CN103497846A - Color-flame candle - Google Patents
Color-flame candle Download PDFInfo
- Publication number
- CN103497846A CN103497846A CN201310457500.3A CN201310457500A CN103497846A CN 103497846 A CN103497846 A CN 103497846A CN 201310457500 A CN201310457500 A CN 201310457500A CN 103497846 A CN103497846 A CN 103497846A
- Authority
- CN
- China
- Prior art keywords
- parts
- color
- candle
- sodium hydroxide
- urethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a color-flame candle which comprises the following components in parts by weight: 85-90 parts of urethane or oxalate, 5-15 parts of stearic acid, 2-5 parts of higher aliphatic alcohol, 60-80 parts of vegetable wax, 0.1-0.5 part of polyvinyl alcohol, 2-4 parts of boron fat, 0.5-1 part of lithium chloride, 0.1-0.5 part of sodium hydroxide and 20-40 parts of ceresin. By adopting the color-flame candle disclosed by the invention, the raw materials are easily available, the process is simple, and the performance is good; moreover, the ignitability of the candle is good, and the flame of the ignited candle has pure and bright color without yellow core and smoke and does not absorb moisture easily.
Description
Technical field
The present invention relates to a kind of articles for daily use, be specifically related to a kind of color flame candles.
Background technology
The flame of the color flame candles of existing market is pure not, usually have cigarette easily to produce pollutes and non-refractory.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the purpose of this invention is to provide a kind of color flame candles.
Technical scheme: a kind of color flame candles of the present invention comprises following component by weight: 85 ~ 90 parts of urethane or oxalic acid esters, 5 ~ 15 parts of stearic acid, 2 ~ 5 parts of high fatty alcohols, 60 ~ 80 parts of vegetable waxs, 0.1 ~ 0.5 part of polyvinyl alcohol, 2 ~ 4 parts, boron fat, 0.5 ~ 1 part of lithium chloride, 0.1 ~ 0.5 part, sodium hydroxide, 20 ~ 40 parts of mineral tallows.
Preferably, 90 ~ 95 parts of described urethane or oxalic acid esters, 7 ~ 13 parts of stearic acid, 3 ~ 4 parts of high fatty alcohols, 65 ~ 77 parts of vegetable waxs, 0.1 ~ 0.4 part of polyvinyl alcohol, 2.5 ~ 3.8 parts, boron fat, 0.6 ~ 0.95 part of lithium chloride, 0.15 ~ 0.45 part, sodium hydroxide, 23 ~ 35 parts of mineral tallows.
By urethane or oxalic acid ester, stearic acid, high fatty alcohol, vegetable wax, polyvinyl alcohol, boron fat, lithium chloride, sodium hydroxide, the fusing of mineral tallow Hybrid Heating, be dissolved to evenly, cooling, Shi Xin, casting moulding, the demoulding, coating, make color flame candle.
Beneficial effect: the present invention compared with prior art, has significant advantage, and raw material of the present invention is easy to get, and technique is simple, excellent property, and the candle kindling is good, the flame color after lighting is pure, bright-coloured, without yellow core, be difficult for the moisture absorption, smokeless.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1:
A kind of color flame candles takes following component by weight: 90 parts of urethane or oxalic acid esters, 7 parts of stearic acid, 3 parts of high fatty alcohols, 65 parts of vegetable waxs, 0.1 part of polyvinyl alcohol, 2.5 parts, boron fat, 0.6 part of lithium chloride, 0.15 part, sodium hydroxide, 23 parts of mineral tallows.
By urethane or oxalic acid ester, stearic acid, high fatty alcohol, vegetable wax, polyvinyl alcohol, boron fat, lithium chloride, sodium hydroxide, the fusing of mineral tallow Hybrid Heating, be dissolved to evenly, cooling, Shi Xin, casting moulding, the demoulding, coating, make color flame candle.
Embodiment 2:
A kind of color flame candles comprises following component by weight: 95 parts of urethane or oxalic acid esters, 13 parts of stearic acid, 4 parts of high fatty alcohols, 77 parts of vegetable waxs, 0.4 part of polyvinyl alcohol, 3.8 parts, boron fat, 0.95 part of lithium chloride, 0.45 part, sodium hydroxide, 35 parts of mineral tallows.
By urethane or oxalic acid ester, stearic acid, high fatty alcohol, vegetable wax, polyvinyl alcohol, boron fat, lithium chloride, sodium hydroxide, the fusing of mineral tallow Hybrid Heating, be dissolved to evenly, cooling, Shi Xin, casting moulding, the demoulding, coating, make color flame candle.
Embodiment 3:
A kind of color flame candles comprises following component by weight: 92 parts of urethane or oxalic acid esters, 9 parts of stearic acid, 3.5 parts of high fatty alcohols, 68 parts of vegetable waxs, 0.25 part of polyvinyl alcohol, 2.9 parts, boron fat, 0.75 part of lithium chloride, 0.2 part, sodium hydroxide, 29 parts of mineral tallows.
By urethane or oxalic acid ester, stearic acid, high fatty alcohol, vegetable wax, polyvinyl alcohol, boron fat, lithium chloride, sodium hydroxide, the fusing of mineral tallow Hybrid Heating, be dissolved to evenly, cooling, Shi Xin, casting moulding, the demoulding, coating, make color flame candle.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (2)
1. a color flame candles, is characterized in that: comprise by weight following component: 85 ~ 90 parts of urethane or oxalic acid esters, 5 ~ 15 parts of stearic acid, 2 ~ 5 parts of high fatty alcohols, 60 ~ 80 parts of vegetable waxs, 0.1 ~ 0.5 part of polyvinyl alcohol, 2 ~ 4 parts, boron fat, 0.5 ~ 1 part of lithium chloride, 0.1 ~ 0.5 part, sodium hydroxide, 20 ~ 40 parts of mineral tallows.
2. color flame candles according to claim 1, is characterized in that: 90 ~ 95 parts of described urethane or oxalic acid esters, 7 ~ 13 parts of stearic acid, 3 ~ 4 parts of high fatty alcohols, 65 ~ 77 parts of vegetable waxs, 0.1 ~ 0.4 part of polyvinyl alcohol, 2.5 ~ 3.8 parts, boron fat, 0.6 ~ 0.95 part of lithium chloride, 0.15 ~ 0.45 part, sodium hydroxide, 23 ~ 35 parts of mineral tallows.