CN103524932A - 一种雾面阻燃聚氯乙烯电线电缆料及其制备方法 - Google Patents
一种雾面阻燃聚氯乙烯电线电缆料及其制备方法 Download PDFInfo
- Publication number
- CN103524932A CN103524932A CN201310461352.2A CN201310461352A CN103524932A CN 103524932 A CN103524932 A CN 103524932A CN 201310461352 A CN201310461352 A CN 201310461352A CN 103524932 A CN103524932 A CN 103524932A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- powder
- fog
- cable material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种雾面阻燃聚氯乙烯电线电缆料,由下列重量份的原料制成:聚氯乙烯60-80、有机硅改性热塑性酚醛树脂15-20,硅酸钙1-2、木粉8-10,碳酸钙40-50、环氧化甘油三酸酯40-50、棕榈油4-5、月桂酸甲酯4-10、氢氧化镁20-30、十溴二苯乙烷3-5、钼酸铵1.0-2.0、稳定剂3-7、微晶蜡0.5-1.5、亚硒酸钠1-2、次磷酸铝8-10、聚磷酸铵1-2、醇酯十二1-2、改性填料8-10。本雾面阻燃聚氯乙烯电线电缆料具有阻燃、耐油、耐老化、耐酸碱的特点,且比重较低、成本低。
Description
技术领域
本发明涉及电缆料领域,具体涉及一种雾面阻燃聚氯乙烯电线电缆料及其制备方法。
背景技术
随着全球经济的迅猛发展,及人类环保意识的增强,各领域对电线电缆的质量和性能的要求越来越高,因电线、电缆的老化而引发的火灾也越来越多,如何降低火灾的发生率及发生火灾的时的死亡率,低烟、无卤、阻燃、环保也成为电线电缆行业的发展方向。其中无卤低烟阻燃电缆料的需求量越来越大,目前无卤低烟阻燃电缆料的生产大多是在聚烯烃基材中加入大量的氢氧化铝来达到阻燃效果,然而,大量无机材料的加入,影响了电缆料的物理机械性能和加工工艺性能,其在常温下柔软性能、耐气候性差、耐油性、耐低温性能都不是很好。
发明内容
本发明提供了一种雾面阻燃聚氯乙烯电线电缆料及其制备方法。
本发明采用的技术方案为:
一种雾面阻燃聚氯乙烯电线电缆料,其特征在于:由下列重量份的原料制成:聚氯乙烯60-80、有机硅改性热塑性酚醛树脂15-20,硅酸钙1-2、木粉8-10,碳酸钙40-50、环氧化甘油三酸酯40-50、棕榈油4-5、月桂酸甲酯4-10、氢氧化镁20-30、十溴二苯乙烷3-5、钼酸铵1.0-2.0、稳定剂3-7、微晶蜡0.5-1.5、亚硒酸钠1-2、次磷酸铝8-10、聚磷酸铵1-2、醇酯十二1-2、改性填料8-10。
所述的雾面阻燃聚氯乙烯电线电缆料,其特征在于,由下列重量份的组分原料制备而得:聚氯乙烯70、有机硅改性热塑性酚醛树脂18,硅酸钙2、木粉9、碳酸钙45、环氧化甘油三酸酯48、棕榈油5、月桂酸甲酯8、氢氧化镁25、十溴二苯乙烷4、钼酸铵1.5、稳定剂4、微晶蜡0.8、亚硒酸钠1、次磷酸铝10、聚磷酸铵1、醇酯十二2、改性填料9。
所述的雾面阻燃聚氯乙烯电线电缆料,其特征在于,所述的改性填料是通过下列方法制备而得:
将凹凸棒土在540-580℃下煅烧3-4小时,取出后,加入3-4%的氢氧化钠溶液中研磨1-2小时,然后,加入12-15%的盐酸溶液,调节PH值为4-5,陈化10-15小时,再加氢氧化钠溶液调节研磨液pH为中性,过滤,烘干得到填料粉末,然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉,共同研磨1-2小时后,再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉,以11000-12000转/分的高速分散均匀,即得。
按配方比例称取各组分原料,将称取的组分原料,在高速混合机中搅拌均匀,再在135-165℃的温度区间下经密炼机密炼,双螺杆挤出,磨面热切造粒,旋风分离机送料,振动筛筛分然后包装,即制得电缆料成品。
有益效果
本雾面阻燃聚氯乙烯电线电缆料具有阻燃、耐油、耐老化、耐酸碱的特点,且比重较低、成本低。
具体实施方式
雾面阻燃聚氯乙烯电线电缆料,由下列重量(kg)的原料制成:
聚氯乙烯70、有机硅改性热塑性酚醛树脂18,硅酸钙2、木粉9、碳酸钙45、环氧化甘油三酸酯48、棕榈油5、月桂酸甲酯8、氢氧化镁25、十溴二苯乙烷4、钼酸铵1.5、稳定剂4、微晶蜡0.8、亚硒酸钠1、次磷酸铝10、聚磷酸铵1、醇酯十二2、改性填料9,其中,改性填料是通过下列方法制备而得:
将凹凸棒土在540-580℃下煅烧3-4小时,取出后,加入3-4%的氢氧化钠溶液中研磨1-2小时,然后,加入12-15%的盐酸溶液,调节PH值为4-5,陈化10-15小时,再加氢氧化钠溶液调节研磨液pH为中性,过滤,烘干得到填料粉末,然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉,共同研磨1-2小时后,再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉,以11000-12000转/分的高速分散均匀,即得。
成品电缆料的制备方法:
按配方比例称取各组分原料,将称取的组分原料,在高速混合机中搅拌均匀,再在135-165℃的温度区间下经密炼机密炼,双螺杆挤出,磨面热切造粒,旋风分离机送料,振动筛筛分然后包装,即制得电缆料成品。
本实施例制得的电缆料的性能测试结果如下表:
Claims (3)
1.一种雾面阻燃聚氯乙烯电线电缆料,其特征在于:由下列重量份的原料制成:聚氯乙烯60-80、有机硅改性热塑性酚醛树脂15-20,硅酸钙1-2、木粉8-10,碳酸钙40-50、环氧化甘油三酸酯40-50、棕榈油4-5、月桂酸甲酯4-10、 氢氧化镁20-30、十溴二苯乙烷3-5、钼酸铵1.0-2.0、稳定剂3-7、微晶蜡0.5-1.5、亚硒酸钠1-2、次磷酸铝8-10、聚磷酸铵1-2 、醇酯十二1-2、改性填料8-10。
2.根据权利要求1所述的雾面阻燃聚氯乙烯电线电缆料,其特征在于,由下列重量份的组分原料制备而得:聚氯乙烯70、有机硅改性热塑性酚醛树脂18,硅酸钙2、木粉9、碳酸钙45、环氧化甘油三酸酯48、棕榈油5、月桂酸甲酯8、 氢氧化镁25、十溴二苯乙烷4、钼酸铵1.5、稳定剂4、微晶蜡0.8、亚硒酸钠1、次磷酸铝10、聚磷酸铵1、醇酯十二2、改性填料9。
3. 根据权利要求1或2所述的雾面阻燃聚氯乙烯电线电缆料,其特征在于, 所述的改性填料是通过下列方法制备而得:
将凹凸棒土在540-580℃下煅烧3-4小时,取出后,加入3-4%的氢氧化钠溶液中研磨1-2小时,然后,加入12-15%的盐酸溶液,调节PH值为4-5,陈化10-15小时,再加氢氧化钠溶液调节研磨液pH为中性,过滤,烘干得到填料粉末,然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉,共同研磨1-2小时后,再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉,以11000-12000转/分的高速分散均匀,即得。