CN103525294A - Rusted antirust paint and preparation method thereof - Google Patents
Rusted antirust paint and preparation method thereof Download PDFInfo
- Publication number
- CN103525294A CN103525294A CN201310449014.7A CN201310449014A CN103525294A CN 103525294 A CN103525294 A CN 103525294A CN 201310449014 A CN201310449014 A CN 201310449014A CN 103525294 A CN103525294 A CN 103525294A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- ethyl acetate
- preparation
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rusted antirust paint which is prepared by components of raw materials in parts by weight as follows: 6-9 parts of calcium ferrite, 5-6 parts of zinc phosphate, 8-10 parts of zinc oxide, 32-35 part of unsaturated polyesterimide resin, 12-14 parts of bismaleimide resin, 1-2 parts of tert-butyl peroxybenzoate, 6-9 parts of butadiene, 4-5 parts of polypropylene glycol acrylate, 4-5 parts of amino resin, 10-15 parts of ethyl acetate, 1-2 parts of vermiculite powder, 3-4 parts of sodium carbonate and 4-5 parts of film-forming resin. The rusted antirust paint has the capacity of resisting ultraviolet rays and can delay aging of a paint film; and the paint film has the characteristics of good corrosion resistance, durability, acid proofing, alkali resistance, salt tolerance, water proofing, excellent adhesive force, impact resistance, bend resistance, long corrosion-resistant age limit and the like.
Description
Technical field
The present invention relates to rust-inhibiting paint field, specifically a kind of band rust anticorrosive paint and preparation method thereof.
Background technology
According to statistics, the direct economic loss that China causes due to metallic corrosion every year accounts for 4% of gross national product.Therefore the Anticorrosion Problems of metal more and more causes people's concern.In anticorrosive metal application techniques before, before japanning, pretreatment of metal surface accounts for 45% left and right of whole coating project total price.If can reduce or save rust cleaning, oil removing, the surface treatment procedure such as dewater, can significantly lower painting cost, also can greatly simplify enamelling process simultaneously, thereby reduce labor intensity and reduce the harm of rust dirt to human body.Develop not only environmental protection but also convenient use, the paint of superior performance becomes exigence.
Summary of the invention
The invention provides a kind of band rust anticorrosive paint and preparation method thereof, paint film has good mechanical stability, snappiness and surface hardness, good weatherability.
Technical scheme of the present invention is:
A kind of band rust anticorrosive paint, it is characterized in that, by the raw material preparation of following weight part, obtained: calcium ferrite 6-9, zinc phosphate 5-6, zinc oxide 8-10, unsaturated polyester-imide resin 32-35, bimaleimide resin 12-14, peroxidized t-butyl perbenzoate 1-2, divinyl 6-9, polypropylene glycol acrylate 4-5, aminoresin 4-5, ethyl acetate 10-15, vermiculite power 1-2, sodium carbonate 3-4, film-forming resin 4-5.
The preparation method of described band rust anticorrosive paint, is characterized in that, comprises the following steps:
(1), successively ethyl acetate, divinyl, polypropylene glycol acrylate, unsaturated polyester-imide resin, bimaleimide resin are added to reactor stirring reaction 10-15 minute, reheat to 65-75 ℃, under whipped state, add peroxidized t-butyl perbenzoate, aminoresin, stirring reaction 30-40 minute again under 800-1000 rev/min;
(2), reactor material is put into Scattered Kettle, add the rest materials in formula simultaneously, stir, disperse in Scattered Kettle, the mass transport after dispersion is carried out wet type sand milling, dispersion in sand mill;
(3), scattered mass transport is filtered and screened in vibrating filter, require the fineness of materials≤60um after filtering, the product after filtering is packed, warehouse-in.
Described band rust anticorrosive paint, is characterized in that: described film-forming resin is obtained by the raw material preparation of following weight part:
Alcohol ester 12 12-14, calcium stearate 1-2, Iron-ore Slag powder 1-2, nano silicon 1-2, dimethyl silicone oil 4-5, Vulcanization accelerator TMTD 1-2, aluminium hydroxide 8-10, ethyl acetate 18-21, Union carbide A-162 2-3;
Preparation method adds calcium stearate, Iron-ore Slag powder, nano silicon in ethyl acetate, grinding distribution, then, add again aluminium hydroxide, Union carbide A-162, be warming up to 50-55 ℃, stirring reaction 30-45 minute, then add other remaining component, continue to stir 45-60 minute, obtain.
Band rust anticorrosive paint of the present invention has the ultraviolet ability of opposing, can delay the aging of paint film.Paint film has good preservative property, weather resistance, can be acidproof, alkaline-resisting, salt tolerant, water-fast corrosion, and sticking power, resistance to impulse force, the excellent performance such as counter-bending, the features such as anticorrosion year limit for length.
Embodiment
Rust an anticorrosive paint, by following weight (kilogram) feed composition make:
Calcium ferrite 7, zinc phosphate 5, zinc oxide 9, unsaturated polyester-imide resin 33, bimaleimide resin 14, peroxidized t-butyl perbenzoate 1, divinyl 7, polypropylene glycol acrylate 5, aminoresin 4, ethyl acetate 13, vermiculite power 2, sodium carbonate 3, film-forming resin 5.
Preparation method, comprises the following steps:
(1), successively ethyl acetate, divinyl, polypropylene glycol acrylate, unsaturated polyester-imide resin, bimaleimide resin are added to reactor stirring reaction 15 minutes, reheat to 70 ℃, under whipped state, add peroxidized t-butyl perbenzoate, aminoresin, stirring reaction 35 minutes again under 1000 revs/min;
(2), reactor material is put into Scattered Kettle, add the rest materials in formula simultaneously, stir, disperse in Scattered Kettle, the mass transport after dispersion is carried out wet type sand milling, dispersion in sand mill;
(3), scattered mass transport is filtered and screened in vibrating filter, require the fineness of materials≤60um after filtering, the product after filtering is packed, warehouse-in.
Wherein, film-forming resin is obtained by the raw material preparation of following weight (kg):
Alcohol ester 12, calcium stearate 2, Iron-ore Slag powder 1, nano silicon 1, dimethyl silicone oil 4, Vulcanization accelerator TMTD 2, aluminium hydroxide 9, ethyl acetate 19, Union carbide A-162 3;
Preparation method adds calcium stearate, Iron-ore Slag powder, nano silicon in ethyl acetate, grinding distribution, then, add again aluminium hydroxide, Union carbide A-162, be warming up to 51 ℃, stirring reaction 32 minutes, add again other remaining component, continue to stir 46 minutes, obtain.
Band rust anticorrosive paint performance index of the present invention:
1, time of drying (25 ℃): surface drying 23min, does solid work 33h
2, snappiness mm≤2
3, hardness >=3H
4, high temperature resistant (130 ℃) >=540h
5, shock-resistance 55
6, salt spray resistance (120h level) >=3
7, water tolerance (29 ± 1 ℃ of 240h): non-foaming, do not come off
8, oil resistant (90# gasoline, 56h): non-foaming, do not come off
9, alkali resistance (GB/T9755-2001): by 48 hours
10, artificial weathering ageing resistance (GB/T9755-2001): by 1200 hours.
Claims (3)
1. be with rust anticorrosive paint for one kind, it is characterized in that, by the raw material preparation of following weight part, obtained: calcium ferrite 6-9, zinc phosphate 5-6, zinc oxide 8-10, unsaturated polyester-imide resin 32-35, bimaleimide resin 12-14, peroxidized t-butyl perbenzoate 1-2, divinyl 6-9, polypropylene glycol acrylate 4-5, aminoresin 4-5, ethyl acetate 10-15, vermiculite power 1-2, sodium carbonate 3-4, film-forming resin 4-5.
2. the preparation method of band rust anticorrosive paint according to claim 1, is characterized in that, comprises the following steps:
(1), successively ethyl acetate, divinyl, polypropylene glycol acrylate, unsaturated polyester-imide resin, bimaleimide resin are added to reactor stirring reaction 10-15 minute, reheat to 65-75 ℃, under whipped state, add peroxidized t-butyl perbenzoate, aminoresin, stirring reaction 30-40 minute again under 800-1000 rev/min;
(2), reactor material is put into Scattered Kettle, add the rest materials in formula simultaneously, stir, disperse in Scattered Kettle, the mass transport after dispersion is carried out wet type sand milling, dispersion in sand mill;
(3), scattered mass transport is filtered and screened in vibrating filter, require the fineness of materials≤60um after filtering, the product after filtering is packed, warehouse-in.
3. band according to claim 1 rust anticorrosive paint, is characterized in that: described film-forming resin is by the raw material preparation of following weight part and obtain:
Alcohol ester 12 12-14, calcium stearate 1-2, Iron-ore Slag powder 1-2, nano silicon 1-2, dimethyl silicone oil 4-5, Vulcanization accelerator TMTD 1-2, aluminium hydroxide 8-10, ethyl acetate 18-21, Union carbide A-162 2-3;
Preparation method adds calcium stearate, Iron-ore Slag powder, nano silicon in ethyl acetate, grinding distribution, then, add again aluminium hydroxide, Union carbide A-162, be warming up to 50-55 ℃, stirring reaction 30-45 minute, then add other remaining component, continue to stir 45-60 minute, obtain.