CN103496904A - Masonry insulating mortar dry material for wall - Google Patents
Masonry insulating mortar dry material for wall Download PDFInfo
- Publication number
- CN103496904A CN103496904A CN201310439251.5A CN201310439251A CN103496904A CN 103496904 A CN103496904 A CN 103496904A CN 201310439251 A CN201310439251 A CN 201310439251A CN 103496904 A CN103496904 A CN 103496904A
- Authority
- CN
- China
- Prior art keywords
- under
- take out
- minute
- parts
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a masonry insulating mortar dry material for a wall. The masonry insulating mortar dry material is prepared form the following raw materials in parts by weight: 8-10 parts of ceramic sands, 380-450 parts of cement, 70-90 parts of glass beads, 5-8 parts of water soluble phenolic resin, 20-25 parts of modified kaolin, 1-2 parts of graphene oxide, 1.3-3.2 parts of sodium aluminate and 1-2 parts of fatty alcohol-polyoxyethylene ether.
Description
Technical field
The present invention relates to the thermal insulation mortar field, is exactly a kind of wall body placing heat-insulating mortar dry material.
Background technology
Inorganic heat insulation mortar (glass bead fireproof heat insulating mortar; complex silicate aluminium thermal insulation mortar) be a kind of mortar material of the novel heat-preserving energy-saving for external rendering in buildings; using inorganic glass bead (claiming again closed-cell expanded perlite) as light skeletal, add the dry-mix formed by gelling material, anticrack additive and other stopping composition etc.There are antifreeze, the ageing-resistant excellent properties of energy-conserving profit waste, heat insulating, fire prevention and the cheap characteristics such as price, the market requirement is widely arranged.
Summary of the invention
The object of the present invention is to provide a kind of wall body placing heat-insulating mortar dry material.
Above-mentioned purpose realizes by following scheme:
A kind of wall body placing heat-insulating mortar dry material is characterized in that: it is that raw material by following weight parts makes: pottery sand 8-10, cement 380-450, glass bead 70-90, water soluble phenol resin 5-8, modified kaolin 20-25, graphene oxide 1-2, sodium aluminate 1.3-3.2, fatty alcohol-polyoxyethylene ether 1-2;
Described modified kaolin is made by the raw material of following weight part:
Kaolin 20-25, fluorite slag 7-12, maize straw 3-5, sisal fibers 1-2, aluminium nitride 1-2, dimethyl tin oxide 1-2, silane coupling agent KH5300.4-0.6, rapeseed cake 1-2, dioctyl maleate 1-2, magnesium oxide 1-2, starch 1-2;
The preparation method of described modified kaolin is: by after maize straw, the fragmentation of fluorite slag, cross the 200-400 mesh sieve, calcine 4-5 hour after taking-up under 700-750 ℃, take out, soak 8-12 hour in the hydrogen peroxide that is 1-3% in concentration, take out, dry, after mixing with sisal fibers, aluminium nitride again, add in suitable quantity of water and grind, then mix with other surplus stock, under 100-300r/min, stir after 5-10 minute, in kneader, under 60-70 ℃, insulation, after 20-25 minute, is taken out, and obtains.
Described a kind of wall body placing heat-insulating mortar dry material is characterized in that:
The preparation method is:
(1) get in the hydrogen peroxide that pottery sand is 1-2% in concentration and soak 7-8 hour, take out, deionized water wash, dry, add again the clay that is equivalent to its weight 1-2%, the boron nitride of 0.5-0.8% and appropriate water, under 100-200 rev/min, stir after 10-15 minute, add the water glass that is equivalent to its weight 0.5-1.2%, the butadiene-styrene latex of 1-2%, after mixing, granulation, the balling-up particle diameter is at 0.7-1.2mm, then fire 1.8-2.5 hour under 200-300 ℃ after, take out coolingly, obtain the modification haydite standby;
(2) modification haydite, glass bead are mixed by weight; stir 3-5 minute under 100-200 rev/min; take out; again with the whole raw material blendings of residue after, 100-200 rev/min is at the uniform velocity stirred 20-30 minute, then the material three-roll grinder that is stirred is ground to 1.8-2.5 hour; be incubated again 10-15 minute under 50-60 ℃; take out, cooling, after packing and get final product.
Beneficial effect of the present invention is: this heat-insulating mortar dry material thermal conductivity is low, can avoid the generation of the hot and cold bridge of building block seam crossing, thereby effectively forms the self-heat conserving effect of masonry panel, simultaneously, this heat-insulating mortar dry material is nontoxic, pollution-free, and the life-span is long, water-proofing anticracking.
Embodiment
A kind of wall body placing heat-insulating mortar dry material, it is that raw material by following weight Kg makes:
Pottery sand 10, cement 450, glass bead 90, water soluble phenol resin 8, modified kaolin 25, graphene oxide 1, sodium aluminate 2.2, fatty alcohol-polyoxyethylene ether 2;
Described modified kaolin is made by the raw material of following weight kg:
Kaolin 22, fluorite slag 10, maize straw 5, sisal fibers 1, aluminium nitride 1, dimethyl tin oxide 2, silane coupling agent KH5300.5, rapeseed cake 2, dioctyl maleate 1, magnesium oxide 2, starch 2;
The preparation method of described modified kaolin is: by after maize straw, the fragmentation of fluorite slag, cross 400 mesh sieves, calcine 5 hours under 700 ℃ after taking-up, take out, soak 8 hours in the hydrogen peroxide that is 2% in concentration, take out, dry, after mixing with sisal fibers, aluminium nitride again, add in suitable quantity of water and grind, then mix with other surplus stock, under 200r/min, stir after 8 minutes, in kneader, under 65 ℃, insulation, after 20 minutes, is taken out, and obtains.
Described a kind of wall body placing heat-insulating mortar dry material, the preparation method is:
(1) get in the hydrogen peroxide that pottery sand is 2% in concentration and soak 8 hours, take out deionized water wash, dry, add again the clay that is equivalent to its weight 1.5%, 0.8% boron nitride and appropriate water, stir after 12 minutes under 200 rev/mins, add the water glass that is equivalent to its weight 0.8%, 2% butadiene-styrene latex, after mixing, granulation, the balling-up particle diameter is at 0.7-1.2mm, then fire 2 hours under 300 ℃ after, take out coolingly, obtain the modification haydite standby;
(2) by modification haydite, glass bead by weight proportion kg mix; under 200 rev/mins, stir 5 minutes; take out; again with the whole raw material blendings of residue after, 100 rev/mins are at the uniform velocity stirred 30 minutes, then the material three-roll grinder that is stirred is ground 2.5 hours; be incubated 15 minutes again under 60 ℃; take out, cooling, after packing and get final product.
The products obtained therefrom test result is as follows:
Claims (2)
1. a wall body placing heat-insulating mortar dry material is characterized in that: it is that raw material by following weight parts makes:
Pottery sand 8-10, cement 380-450, glass bead 70-90, water soluble phenol resin 5-8, modified kaolin 20-25, graphene oxide 1-2, sodium aluminate 1.3-3.2, fatty alcohol-polyoxyethylene ether 1-2;
Described modified kaolin is made by the raw material of following weight part:
Kaolin 20-25, fluorite slag 7-12, maize straw 3-5, sisal fibers 1-2, aluminium nitride 1-2, dimethyl tin oxide 1-2, silane coupling agent KH530 0.4-0.6, rapeseed cake 1-2, dioctyl maleate 1-2, magnesium oxide 1-2, starch 1-2;
The preparation method of described modified kaolin is: by after maize straw, the fragmentation of fluorite slag, cross the 200-400 mesh sieve, calcine 4-5 hour after taking-up under 700-750 ℃, take out, soak 8-12 hour in the hydrogen peroxide that is 1-3% in concentration, take out, dry, after mixing with sisal fibers, aluminium nitride again, add in suitable quantity of water and grind, then mix with other surplus stock, under 100-300r/min, stir after 5-10 minute, in kneader, under 60-70 ℃, insulation, after 20-25 minute, is taken out, and obtains.
2. a kind of wall body placing heat-insulating mortar dry material according to claim 1 is characterized in that:
The preparation method is:
(1) get in the hydrogen peroxide that pottery sand is 1-2% in concentration and soak 7-8 hour, take out, deionized water wash, dry, add again the clay that is equivalent to its weight 1-2%, the boron nitride of 0.5-0.8% and appropriate water, under 100-200 rev/min, stir after 10-15 minute, add the water glass that is equivalent to its weight 0.5-1.2%, the butadiene-styrene latex of 1-2%, after mixing, granulation, the balling-up particle diameter is at 0.7-1.2mm, then fire 1.8-2.5 hour under 200-300 ℃ after, take out coolingly, obtain the modification haydite standby;
(2) modification haydite, glass bead are mixed by weight; stir 3-5 minute under 100-200 rev/min; take out; again with the whole raw material blendings of residue after, 100-200 rev/min is at the uniform velocity stirred 20-30 minute, then the material three-roll grinder that is stirred is ground to 1.8-2.5 hour; be incubated again 10-15 minute under 50-60 ℃; take out, cooling, after packing and get final product.