CN103553536A - Preparation method of ceramic simulating coating - Google Patents
Preparation method of ceramic simulating coating Download PDFInfo
- Publication number
- CN103553536A CN103553536A CN201310460288.6A CN201310460288A CN103553536A CN 103553536 A CN103553536 A CN 103553536A CN 201310460288 A CN201310460288 A CN 201310460288A CN 103553536 A CN103553536 A CN 103553536A
- Authority
- CN
- China
- Prior art keywords
- porcelain
- compound method
- preparation
- imitated coating
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a ceramic simulating coating, and the preparation method comprises the following steps: (1) preparing raw materials; (2) preparing a film-forming base material; (3) taking an agent for adding; (4) adding a modified PVA (Polyvinyl Acetate) adhesive; and (5) testing and packaging. The preparation method of the ceramic simulating coating is simple in process, conventional preparation equipment is used for completing the production, the prepared ceramic simulating coating has not only the same characteristics of scrub resistant ceramic simulating coating products, also has fouling resistance and other technical performances, can clean ink and tea stains, and has good development prospects.
Description
Technical field
The present invention relates to a kind of compound method of porcelain-imitated coating.
Background technology
Porcelain-imitated coating not only uses in house ornamentation and wall skill, and also can play good effect in artwork, and the imitative porcelain effect of product with this paint spay-coating, can arrive degree true to nature.
The porcelain-imitated coating that development in recent years is got up has overcome traditional interior wall coating and has easily peeled, play powder, the defect such as moisture-proof wiping not, as a Chinese patent application < < steel ceramics-like coating > > (publication number CN10290460A) discloses the main components by weight percent of this steel ceramics-like coating: methylcellulose gum 6～10, polyvinyl acetate emulsion 50～80, calcium hydroxide powder 250～320, calcite in powder 250～320, pigment 1～3, defoamer 0.05～0.5, surplus is water, this porcelain-imitated coating water-proof, coating is crackle not, water-proof performance reaches national exterior coating standard.And for example the preparation method > > (publication No. CN102391731A) of Chinese patent < < rare earth anti-bacteria tilelike coating discloses a kind of rare earth anti-bacteria tilelike coating, it take Rare Earth Lanthanum element and the nano zine oxide self with anti-microbial property is main raw material, selecting the polystyrene that adhesive property is good and cheap is binding agent, has added the fillers such as the multiple auxiliary agent such as thickening material, dispersion agent, defoamer and water-ground limestone and has made porcelain-imitated coating; Antibiotic paint prepared by the method belongs to water-borne coatings, and antibiotic, imitative porcelain performance is high, but Rare Earth Lanthanum element is expensive, and production cost is high.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of compound method of giving birth to technique porcelain-imitated coating simple, with low cost.
For solving the problems of the technologies described above, a kind of compound method of porcelain-imitated coating, comprises the steps:
(1) raw material is prepared: each component takes by following weight percent:
(2) film forming base-material preparation: by the above-mentioned silicon sol taking, benzene emulsion, wollastonite powder and water-proofing powder, add water under whipped state, then be ground to fineness and be less than 20 microns;
(3) getting agent adds: above-mentioned each analog assistant and the organobentonite taking added, stir;
(4) add again modified PVA glue, add suitable quantity of water, stir;
(5) check, packing.
As improvement of the present invention, above-mentioned dispersion agent is Sodium hexametaphosphate 99.
Further, above-mentioned thickening material is Natvosol.
Above-mentioned film coalescence aid is Texanol ester alcohol.
Other above-mentioned auxiliary agents comprise mould inhibitor and hydrophober.
Compared with prior art, beneficial effect of the present invention is:
The compound method technique of porcelain-imitated coating of the present invention is simple, normal compound equipment can complete production, the imitative porcelain of preparation not only has the same products characteristics of ceramic simulating coating, simultaneously, also there is the technical features such as stain resistant, ink capable of washing, tea stain, be different from the products such as porcelain-imitated coating in the market especially, has good development prospect.
Embodiment
For ease of understanding the present invention, it is as follows that the present invention enumerates embodiment.Those skilled in the art should understand, described embodiment only, for helping to understand the present invention, should not be considered as concrete restriction of the present invention.
As no specific instructions, various raw material of the present invention all can obtain by commercially available; Or prepare according to the ordinary method of this area.Unless otherwise defined or described herein, all specialties used herein and scientific words and the art technology same meaning that skillfully person of entering is familiar.In addition any method similar or impartial to described content and material all can be applicable in the inventive method.
Unless otherwise indicated, the familiar same meaning of all specialties used herein and scientific words and those skilled in the art.In addition any method similar or impartial to described content and material all can be applicable in the inventive method.
Embodiment 1
A compound method for porcelain-imitated coating, comprises the steps:
(1) raw material is prepared: each component takes by following weight percent:
(2) film forming base-material preparation: by the above-mentioned silicon sol taking, benzene emulsion, wollastonite powder and water-proofing powder, add water under whipped state, then be ground to fineness and be less than 20 microns;
(3) getting agent adds: above-mentioned each analog assistant and the organobentonite taking added, stir;
(4) add again modified PVA glue, add suitable quantity of water, stir;
(5) check, packing.
Its product technology performance sees the following form:
Embodiment 2
A compound method for porcelain-imitated coating, comprises the steps:
(1) raw material is prepared: each component takes by following weight percent:
(2) film forming base-material preparation: by the above-mentioned silicon sol taking, benzene emulsion, wollastonite powder and water-proofing powder, add water under whipped state, then be ground to fineness and be less than 20 microns;
(3) getting agent adds: above-mentioned each analog assistant and the organobentonite taking added, stir;
(4) add again modified PVA glue, add suitable quantity of water, stir;
(5) check, packing.
Embodiment 3
A compound method for porcelain-imitated coating, comprises the steps:
(1) raw material is prepared: each component takes by following weight percent:
(2) film forming base-material preparation: by the above-mentioned silicon sol taking, benzene emulsion, wollastonite powder and water-proofing powder, add water under whipped state, then be ground to fineness and be less than 20 microns;
(3) getting agent adds: above-mentioned each analog assistant and the organobentonite taking added, stir;
(4) add again modified PVA glue, add suitable quantity of water, stir;
(5) check, packing.
Applicant's statement, person of ordinary skill in the field is on the basis of above-described embodiment, by the concrete content point value of above-described embodiment component, combined with the technical scheme of summary of the invention part, thereby the new numerical range producing, also be one of record scope of the present invention, the application, for making specification sheets simple and clear, is no longer enumerated these numerical ranges.
Claims (5)
1. a compound method for porcelain-imitated coating, is characterized in that, comprises the steps:
(1) raw material is prepared: each component takes by following weight percent:
(2) film forming base-material preparation: by the above-mentioned silicon sol taking, benzene emulsion, wollastonite powder and water-proofing powder, add water under whipped state, then be ground to fineness and be less than 10～30 microns;
(3) getting agent adds: above-mentioned each analog assistant and the organobentonite taking added, stir;
(4) add again modified PVA glue, add suitable quantity of water, stir;
(5) check, packing.
2. the compound method of a kind of porcelain-imitated coating according to claim 1, is characterized in that: described dispersion agent is Sodium hexametaphosphate 99.
3. the compound method of a kind of porcelain-imitated coating according to claim 1, is characterized in that: described thickening material is Natvosol.
4. the compound method of a kind of porcelain-imitated coating according to claim 1, is characterized in that: described film coalescence aid is Texanol ester alcohol.
5. the compound method of a kind of porcelain-imitated coating according to claim 1, is characterized in that: other described auxiliary agents comprise mould inhibitor and hydrophober.