CN103484865B - A kind of medal polish anti-corrosive pulp - Google Patents
A kind of medal polish anti-corrosive pulp Download PDFInfo
- Publication number
- CN103484865B CN103484865B CN201310434220.0A CN201310434220A CN103484865B CN 103484865 B CN103484865 B CN 103484865B CN 201310434220 A CN201310434220 A CN 201310434220A CN 103484865 B CN103484865 B CN 103484865B
- Authority
- CN
- China
- Prior art keywords
- medal polish
- kilogram
- corrosive pulp
- polish anti
- corrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of medal polish anti-corrosive pulp of the present invention, this slurry contains the aluminum oxide polishing powder of 10 ~ 30wt%, the APTES of 1 ~ 5wt%, the stearic acid of 0.1 ~ 3wt%, the glycerol of 1 ~ 2wt%, the Manganse Dioxide of 0.1 ~ 1wt%, the phosphoric acid of 0.1 ~ 1wt%, 0.1 ~ 0.5wt% tensio-active agent, surplus is water.Adopt medal polish anti-corrosive pulp of the present invention while completing metal surface polishing, form layer protecting film in metallic surface and prevent corrosion of metal.
Description
Technical field
The present invention relates to a kind of for metal surface polishing rot-resistant slurry.
Background technology
In use inevitably there is corrosion to a certain degree in metal, every year because of corrosion cause a large amount of financial losses.Before anti-corrosive treatment is carried out to metal, generally need the zone of oxidation of metal to remove, usually need multistep operation just can complete anticorrosion.
Summary of the invention
The object of this invention is to provide a kind of medal polish anti-corrosive pulp.
To achieve these goals, the invention provides following technical scheme:
A kind of medal polish anti-corrosive pulp, aluminum oxide polishing powder containing 10 ~ 30wt%, the APTES of 1 ~ 5wt%, the stearic acid of 0.1 ~ 3wt%, the glycerol of 1 ~ 2wt%, the Manganse Dioxide of 0.1 ~ 1wt%, the phosphoric acid of 0.1 ~ 1wt%, 0.1 ~ 0.5wt% tensio-active agent, surplus is water.
Further, the particle diameter of described aluminum oxide polishing powder is 4 ~ 50 μm.
Further, described tensio-active agent is sodium laurylsulfonate or polyoxyethylene nonylphenol ether NP-10.
Adopt medal polish anti-corrosive pulp of the present invention while completing metal surface polishing, layer protecting film can be formed in metallic surface and prevent corrosion of metal.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
Embodiment 1
A kind of medal polish anti-corrosive pulp, by 1 kilogram of aluminum oxide polishing powder, (particle diameter is the α-Al of 4 ~ 15 μm
2o
3), the APTES of 0.1 kilogram, the stearic acid of 0.2 kilogram, the glycerol of 0.1 kilogram, the Manganse Dioxide of 0.01 kilogram, the phosphoric acid of 0.01 kilogram, the water of the sodium laurylsulfonate of 0.01 kilogram and 8.57 kilograms, ground and mixed evenly after obtain.
Embodiment 2
A kind of medal polish anti-corrosive pulp, by 2 kilograms of aluminum oxide polishing powders, (particle diameter is the α-Al of 10 ~ 25 μm
2o
3), the APTES of 0.3 kilogram, the stearic acid of 0.3 kilogram, the glycerol of 0.1 kilogram, the Manganse Dioxide of 0.1 kilogram, the phosphoric acid of 0.1 kilogram, the water of the sodium laurylsulfonate of 0.05 kilogram and 7.05 kilograms, ground and mixed evenly after obtain.
Embodiment 3
A kind of medal polish anti-corrosive pulp, by 3 kilograms of aluminum oxide polishing powders, (particle diameter is the α-Al of 25 ~ 50 μm
2o
3), the APTES of 0.5 kilogram, the stearic acid of 0.01 kilogram, the glycerol of 0.2 kilogram, the Manganse Dioxide of 0.05 kilogram, the phosphoric acid of 0.05 kilogram, the water of polyoxyethylene nonylphenol ether NP-10 and 6.16 kilogram of 0.03 kilogram, obtains after ground and mixed is even.
The use of this medal polish anti-corrosive pulp, uses spray gun to be sprayed pending iron or aluminum metal utensil by slurry, after showing metalluster, places 10 ~ 20 minutes, then rinse with water to utensil.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. a medal polish anti-corrosive pulp, aluminum oxide polishing powder containing 10 ~ 30wt%, the APTES of 1 ~ 5wt%, the stearic acid of 0.1 ~ 3wt%, the glycerol of 1 ~ 2wt%, the Manganse Dioxide of 0.1 ~ 1wt%, the phosphoric acid of 0.1 ~ 1wt%, 0.1 ~ 0.5wt% tensio-active agent, surplus is water, and described tensio-active agent is sodium laurylsulfonate or polyoxyethylene nonylphenol ether NP-10.
2. medal polish anti-corrosive pulp according to claim 1, is characterized in that, the particle diameter of described aluminum oxide polishing powder is 4 ~ 50 μm.