CN103509519A - Epoxy resin abrasive paste - Google Patents
Epoxy resin abrasive paste Download PDFInfo
- Publication number
- CN103509519A CN103509519A CN201310115144.7A CN201310115144A CN103509519A CN 103509519 A CN103509519 A CN 103509519A CN 201310115144 A CN201310115144 A CN 201310115144A CN 103509519 A CN103509519 A CN 103509519A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- grinding tool
- abrasive paste
- user
- abrasive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of grinding and cutting, and specifically relates to an epoxy resin abrasive paste. The abrasive paste is prepared according to characteristics of epoxy resin. Before curing, the epoxy resin abrasive paste processes a linear structure with thermoplasticity; an abrasive tool with required performances can be prepared by adding a curing agent into the epoxy resin abrasive paste; or a related object is coated with the epoxy resin abrasive paste, and then the object will processes functions of abrasive tools; so that individual requirements of users are met.
Description
Technical field
The present invention relates to grinding, cutting field, specifically refer to a kind of epoxy resin grinding tool cream.
Background technology
Epoxy resin is widely used in grinding tool Abrasive Industry, and it has the performance of many excellences, and its erosion resistance is good, shrinking percentage is low, has good chemistry and thermostability, and bonding properties is high and processing characteristics is good, and usually the bonding agent as grinding tool is used.Epoxy resin is thermoplastic linear structure before uncured, during use, need add solidifying agent, and epoxy group(ing) of solidifying agent and epoxy resin etc. is reacted, and becomes cancellated macromole, becomes insoluble, not molten thermoset finished product.Epoxy resin relative molecular mass before solidifying is not high, only has by solidifying and could form bodily form polymer.Solidifying of epoxy resin will be by solidifying agent, and the kind of solidifying agent is a lot, mainly contains polyamine and polyprotonic acid, all contains ripple hydrogen atom alive in their molecule.
At this traditional class grinding tool, being cemented in factory of epoxy resin grinding tool completes, user directly uses product, do not participate in the production process of grinding tool product, can bring like this problem: when user needs a kind of grinding tool of personalization, during a kind of purposes of personalization, production firm cannot provide or be unwilling and provide, and production firm only can provide popular product.
The present invention, after the bonding agent of producing grinding tool, abrasive material, subsidiary material, additive etc. are mixed, does not allow them solidify, and divides and installs in soft container, makes grinding tool cream, is sold to user, when is solidified into product, by user, is freely controlled.Like this, can allow user participate in grinding tool cure stage, according to user's oneself personal needs, produce the personalized grinding tool that user needs, the more needed personalized grinding tools of solution user, the purposes that some are personalized.For example: user can squeeze out grinding tool cream a bit, mixes in proportion with solidifying agent, spread upon on Nail scissors, after grinding tool cream solidifies, this nail clipper has just possessed the function of grinding nail.
Summary of the invention
The object of the invention is to utilize the character of epoxy resin, produce a kind of grinding tool cream, before uncured, be thermoplastic linear structure, user adds solidifying agent before use, make own required grinding tool, or spread upon on relevant article, make article also possess the function of grinding tool, thereby solve user's individual demand.
The object of the invention is to be achieved through the following technical solutions.
Epoxy resin grinding tool cream, is characterized in that being comprised of following formula: liquid bisphenol A epoxide resin, abrasive material.
The composition of described epoxy resin grinding tool cream is by weight
:
15 25 parts of liquid bisphenol A epoxide resins
75 85 parts, abrasive material
Above-mentioned raw materials mixes, and divides and installs in soft container.
Described solidifying agent is Versamid, divides and installs in flexible container.
Epoxy resin grinding tool cream and solidifying agent Versamid by weight, are 4:1.
Beneficial effect of the present invention.
1. by user, control the curing time of grinding tool.
2, by user, control the curing form of grinding tool.
3. according to user's oneself personal needs, produce the personalized grinding tool that user needs.
4. meet some personalized purposes of user's grinding and polishing.
5, grinding tool cream is spread upon on some article or machine part, make these article or machine part possess the function of grinding tool.
Embodiment
Below in conjunction with embodiment, describe the present invention.
Embodiment 1.
The epoxy resin grinding tool cream of the present embodiment, its composition is by weight:
20 parts of liquid bisphenol A epoxide resins
80 parts, No. 120 silicon carbide
Above-mentioned raw materials mixes, and divides and installs in soft container.
25 parts of Versamids divide and install in flexible container.
User, by above-mentioned two kinds of ointment, after squeezing out, mixes, and spreads upon on towel, under the condition of normal temperature 25 degree Celsius, place and solidify for one day, or under the condition of 75 degree Celsius, solidify 2 hours, these towels have just been made into soft grinding towel, have possessed the function of grinding and polishing.
Claims (2)
1. epoxy resin grinding tool cream, comprising: 15 25 parts of liquid bisphenol A epoxide resins, 75 85 parts, abrasive material.
2. epoxy resin grinding tool cream according to claim 1, is characterized in that, in use, also needs to add 1/4th the solidifying agent Versamid calculating by epoxy resin grinding tool cream weight.