CN103496883B - A kind of parian substrate and preparation method thereof - Google Patents
A kind of parian substrate and preparation method thereof Download PDFInfo
- Publication number
- CN103496883B CN103496883B CN201310444112.1A CN201310444112A CN103496883B CN 103496883 B CN103496883 B CN 103496883B CN 201310444112 A CN201310444112 A CN 201310444112A CN 103496883 B CN103496883 B CN 103496883B
- Authority
- CN
- China
- Prior art keywords
- weight parts
- resin
- parian
- substrate
- weighting agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to parian matrix technique field, provide a kind of preparation technology simple, without the need to the preparation method of the parian substrate of vacuum pressing mold, mainly comprise: (1) top layer is solidified; (2) middle layer raw material is added: (3) add bottom raw material.The parian substrate utilizing the method to obtain has the dynamic effect of ink cloud, stereoscopic sensation is strong, practical and attractive, price is lower relative to marble, described parian substrate comprises top layer, bottom and the middle layer be located between the two, described skin-material component comprises the resin of 100 weight parts, the solidifying agent of 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts, described interlayer material components comprises the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts, described primer component comprises the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part.
Description
Technical field
The present invention relates to parian matrix technique field, particularly relate to a kind of parian substrate and preparation method thereof.
Background technology
Natural marble material, due to the impact by the factor such as country of origin, output, makes the raw-material price of natural marble can not be in any more.Simultaneously because the raw-material hardness of natural marble is very high, make processing, just more difficult when being engraved as product, thus the cost of the course of processing adopting natural marble starting material decorated articles is improved, directly enhance the price of whole natural marble starting material decorated articles.Expensive price makes general common people not accept, and is not suitable for batch production.From the angle of environmental protection, natural marble starting material decorated articles is all very heavy, not easily installs, and has certain radiativity, be unfavorable for the health of human body.Therefore, a kind of parian goods of exploitation are badly in need of in order to meet market demand.
Parian goods on existing market all need the process of vacuum pressing mold in preparation process, can obtain the good product of stereoeffect, and its preparation technology's more complicated.
Summary of the invention
Therefore, for above content, the invention provides a kind of preparation technology simple, without the need to the preparation method of the parian substrate of vacuum pressing mold, the parian substrate utilizing the method to obtain has the dynamic effect of ink cloud, stereoscopic sensation is strong, and practical and attractive, price is lower relative to marble.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of parian substrate, the middle layer comprising top layer, bottom and be located between the two, described skin-material component comprises the resin of 100 weight parts, the solidifying agent of 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts, described interlayer material components comprises the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts, and described primer component comprises resin, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part of 33 ~ 35 weight parts.
Further improvement is: described skin-material component comprises the resin of 100 weight parts, the solidifying agent of 15 weight parts, the promotor of 3 weight parts, described interlayer material components comprises the resin of 50 weight parts, the weighting agent of 50 weight parts, and described primer component comprises resin, the weighting agent of 67 weight parts, the mill base of 0.22 weight part of 33 weight parts.
Further improvement is: described resin is vibrin or epoxy resin.
Further improvement is: described weighting agent is aluminium hydroxide or Paris white.
Further improvement is: described aluminium hydroxide and Paris white are 220 ~ 250 object fine powders.
A preparation method for parian substrate, comprises following processing step:
(1) top layer solidification: the solidifying agent of the resin of 100 weight parts, 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts are put into mould and stirred, at room temperature solidifies;
(2) middle layer raw material is added: the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts are added in top layer after hardening, stir;
(3) bottom raw material is added: after step (2) stirs, add the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part immediately, at room temperature shaping, namely obtain parian substrate after die sinking.
Further improvement is: the resin in described step (1), (2), (3) is vibrin or epoxy resin.
By adopting preceding solution, the invention has the beneficial effects as follows: the present invention adopts specific formula, skin-material component comprises the resin of 100 weight parts, the solidifying agent of 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts, interlayer material components comprises the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts, primer component comprises the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part, first top layer is solidified during preparation, then middle layer raw material is added, bottom raw material is added immediately after stirring, transparent structural sheet is formed after the solidification of top layer, middle layer and bottom are owing to defining concentration difference, and bottom be middle layer add stir after add rapidly, the parian substrate obtained is made to have the dynamic effect of ink cloud, stereoscopic sensation is strong, vacuum pressing mold is not needed in preparation method of the present invention, rely on the concentration difference of middle layer and bottom can form the good parian substrate of stereoscopic sensation, preparation technology is simple, product is attractive in appearance, marble can be replaced to use, can be mass, application and finishing material industry, larger Financial cost can be saved, be applicable to extensively promoting the use of.
Embodiment
Describe embodiments of the present invention in detail below with reference to specific embodiment, to the present invention, how utilisation technology means solve technical problem whereby, and the implementation procedure reaching technique effect can fully understand and implement according to this.
If do not specialize, the conventional means that the technique means adopted in embodiment is well known to those skilled in the art, the reagent adopted and product be also can business obtain.Source, the trade(brand)name of agents useful for same and be necessary to list its moiety person, all indicate when occurring first.
Embodiment one
A kind of parian substrate, the middle layer comprising top layer, bottom and be located between the two, described skin-material component comprises the vibrin of 100 weight parts, the solidifying agent of 13 weight parts, the promotor of 2 weight parts, described interlayer material components comprises the vibrin of 45 weight parts, the aluminium hydroxide (220 order) of 50 weight parts, and described primer component comprises vibrin, the aluminium hydroxide (220 order) of 66 weight parts, the mill base of 0.2 weight part of 34 weight parts.
Its preparation method, comprises following processing step:
(1) top layer solidification: the solidifying agent of the resin of 100 weight parts, 13 weight parts, the promotor of 2 weight parts are put into mould and stirred, at room temperature solidifies;
(2) middle layer raw material is added: the vibrin of 45 weight parts, the aluminium hydroxide (220 order) of 50 weight parts are added in top layer after hardening, stir;
(3) bottom raw material is added: after step (2) stirs, add the vibrin of 34 weight parts, the aluminium hydroxide (220 order) of 66 weight parts, the mill base of 0.2 weight part immediately, at room temperature shaping, namely obtain parian substrate after die sinking.
Embodiment two
A kind of parian substrate, the middle layer comprising top layer, bottom and be located between the two, described skin-material component comprises the epoxy resin of 100 weight parts, the solidifying agent of 15 weight parts, the promotor of 3 weight parts, described interlayer material components comprises the epoxy resin of 50 weight parts, the aluminium hydroxide (230 order) of 50 weight parts, and described primer component comprises epoxy resin, the aluminium hydroxide (230 order) of 67 weight parts, the mill base of 0.22 weight part of 33 weight parts.
Its preparation method, comprises following processing step:
(1) top layer solidification: the solidifying agent of the epoxy resin of 100 weight parts, 15 weight parts, the promotor of 3 weight parts are put into mould and stirred, at room temperature solidifies;
(2) middle layer raw material is added: the epoxy resin of 50 weight parts, the aluminium hydroxide (230 order) of 50 weight parts are added in top layer after hardening, stir;
(3) bottom raw material is added: after step (2) stirs, add the epoxy resin of 33 weight parts, the aluminium hydroxide (230 order) of 67 weight parts, the mill base of 0.22 weight part immediately, at room temperature shaping, namely obtain parian substrate after die sinking.
Embodiment three
A kind of parian substrate, the middle layer comprising top layer, bottom and be located between the two, described skin-material component comprises the vibrin of 100 weight parts, the solidifying agent of 16 weight parts, the promotor of 8 weight parts, described interlayer material components comprises the vibrin of 50 weight parts, the aluminium hydroxide (250 order) of 55 weight parts, and described primer component comprises vibrin, the aluminium hydroxide (250 order) of 65 weight parts, the mill base of 0.25 weight part of 35 weight parts.
Its preparation method, comprises following processing step:
(1) top layer solidification: the solidifying agent of the vibrin of 100 weight parts, 16 weight parts, the promotor of 8 weight parts are put into mould and stirred, at room temperature solidifies;
(2) middle layer raw material is added: the vibrin of 50 weight parts, the aluminium hydroxide (250 order) of 55 weight parts are added in top layer after hardening, stir;
(3) bottom raw material is added: after step (2) stirs, add the vibrin of 35 weight parts, the aluminium hydroxide (250 order) of 65 weight parts, the mill base of 0.25 weight part immediately, at room temperature shaping, namely obtain parian substrate after die sinking.
Wherein, in the present invention, the consumption of the solidifying agent on top layer is the promotor of consumption 2 ~ 8 weight part of 13 ~ 16 weight parts, promotor, the resin demand in middle layer at the consumption of 45 ~ 50 weight parts, weighting agent at 50 ~ 55 weight parts, resin demand in bottom at the consumption of 33 ~ 35 weight parts, weighting agent at the consumption of 65 ~ 67 weight parts, mill base at 0.2 ~ 0.25 weight part, all can realize object of the present invention.Described resin is vibrin or epoxy resin preferably, the resin that other performances are close also can use, described weighting agent preferably aluminium hydroxide, the articles for use of the done weighting agent that other functions are close, as calcium carbonate, also aluminium hydroxide can be replaced to use, and described weighting agent controls all can realize object of the present invention at 220 ~ 250 orders.
The present invention adopts specific formula, skin-material component comprises the resin of 100 weight parts, the solidifying agent of 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts, interlayer material components comprises the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts, primer component comprises the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part, first top layer is solidified during preparation, then middle layer raw material is added, bottom raw material is added immediately after stirring, transparent structural sheet is formed after the solidification of top layer, middle layer and bottom are owing to defining concentration difference, and bottom be middle layer add stir after add rapidly, the parian substrate obtained is made to have the dynamic effect of ink cloud, stereoscopic sensation is strong, vacuum pressing mold is not needed in preparation method of the present invention, rely on the concentration difference of middle layer and bottom can form the good parian substrate of stereoscopic sensation, preparation technology is simple, product is attractive in appearance, marble can be replaced to use, can be mass, application and finishing material industry, larger Financial cost can be saved, be applicable to extensively promoting the use of.
Above, be only the embodiment utilizing this origination techniques content, the modification that any those skilled in the art use this creation to do, change, all belong to the scope of the claims that this creation is advocated, and be not limited to those disclosed embodiments.
Claims (5)
1. a parian substrate, it is characterized in that: be made up of top layer, bottom and the middle layer be located between the two, described skin-material component is made up of the resin of 100 weight parts, the solidifying agent of 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts, described interlayer material components is made up of the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts, described primer component is made up of the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part, and described resin is vibrin or epoxy resin.
2. parian substrate according to claim 1, it is characterized in that: described skin-material component is made up of the resin of 100 weight parts, the solidifying agent of 15 weight parts, the promotor of 3 weight parts, described interlayer material components is made up of the resin of 50 weight parts, the weighting agent of 50 weight parts, and described primer component is made up of the resin of 33 weight parts, the weighting agent of 67 weight parts, the mill base of 0.22 weight part.
3. parian substrate according to claim 1 and 2, is characterized in that: described weighting agent is aluminium hydroxide or Paris white.
4. parian substrate according to claim 3, is characterized in that: described aluminium hydroxide and Paris white are 220 ~ 250 object fine powders.
5. a preparation method for parian substrate, is characterized in that: comprise following processing step:
(1) top layer solidification: the solidifying agent of the resin of 100 weight parts, 13 ~ 16 weight parts, the promotor of 2 ~ 8 weight parts are put into mould and stirred, at room temperature solidifies;
(2) middle layer raw material is added: the resin of 45 ~ 50 weight parts, the weighting agent of 50 ~ 55 weight parts are added in top layer after hardening, stir;
(3) bottom raw material is added: after step (2) stirs, add the resin of 33 ~ 35 weight parts, the weighting agent of 65 ~ 67 weight parts, the mill base of 0.2 ~ 0.25 weight part immediately, at room temperature shaping, namely obtain parian substrate after die sinking
;resin in step (1), (2), (3) is vibrin or epoxy resin.