resin, 40-45 parts of poly-4-methylpentene-1, 10-12 parts of octaphenylcyclotetrasiloxane, 8-10 parts of vinyl trialkoxysilane, 4-5 parts of phenyl phosphate, 1-2 parts of morpholine, 3-4 parts of tributyl citrate, 1-2 parts of zinc oxide and 10-12 parts of auxiliaries. The defect that the wear resistance of a polycarbonate material is not good is overcome, and the modified polycarbonate cup shell material disclosed by the invention is better in wear resistance, high in strength and impact strength, wide in using temperature range, good in processing performance, low in forming shrinkage rate, favorable in size stability, tasteless, odorless, harmless to human bodies and conformable to sanitary safety.
Description
Technical field
The present invention relates to plastics field, particularly a kind of modified polycarbonate water tumbler case material and preparation method thereof.
Background technology
Polycarbonate (being called for short PC) is the high molecular polymer that contains carbonate group in molecular chain, due to the singularity on polycarbonate structure, has now become the fastest general engineering plastic of rate of growth in five large-engineering plastics.Due to polycarbonate article, to have quality light, and shock resistance and the transparency are good, and indeformable and keep transparent advantage during by hot water and caustic soln carrying out washing treatment, some field PC bottles replace vial completely.It is predicted, along with people are to the improving constantly of drinking water quality attention degree, polycarbonate consumption rate of growth in this respect will remain on more than 10%, and the water tumbler housing of therefore researching and developing a kind of polycarbonate material is trend of the times.
Summary of the invention
The object of this invention is to provide a kind of modified polycarbonate water tumbler case material and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A water tumbler case material, is made by the raw material of following weight part: bisphenol A-type aromatic polycarbonate resin 500-520, poly--4-methylpentene-1 40-45, octaphenylcyclotetrasiloxane 10-12, vinyl trialkyl oxysilane 8-10, phenyl-phosphite 4-5, morpholine 1-2, tributyl citrate 3-4, zinc oxide 1-2, auxiliary agent 10-12;
Described auxiliary agent is made by the raw material of following weight part: diatomite 40-45, vinylformic acid dimethylamino ethyl ester 4-5, tri (propylene glycol) diacrylate 2-3, zinc oxide 5-6, jade 4-5,3-aminopropyl trimethoxysilane 2-3, linking agent TAC1-2, Zinc Gluconate 1-2, Zinic stearas 1-2, Flos Rosae Rugosae quintessence oil 0.1-0.2; Preparation method puts into diatomite, jade mixing calcining furnace and calcine 3-4 hour at 710-740 ℃, cooling, put into 10-12% hydrochloric acid soln and soak 1-2 hour, filter and take out, with clear water, clean and dry, be ground into 200-400 order powder, mix with other remaining component, grinding distribution is even, obtains.
Modified polycarbonate water tumbler case material of the present invention, by following concrete steps, made:
(1) will gather-4-methylpentene-1 is heated to molten state, adds octaphenylcyclotetrasiloxane, vinyl trialkyl oxysilane, phenyl-phosphite, morpholine, zinc oxide, auxiliary agent, stirs and mediates 15-25 minute, sends into twin screw extruder granulation, obtains A material;
(2) dried polycarbonate is heated to 245-280 ℃, adds other remaining component, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3) after A, B material is mixed, on twin screw extruder, melt extrude granulation, obtain.
The present invention has the following advantages: modified polycarbonate material of the present invention, changed the inadequate shortcoming of polycarbonate material wear resistance, there is good wear resistance, and there is high strength, high impact, use temperature scope is wide, good processability, shaping shrinkage rate is low, dimensional stability is good, the harmless hygienic safety that meets of tasteless odorless.
Embodiment
Below by specific examples, the present invention is described in detail.
A water tumbler case material, by following weight part (kilogram) raw material make: bisphenol A-type aromatic polycarbonate resin 500, poly--4-methylpentene-1 40, octaphenylcyclotetrasiloxane 10, vinyl trialkyl oxysilane 8, phenyl-phosphite 4, morpholine 1, tributyl citrate 3, zinc oxide 1, auxiliary agent 10;
Described auxiliary agent by following weight part (kilogram) raw material make: diatomite 40, vinylformic acid dimethylamino ethyl ester 5, tri (propylene glycol) diacrylate 3, zinc oxide 5, jade 4,3-aminopropyl trimethoxysilane 2, linking agent TAC2, Zinc Gluconate 2, Zinic stearas 2, Flos Rosae Rugosae quintessence oil 0.1; Preparation method puts into diatomite, jade mixing calcining furnace and calcine 3-4 hour at 710-740 ℃, cooling, put into 10-12% hydrochloric acid soln and soak 1-2 hour, filter and take out, with clear water, clean and dry, be ground into 200-400 order powder, mix with other remaining component, grinding distribution is even, obtains.
Modified polycarbonate water tumbler case material of the present invention, by following concrete steps, made:
(1) will gather-4-methylpentene-1 is heated to molten state, adds octaphenylcyclotetrasiloxane, vinyl trialkyl oxysilane, phenyl-phosphite, morpholine, zinc oxide, auxiliary agent, stirs and mediates 15-25 minute, sends into twin screw extruder granulation, obtains A material;
(2) dried polycarbonate is heated to 245-280 ℃, adds other remaining component, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3) after A, B material is mixed, on twin screw extruder, melt extrude granulation, obtain.
Tensile strength of material of the present invention is 50-55MPa, elongation 10-15%, flexural strength 70-80MPA, notched Izod impact strength 370J/M.
Claims (2)
1. a modified polycarbonate water tumbler case material, it is characterized in that, by the raw material of following weight part, made: bisphenol A-type aromatic polycarbonate resin 500-520, poly--4-methylpentene-1 40-45, octaphenylcyclotetrasiloxane 10-12, vinyl trialkyl oxysilane 8-10, phenyl-phosphite 4-5, morpholine 1-2, tributyl citrate 3-4, zinc oxide 1-2, auxiliary agent 10-12;
Described auxiliary agent is made by the raw material of following weight part: diatomite 40-45, vinylformic acid dimethylamino ethyl ester 4-5, tri (propylene glycol) diacrylate 2-3, zinc oxide 5-6, jade 4-5,3-aminopropyl trimethoxysilane 2-3, linking agent TAC1-2, Zinc Gluconate 1-2, Zinic stearas 1-2, Flos Rosae Rugosae quintessence oil 0.1-0.2; Preparation method puts into diatomite, jade mixing calcining furnace and calcine 3-4 hour at 710-740 ℃, cooling, put into 10-12% hydrochloric acid soln and soak 1-2 hour, filter and take out, with clear water, clean and dry, be ground into 200-400 order powder, mix with other remaining component, grinding distribution is even, obtains.
2. modified polycarbonate water tumbler case material according to claim 1, is characterized in that, by following concrete steps, is made:
(1) will gather-4-methylpentene-1 is heated to molten state, adds octaphenylcyclotetrasiloxane, vinyl trialkyl oxysilane, phenyl-phosphite, morpholine, zinc oxide, auxiliary agent, stirs and mediates 15-25 minute, sends into twin screw extruder granulation, obtains A material;
(2) dried polycarbonate is heated to 245-280 ℃, adds other remaining component, stir 7-10 minute, send on twin screw extruder and melt extrude granulation, obtain B material;
(3) after A, B material is mixed, on twin screw extruder, melt extrude granulation, obtain.