CN103497641A - Metallic powder coating - Google Patents
Metallic powder coating Download PDFInfo
- Publication number
- CN103497641A CN103497641A CN201310438412.9A CN201310438412A CN103497641A CN 103497641 A CN103497641 A CN 103497641A CN 201310438412 A CN201310438412 A CN 201310438412A CN 103497641 A CN103497641 A CN 103497641A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- powder coating
- mix
- slag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metallic powder coating. The metallic powder coating consists of the following raw materials in parts by weight: 50-60 parts of epoxy resin E12, 4-5 parts of industrial magnesium-calcium slag, 4-6 parts of light calcium carbonate, 0.2-0.3 part of gas-phase silicon dioxide, 6-8 parts of polyacrylamide, 3-6 parts of ceramic slag powder, 2-3 parts of aluminum powder, 4-10 parts of dipropylenetriamine, 0.4-1 part of silver powder, 1-2 parts of dibenzylamine ether, 2-4 parts of chloroparaffin and 5-10 parts of composite filler. The powder coating has the advantages of good glossiness of the coating film, strong decorative effect, strong surface resistance and good environmental suitability, and can achieve an excellent protection effect when coated on a shell of an instrument.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of metal powder coating.
Background technology
Development along with the appearance of various instrument in recent years especially precision meter and micro-electricity, light current components and parts, large-scale integrated circuit; also require the shell of instrument that reliable electrostatic protection and electrostatic shielding function will be arranged; coating not only want can absorbing high-frequency radiation and the electromagnetic energy of high energy; make inner fragile element obtain good protection; also to there is certain shock resistance and the performance such as corrosion-resistant, to guarantee the user demand of instrument under varying environment.
Summary of the invention
The object of the invention is exactly for a kind of metal powder coating is provided.
The present invention is achieved by the following technical solutions:
A kind of metal powder coating is characterized in that what it was comprised of the raw material of following weight parts:
Epoxy resin E12 50-60, commercial magnesium calcium slag 4-5, light calcium carbonate 4-6, two gaseous oxidation silicon 0.2-0.3, polyacrylamide 6-8, ceramic ground-slag end 3-6, aluminium powder 2-3, two propylene triamine 4-10, silver powder 0.4-1, phenoxybenzamine base ether 1-2, clorafin 2-4, compounded mix 5-10;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 30-45, fluorapatite 5-10, Fluorspar Powder 3-5, aluminium hydroxide 3-4, vanadium diboride 1-2,2,6-ditertbutylparacresol 1-2, cetomacrogol 1000 2-3;
Above-mentioned laterite, fluorapatite, Fluorspar Powder are mixed, and calcining 3-4 hour under 600-700 ℃, mix with vanadium diboride after discharging is cooling, and fully ball milling, must expect a; Above-mentioned cetomacrogol 1000 is joined in 4-5 times of water, be heated to 30-40 ℃, fully stir, add aluminium hydroxide, 100-200 rev/min of dispersed with stirring 3-4 minute, add the 6-ditertbutylparacresol, after fully mixing, with above-mentioned material a, mix, ball milling, dry, cross the 60-80 mesh sieve, obtain described compounded mix.
A kind of preparation method of metal powder coating comprises the following steps:
Above-mentioned commercial magnesium calcium slag, ceramic ground-slag end are mixed with clorafin, at 60-100 ℃ of lower stirring heating 10-12 minute, add silver powder, aluminium powder, fully stir, with each raw material of residue, mix, by mixing extrusion in forcing machine, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described metal powder coating.
Advantage of the present invention is:
Powder coating coating film gloss degree of the present invention is good, and decorative effect is strong, and surperficial strong resistance is good to the adaptability of environment, and being coated in meter case can play a very good protection.
Embodiment
Embodiment 1,
A kind of metal powder coating, it is comprised of the raw material of following weight parts (kilogram):
Epoxy resin E12 60, commercial magnesium calcium slag 5, light calcium carbonate 6, two gaseous oxidation silicon 0.3, polyacrylamide 6, ceramic ground-slag end 3, aluminium powder 3, two propylene triamines 10, silver powder 1, phenoxybenzamine base ether 1, clorafin 4, compounded mix 10;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 45, fluorapatite 10, Fluorspar Powder 5, aluminium hydroxide 3, vanadium diboride 2,2,6-ditertbutylparacresol 1, cetomacrogol 1000 3;
Above-mentioned laterite, fluorapatite, Fluorspar Powder are mixed, and under 700 ℃, calcining is 4 hours, after discharging is cooling, with vanadium diboride, mixes, and fully ball milling, must expect a; Above-mentioned cetomacrogol 1000 is joined in 4 times of water, be heated to 40 ℃, fully stir, add aluminium hydroxide, 200 rev/mins of dispersed with stirring 3 minutes, add the 6-ditertbutylparacresol, mixes ball milling after fully mixing with above-mentioned material a, dry, cross 80 mesh sieves, obtain described compounded mix.
A kind of preparation method of metal powder coating comprises the following steps:
Above-mentioned commercial magnesium calcium slag, ceramic ground-slag end are mixed with clorafin, 100 ℃ of lower stirring heating 12 minutes, add silver powder, aluminium powder, fully stir, with each raw material of residue, mix, by mixing extrusion in forcing machine, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described metal powder coating.
Performance test:
Shock resistance: >=50kg/cm;
Hardness >=2H.
Claims (2)
1. a metal powder coating is characterized in that what it was comprised of the raw material of following weight parts:
Epoxy resin E12 50-60, commercial magnesium calcium slag 4-5, light calcium carbonate 4-6, two gaseous oxidation silicon 0.2-0.3, polyacrylamide 6-8, ceramic ground-slag end 3-6, aluminium powder 2-3, two propylene triamine 4-10, silver powder 0.4-1, phenoxybenzamine base ether 1-2, clorafin 2-4, compounded mix 5-10;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 30-45, fluorapatite 5-10, Fluorspar Powder 3-5, aluminium hydroxide 3-4, vanadium diboride 1-2,2,6-ditertbutylparacresol 1-2, cetomacrogol 1000 2-3;
Above-mentioned laterite, fluorapatite, Fluorspar Powder are mixed, and calcining 3-4 hour under 600-700 ℃, mix with vanadium diboride after discharging is cooling, and fully ball milling, must expect a; Above-mentioned cetomacrogol 1000 is joined in 4-5 times of water, be heated to 30-40 ℃, fully stir, add aluminium hydroxide, 100-200 rev/min of dispersed with stirring 3-4 minute, add the 6-ditertbutylparacresol, after fully mixing, with above-mentioned material a, mix, ball milling, dry, cross the 60-80 mesh sieve, obtain described compounded mix.
2. the preparation method of a metal powder coating as claimed in claim 1 is characterized in that comprising the following steps:
Above-mentioned commercial magnesium calcium slag, ceramic ground-slag end are mixed with clorafin, at 60-100 ℃ of lower stirring heating 10-12 minute, add silver powder, aluminium powder, fully stir, with each raw material of residue, mix, by mixing extrusion in forcing machine, then after the compressing tablet fragmentation, pulverize, sieve through pulverising mill again, obtain described metal powder coating.