CN103553614B - 可低温烧结的微波介电陶瓷La7Nb3Mo4O30及其制备方法 - Google Patents
可低温烧结的微波介电陶瓷La7Nb3Mo4O30及其制备方法 Download PDFInfo
- Publication number
- CN103553614B CN103553614B CN201310478109.1A CN201310478109A CN103553614B CN 103553614 B CN103553614 B CN 103553614B CN 201310478109 A CN201310478109 A CN 201310478109A CN 103553614 B CN103553614 B CN 103553614B
- Authority
- CN
- China
- Prior art keywords
- low temperature
- dielectric ceramic
- hours
- microwave dielectric
- sintered
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种可低温烧结的微波介电陶瓷La7Nb3Mo4O30微波及其制备方法。可低温烧结的微波介电陶瓷的组成为La7Nb3Mo4O30。(1)将纯度为99.9%以上的La2O3、Nb2O5和MoO3的原始粉末按La7Nb3Mo4O30化学式称量配料。(2)将步骤(1)原料混合湿式球磨12小时,溶剂为蒸馏水,烘干后在900℃大气气氛中预烧6小时。(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在950~980℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。本发明制备的陶瓷在950~980℃烧结良好,其介电常数达到21~22,品质因数Qf值高达86000-102000GHz,谐振频率温度系数小,在工业上有着极大的应用价值。
Description
技术领域
本发明涉及介电陶瓷材料,特别是涉及在微波频率使用的介质基板、谐振器和滤波器等微波元器件的微波介电陶瓷材料及其制备方法。
背景技术
微波介电陶瓷是指应用于微波频段(主要是UHF、SHF频段)电路中作为介质材料并完成一种或多种功能的陶瓷,在现代通讯中被广泛用作谐振器、滤波器、介质基片和介质导波回路等元器件,是现代通信技术的关键基础材料,已在便携式移动电话、汽车电话、无绳电话、电视卫星接受器和军事雷达等方面有着十分重要的应用,在现代通讯工具的小型化、集成化过程中正发挥着越来越大的作用。
应用于微波频段的介电陶瓷,应满足如下介电特性的要求:(1)系列化介电常数εr以适应不同频率及不同应用场合的要求;(2)高的品质因数Q值或介质损耗tanδ以降低噪音,一般要求Qf≥3000 GHz;(3) 谐振频率的温度系数τƒ尽可能小以保证器件具有好的热稳定性,一般要求-10/℃≤τƒ≤+10 ppm/℃。国际上从20世纪30年代末就有人尝试将电介质材料应用于微波技术。
根据相对介电常数εr的大小与使用频段的不同,通常可将已被开发和正在开发的微波介电陶瓷分为4类。
(1)超低介电常数微波介电陶瓷,主要代表是Al2O3-TiO2、Y2BaCuO5、MgAl2O4和Mg2SiO4等,其εr≤20,品质因数Q×f≥50000GHz,τƒ≤10 ppm/°C。主要用于微波基板以及高端微波元器件。
(2)低εr和高Q值的微波介电陶瓷,主要是BaO-MgO-Ta2O5,
BaO-ZnO-Ta2O5或BaO-MgO-Nb2O5,
BaO-ZnO-Nb2O5系统或它们之间的复合系统MWDC材料。其εr=25~30, Q=(1~2)×104(在f≥10 GHz下), τƒ≈0。主要应用于f≥8 GHz的卫星直播等微波通信机中作为介质谐振器件。
(3)中等εr和Q值的微波介电陶瓷,主要是以BaTi4O9、Ba2Ti9O20和(Zr、Sn)TiO4等为基的MWDC材料,其εr=35~40,Q=(6~9)×103(在f=3~-4GHz下),τƒ≤5 ppm/°C。主要用于4~8 GHz 频率范围内的微波军用雷达及通信系统中作为介质谐振器件。
(4)高εr而Q值较低的微波介电陶瓷,主要用于0.8~4GHz 频率范围内民用移动通讯系统,这也是微波介电陶瓷研究的重点。80年代以来,Kolar、Kato等人相继发现并研究了类钙钛矿钨青铜型BaO—Ln2O3—TiO2系列(Ln=La、 Sm、 Nd或Pr等,简称BLT系)、复合钙钛矿结构CaO—Li2O—Ln2O3—TiO2系列、铅基系列材料、Ca1-xLn2x/3TiO3系等高εr微波介电陶瓷,其中BLT体系的BaO—Nd2O3—TiO2材料介电常数达到90,铅基系列 (Pb,Ca)ZrO3介电常数达到105。
以上这些材料体系的烧结温度一般高于1300°C,不能直接与Ag和Cu 等低熔点金属共烧形成多层陶瓷电容器。近年来,随着低温共烧陶瓷技术(Low
Temperature Co-fired Ceramics, LTCC)的发展和微波多层器件发展的要求,国内外的研究人员对一些低烧体系材料进行了广泛的探索和研究,主要是采用微晶玻璃或玻璃-陶瓷复合材料体系,因低熔点玻璃相具有相对较高的介质损耗,玻璃相的存在大大提高了材料的介质损耗。目前可低烧的高性能微波介质陶瓷体系仍然非常有限,这在很大程度上限制了低温共烧技术及微波多层器件的发展。
发明内容
本发明的目的是提供一种具有低损耗与良好的热稳定性,烧结温度低,可以与Ag低温共烧的微波介电陶瓷及其制备方法。
本发明涉及的可低温烧结的微波介电陶瓷的化学组成为:La7Nb3Mo4O30。
所述可低温烧结的微波介电陶瓷的制备方法具体步骤为:
(1)将纯度为99.9%以上的La2O3、Nb2O5和MoO3的原始粉末按La7Nb3Mo4O30化学式称量配料。
(2)将步骤(1)原料混合湿式球磨12小时,溶剂为蒸馏水,烘干后在900℃大气气氛中预烧6小时。
(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在950~980℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。
本发明制备的陶瓷在950-980℃烧结良好,其介电常数达到21~22,品质因数Qf值高达86000-102000GHz,谐振频率温度系数小,可以与Ag电极低温共烧,在工业上有着极大的应用价值。
具体实施方式
实施例:
表1示出了构成本发明的不同烧结温度的4个具体实施例及其微波介电性能。其制备方法如上所述,用圆柱介质谐振器法进行微波介电性能的评价。本发明决不限于以上实施例。烧结温度的上下限、区间取值都能实现本发明,在此不一一列举实施例。
本陶瓷可广泛用于各种介质基板、谐振器和滤波器等微波器件的制造,可满足移动通信、卫星通信等系统的技术需要。
表1:
Claims (1)
1.一种可低温烧结的微波介电陶瓷,其特征在于所述可低温烧结的微波介电陶瓷的化学组成式为:La7Nb3Mo4O30;
所述可低温烧结的微波介电陶瓷的制备方法具体步骤为:
(1)将纯度为99.9%以上的La2O3、Nb2O5和MoO3的原始粉末按La7Nb3Mo4O30化学式称量配料;
(2)将步骤(1)原料混合湿式球磨12小时,溶剂为蒸馏水,烘干后在900℃大气气氛中预烧6小时;
(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在950~980℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。