A kind of compound method with the health environment-friendly kieselguhr wall material powder of temperature adjustment function
Technical field
The present invention relates to indoor decorating coating or coated material technical field, specifically, is a kind of compound method with the health environment-friendly kieselguhr wall material powder of temperature adjustment function.
Background technology
Kieselguhr wall material has been widely used in indoor wall finishing because of its health environment-friendly characteristic and good visual effect or has decorated.But existing kieselguhr wall material only has the function of the gaseous organic pollutants such as damping, absorption and removing indoor formaldehyde, toluene, does not regulate the function of room temp.Suitable room temp guarantees one of human comfort degree and healthy important factor, guarantee at present the main method of indoor comfortable temperature be summer air conditioner refrigerating, heating in winter heats up, need to consume a large amount of energy.
Summary of the invention
The object of this invention is to provide a kind of compound method with the health environment-friendly kieselguhr wall material of temperature adjustment function.
The health environment-friendly kieselguhr wall material powder with temperature adjustment function of the present invention is realized by following technique means.
There is a health environment-friendly kieselguhr wall material powder for temperature adjustment function, formed by following component proportion according to weight percentage: diatomite/organic phase change energy storage composite material 35% ~ 50%, 200 ~ 800 order opoka powder 15% ~ 25%, 600 ~ 1250 order calcined kaolin 10% ~ 20%, 200 ~ 400 order calcined dolomite powder 5%, white cement 5%, 40 ~ 200 order silica powder 10%, super-cell loaded with nano TiO
2wollastonite mineral fiber 2% ~ 4%, superfine latex powder 0.5% ~ 1.0%, ether of cellulose 0.3% that matrix material 0.5% ~ 1.5%, length-to-diameter ratio>=15 and median size are less than 15 μm; Above-mentioned each composition weight sum is 100%.
The composite powder material that described diatomite/organic phase change energy storage composite material is a kind of modification infusorial earth is carrier, load organic phases becomes material, its transformation temperature 20 ~ 28 DEG C, latent heat of phase change >=75J/g.The preparation method of this phase change composite material is open by invention patent mandate notification number CN 102199416 B.
Described opoka powder is a kind of main component is unformed SiO
2, natural porous silicoide powder that porosity is larger, its pore size distribution range be zero point several nanometer to tens nanometers (mean pore size is 3 ~ 5nm about), there is the comparatively large (60 ~ 100m of specific surface area
2/ more than g is diatomaceous about 3 times), the characteristics such as absorption property is strong, stable chemical nature, not only have good moisture absorption and moisture releasing (i.e. damping) function, and PARA FORMALDEHYDE PRILLS(91,95) gas have good absorption capturing ability.Opoka ore deposit is at Nen River Region, China northeast rich reserves, and easily exploitation and processing, have the advantages such as cost is lower.
Described calcined kaolin is the inorganic non-metallic powder body material of natural kaolin ore deposit after fine grinding and less than 1000 DEG C calcination process, and main component is pure aluminium silicate.The water of constitution of contained by kaolin is stripped of wherein after calcining about 15% and organic matter, leave a large amount of hole, specific surface area reaches 5m
2/ more than g, have good damping and adsorption function, and whiteness is up to more than 90%, good weatherability.
The product of described light dolomite powder to be a kind of with dolomite mineral be fine grinding after raw material calcines under about 900 DEG C, main component is MgO and CaO, belongs to inorganic coagulation material, can slowly carbonatization under the effect of moisture in atmosphere.
Described super-cell loaded with nano TiO
2matrix material is a kind of take super-cell as the loaded nano TiO of carrier
2composite photocatalyst material, its preparation method is open by invention patent mandate notification number CN102039118 B.Super-cell loaded with nano TiO
2photocatalyst material all has excellent photocatalysis performance under UV-light and visible ray, under fluorescent lamp, and degraded clearance>=80% of PARA FORMALDEHYDE PRILLS(91,95) in 48 hours.
The natural mineral fiber of described wollastonite mineral fiber to be main chemical compositions be Calucium Silicate powder, this natural mineral fiber can not only increase the intensity of wall material, and can also produce good vision (tiffany) effect.
The above-mentioned compound method with the health environment-friendly kieselguhr wall material powder of temperature adjustment function, comprises the steps: to take raw material with meter electronics, joins in stirring mixer in proportion and stir, namely obtain kieselguhr wall material powder of the present invention.
The paste slurry obtained after the kieselguhr wall material powder obtained after above-mentioned each component being stirred and clear water are uniformly mixed according to the weight ratio of 1:0.9 ~ 1.5 is the health environment-friendly kieselguhr wall material with temperature adjustment function.This wall material is used for decorate indoor wall, and can adopt form construction of plastering, the diatom ooze wall material use quantity of every square metre of wall is 1.5 ~ 2.5kg, scrapes the decorated wall surface that can form thickness 2 ~ 4mm after smearing 2 ~ 4 times on wall.
Temperature adjustment function health environment-friendly kieselguhr wall material powder of the present invention there is the diatomite phase change composite material of accumulation of energy function and specific surface area is large and pore size distribution$ is suitable opoka for main ingredient, and by interpolation super-cell loaded with nano TiO
2matrix material, makes it not only have the function of damping and air pollutant such as degraded removal indoor formaldehyde, toluene etc., and has the function regulating room temp.This wall material powder is used for fitting up indoor wall, office can be saved winter and live room heating energy consumption; Can save the power consumption of air conditioner refrigerating summer, be a kind ofly collect damping, the multi-functional interior walls material of environmental protection and temperature adjustment function or coating.
Embodiment
Be below embodiments of the invention.The product that super-cell load sensitive control matrix material wherein adopts health care nanometer matrix material Science and Technology Ltd. of Linjiang City of Jilin Province to produce.
Embodiment 1:
Diatomite/organic phase change energy storage composite material 36kg
325 order opoka powder 24kg
1250 order calcined kaolin 15kg
240 order calcined dolomite powder 5kg
40 ~ 200 order silica powder 10kg
White cement 5kg
Super-cell loaded with nano TiO
2matrix material 0.5kg
The wollastonite mineral fiber 3.5kg that length-to-diameter ratio >=15 and median size are less than 15 μm
Superfine latex powder 0.7kg
Ether of cellulose 0.3kg.
Embodiment 2:
Diatomite/organic phase change energy storage composite material 40kg
500 order opoka powder 20kg
800 order calcined kaolin 15kg
325 order calcined dolomite powder 5kg
40 ~ 200 order silica powder 10kg
White cement 5kg
Super-cell loaded with nano TiO
2matrix material 0.7kg
The wollastonite mineral fiber 3.2kg that length-to-diameter ratio >=15 and median size are less than 15 μm
Superfine latex powder 0.8kg
Ether of cellulose 0.3kg.
Embodiment 3:
Diatomite/organic phase change energy storage composite material 43kg
600 order opoka powder 15kg
1000 order calcined kaolin 17kg
200 order calcined dolomite powder 5kg
40 ~ 200 order silica powder 10kg
White cement 5kg
Super-cell loaded with nano TiO
2matrix material 1.0kg
The wollastonite mineral fiber 2.8kg that length-to-diameter ratio >=15 and median size are less than 15 μm
Superfine latex powder 0.9kg
Ether of cellulose 0.3kg.
Embodiment 4:
Diatomite/organic phase change energy storage composite material 47kg
800 order opoka powder 15kg
600 order calcined kaolin 13kg
280 order calcined dolomite powder 5kg
40 ~ 200 order silica powder 10kg
White cement 5kg
Super-cell loaded with nano TiO
2matrix material 1.2kg
The wollastonite mineral fiber 2.9kg that length-to-diameter ratio >=15 and median size are less than 15 μm
Superfine latex powder 0.6kg
Ether of cellulose 0.3kg.
Constituent materials in above-mentioned four embodiments added in dry powder stirring mixer and stirs, after the assay was approved, adopt weather-proof dressing, packedly can to dispatch from the factory.