CN103549917A - Method for preparing wet tissue with defogging function - Google Patents
Method for preparing wet tissue with defogging function Download PDFInfo
- Publication number
- CN103549917A CN103549917A CN201310516861.0A CN201310516861A CN103549917A CN 103549917 A CN103549917 A CN 103549917A CN 201310516861 A CN201310516861 A CN 201310516861A CN 103549917 A CN103549917 A CN 103549917A
- Authority
- CN
- China
- Prior art keywords
- sodium phosphate
- polyethylene glycol
- wet tissue
- stir
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for preparing a smearing preparation wet tissue for decreasing smooth adhesion of water fogs, in particular to a method for preparing a wet tissue with a defogging function. Preferably, the wet tissue comprises, in weight percent, 8% of sodium phosphate, 6% of sodium tripolyphosphate, 2% of ethylene copolymer, 2% of polyethylene glycol, 2% of propylene glycol, 3% of fatty acid amide, 1.5% of nano-scale titanium dioxide and deionized water, the sodium phosphate and the sodium tripolyphosphate are used as dispersing agents, the fatty acid amide is used as an emulsifying agent, the wet tissue has fine hydrophilicity and the anti-fogging function by the aid of the polyethylene glycol and the propylene glycol, anti-fogging time can be prolonged and anti-fogging effect can be improved as the nano-scale titanium dioxide with a hydrophilic performance is added, and substances harmful to human bodies are not added so that the human bodies cannot be harmed.
Description
Technical field
The present invention relates to a kind of preparation method of wet tissue, specifically relate to a kind of preparation method with defrosting function wet tissue, it belongs to wet tissue field.
Background technology
As everyone knows, the effect in cold season due to temperature and humidity, fumulus can be coverd with in the surface of glass, as the glass pane in house, vehicle glass, the glasses that people wear in addition etc., these make troubles to people's life and safety, even endanger people's life security.For fear of such problem, people have carried out a large amount of research.But, generally adopt directly at method of smearing antifoggant on glass, its complicated operation.
Summary of the invention
In view of the problem that prior art exists, the object of the invention is to provide a kind of preparation method of glass antidimmer wet tissue easy to use, safe.
To achieve these goals, the technical solution adopted in the present invention is a kind of preparation method of glass antidimmer wet tissue, and its raw material comprises: cotton spun laced fabric and mixed liquor; The weight fraction of described its each material of raw material: sodium phosphate 7 ~ 10, sodium phosphate trimer 7 ~ 10, copolymerization of ethylene 1 ~ 3, polyethylene glycol 1 ~ 3, propane diols 1 ~ 3%, fatty acid amine 2 ~ 5, Nano titanium dioxide 1 ~ 2 and surplus deionized water; Its step is as follows:
1) deionized water is added in stirred tank, adding sodium phosphate to stir 10 ~ 15 minutes, add sodium phosphate trimer to stir, be stirred to dissolve complete;
2) in reactor, add fatty acid amine and Nano titanium dioxide, stir 30 minutes, standing 1 ~ 2 hour, stirring 30 minutes;
3) in reactor, add copolymerization of ethylene, stir, standing 1 ~ 2 hour;
4) in reactor, add polyethylene glycol, be stirred to polyethylene glycol and fully mix with the solution in reactor;
5) finally add propane diols, stir latter standing 3 ~ 5 hours, make mixed liquor;
6) will after the sterilizing of cotton spun laced fabric, sterilization, be immersed in mixed liquor 6 ~ 10 hours, sealed, sterile packing makes glass antidimmer wet tissue.
The percentage by weight of described each material is preferably: sodium phosphate 8%, sodium phosphate trimer 6%, copolymerization of ethylene 2%, polyethylene glycol 2%, propane diols 2%, fatty acid amine 3%, Nano titanium dioxide 1.5% and deionized water.
The weight ratio of described sodium phosphate and sodium phosphate trimer is 1:1.
The weight ratio of described copolymerization of ethylene, polyethylene glycol and propane diols is 1:1:1.
The invention has the advantages that: with cotton spun laced fabric, make base-material cloth and can not produce paper scrap, and to invade bubble be dispersant adopting sodium phosphate and sodium phosphate trimer, fatty acid amine is emulsifying agent, and be equipped with in the mixed liquor that polyethylene glycol and propane diols make, make wet tissue there is good hydrophily and anti-fog function, can extend the antifog time, improve anti-fog effect; And easy to use, to human body without any harm.
The specific embodiment
A preparation method for glass antidimmer wet tissue, its raw material comprises: cotton spun laced fabric and mixed liquor; The weight fraction of described its each material of raw material: sodium phosphate 7 ~ 10, sodium phosphate trimer 7 ~ 10, copolymerization of ethylene 1 ~ 3, polyethylene glycol 1 ~ 3, propane diols 1 ~ 3%, fatty acid amine 2 ~ 5, Nano titanium dioxide 1 ~ 2 and surplus deionized water; Its step is as follows:
1) deionized water is added in stirred tank, adding sodium phosphate to stir 10 ~ 15 minutes, add sodium phosphate trimer to stir, be stirred to dissolve complete;
2) in reactor, add fatty acid amine and Nano titanium dioxide, stir 30 minutes, standing 1 ~ 2 hour, stirring 30 minutes;
3) in reactor, add copolymerization of ethylene, stir, standing 1 ~ 2 hour;
4) in reactor, add polyethylene glycol, be stirred to polyethylene glycol and fully mix with the solution in reactor;
5) finally add propane diols, stir latter standing 3 ~ 5 hours, make mixed liquor;
6) will after the sterilizing of cotton spun laced fabric, sterilization, be immersed in mixed liquor 6 ~ 10 hours, sealed, sterile packing makes glass antidimmer wet tissue.
The percentage by weight of described each material is preferably: sodium phosphate 8%, sodium phosphate trimer 6%, copolymerization of ethylene 2%, polyethylene glycol 2%, propane diols 2%, fatty acid amine 3%, Nano titanium dioxide 1.5% and deionized water.
The weight ratio of described sodium phosphate and sodium phosphate trimer is 1:1.
The weight ratio of described copolymerization of ethylene, polyethylene glycol and propane diols is 1:1:1.
Claims (4)
1. a preparation method for glass antidimmer wet tissue, its raw material comprises: cotton spun laced fabric and mixed liquor; The weight fraction of described its each material of raw material: sodium phosphate 7 ~ 10, sodium phosphate trimer 7 ~ 10, copolymerization of ethylene 1 ~ 3, polyethylene glycol 1 ~ 3, propane diols 1 ~ 3%, fatty acid amine 2 ~ 5, Nano titanium dioxide 1 ~ 2 and surplus deionized water; Its step is as follows:
1) deionized water is added in stirred tank, adding sodium phosphate to stir 10 ~ 15 minutes, add sodium phosphate trimer to stir, be stirred to dissolve complete;
2) in reactor, add fatty acid amine and Nano titanium dioxide, stir 30 minutes, standing 1 ~ 2 hour, stirring 30 minutes;
3) in reactor, add copolymerization of ethylene, stir, standing 1 ~ 2 hour;
4) in reactor, add polyethylene glycol, be stirred to polyethylene glycol and fully mix with the solution in reactor;
5) finally add propane diols, stir latter standing 3 ~ 5 hours, make mixed liquor;
6) will after the sterilizing of cotton spun laced fabric, sterilization, be immersed in mixed liquor 6 ~ 10 hours, sealed, sterile packing makes glass antidimmer wet tissue.
2. a kind of fog remover according to claim 1, is characterized in that: the percentage by weight of described each material is: sodium phosphate 8%, sodium phosphate trimer 6%, copolymerization of ethylene 2%, polyethylene glycol 2%, propane diols 2%, fatty acid amine 3%, Nano titanium dioxide 1.5% and deionized water.
3. a kind of fog remover according to claim 1, is characterized in that: the weight ratio of described sodium phosphate and sodium phosphate trimer is 1:1.
4. a kind of fog remover according to claim 1, is characterized in that: the weight ratio of described copolymerization of ethylene, polyethylene glycol and propane diols is 1:1:1.