CN101948282A - Cement artware and manufacturing method thereof - Google Patents
Cement artware and manufacturing method thereof Download PDFInfo
- Publication number
- CN101948282A CN101948282A CN2010102685486A CN201010268548A CN101948282A CN 101948282 A CN101948282 A CN 101948282A CN 2010102685486 A CN2010102685486 A CN 2010102685486A CN 201010268548 A CN201010268548 A CN 201010268548A CN 101948282 A CN101948282 A CN 101948282A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement industry
- industry product
- cement
- artwork
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses cement artware, which comprises the following raw material components in part by mass: 100 to 120 parts of white cement, 15 to 20 parts of ammonium chloride, 10 to 15 parts of floor glue and 30 to 40 parts of water. A manufacturing method comprises the following steps of: (1) proportioning each raw material component, uniformly mixing, and pouring the mixture into a mold; (2) curing for forming; and (3) stripping the mold, putting in the shade and curing for forming. The cement artware with low cost, light weight, high finished product forming rate and high and stable quality is prepared from low-cost raw materials by a simple process method; and the used raw materials do not cause pollution to environment and the method is an environmentally-friendly process.
Description
Technical field
The present invention relates to a kind of making method of artwork, especially a kind of cement industry product and preparation method thereof.
Background technology
The artwork of comparatively thick hair style as container, flowerpot, candlestick, ikebana etc., mostly adopts cement products in the market, and resin, metal products are main, and metal products is sayed, its weak point is the cost height, Heavy Weight; Resin is sayed its weak point is: cost is higher, become product speed slow, not environmental protection, preparation technology is complicated; Existing cement products is sayed its weak point is: preparation technology falls behind, Heavy Weight, and ratio of briquetting is low, and quality product is relatively poor.Chinese patent CN1562856A in the prior art, open day is on January 12nd, 2005, discloses a kind of cement industry product, it adopts cement 40-50%, silica 1 2-16%, silica sand 8-10%, Mierocrystalline cellulose 5-7%, water 15-20% to make.But the hardness of this product is bigger, and the ratio of briquetting of product is not high, and quality is not very desirable.
Summary of the invention
In order to overcome above defective, the technical problem to be solved in the present invention provides that a kind of cost is low, in light weight, finished product ratio of briquetting height, quality height, stay in grade cement industry product and preparation method thereof.
The technical solution adopted in the present invention is: a kind of cement industry product, and the feed composition proportioning of this artwork is:
100～120 parts of white cements,
15～20 parts of ammonium chlorides,
10～15 parts of floor glues,
30～40 parts in water.
According to another preferred embodiment, a kind of cement industry product comprise that further the optimum feed stock set of dispense ratio of this artwork is:
110 parts of white cements,
18 parts of ammonium chlorides,
12 parts of floor glues,
35 parts in water.
According to another preferred embodiment, a kind of cement industry product further comprise and can add corresponding look essence in composition according to the required color of artwork.
The invention also discloses a kind of making method of cement industry product, this method may further comprise the steps:
(1) takes by weighing each feed composition by mass fraction, mix, pour in the grinding tool;
(2) curing molding;
(3) molding is positioned over shady and cool place, the maintenance moulding.
According to another preferred embodiment, a kind of making method of cement industry product comprises that further the time of described curing molding is 24～30 hours.
According to another preferred embodiment, a kind of making method of cement industry product comprises that further described curing time is 3～7 days.
The invention has the beneficial effects as follows: the present invention utilizes cheap raw material, adopt simple processing method, prepare that cost is low, in light weight, finished product ratio of briquetting height, quality height, stay in grade cement industry product, and the raw material that uses do not pollute environment, is a kind of environment-protective process.
Embodiment
The present invention is further detailed explanation in conjunction with the preferred embodiments now.
Embodiment 1
(1) takes by weighing each feed composition by mass fraction, mix, pour in the grinding tool, in composition, add corresponding look essence according to the color that artwork is required;
100 parts of white cements,
15 parts of ammonium chlorides,
10 parts of floor glues,
30 parts in water.
(2) curing molding, the time of curing molding is 24 hours;
(3) molding is positioned over shady and cool place, and the maintenance curing time is 3 days, moulding.
Embodiment 2
(1) takes by weighing each feed composition by mass fraction, mix, pour in the grinding tool, in composition, add corresponding look essence according to the color that artwork is required;
110 parts of white cements,
18 parts of ammonium chlorides,
12 parts of floor glues,
35 parts in water.
(2) curing molding, the time of curing molding is 28 hours;
(3) molding is positioned over shady and cool place, and the maintenance curing time is 5 days, moulding.
Embodiment 3
120 parts of white cements,
20 parts of ammonium chlorides,
15 parts of floor glues,
40 parts in water.
(2) curing molding, the time of curing molding is 30 hours;
(3) molding is positioned over shady and cool place, and the maintenance curing time is 7 days, moulding.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.
Claims (6)
1. cement industry product is characterized in that the feed composition proportioning of this artwork is:
100～120 parts of white cements,
15～20 parts of ammonium chlorides,
10～15 parts of floor glues,
30～40 parts in water.
2. a kind of cement industry product according to claim 1 is characterized in that the optimum feed stock set of dispense ratio of this artwork is:
110 parts of white cements,
18 parts of ammonium chlorides,
12 parts of floor glues,
35 parts in water.
3. a kind of cement industry product according to claim 1 is characterized in that and can add corresponding look essence in composition according to the required color of artwork.
4. the making method of cement industry product is characterized in that this method may further comprise the steps:
(1) takes by weighing each feed composition by mass fraction, mix, pour in the grinding tool;
(2) curing molding;
(3) molding is positioned over shady and cool place, the maintenance moulding.
5. the making method of a kind of cement industry product according to claim 3, the time that it is characterized in that described curing molding is 24～30 hours.
6. the making method of a kind of cement industry product according to claim 3 is characterized in that described curing time is 3～7 days.