CN103525028A - 阻燃玻纤维增强pbt色母粒及其制备方法 - Google Patents
阻燃玻纤维增强pbt色母粒及其制备方法 Download PDFInfo
- Publication number
- CN103525028A CN103525028A CN201210222375.3A CN201210222375A CN103525028A CN 103525028 A CN103525028 A CN 103525028A CN 201210222375 A CN201210222375 A CN 201210222375A CN 103525028 A CN103525028 A CN 103525028A
- Authority
- CN
- China
- Prior art keywords
- flame
- pbt
- district
- temperature
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃玻纤维增强PBT色母粒及其制备方法。本发明的阻燃玻纤维增强PBT色母粒,其组分按质量百分数配比为:PBT聚脂树脂20%~40%、颜料30%~50%、PBO阻燃剂8%~15%、分散剂15%~20%、KY-1010抗氧剂0.2%~1%、钛酸酯偶联剂0.1%~1%。将上述各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒。按照本发明制备的阻燃玻纤维增强PBT色母粒具有分散性好、着色均匀、使用方便、便于储运和环保的特点,而且其制备工艺简单、成本低。
Description
技术领域
本发明涉及一种色母粒及其制备方法,具体地说是一种阻燃玻纤维增强PBT色母粒及其制备方法。
背景技术
玻纤维增强PBT材料不仅具有优良的物理机械性能,如机械强度高、耐疲劳性和尺寸稳定性好、蠕变小、耐老化性能优异,而且其电气性能也极为优异,如其体积电阻率和介电强度高、耐电弧性能优良、在潮湿高温环境下电性能稳定,所以是制造电子、电气零件的理想材料。而现有技术的PBT着色一般采用色粉染色,不但操作中颜料粉尘大,污染环境,颜色不稳定,而且着色剂使用不当也直接影响产品质量等;也有的采用PBT色母料着色,但其阻燃性能差,这显然不能适应于玻纤维增强PBT材料用于电子、电气零件的高阻燃性要求。
发明内容
鉴于上述现有技术的不足,本发明提供一种分散性好、着色均匀、使用方便和环保的阻燃玻纤维增强PBT色母粒及其制备方法。
本发明解决其技术问题所采用的技术方案是:阻燃玻纤维增强PBT色母粒,其组分按质量百分数配比为:PBT聚脂树脂20%~40%、颜料30%~50%、PBO阻燃剂8%~15%、分散剂15%~20%、KY-1010抗氧剂0.2%~1%、钛酸酯偶联剂0.1%~1%。
所述的颜料为二氧化钛。
所述的PBO阻燃剂为聚2,6-二溴亚苯基醚,是由2,4,6-三溴苯酚在引发剂作用下进行缩聚反应制得,其理论溴含量64%,软化点210℃-240℃,相对密度2.07。
所述的分散剂为EVA蜡、聚丙烯蜡、AClyn低分子量离聚物的一种或多种。
上述一种阻燃玻纤维增强PBT色母粒的制备方法为:将上述各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒,其工艺为:双螺杆挤出机的一区温度为90℃~110℃,二区温度为155℃~175℃,三区温度为200℃~220℃,四区温度为205℃~215℃,五区温度为200℃~210℃;停留时间为1~2分钟,压力为10~15MPa。
本发明的有益效果是,添加高效的阻燃剂所制得的阻燃玻纤维增强PBT色母粒用于玻纤维增强PBT制品中,其配合加工性和阻燃性突出,并赋于良好的电绝缘性,所制备的色母粒具有分散性好、着色均匀、使用方便、便于储运和环保的特点,而且其制备工艺简单、成本低。
具体实施方式
下面结合具体实施例来进一步说明本发明的技术方案。
实施例1:
一种阻燃玻纤维增强PBT色母粒,其组分按质量百分数配比为:PBT聚脂树脂30%、二氧化钛40%、聚2,6-二溴亚苯基醚8%、EVA蜡20%、KY-1010抗氧剂1%、钛酸酯偶联剂1%。
制备方法:将上述各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒,其工艺为:双螺杆挤出机的一区温度为90℃~110℃,二区温度为155℃~175℃,三区温度为200℃~220℃,四区温度为205℃~215℃,五区温度为200℃~210℃;停留时间为1~2分钟,压力为10~15MPa。
实施例2:
一种阻燃玻纤维增强PBT色母粒,其组分按质量百分数配比为:PBT聚脂树脂20%、二氧化钛50%、聚2,6-二溴亚苯基醚11.5%、AClyn低分子量离聚物18%、KY-1010抗氧剂0.2%、钛酸酯偶联剂0.3%。
制备方法:将上述各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒,其工艺为:双螺杆挤出机的一区温度为90℃~110℃,二区温度为155℃~175℃,三区温度为200℃~220℃,四区温度为205℃~215℃,五区温度为200℃~210℃;停留时间为1~2分钟,压力为10~15MPa。
实施例3:
一种阻燃玻纤维增强PBT色母粒,其组分按质量百分数配比为:PBT聚脂树脂40%、二氧化钛30%、聚2,6-二溴亚苯基醚12%、EVA蜡8.5%、聚丙烯蜡8.5%、KY-1010抗氧剂0.5%、钛酸酯偶联剂0.5%。
制备方法:将上述各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒,其工艺为:双螺杆挤出机的一区温度为90℃~110℃,二区温度为155℃~175℃,三区温度为200℃~220℃,四区温度为205℃~215℃,五区温度为200℃~210℃;停留时间为1~2分钟,压力为10~15MPa。
Claims (6)
1.一种阻燃玻纤维增强PBT色母粒,其特征在于,其组分按质量百分数配比为:PBT聚脂树脂20%~40%、颜料30%~50%、PBO阻燃剂8%~15%、分散剂15%~20%、KY-1010抗氧剂0.2%~1%、钛酸酯偶联剂0.1%~1%。
2.根据权利要求1所述的阻燃玻纤维增强PBT色母粒,其特征在于,所述的颜料为二氧化钛。
3.根据权利要求1所述的阻燃玻纤维增强PBT色母粒,其特征在于,所述的PBO阻燃剂为聚2,6-二溴亚苯基醚。
4.根据权利要求1所述的阻燃玻纤维增强PBT色母粒,其特征在于,所述的分散剂为EVA蜡、聚丙烯蜡、AClyn低分子量离聚物的一种或多种。
5.根据权利要求1所述的阻燃玻纤维增强PBT色母粒的制备方法,其特征在于,包括以下步骤:按照权利要求1~4所述的各组分按比例配料,然后在高速混合机中干混3~5分钟,再置于双螺杆挤出机中经熔融挤出、造粒。
6.根据权利要求5所述的阻燃玻纤维增强PBT色母粒的制备方法,其特征在于,双螺杆挤出机的一区温度为90℃~110℃,二区温度为155℃~175℃,三区温度为200℃~220℃,四区温度为205℃~215℃,五区温度为200℃~210℃,停留时间为1~2分钟,压力为10~15MPa。