CN103484199A - 一种防锈油 - Google Patents
一种防锈油 Download PDFInfo
- Publication number
- CN103484199A CN103484199A CN201310362691.5A CN201310362691A CN103484199A CN 103484199 A CN103484199 A CN 103484199A CN 201310362691 A CN201310362691 A CN 201310362691A CN 103484199 A CN103484199 A CN 103484199A
- Authority
- CN
- China
- Prior art keywords
- oil
- parts
- base oil
- stirring
- coalescence aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防锈油,它是由下述重量份的原料组成的:0#轻柴油30-40、100SN基础油20-30、500SN基础油20-25、丙酮1-2、癸酸1-2、六甲氧甲基三聚氰胺树脂3-4、二烷基二硫代磷酸锌0.6-1、烷基二苯胺1-2、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、成膜助剂3-5;本发明的防锈油具有很好的抗湿热、耐水、耐盐雾、耐腐蚀、抗紫外线等性能,加入的成膜助剂改善了成膜效果,增强了涂膜的稳定持久性,能够应用在各种金属工件表面,可以起到很好的防锈保护作用。
Description
技术领域
本发明主要涉及一种防锈剂,尤其涉及一种防锈油。
背景技术
在金属加工行业,由于工件从毛坯到成品,中间要经过多个工序,由于储备用或者短期内无法进行下一道工序的加工,因此要将其放在仓库中保存,在库存过程中,金属会因为周围不同的环境,或多或少的遭到腐蚀,腐蚀后会影响其本身的特性以及妨碍其后续加工或使用,每年由于金属腐蚀造成的损失是巨大的,防护的意义尤为重要。
为避免锈蚀、减少损失,人们采用了各种各样的方法,用防锈油脂来保护金属紧固件,便是目前最常见的防护方法之一。
防锈油脂是在石油类基本组分中加入一种或多种防锈添加剂(又称油溶性缓蚀剂)及其辅助添加剂组成,它使用方便,成本低廉,效果好,操作简单,紧固件行业都在大量使用。
发明内容
本发明目的就是提供一种防锈油。
本发明是通过以下技术方案实现的:
一种防锈油,它是由下述重量份的原料组成的:
0#轻柴油30-40、100SN基础油20-30、500SN基础油20-25、丙酮1-2、癸酸1-2、六甲氧甲基三聚氰胺树脂3-4、二烷基二硫代磷酸锌0.6-1、烷基二苯胺1-2、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、成膜助剂3-5;
所述的成膜助剂是由下述重量份的原料组成的:
十二烯基丁二酸10-14、虫胶树脂1-2、双硬脂酸铝6-7、丙二醇甲醚醋酸酯6-8、乙二醇单乙醚0.2-0.3、霍霍巴油0.3-0.4;
将上述双硬脂酸铝加热到80-90℃,加入丙二醇甲醚醋酸酯,充分搅拌后降低温度为60-70℃,加入乙二醇单乙醚,300-400转/分搅拌分散4-6分钟,得预混料;将上述十二烯基丁二酸与虫胶树脂在80-100℃下混合,搅拌均匀后加入到上述预混料中,充分搅拌后,加入霍霍巴油,冷却至常温,即得所述成膜助剂。
一种防锈油的制备方法,包括以下步骤:
将上述0#轻柴油、100SN基础油、500SN基础油混合,加热到110-140℃,加入癸酸、六甲氧甲基三聚氰胺树脂,搅拌冷却至75-80℃,加入丙酮、烷基二苯胺、成膜助剂,搅拌冷却至60-65℃,加入剩余各原料,脱水,保温搅拌3-4 小时,降低温度至35-40℃,过滤,即得所述防锈油。
本发明的优点是:
本发明的防锈油具有很好的抗湿热、耐水、耐盐雾、耐腐蚀、抗紫外线等性能,加入的成膜助剂改善了成膜效果,增强了涂膜的稳定持久性,能够应用在各种金属工件表面,可以起到很好的防锈保护作用。
具体实施方式
实施例1
一种防锈油,它是由下述重量份(公斤)的原料组成的:
0#轻柴油40、100SN基础油30、500SN基础油25、丙酮1、癸酸1、六甲氧甲基三聚氰胺树脂3、二烷基二硫代磷酸锌0.6、烷基二苯胺1、二硬脂酰氧异丙氧基铝酸酯0.2、成膜助剂3;
所述的成膜助剂是由下述重量份的原料组成的:
十二烯基丁二酸14、虫胶树脂1、双硬脂酸铝6、丙二醇甲醚醋酸酯8、乙二醇单乙醚0.3、霍霍巴油0.4;
将上述双硬脂酸铝加热到90℃,加入丙二醇甲醚醋酸酯,充分搅拌后降低温度为70℃,加入乙二醇单乙醚,400转/分搅拌分散6分钟,得预混料;将上述十二烯基丁二酸与虫胶树脂在100℃下混合,搅拌均匀后加入到上述预混料中,充分搅拌后,加入霍霍巴油,冷却至常温,即得所述成膜助剂。
一种防锈油的制备方法,包括以下步骤:
将上述0#轻柴油、100SN基础油、500SN基础油混合,加热到140℃,加入癸酸、六甲氧甲基三聚氰胺树脂,搅拌冷却至80℃,加入丙酮、烷基二苯胺、成膜助剂,搅拌冷却至65℃,加入剩余各原料,脱水,保温搅拌4 小时,降低温度至40℃,过滤,即得所述防锈油。
性能测试:
湿热试验:20天,结果:10# 钢合格、T3铜合格;
腐蚀试验:7天,结果:10# 钢合格、T3铜合格;
盐雾试验:7天,10# 钢合格、T3铜合格。
Claims (2)
1.一种防锈油,其特征在于它是由下述重量份的原料组成的:
0#轻柴油30-40、100SN基础油20-30、500SN基础油20-25、丙酮1-2、癸酸1-2、六甲氧甲基三聚氰胺树脂3-4、二烷基二硫代磷酸锌0.6-1、烷基二苯胺1-2、二硬脂酰氧异丙氧基铝酸酯0.1-0.2、成膜助剂3-5;
所述的成膜助剂是由下述重量份的原料组成的:
十二烯基丁二酸10-14、虫胶树脂1-2、双硬脂酸铝6-7、丙二醇甲醚醋酸酯6-8、乙二醇单乙醚0.2-0.3、霍霍巴油0.3-0.4;
将上述双硬脂酸铝加热到80-90℃,加入丙二醇甲醚醋酸酯,充分搅拌后降低温度为60-70℃,加入乙二醇单乙醚,300-400转/分搅拌分散4-6分钟,得预混料;将上述十二烯基丁二酸与虫胶树脂在80-100℃下混合,搅拌均匀后加入到上述预混料中,充分搅拌后,加入霍霍巴油,冷却至常温,即得所述成膜助剂。
2.一种如权利要求1所述的防锈油的制备方法,其特征在于包括以下步骤:
将上述0#轻柴油、100SN基础油、500SN基础油混合,加热到110-140℃,加入癸酸、六甲氧甲基三聚氰胺树脂,搅拌冷却至75-80℃,加入丙酮、烷基二苯胺、成膜助剂,搅拌冷却至60-65℃,加入剩余各原料,脱水,保温搅拌3-4 小时,降低温度至35-40℃,过滤,即得所述防锈油。