CN103483858A - 一种颜料橙71微胶囊的制备方法 - Google Patents
一种颜料橙71微胶囊的制备方法 Download PDFInfo
- Publication number
- CN103483858A CN103483858A CN201310424913.1A CN201310424913A CN103483858A CN 103483858 A CN103483858 A CN 103483858A CN 201310424913 A CN201310424913 A CN 201310424913A CN 103483858 A CN103483858 A CN 103483858A
- Authority
- CN
- China
- Prior art keywords
- pigment orange
- parts
- preparation
- microcapsule
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种颜料橙71微胶囊的制备方法,制备方法包括以下步骤:(1)将颜料橙71粉末使用超微冲击磨研磨至450目~500目;(2)室温下向恒温搅拌罐中加入正己烷为90~110份;(3)取450目~500目的颜料橙71为9~14份,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为18~22份,聚乙二醇为15~17份,加入后进行搅拌,搅拌转速为100rpm,时间为3~5min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。颜料橙71微胶囊的制备方法简单易行,制备得到的颜料橙71微胶囊增强了颜料橙71的稳定性,扩大了颜料橙71的应用空间。
Description
技术领域
本发明涉及一种微胶囊的制备方法,特别是涉及一种颜料橙71微胶囊的制备方法。
背景技术
颜料橙71在储藏过程中,随着贮藏时间的增长,颜料橙71的性质会逐渐改变。为了避免上述情况的发生,同时也为了拓展颜料橙71的应用空间,我们可以对颜料橙71进行微胶囊化。对颜料橙71进行微胶囊化后,颜料橙71的外层壁材会对颜料橙71进行一个保护,防止颜料橙71的性质发生变化,同时对颜料橙71进行微胶囊化后,颜料橙71的色彩表现力会进一步增强。
发明内容
要解决的技术问题:颜料橙71长时间放置后性质不稳定的问题。
技术方案:本发明公开了一种颜料橙71微胶囊的制备方法,制备方法包括以下步骤:(1)将颜料橙71粉末使用超微冲击磨研磨至450目~500目;(2)室温下向恒温搅拌罐中加入正己烷为90~110份;(3)取450目~500目的颜料橙71为9~14份,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为18~22份,聚乙二醇为15~17份,加入后进行搅拌,搅拌转速为100rpm,时间为3~5min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。其中,优选将颜料橙71粉末使用超微冲击磨研磨至500目;加入正己烷的量优选为90份;颜料橙71的用量优选为14份;加入丙烯酸乙酯的用量优选为22份。
有益效果:本发明的制备方法简单易行,制备的颜料橙71的微胶囊性质非常稳定,在常温下放置2年后,性质没有改变。
具体实施方式
实施例1
(1)将颜料橙71粉末使用超微冲击磨研磨至500目;(2)室温下向恒温搅拌罐中加入正己烷为110kg;(3)取500目的颜料橙71为14kg,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为18kg,聚乙二醇为15kg,加入后进行搅拌,搅拌转速为100rpm,时间为5min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。
实施例2
(1)将颜料橙71粉末使用超微冲击磨研磨至450目;(2)室温下向恒温搅拌罐中加入正己烷为100kg;(3)取450目的颜料橙71为12kg,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为20kg,聚乙二醇为17kg,加入后进行搅拌,搅拌转速为100rpm,时间为3min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。
实施例3
(1)将颜料橙71粉末使用超微冲击磨研磨至500目;(2)室温下向恒温搅拌罐中加入正己烷为90kg;(3)取500目的颜料橙71为9kg,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为22kg,聚乙二醇为16kg,加入后进行搅拌,搅拌转速为100rpm,时间为4min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。
实施例1、实施例2、实施例3制备得到的颜料橙71微胶囊在放置了2年后没有发生变化,具有良好的稳定性。
Claims (5)
1. 一种颜料橙71微胶囊的制备方法,其特征在于制备方法包括以下步骤:(1)将颜料橙71粉末使用超微冲击磨研磨至450目~500目;(2)室温下向恒温搅拌罐中加入正己烷为90~110份;(3)取450目~500目的颜料橙71为9~14份,放入恒温搅拌罐中,温度设定为40℃;(4)向搅拌罐中缓慢加入丙烯酸乙酯为18~22份,聚乙二醇为15~17份,加入后进行搅拌,搅拌转速为100rpm,时间为3~5min;(5)搅拌后将搅拌罐温度设定为65℃,待正己烷挥发干后得到颜料橙71微胶囊。
2.根据权利要求1所述的一种颜料橙71微胶囊的制备方法,其特征在于将颜料橙71粉末使用超微冲击磨研磨至500目。
3.根据权利要求1所述的一种颜料橙71微胶囊的制备方法,其特征在于加入正己烷为90份。
4.根据权利要求1所述的一种颜料橙71微胶囊的制备方法,其特征在于颜料橙71为14份。
5.根据权利要求1所述的一种颜料橙71微胶囊的制备方法,其特征在于加入丙烯酸乙酯为22份。