CN103509270A - 一种阻燃泡沫墙体保温板及其制备方法 - Google Patents
一种阻燃泡沫墙体保温板及其制备方法 Download PDFInfo
- Publication number
- CN103509270A CN103509270A CN201310402375.6A CN201310402375A CN103509270A CN 103509270 A CN103509270 A CN 103509270A CN 201310402375 A CN201310402375 A CN 201310402375A CN 103509270 A CN103509270 A CN 103509270A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- flame
- loess
- powder
- retardant foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阻燃泡沫墙体保温板及其制备方法，其特征在于由下列重量份的原料制成：聚苯乙烯95-105、丙烯酸乳液8-10、月桂醇硫酸钠5-8、氟利昂2-4、氰尿酸锌3.5-5、硅烷偶联剂KH5604-6、二甲基硅油5-6、三氧化二锑8-10、氢氧化铝粉38-45、改性黄土30-35；本发明的导热系数、阻燃性、耐热及耐寒性、热稳定性、强度等指标均高于已有的挤塑聚苯泡沫保温板。
Description
技术领域
本发明涉及一种墙板，更具体地说，是一种阻燃泡沫墙体保温板及其制备方法。
背景技术
房屋建筑，特别是高寒地区的房屋建筑，建筑屋中的大量热量是通过屋顶和墙体散失的。因此，需要在屋顶和外墙铺砌保温板，起到保温隔热和节约能源的作用。现有的挤塑保温板，具有强度低、抗压低、密度低、抗老化性弱、成本高的缺点，需要有新的产品面世，参与竞争。
发明内容
本发明的目的是提供一种阻燃泡沫墙体保温板及其制备方法。
本发明所采用的技术方案是：
一种阻燃泡沫墙体保温板，其特征在于由下列重量份的原料制成：
聚苯乙烯95-105、丙烯酸乳液8-10、月桂醇硫酸钠5-8、氟利昂2-4、氰尿酸锌3.5-5、硅烷偶联剂KH560 4-6、二甲基硅油5-6、三氧化二锑8-10、氢氧化铝粉38-45、改性黄土30-35；
所述的改性黄土由以下重量份的原料制得：黄土100-120、草木灰30-40、废机油10-12、淀粉10-12、十二烷基苯磺酸钠1-2、铝粉0.2-0.3、水适量；
制备方法是：将黄土在460-480℃下煅烧2-3小时，研成粉末；将淀粉、十二烷基苯磺酸钠加入到适量水中，加热成糊状；向糊中加入所述的煅烧黄土粉、草木灰、铝粉、废机油，混合搅拌40-50分钟，送入60-70℃烘房中烘干，打碎成粗颗粒，筛出1-3mm的粗颗粒即可。
所述的阻燃泡沫墙体保温板的制备方法，其特征在于包括以下步骤：
（1）将丙烯酸乳液、月桂醇硫酸钠、氰尿酸锌、硅烷偶联剂KH560、二甲基硅油、三氧化二锑、氢氧化铝粉、改性黄土混合，搅拌均匀；
（2）然后将聚苯乙烯与步骤（1）物料混合，加热至190-235℃；使各物料熔融和混合，形成聚合物熔体；然后加入氟利昂搅拌混合；将熔体降温至100-125℃，然后，送入挤塑机，挤出成型。
本发明的导热系数、阻燃性、耐热及耐寒性、热稳定性、强度等指标均高于已有的挤塑聚苯泡沫保温板。
具体实施方式
一种阻燃泡沫墙体保温板，由下列重量份（公斤）的原料制成：
聚苯乙烯105、丙烯酸乳液10、月桂醇硫酸钠8、氟利昂2、氰尿酸锌5、硅烷偶联剂KH560 6、二甲基硅油6、三氧化二锑10、氢氧化铝粉45、改性黄土35；
所述的改性黄土由以下重量份（公斤）的原料制得：黄土120、草木灰30、废机油10、淀粉12、十二烷基苯磺酸钠2、铝粉0.3、水适量；
制备方法是：将黄土在460-480℃下煅烧2-3小时，研成粉末；将淀粉、十二烷基苯磺酸钠加入到适量水中，加热成糊状；向糊中加入所述的煅烧黄土粉、草木灰、铝粉、废机油，混合搅拌40-50分钟，送入60-70℃烘房中烘干，打碎成粗颗粒，筛出1-3mm的粗颗粒即可。
阻燃泡沫墙体保温板的制备方法，包括以下步骤：
（1）将丙烯酸乳液、月桂醇硫酸钠、氰尿酸锌、硅烷偶联剂KH560、二甲基硅油、三氧化二锑、氢氧化铝粉、改性黄土混合，搅拌均匀；
（2）然后将聚苯乙烯与步骤（1）物料混合，加热至190-235℃；使各物料熔融和混合，形成聚合物熔体；然后加入氟利昂搅拌混合；将熔体降温至100-125℃，然后，送入挤塑机，挤出成型。
本发明经检测，抗压强度≥ 280kPa，导热系数≤ 0.03W/mk，吸水率≤ 1％ (V/V)，水气透湿系数≤ 3ng/m.s.Pa。
Claims (2)
1.一种阻燃泡沫墙体保温板，其特征在于由下列重量份的原料制成：
聚苯乙烯95-105、丙烯酸乳液8-10、月桂醇硫酸钠5-8、氟利昂2-4、氰尿酸锌3.5-5、硅烷偶联剂KH560 4-6、二甲基硅油5-6、三氧化二锑8-10、氢氧化铝粉38-45、改性黄土30-35；
所述的改性黄土由以下重量份的原料制得：黄土100-120、草木灰30-40、废机油10-12、淀粉10-12、十二烷基苯磺酸钠1-2、铝粉0.2-0.3、水适量；
制备方法是：将黄土在460-480℃下煅烧2-3小时，研成粉末；将淀粉、十二烷基苯磺酸钠加入到适量水中，加热成糊状；向糊中加入所述的煅烧黄土粉、草木灰、铝粉、废机油，混合搅拌40-50分钟，送入60-70℃烘房中烘干，打碎成粗颗粒，筛出1-3mm的粗颗粒即可。
2.根据权利要求1所述的阻燃泡沫墙体保温板的制备方法，其特征在于包括以下步骤：
（1）将丙烯酸乳液、月桂醇硫酸钠、氰尿酸锌、硅烷偶联剂KH560、二甲基硅油、三氧化二锑、氢氧化铝粉、改性黄土混合，搅拌均匀；
（2）然后将聚苯乙烯与步骤（1）物料混合，加热至190-235℃；使各物料熔融和混合，形成聚合物熔体；然后加入氟利昂搅拌混合；将熔体降温至100-125℃，然后，送入挤塑机，挤出成型。