CN1034879C - Technology for preparation of collar bottom wool fabric - Google Patents
Technology for preparation of collar bottom wool fabric Download PDFInfo
- Publication number
- CN1034879C CN1034879C CN94109073A CN94109073A CN1034879C CN 1034879 C CN1034879 C CN 1034879C CN 94109073 A CN94109073 A CN 94109073A CN 94109073 A CN94109073 A CN 94109073A CN 1034879 C CN1034879 C CN 1034879C
- Authority
- CN
- China
- Prior art keywords
- collar bottom
- wool fabric
- preparation technology
- fibre
- bottom wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to preparation technology of auxiliary material of clothing-nonwoven fabric undercollar cloth. 65 to 75% of wool fibers, 10 to 15% of viscose fibers, 5 to 15% of acrylon fibers, and 5 to 15 % of polyester fibers are made into undercollar cloth through the steps of dyeing, combination, cotton carding to form a net, needling, calendering shaping, etc. The undecollar cloth has the characteristics of large warp-wise breaking strength, large weft-wise breaking strength, exquisite and soft hand feeling, uniform thickness, etc. The stiffness can be changed as required to reach an ideal shaping effect, and the present invention is suitable for being used as cushion material of high-grade garments.
Description
The present invention relates to a kind of preparation technology who manufactures a kind of bondedfibre fabric by wool fibre, viscose, acrylic fibre, polyster fibre and nonwoven base fabric.
Along with living standards of the people improve constantly, clothes such as high-grade western-style clothes consumption quantity is very big, also seems important further as the batching of high-grade clothes collar liners such as western-style clothes.As clothes collar liner common used material the resin-bonding lining is arranged at present, it is that resin is gone up in the spraying of a kind of textiles two sides, and lining is on the clothes collar, and heating and pressurizing is finalized the design again.This resinoid adhesive lining has Boardy Feeling, easily comes unstuck, the defective of poor visual effect.Flannel also is the material as high-grade clothes collar liners such as western-style clothes, and this is a kind of textiles, and as liner, it has shrink property to a certain extent, the also poor and easy pilling of poor dimensional stability, elasticity.Application number provides a kind of preparation technique for cold-proof cashmere insulating padding that not only can make warming material but also can make gasket material for 91111495.5 Chinese patent, and it has overcome, and blending also needs heat welded in Japanese clear and a kind of fibre gasket manufacture method that 60-29182 introduces, operation is loaded down with trivial details and this fibre gasket feel lightweight flexible difference shortcoming.But this preparation technique for cold-proof cashmere insulating padding of Chinese patent is 65～75% thin cashmere 25～35% polyster fibres to be mixed become net, acupuncture three process to make through blowing rolling, comb and parallel cotton fibers prior to spinning.Because it only adopts polyster fibre and fine, soft fur cashmere is material, the blended fiber composition is too simple, so it is on the low side to be embodied in cashmere-wadded longitude and latitude fracture strength, shrinkage factor is also bigger than normal in length and breadth.Particularly cashmere-wadded only acupuncture handle, without impregnation, pressure roller, bake, post processing such as typing, the fibre gasket thickness is difficult for evenly like this, stiffness is also relatively poor, a little less than the typing ability, and the plentiful inadequately exquisiteness of feel.
The object of the present invention is to provide that a kind of outward appearance is smoothly well-pressed, good hand touch, the water-fast collar bottom wool fabric preparation technology who washes dry-cleaning, can reach desirable typing effect.
Collar bottom wool fabric preparation technology of the present invention comprises the steps:
With the wool fibre of weight 65～75%, 10～15% viscoses, 5～15% acrylic fibres, 5～15% polyster fibre through following four procedures: a mao operation is closed in a dyeing: will be after above-mentioned four kinds of stock-dyes with mix with crude oil full and uniformly after, seal hair 6～10 hours, yet bloom into the blended fiber of fluffy easy combing; Two comb and parallel cotton fibers prior to spinnings become the net operation: above-mentioned blended fiber is carded to thin fibrous web equably through combing machine for fur, enters the lapping machine, by the reciprocating motion of lapping curtain, laying is on the one-tenth lace curtaining across with fiber web, and the shop is to 10～20 layers; Three acupuncture operations: with 10～20 layers above-mentioned fiber web, sting in advance by pre-pricking machine, make the fluffy flocculus of structure, again behind thorn on the main-needling machine, the nonwoven base fabric is entered down the thorn part with fibrefill, make the nonwoven base fabric with the compound semi-finished product that become collar bottom wool fabric on the fibrefill that become entangled in of backing mode; Four calendering shaping process: with above-mentioned semi-finished product deliver to impregnation, pressure roller, bake, plating is shaped into collar bottom wool fabric, 120～160 ℃ of baking temperatures bake time 5～8min, pressure roller pressure 3～5Kg/cm
2, go out cloth speed 6～8m/min.
The wool fibre that is adopted is 60
-～64
-Fine wool, viscose is 2.5～3D * 65～75mm, acrylic fibre is 2.5～3D * 65～75mm, polyster fibre is 2.5～3D * 65～75mm.Every square decimeter 60～80 pin on the above-mentioned pre-pricking machine, every square decimeter 80～100 pin on the main-needling machine, depth of needling is controlled at 6～10mm scope, and the sizing material of impregnation is the water-soluble polypropylene acid resin, its content 12～18%, sizing material solid content 12～16%.
In sum, the blended fiber raw material that preparation technology adopted of collar bottom wool fabric of the present invention is that wool fibre, viscose, acrylic fibre, polyster fibre are multiple fibrous, can further improve the fibrefill performance, as strengthen fracture strength between the warp, latitude of collar bottom wool fabric, soft exquisiteness and high temperature resistant.The fiber web number of plies can be adjusted as required and adopt the calendering shaping process, makes the collar bottom wool fabric thickness even, and outward appearance is well-pressed, has been difficult for pleat, and resistance to water dry-cleaning and stiffness can be variable as required and reach the effect of desirable typing, is fit to make the collar gasket material of high-grade clothes such as western-style clothes.
With the collar bottom wool fabric of the present invention's preparation, to check by national military supplies product quality supervision and inspection center, its measurement result is as follows:
Wear-resisting crease recovery angle (degree) warp-wise: 156
Broadwise: 156
Fracture strength (N) warp-wise: 163.2
Broadwise: 171.5
Stiffness warp-wise: 11.1
Broadwise: 8.8
The water-fast change in size warp-wise of washing: 0.3%
Broadwise: 0.7%
Oblique: 0.7%
Embodiment:
1. with weight 75% specification 60
-～64
-Wool fibre, the viscose of 10% specification, 2.5～3D * 65～75mm, the acrylic fibre of 10% specification, 2.5～3D * 65～75mm, the polyster fibre of 5% specification, 2.5～3D * 65～75mm, close mao operation with four kinds of stock-dyes, interpolation and crude oil agent through above-mentioned first road dyeing, mix full and uniformly, sealed hair eight hours, rebloom into the blended fiber of fluffy easy combing, and control regain 14～18%, do not allow the dirty hair of hard foreign material and greasy dirt.Become the net operation that above-mentioned blended fiber is carded to thin fibrous web in the second road comb and parallel cotton fibers prior to spinning, again through the lapping machine, through the reciprocating motion of lapping curtain the fiber web intersection is stacked in on the lace curtaining, the shop requires lapping even to 15 layers, does not allow cotton knot.Yet through the 3rd road acupuncture operation, with pre-pricking machine fiber web is stung in advance, make the fluffy flocculus of structure, pre-pricking machine is 70 pins/(dm)
2, sting grammes per square metre in advance and be controlled at 190 ± 10g/m
2, behind thorn on the main-needling machine, the nonwoven base fabric being entered down the thorn part with fibrefill again, and make the nonwoven base fabric with the compound one-tenth collar bottom wool fabric semi-finished product that become entangled on the fibrefill of backing mode, main-needling machine is 90 pins/(dm)
2, main thorn grammes per square metre is controlled at 135～140g/m
2, depth of needling is controlled at 6～10mm scope, requires nonwoven base fabric and fibrefill combination stitch even, and depth unanimity is difficult for peeling off.At the 4th road calendering shaping process, above-mentioned semi-finished product to be delivered to carry out impregnation in the water-soluble polypropylene acid resin, the sizing material of impregnation is formulated as 12～18%, sizing material solid content 12～16%, and then through hydraulic pressure roll-in roller, Pressure control 3～5kg/cm
2, go out cloth speed 6～8m/min, to deliver to again and bake, 120～160 ℃ of control baking temperatures bake time 5～8min, baking the back and plating and makes the collar bottom wool fabric product, and the product mass area ratio is controlled at 130 ± 10g/m
2, amplitude 99 ± 1cm can dispatch from the factory through the side cut rolling.
2. with weight 70% specification 60
-～64
-Wool fibre, the viscose of 10% specification, 2.5～3D * 65～75mm, the acrylic fibre of 10% specification, 2.5～3D * 65～75mm, the polyster fibre of 10% specification, 2.5～3D * 65～75mm, be 10 layers with the above embodiments 1 method and lapping and make collar bottom wool fabric.
3. with weight 65% specification 60
-～64
-Wool fibre, the viscose of 5% specification, 2.5～3D * 65～75mm, the acrylic fibre of 15% specification, 2.5～3D * 65～75mm, the polyster fibre of 15% specification, 2.5～3D * 65～75mm, be 20 layers with the above embodiments 1 method and lapping and make collar bottom wool fabric.
Claims (8)
1. the preparation technology of a garment accessories bondedfibre fabric collar bottom wool fabric is characterized in that the wool fibre of weight 65～75%, 10～15% viscoses, 5～15% acrylic fibres, 5～15% polyster fibre through following four procedures:
One. a mao operation is closed in dyeing: will be after above-mentioned four kinds of stock-dyes with mix with crude oil full and uniformly after, seal maos 6～10 hours, yet bloom into the blended fiber of fluffy easy combing:
Two. comb and parallel cotton fibers prior to spinning becomes the net operation: above-mentioned blended fiber is carded to thin fibrous web equably through combing machine for fur, enters the lapping machine, by the reciprocating motion of lapping curtain, laying is on the one-tenth lace curtaining across with fiber web, and the shop is to 10～20 layers:
Three. acupuncture operation: with 10～20 layers above-mentioned fiber web, sting in advance by pre-pricking machine, make the fluffy flocculus of structure, again behind thorn on the main-needling machine, the nonwoven base fabric is entered down the thorn part with fibrefill, makes the nonwoven base fabric with the compound semi-finished product that become entangled on the fibrefill collar bottom wool fabric of backing mode:
Four. the calendering shaping process: with above-mentioned semi-finished product deliver to impregnation, pressure roller, bake, plating is shaped into collar bottom wool fabric, 120～160 ℃ of its described baking temperatures. the time of baking is 5～8min, pressure roller pressure 3～5Kg/cm
2, go out cloth speed 6～8m/min.
2. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that the wool fibre that is adopted is 60
-～64
-Fine wool.
3. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that the viscose that is adopted is the viscose of 2.5～3D * 65～75mm.
4. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that the acrylic fibre that is adopted is the acrylic fibre of 2.5～3D * 65～75mm
5. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that the polyster fibre that adopts is the polyster fibre of 2.5～3D * 65～75mm.
6. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that every square decimeter 60～80 pin on the described pre-pricking machine
7. the preparation technology of collar bottom wool fabric according to claim 1 is characterized in that every square decimeter 80～100 pin on the described main-needling machine, and depth of needling is controlled at 6～10mm scope.
8. the preparation technology of collar bottom wool fabric according to claim 1, the sizing material that it is characterized in that described impregnation is the water-soluble polypropylene acid resin, its content 12～18%, sizing material solid content 12～16%.