CN103497652A - 一种环保型户外无光粉末涂料 - Google Patents
一种环保型户外无光粉末涂料 Download PDFInfo
- Publication number
- CN103497652A CN103497652A CN201310438417.1A CN201310438417A CN103497652A CN 103497652 A CN103497652 A CN 103497652A CN 201310438417 A CN201310438417 A CN 201310438417A CN 103497652 A CN103497652 A CN 103497652A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- powder
- mixed
- glossless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型户外无光粉末涂料,它是由下述重量份的原料组成的:P9335聚酯树酯70-80、丙烯酸树脂10-14、流平剂(FC-100)3-4、皱纹剂(XG608)0.4-3、乙烯基三乙氧基硅烷2-3、苯骈三氮唑2.0-3.0、空心微珠2-3、过氧化环己酮0.6-2、云母粉10-13、乙酸2-3、三烯丙基异氰脲酸酯6-10、防老剂MB1-2、复合填料5-10;本发明粉末涂料具有良好的耐化学腐蚀性,耐候性强,抗冲击性好,不需要另外加入消光剂即可达到消光的效果,原料安全环保。
Description
技术领域
本发明主要涉及一种涂料,尤其涉及一种环保型户外无光粉末涂料。
背景技术
热固型粉末涂料是指以热固性树脂作为成膜物质,加入起交联反应的固化剂经加热后能形成不溶不熔的质地坚硬涂层。温度再高该涂层也不会像热塑性涂层那样软化,而只能发生分解。由于热固性粉末涂料所采用的树脂为聚合度较低的预聚物,分子量较低,所以涂层的流平性较好,具有较好的装饰性,而且低分子量的预聚物经固化后,能形成网状交联的大分子,因而涂层具有较好防腐性和机械性能。故热固性粉末涂料发展尤为迅速,为了更好的服务于现代化建设,高品质的粉末涂料一直是人们研究的重点。
发明内容
本发明目的就是为了提供一种环保型户外无光粉末涂料。
本发明是通过以下技术方案实现的:
一种环保型户外无光粉末涂料,其特征在于它是由下述重量份的原料组成的:
P9335聚酯树酯70-80、丙烯酸树脂10-14、流平剂(FC-100)3-4、皱纹剂(XG608)0.4-3、乙烯基三乙氧基硅烷2-3、苯骈三氮唑2.0-3.0、空心微珠2-3、过氧化环己酮0.6-2、云母粉10-13、乙酸2-3、三烯丙基异氰脲酸酯6-10、防老剂MB1-2、复合填料5-10;
所述的复合填料是由下述重量份的原料组成的:
红土40-50、玉石粉10-20、六方氮化硼4-6、铝矾土5-7、环氧大豆油2-4、硬酯酸单甘油酯1-2、双巯基乙羧甲基纤维素钠正辛基锡0.6-1;
将上述红土与铝矾土混合,600-800℃下煅烧2-3小时,出料冷却后与玉石粉混合研磨成粉;将上述六方氮化硼与硬酯酸单甘油酯、环氧大豆油混合,80-90℃下搅拌加热反应10-20分钟,冷却后与上述得到的粉料混合,搅拌均匀,滴加双巯基乙酸异辛酯二正辛基锡,充分球磨,过160-180目筛,即得所述复合填料。
一种环保型户外无光粉末涂料的制备方法,包括以下步骤:
将上述各原料混合,通过挤出机中混炼挤出,然后压片破碎后,再经过微粉碎机粉碎、过筛,即得所述环保型户外无光粉末涂料。
本发明的优点是:
本发明粉末涂料具有良好的耐化学腐蚀性,耐候性强,抗冲击性好,不需要另外加入消光剂即可达到消光的效果,原料安全环保。
具体实施方式
实施例1,
一种环保型户外无光粉末涂料,它是由下述重量份(公斤)的原料组成的:
P9335聚酯树酯80、丙烯酸树脂14、流平剂(FC-100)3、皱纹剂(XG608)3、乙烯基三乙氧基硅烷3、苯骈三氮唑3.0、空心微珠2、过氧化环己酮2、云母粉13、乙酸2-3、三烯丙基异氰脲酸酯8、防老剂MB2、复合填料10;
所述的复合填料是由下述重量份的原料组成的:
红土50、玉石粉20、六方氮化硼4、铝矾土7、环氧大豆油4、硬酯酸单甘油酯1、双巯基乙羧甲基纤维素钠正辛基锡0.6;
将上述红土与铝矾土混合,800℃下煅烧2小时,出料冷却后与玉石粉混合研磨成粉;将上述六方氮化硼与硬酯酸单甘油酯、环氧大豆油混合,90℃下搅拌加热反应20分钟,冷却后与上述得到的粉料混合,搅拌均匀,滴加双巯基乙酸异辛酯二正辛基锡,充分球磨,过180目筛,即得所述复合填料。
一种环保型户外无光粉末涂料的制备方法,包括以下步骤:
将上述各原料混合,通过挤出机中混炼挤出,然后压片破碎后,再经过微粉碎机粉碎、过筛,即得所述环保型户外无光粉末涂料。
性能测试:
抗冲击性:≥50kg/cm;
硬度≥2H。
Claims (2)
1.一种环保型户外无光粉末涂料,其特征在于它是由下述重量份的原料组成的:
P9335聚酯树酯70-80、丙烯酸树脂10-14、流平剂(FC-100)3-4、皱纹剂(XG608)0.4-3、乙烯基三乙氧基硅烷2-3、苯骈三氮唑2.0-3.0、空心微珠2-3、过氧化环己酮0.6-2、云母粉10-13、乙酸2-3、三烯丙基异氰脲酸酯6-10、防老剂MB1-2、复合填料5-10;
所述的复合填料是由下述重量份的原料组成的:
红土40-50、玉石粉10-20、六方氮化硼4-6、铝矾土5-7、环氧大豆油2-4、硬酯酸单甘油酯1-2、双巯基乙羧甲基纤维素钠正辛基锡0.6-1;
将上述红土与铝矾土混合,600-800℃下煅烧2-3小时,出料冷却后与玉石粉混合研磨成粉;将上述六方氮化硼与硬酯酸单甘油酯、环氧大豆油混合,80-90℃下搅拌加热反应10-20分钟,冷却后与上述得到的粉料混合,搅拌均匀,滴加双巯基乙酸异辛酯二正辛基锡,充分球磨,过160-180目筛,即得所述复合填料。
2.一种如权利要求1所述的环保型户外无光粉末涂料的制备方法,其特征在于包括以下步骤:
将上述各原料混合,通过挤出机中混炼挤出,然后压片破碎后,再经过微粉碎机粉碎、过筛,即得所述环保型户外无光粉末涂料。