CN103496872A - 一种水泥添加剂及其制备方法 - Google Patents

一种水泥添加剂及其制备方法 Download PDF

Info

Publication number
CN103496872A
CN103496872A CN201310443529.6A CN201310443529A CN103496872A CN 103496872 A CN103496872 A CN 103496872A CN 201310443529 A CN201310443529 A CN 201310443529A CN 103496872 A CN103496872 A CN 103496872A
Authority
CN
China
Prior art keywords
parts
cement
vitriol
talcum powder
container
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310443529.6A
Other languages
English (en)
Other versions
CN103496872B (zh
Inventor
周建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liaocheng Shanshui Cement Co., Ltd
Original Assignee
JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd filed Critical JURONG LIANZHONG TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201310443529.6A priority Critical patent/CN103496872B/zh
Publication of CN103496872A publication Critical patent/CN103496872A/zh
Application granted granted Critical
Publication of CN103496872B publication Critical patent/CN103496872B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉15～22份、滑石粉8～12份、石膏粉30～38份、硫酸盐28～38份、木质素磺酸钙9～21份、二甘醇9～18份、丙烯酰胺2～4份、烷基多苷5～9份。本发明制得的产品渗入水泥少许，就能显著提高水泥的粉磨效率和水泥的抗压抗折强度。本发明渗入水泥后，水泥和水，能够形成碱性溶液，在极性水分子和活性钠离子的作用下，可以促使水泥中矿渣玻璃体结构的溶解，充分发挥水泥强矿渣的活性，从而提升水泥的强度。

Description

一种水泥添加剂及其制备方法
技术领域
本发明涉及一种水泥添加剂，具体涉及一种水泥添加剂。
背景技术
从全国水泥行业整体情况看，2010年全国水泥产量为18.68亿吨，同比增长15.5%。2011年预计新增产能约9000万吨，淘汰落后产能约1亿吨，总产能比2010年略减一些，约为22.5亿吨。从需求上看，在2011年，“4万亿刺激政策”对水泥向上的推动效应已大大减弱，但其大多数工程仍然在建，对水泥需求的支撑作用还在，而水利、高铁等建设的兴起也使水泥需求得到了一定保障。
然而一些市政工程、基础设施工程，比如铁路、公路等设施由于工程质量关乎社会公共安全，所以对水泥的各方面性能都有较高标准的要求，市面上售出的水泥很难达到这种要求，并且售价比普通水泥高出不少。
发明内容
发明目的：为了克服现有技术中存在的不足，本发明提供一种水泥添加剂。
技术方案：为实现上述目的，本发明提供的一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉15～22份、滑石粉8～12份、石膏粉30～38份、硫酸盐28～38份、木质素磺酸钙9～21份、二甘醇9～18份、丙烯酰胺2～4份、烷基多苷5～9份。
优选地，其组分原料按重量百分比包括：石灰石粉18～20份、滑石粉9～12份、石膏粉35～38份、硫酸盐32～38份、木质素磺酸钙15～21份、二甘醇15～18份、丙烯酰胺2～4份、烷基多苷5～9份。
优选地，其组分原料按重量百分比包括：石灰石粉19份、滑石粉10份、石膏粉36份、硫酸盐34份、木质素磺酸钙18份、二甘醇16份、丙烯酰胺3份、烷基多苷7份。
优选地，所述硫酸盐为硫酸钠、硫酸钾、硫酸铁、硫酸铜中的一种或者多种。
上述的水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌10～15min，使其溶液达到饱和状态；然后将溶液温度升至65～75℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌20～30min形成凝胶，再经烘干、粉碎、筛分，制得粒度为12～25mm的添加剂。
有益效果：本发明提供的水泥添加剂加到常规水泥后，相对于现有技术而言具有以下优势：
（1）本发明制得的产品渗入水泥少许，就能显著提高水泥的粉磨效率和水泥的抗压抗折强度。
（2）本发明渗入水泥后，水泥和水，能够形成碱性溶液，在极性水分子和活性钠离子的作用下，可以促使水泥中矿渣玻璃体结构的溶解，充分发挥水泥强矿渣的活性，从而提升水泥的强度。
具体实施方式
下面结合实施例对本发明作更进一步的说明。
实施例1：
一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉15份、滑石粉12份、石膏粉38份、硫酸盐38份、木质素磺酸钙21份、二甘醇18份、丙烯酰胺4份、烷基多苷9份。
上述水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌12min，使其溶液达到饱和状态；然后将溶液温度升至70℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌25min形成凝胶，再经烘干、粉碎、筛分，制得粒度为20mm的添加剂。
实施例2：
一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉22份、滑石粉8份、石膏粉30份、硫酸盐28份、木质素磺酸钙9份、二甘醇9份、丙烯酰胺2份、烷基多苷5份。
上述水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌10min，使其溶液达到饱和状态；然后将溶液温度升至75℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌30min形成凝胶，再经烘干、粉碎、筛分，制得粒度为12mm的添加剂。
实施例3：
一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉20份、滑石粉9份、石膏粉38份、硫酸盐32份、木质素磺酸钙21份、二甘醇18份、丙烯酰胺3份、烷基多苷8份。
上述水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌15min，使其溶液达到饱和状态；然后将溶液温度升至65℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌20min形成凝胶，再经烘干、粉碎、筛分，制得粒度为25mm的添加剂。
实施例4：
一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉18份、滑石粉12份、石膏粉35份、硫酸盐38份、木质素磺酸钙15份、二甘醇15份、丙烯酰胺4份、烷基多苷6份。
上述水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌15min，使其溶液达到饱和状态；然后将溶液温度升至65℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌20min形成凝胶，再经烘干、粉碎、筛分，制得粒度为25mm的添加剂。
实施例5：
一种水泥添加剂，其组分原料按重量百分比包括：石灰石粉19份、滑石粉10份、石膏粉36份、硫酸盐34份、木质素磺酸钙18份、二甘醇16份、丙烯酰胺3份、烷基多苷7份。
上述水泥添加剂的制备方法，包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌18min，使其溶液达到饱和状态；然后将溶液温度升至68℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌26min形成凝胶，再经烘干、粉碎、筛分，制得粒度为18mm的添加剂。
实施例1～5所制备的产品性能见下表：
Figure BDA0000387335640000031
Figure BDA0000387335640000041
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (5)

1.一种水泥添加剂，其特征在于：其组分原料按重量百分比包括：石灰石粉15～22份、滑石粉8～12份、石膏粉30～38份、硫酸盐28～38份、木质素磺酸钙9～21份、二甘醇9～18份、丙烯酰胺2～4份、烷基多苷5～9份。
2.根据权利要求1所述的水泥添加剂，其特征在于：其组分原料按重量百分比包括：石灰石粉18～20份、滑石粉9～12份、石膏粉35～38份、硫酸盐32～38份、木质素磺酸钙15～21份、二甘醇15～18份、丙烯酰胺2～4份、烷基多苷5～9份。
3.根据权利要求1所述的水泥添加剂，其特征在于：其组分原料按重量百分比包括：石灰石粉19份、滑石粉10份、石膏粉36份、硫酸盐34份、木质素磺酸钙18份、二甘醇16份、丙烯酰胺3份、烷基多苷7份。
4.根据权利要求1、2或者3所述的水泥添加剂，其特征在于：所述硫酸盐为硫酸钠、硫酸钾、硫酸铁、硫酸铜中的一种或者多种。
5.一种权利要求1所述的水泥添加剂的制备方法，其特征在于：包括如下步骤：
按照原料重量份计称取相应组成原料；取水放入带有搅拌装置的容器内，开动搅拌器，将二甘醇、丙烯酰胺、烷基多苷投入到容器中，加入水溶解搅拌10～15min，使其溶液达到饱和状态；然后将溶液温度升至65～75℃，将石灰石粉、滑石粉、石膏粉、硫酸盐、木质素磺酸钙混均后，加入至容器中，充分搅拌20～30min形成凝胶，再经烘干、粉碎、筛分，制得粒度为12～25mm的添加剂。
CN201310443529.6A 2013-09-25 2013-09-25 一种水泥添加剂及其制备方法 Active CN103496872B (zh)