CN103521208A - 一种光催化剂的制备方法 - Google Patents

一种光催化剂的制备方法 Download PDF

Info

Publication number
CN103521208A
CN103521208A CN201310475309.1A CN201310475309A CN103521208A CN 103521208 A CN103521208 A CN 103521208A CN 201310475309 A CN201310475309 A CN 201310475309A CN 103521208 A CN103521208 A CN 103521208A
Authority
CN
China
Prior art keywords
tio
nano
dry
preparation
mao bamboon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310475309.1A
Other languages
English (en)
Inventor
王耀斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi Shengmai Petroleum Co Ltd
Original Assignee
Shaanxi Shengmai Petroleum Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi Shengmai Petroleum Co Ltd filed Critical Shaanxi Shengmai Petroleum Co Ltd
Priority to CN201310475309.1A priority Critical patent/CN103521208A/zh
Publication of CN103521208A publication Critical patent/CN103521208A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种废水处理物的制备方法。包括：先制备纳米TiO2；再制备毛竹活性炭；然后将毛竹活性炭与质量分数为17％的HN03溶液混合，100℃下加热搅拌2h，然后用蒸馏水洗至中性，过滤，110℃干燥2h；将其加入到纳米TiO2中，振荡1h，静置过滤，110℃下干燥2h，再在500℃下加热lh后，自然冷却后重复加入到纳米TiO2中处理。本发明用毛竹活性炭负载TiO2制备光催化剂，对制药废水进行协同降解，制取回用水。实验结果表明．可以明显改善光催化效果，并且其稳定性高，可重复使用，是处理生物难降解有机废水的有效方法，具有较好的应用前景。

Description

一种光催化剂的制备方法
技术领域
     本发明涉及一种废水处理物的制备方法。
背景技术
 生物难降解有机废水作为工业生产中常见的一类废水，多产生于制药、化工等行业，该类废水具有水质多变、浓度高、盐度高、生色物质成分复杂等特点。传统的物化及生物处理技术，工艺复杂、成本高，且存在二次污染．难以满足对其净化处理的要求。近年来，多利用TiO2等半导体材料作为光催化剂对有机污染物进行光催化降解。最终使污染物降解为C02、H20等简单分子，达到消毒、脱色、除臭的目的。但该技术存在纳米TiO2光催化剂难以分离、回收。处理效率不高的问题。
发明内容
 本发明旨在提供一种能有效处理生物难降解有机废水的光催化剂的制备方法。
本发明所述的一种光催化剂的制备方法，包括：将钛酸丁酯溶解在无水乙醇中，再加入三乙醇胺，混合均匀，用硝酸调节pH=3后滴加蒸馏水和乙醇混合液，搅拌2 h，80℃下真空干燥．待溶胶变为淡黄色后继续干燥24 h，研磨并放入马弗炉中于400℃下煅烧2h，即得纳米TiO2；。
将洗净的毛竹放入120℃烘箱中烘干，粉碎到O.25 mm，按1：1的体积比加入0.3 mol／L的硫酸亚铁溶液，80℃恒温中浸渍6 h后，于120℃下干燥，然后在氮气流量为30 mL/min的条件下，升温至680℃，维持3 h后降后取出，即得备用毛竹活性炭；。
将毛竹活性炭与质量分数为17％的HN03溶液混合，100℃下加热搅拌2 h，然后用蒸馏水洗至中性，过滤，110℃干燥2 h；。
将其加入到纳米TiO2中，振荡1 h，静置过滤，110℃下干燥2 h，再在500℃下加热l h后，自然冷却后重复加入到纳米TiO2中处理。
优选地，重复加入到纳米TiO2中处理两次。
本发明用毛竹活性炭负载TiO2制备光催化剂，对制药废水进行协同降解，制取回用水。实验结果表明．可以明显改善光催化效果，并且其稳定性高，可重复使用，是处理生物难降解有机废水的有效方法，具有较好的应用前景。
具体实施方式
 实施例一。
将钛酸丁酯溶解在无水乙醇中，再加入三乙醇胺，混合均匀，用硝酸调节pH=3后滴加蒸馏水和乙醇混合液，搅拌2 h，80℃下真空干燥．待溶胶变为淡黄色后继续干燥24 h，研磨并放入马弗炉中于400℃下煅烧2h，即得纳米TiO2；。
将洗净的毛竹放入120℃烘箱中烘干，粉碎到0.25 mm，按1：1的体积比加入0.3 mol／L的硫酸亚铁溶液，80℃恒温中浸渍6 h后，于120℃下干燥，然后在氮气流量为30 mL/min的条件下，升温至680℃，维持3 h后降后取出，即得备用毛竹活性炭；。
将毛竹活性炭与质量分数为17％的HN03溶液混合，100℃下加热搅拌2 h，然后用蒸馏水洗至中性，过滤，110℃干燥2 h后称取50g，加入到纳米TiO2中，振荡1 h，静置过滤，110℃下干燥2 h，再在500℃下加热l h后，自然冷却后重复加入到纳米TiO2中处理两次。
然后将制得的光催化剂，传统的纳米TiO2粉末和玻璃负载TiO2三种催化剂分别对废水进行耦合催化，结果见下表。
催化剂种类 本发明的光催化剂 传统的纳米TiO2粉末 玻璃负载TiO2
COD去除率/% 55.61 82.63 91.74
脱色率/% 70.15 87.22 94.52
由上表可知，本发明的光催化剂对废水的COD去除率及脱色率均有明显提高，说明活性炭负载后提高了TiO2的光催化效率，其性能优于传统吸附材料，且催化剂的可回收性得以改善。

Claims (2)

1.一种光催化剂的制备方法，其特征在于包括：
将钛酸丁酯溶解在无水乙醇中，再加入三乙醇胺，混合均匀，用硝酸调节pH=3后滴加蒸馏水和乙醇混合液，搅拌2 h，80℃下真空干燥．待溶胶变为淡黄色后继续干燥24 h，研磨并放入马弗炉中于400℃下煅烧2h，即得纳米TiO2；
将洗净的毛竹放入120℃烘箱中烘干，粉碎到O.25 mm，按1：1的体积比加入0.3 mol／L的硫酸亚铁溶液，80℃恒温中浸渍6 h后，于120℃下干燥，然后在氮气流量为30 mL/min的条件下，升温至680℃，维持3 h后降后取出，即得备用毛竹活性炭；
将毛竹活性炭与质量分数为17％的HN03溶液混合，100℃下加热搅拌2 h，然后用蒸馏水洗至中性，过滤，110℃干燥2 h；
将其加入到纳米TiO2中，振荡1 h，静置过滤，110℃下干燥2 h，再在500℃下加热l h后，自然冷却后重复加入到纳米TiO2中处理。
2.如权利要求1所述的微波协同光催化降解反应器，其特征在于重复加入到纳米TiO2中处理两次。
CN201310475309.1A 2013-10-13 2013-10-13 一种光催化剂的制备方法 Pending CN103521208A (zh)